ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Displaying 1 - 2 of 2
Filtering by
- Creators: Sieradzki, Karl
Description
Shock loading is a complex phenomenon that can lead to failure mechanisms such as strain localization, void nucleation and growth, and eventually spall fracture. Studying incipient stages of spall damage is of paramount importance to accurately determine initiation sites in the material microstructure where damage will nucleate and grow and to formulate continuum models that account for the variability of the damage process due to microstructural heterogeneity. The length scale of damage with respect to that of the surrounding microstructure has proven to be a key aspect in determining sites of failure initiation. Correlations have been found between the damage sites and the surrounding microstructure to determine the preferred sites of spall damage, since it tends to localize at and around the regions of intrinsic defects such as grain boundaries and triple points. However, considerable amount of work still has to be done in this regard to determine the physics driving the damage at these intrinsic weak sites in the microstructure. The main focus of this research work is to understand the physical mechanisms behind the damage localization at these preferred sites. A crystal plasticity constitutive model is implemented with different damage criteria to study the effects of stress concentration and strain localization at the grain boundaries. A cohesive zone modeling technique is used to include the intrinsic strength of the grain boundaries in the simulations. The constitutive model is verified using single elements tests, calibrated using single crystal impact experiments and validated using bicrystal and multicrystal impact experiments. The results indicate that strain localization is the predominant driving force for damage initiation and evolution. The microstructural effects on theses damage sites are studied to attribute the extent of damage to microstructural features such as grain orientation, misorientation, Taylor factor and the grain boundary planes. The finite element simulations show good correlation with the experimental results and can be used as the preliminary step in developing accurate probabilistic models for damage nucleation.
ContributorsKrishnan, Kapil (Author) / Peralta, Pedro (Thesis advisor) / Mignolet, Marc (Committee member) / Sieradzki, Karl (Committee member) / Jiang, Hanqing (Committee member) / Oswald, Jay (Committee member) / Arizona State University (Publisher)
Created2013
Description
Shock loading is a complex phenomenon that can lead to failure mechanisms such as strain localization, void nucleation and growth, and eventually spall fracture. The length scale of damage with respect to that of the surrounding microstructure has proven to be a key aspect in determining sites of failure initiation. Studying incipient stages of spall damage is of paramount importance to accurately determine initiation sites in the material microstructure where damage will nucleate and grow and to formulate continuum models that account for the variability of the damage process due to microstructural heterogeneity, which is the focus of this research. Shock loading experiments were conducted via flyer-plate impact tests for pressures of 2-6 GPa and strain rates of 105/s on copper polycrystals of varying thermomechanical processing conditions. Serial cross sectioning of recovered target disks was performed along with electron microscopy, electron backscattering diffraction (EBSD), focused ion beam (FIB) milling, and 3-D X-ray tomogrpahy (XRT) to gain 2-D and 3-D information on the spall plane and surrounding microstructure. Statistics on grain boundaries (GB) containing damage were obtained from 2-D data and GBs of misorientations 25° and 50° were found to have the highest probability to contain damage in as-received (AR), heat treated (HT), and fully recrystallized (FR) microstructures, while {111} Σ3 GBs were globally strong. The AR microstructure’s probability peak was the most pronounced indicating GB strength is the dominant factor for damage nucleation. 3-D XRT data was used to digitally render the spall planes of the AR, HT, and FR microstructures. From shape fitting the voids to ellipsoids, it was found that the AR microstructure contained greater than 55% intergranular damage, whereas the HT and FR microstructures contained predominantly transgranular and coalesced damage modes, respectively. 3-D reconstructions of large volume damage sites in shocked Cu multicrystals showed preference for damage nucleation at GBs between adjacent grains of a high Taylor factor mismatches as well as an angle between the shock direction and the GB physical normal of ~30°-45°. 3-D FIB sectioning of individual voids led to the discovery of uniform plastic zones ~25-50% the size of the void diameter and plastic deformation directions were characterized via local average misorientation maps. Incipient transgranular voids revealed from the sectioning process were present in grains of high Taylor factors along the shock direction, which is expected as materials with a low Taylor factor along the shock direction are susceptible to growth due their accomodation of plastic deformation. Fabrication of square waves using photolithography and chemical etching was developed to study the nature of plasticity at GBs away from the spall plane. Grains oriented close to <0 1 1> had half the residual amplitudes than grains oriented close to <0 0 1>.
ContributorsBrown, Andrew (Author) / Peralta, Pedro (Committee member) / Mignolet, Marc (Committee member) / Sieradzki, Karl (Committee member) / Solanki, Kiran (Committee member) / Jiang, Hanqing (Committee member) / Arizona State University (Publisher)
Created2015