ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Filtering by
- All Subjects: Statistics
- Creators: Tamizhmani, Govindasamy
This research study focuses on the behavior of crystalline silicon PV module technology in the dry and hot climatic condition of Tempe/Phoenix, Arizona. A three-phase approach was developed: (1) A quantitative failure modes, effects, and criticality analysis (FMECA) was developed for prioritizing failure modes or mechanisms in a given environment; (2) A time-series approach was used to model environmental stress variables involved and prioritize their effect on the power output drop; and (3) A procedure for developing a prediction model was proposed for the climatic specific condition based on accelerated degradation testing
Part 1 investigates the behavior of temperature distribution of PV cells within a module through outdoor temperature monitoring under various operating conditions (Pmax, Voc and Isc) and examines deviation in the temperature coefficient values pertaining to this temperature variation. ANOVA, a statistical tool, was used to study the influence of various factors on temperature variation. This study also investigated the thermal non-uniformity affecting I-V parameters and performance of four different PV technologies (crystalline silicon, CdTe, CIGS, a-Si). Two new approaches (black-colored frame and aluminum tape on back-sheet) were implemented in addition to the two previously-used approaches (thermally insulating the frame, and frame and back sheet) to study temperature uniformity improvements within c-Si PV modules on a fixed latitude-tilt array. This thesis concludes that frame thermal insulation and black frame help reducing thermal gradients and next best viable option to improve temperature uniformity measurements is by using average of four thermocouples as per IEC 61853-2 standard.
Part 2 analyzes the temperature data for two power plants (fixed-tilt and one-axis) to study the temperature variation across the cells in a module and across the modules in a power plant. The module placed in the center of one-axis power plant had higher temperature, whereas in fixed-tilt power plant, the module in north-west direction had higher temperatures. Higher average operating temperatures were observed in one-axis tracking as compared to the fixed-tilt PV power plant, thereby expected to lowering their lifetime.
Part 3 focuses on determination of a thermal model coefficients, using parameters similar to Uc and Uv thermal loss factors used in PVsyst, for modules of four different PV technologies experiencing hot-desert climate conditions by statistically correlating a year-long monitored data. Thermal models help to effectively quantity factors influencing module temperatures to estimate performance and energy models.
Part 1 characterizes soiling losses using various techniques to understand the effect of soiling on photovoltaic modules. The higher the angle of incidence (AOI), the lower will be the photovoltaic (PV) module performance. Our research group has already reported the AOI investigation for cleaned modules of five different technologies with air/glass interface. However, the modules that are installed in the field would invariably develop a soil layer with varying thickness depending on the site condition, rainfall and tilt angle. The soiled module will have the air/soil/glass interface rather than air/glass interface. This study investigates the AOI variations on soiled modules of five different PV technologies. It is demonstrated that AOI effect is inversely proportional to the soil density. In other words, the power or current loss between clean and soiled modules would be much higher at a higher AOI than at a lower AOI leading to excessive energy production loss of soiled modules on cloudy days, early morning hours and late afternoon hours. Similarly, the spectral influence of soil on the performance of the module was investigated through reflectance and transmittance measurements. It was observed that the reflectance and transmittances losses vary linearly with soil density variation and the 600-700 nm band was identified as an ideal band for soil density measurements.
Part 2 of this thesis performs statistical risk analysis for a power plant through FMECA (Failure Mode, Effect, and Criticality Analysis) based on non-destructive field techniques and count data of the failure modes. Risk Priority Number is used for the grading guideline for criticality analysis. The analysis was done on a 19-year-old power plant in cold-dry climate to identify the most dominant failure and degradation modes. In addition, a comparison study was done on the current power plant (framed) along with another 18-year-old (frameless) from the same climate zone to understand the failure modes for cold-dry climatic condition.