ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Displaying 1 - 2 of 2
Filtering by
- Creators: Mobasher, Barzin
Description
Sustainable materials and methods have achieved a pivotal role in the research plethora of the new age due to global warming. Cement production is responsible in contributing to 5% of global CO2 emissions. Complete replacement of cement by alkaline activation of aluminosilicate waste materials such as slag and fly ash is a major advancement towards reducing the adverse impacts of cement production. Comprehensive research has been done, to understand the optimized composition and hydration products. The focus of this dissertation is to understand the multiscale behavior ranging from early age properties, fundamental material structure, fracture and crack resistance properties, durability responses and alternative activation methods to existing process.
The utilization of these materials has relied primarily on the dual benefits of reduced presence in landfills and cost. These have also proven to yield a higher service life as opposed to conventional ordinary portland cement (OPC) concrete due to an enhanced microstructure. The use of such materials however has not been readily acceptable due to detrimental early age behavior. The influence of design factors is studied to understand the reaction mechanism. Silicon polymerization at the molecular level is studied to understand the aluminosilicate interactions which are responsible for prevention of any leaching of ions. A comparative study between fly ash and slag binders is carried out to evaluate the stable states of sodium, aluminum and silicon in both these binders, since the likelihood of the sodium ions leaching out is high.
Compressive and flexural strength have been reported in previous literature, but the impact of crack resistance was unevaluated from an approach of characterizing the fracture process zone. Alternative routes of activation are explored with an intent to reduce the high alkalinity by use of neutral salts such as sodium sulfate. High volume OPC replacement by both class C and F fly ash is performed to evaluate the differences in hydration phase formation responsible for its pore refinement and strength. Spectroscopic studies have also allowed to study the fundamental material structure. Durability studies are also performed on these samples to understand the probability external sulfate attacks as opposed to OPC mixes.
The utilization of these materials has relied primarily on the dual benefits of reduced presence in landfills and cost. These have also proven to yield a higher service life as opposed to conventional ordinary portland cement (OPC) concrete due to an enhanced microstructure. The use of such materials however has not been readily acceptable due to detrimental early age behavior. The influence of design factors is studied to understand the reaction mechanism. Silicon polymerization at the molecular level is studied to understand the aluminosilicate interactions which are responsible for prevention of any leaching of ions. A comparative study between fly ash and slag binders is carried out to evaluate the stable states of sodium, aluminum and silicon in both these binders, since the likelihood of the sodium ions leaching out is high.
Compressive and flexural strength have been reported in previous literature, but the impact of crack resistance was unevaluated from an approach of characterizing the fracture process zone. Alternative routes of activation are explored with an intent to reduce the high alkalinity by use of neutral salts such as sodium sulfate. High volume OPC replacement by both class C and F fly ash is performed to evaluate the differences in hydration phase formation responsible for its pore refinement and strength. Spectroscopic studies have also allowed to study the fundamental material structure. Durability studies are also performed on these samples to understand the probability external sulfate attacks as opposed to OPC mixes.
ContributorsDakhane, Akash (Author) / Neithalath, Narayanan (Thesis advisor) / Rajan, Subramaniam D. (Committee member) / Mobasher, Barzin (Committee member) / Marzke, Robert (Committee member) / Das, Sumanta (Committee member) / Arizona State University (Publisher)
Created2016
Description
There has been a renewed interest to understand the degradation mechanism of concrete under radiation as many nuclear reactors are reaching their expiration date. Much of the information on the degradation mechanism of concrete under radiation comes from the experiments, which are carried out on very small specimens. With the advent of finite element analysis, a numerical predictive tool is desired that can predict the extent of damage in the nuclear concrete structure.
A mesoscale micro-structural framework is proposed in Multiphysics Object-Oriented Simulation Environment (MOOSE) finite element framework which represents the first step in this direction. As part of the framework, a coupled creep damage algorithm was developed and implemented in MOOSE. The algorithm considers creep through rheological models, while damage evolves exponentially as a function of elastic strain and creep strain. A characteristic length is introduced in the formulation such that the energy release rate associated with each element remains the same to avoid vanishing energy dissipation with mesh refinement. A creep damage parameter quantifies the effect of creep strain on the damage that was calibrated using three-point bending experiments with varying rates of loading.
The creep damage model was also validated with restrained ring shrinkage tests on cementitious materials containing compliant/stiff inclusions subjected to variable drying conditions. The simulation approach explicitly considers: (i) moisture diffusion driven differential shrinkage along the depth of the specimen (ii) viscoelastic response of aging cementitious materials (iii) isotropic damage model with Rankine′s failure initiation criterion, and (iv) random distribution of tensile strengths of individual finite elements.
The model was finally validated with experimental results on neutron-irradiated concrete. The simulation approach considers: (i) coupled hygro-thermal model to predict the temperature and humidity profile inside the specimen (ii) radiation-induced volumetric expansion of aggregates (RIVE) (iii) thermal, shrinkage and creep effects based on the temperature and humidity profile and (iv) isotropic damage model with Rankine’s criterion to determine failure initiation.
A mesoscale micro-structural framework is proposed in Multiphysics Object-Oriented Simulation Environment (MOOSE) finite element framework which represents the first step in this direction. As part of the framework, a coupled creep damage algorithm was developed and implemented in MOOSE. The algorithm considers creep through rheological models, while damage evolves exponentially as a function of elastic strain and creep strain. A characteristic length is introduced in the formulation such that the energy release rate associated with each element remains the same to avoid vanishing energy dissipation with mesh refinement. A creep damage parameter quantifies the effect of creep strain on the damage that was calibrated using three-point bending experiments with varying rates of loading.
The creep damage model was also validated with restrained ring shrinkage tests on cementitious materials containing compliant/stiff inclusions subjected to variable drying conditions. The simulation approach explicitly considers: (i) moisture diffusion driven differential shrinkage along the depth of the specimen (ii) viscoelastic response of aging cementitious materials (iii) isotropic damage model with Rankine′s failure initiation criterion, and (iv) random distribution of tensile strengths of individual finite elements.
The model was finally validated with experimental results on neutron-irradiated concrete. The simulation approach considers: (i) coupled hygro-thermal model to predict the temperature and humidity profile inside the specimen (ii) radiation-induced volumetric expansion of aggregates (RIVE) (iii) thermal, shrinkage and creep effects based on the temperature and humidity profile and (iv) isotropic damage model with Rankine’s criterion to determine failure initiation.
ContributorsSaklani, Naman (Author) / Neithalath, Narayanan (Thesis advisor) / Rajan, Subramanian (Committee member) / Mobasher, Barzin (Committee member) / Hoover, Christian (Committee member) / Chawla, Nikhilesh (Committee member) / Arizona State University (Publisher)