The tapered joints of modular hip implants are prone to fretting and crevice-corrosion. This can lead to total failure in under a year, especially for heavier, more active implant recipients. In this study, fractography of a failed Profemur Z implant…

The tapered joints of modular hip implants are prone to fretting and crevice-corrosion. This can lead to total failure in under a year, especially for heavier, more active implant recipients. In this study, fractography of a failed Profemur Z implant showed that a life limiting fatigue crack was nucleated on the anterolateral surface of the implant's neck. The fatigue crack nucleation area appeared to have both more fretting damage and a higher corrosion rate than on other surfaces of the neck.

Copyright Statement
    • Reuse Permissions
    • Downloads
    pdf (2.4 MB)

    Details

    Title
    • Fractography of a Neck Failure in a Double-Modular Hip Implant
    Contributors
    Date Created
    2014-04-08
    Resource Type
  • Text
    • Collections this item is in
    ASU Scholarship Showcase
    Identifier
    • Digital object identifier: 10.1016/j.csefa.2014.03.001
    • International standard serial number
      2213-2902

    Citation and reuse

    Cite this item

    This is a suggested citation. Consult the appropriate style guide for specific citation guidelines.

    Williams, J. J., & Chawla, N. (2014). Fractography of a neck failure in a double-modular hip implant. Case Studies in Engineering Failure Analysis, 2(1), 45-50. doi:10.1016/j.csefa.2014.03.001

    Machine-readable links