ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Filtering by
- All Subjects: chemical engineering
- Creators: Li, Jian
Different heat treatments were applied to commercial Pd77Ag23 membranes to promote surface segregation. X-ray photoelectron spectroscopy (XPS) analysis indicates that the membrane surface composition changed after heat treatment. The surface area of all membranes increased after heat treatment. The higher the surface Pd/(Pd+Ag) ratio, the higher the hydrogen permeability. Surface carbon removal and surface area increase cannot explain the observed permeability differences.
Previous computational modeling predicted that Cu54Zr46 would have high hydrogen permeability. Amorphous metallic Cu-Zr (Zr=37, 54, 60 at. %) membranes were synthesized and investigated. The surface oxides may result in the lower experimental hydrogen permeability lower than that predicted by the simulations. The permeability decrease indicates that the Cu-Zr alloys crystallized in less than two hours during the test (performed at 300 °C) at temperatures below the glass transition temperature. This original experimental results show that thermal stability of amorphous metallic membranes is critical for hydrogen separation applications.
The hydrogen permeability of Ni60Nb35M5 (M=Sn, Ti and Zr) amorphous metallic membranes was investigated. Nanoindentation shows that the Young’s modulus and hardness increased after hydrogen permeability test. The structure is maintained amorphous after 24 hours of hydrogen permeability testing at 400°C. The maximum hydrogen permeability of three alloys is 10-10 mol m-1 s-1 Pa-0.5. Though these alloys exhibited a slight hydrogen permeability decreased during the test, the amorphous metallic membranes were thermally stable and did not crystalize.