This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Alkali activated mine tailing-slag blends and mine tailing-cement blends containing mine tailings as the major binder constituent are evaluated for their setting time behavior,
reactivity properties, flow characteristics, and compressive strengths. Liquid sodium
silicate and sodium hydroxide are used as the activator solution. The effects of varying
alkali oxide-to-powder ratio…
Alkali activated mine tailing-slag blends and mine tailing-cement blends containing mine tailings as the major binder constituent are evaluated for their setting time behavior,
reactivity properties, flow characteristics, and compressive strengths. Liquid sodium
silicate and sodium hydroxide are used as the activator solution. The effects of varying
alkali oxide-to-powder ratio (n value) and silicon oxide-to-alkali oxide ratio (Ms value) is
explored. The reactivity of all blends prepared in this study is studied using an isothermal
calorimeter. Mine tailing-cement blends show a higher initial heat release peak than mine
tailing-slag blends, whereas their cumulative heat release is comparable for higher n values
of 0.050 to 0.100. Compressive strength tests and rheological studies were done for the
refined blends selected based on setting time criterion. Setting times and compressive
strengths are found to depend significantly on the activator parameters and binder
compositions, allowing fine-tuning of the mix proportion parameters based on the intended
end applications. The compressive strength of the selected mine tailing-slag blends and
mine tailing-cement blends are in the range of 7-40 MPa and 4-11 MPa, respectively.
Higher compressive strength is generally achieved at lower Ms and higher n values for mine
tailing-slag blends, while a higher Ms yields better compressive strength in the case of mine
tailing-cement blends. Rheological studies indicate a decrease in yield stress and viscosity
with increase in the replacement ratio, while a higher activator concentration increase both.
Oscillatory shear studies were used to evaluate the storage modulus and loss modulus of
the mine tailing binders. The paste is seen to exhibit a more elastic behavior at n values of
0.05 and 0.075, however the viscous behavior is seen to dominate at higher n value of 0.1
at similar replacement ratios and Ms value. A higher Ms value is also seen to increase the
onset point of the drop in both the storage and loss modulus of the pastes. The studied also
investigated the potential use of mine tailing blends for coating applications. The pastes
with higher alkalinity showed a lesser crack percentage, with a 10% slag replacement ratio
having a better performance compared to 20% and 30% slag replacement ratios. Overall,
the study showed that the activation parameters and mine tailings replacement level have
a significant influence on the properties of both mine tailing-slag binders and mine tailing-cement binders, thereby allowing selection of suitable mix design for the desired end
application, allowing a sustainable approach to dispose the mine tailings waste