ASU Electronic Theses and Dissertations

A recent joint study by Arizona State University and the Arizona Department of Transportation (ADOT) was conducted to evaluate certain Warm Mix Asphalt (WMA) properties in the laboratory. WMA material was taken from an actual ADOT project that involved two WMA sections. The first section used a foamed-based WMA admixture, and the second section used a chemical-based WMA admixture. The rest of the project included control hot mix asphalt (HMA) mixture. The evaluation included testing of field-core specimens and laboratory compacted specimens. The laboratory specimens were compacted at two different temperatures; 270 °F (132 °C) and 310 °F (154 °C). The experimental plan included four laboratory tests: the dynamic modulus (E*), indirect tensile strength (IDT), moisture damage evaluation using AASHTO T-283 test, and the Hamburg Wheel-track Test. The dynamic modulus E* results of the field cores at 70 °F showed similar E* values for control HMA and foaming-based WMA mixtures; the E* values of the chemical-based WMA mixture were relatively higher. IDT test results of the field cores had comparable finding as the E* results. For the laboratory compacted specimens, both E* and IDT results indicated that decreasing the compaction temperatures from 310 °F to 270 °F did not have any negative effect on the material strength for both WMA mixtures; while the control HMA strength was affected to some extent. It was noticed that E* and IDT results of the chemical-based WMA field cores were high; however, the laboratory compacted specimens results didn't show the same tendency. The moisture sensitivity findings from TSR test disagreed with those of Hamburg test; while TSR results indicated relatively low values of about 60% for all three mixtures, Hamburg test results were quite excellent. In general, the results of this study indicated that both WMA mixes can be best evaluated through field compacted mixes/cores; the results of the laboratory compacted specimens were helpful to a certain extent. The dynamic moduli for the field-core specimens were higher than for those compacted in the laboratory. The moisture damage findings indicated that more investigations are needed to evaluate moisture damage susceptibility in field.

Bio-modification of asphalt binder brings significant benefits in terms of increasing sustainable and environmental practices, stabilizing prices, and decreasing costs. However, bio-modified asphalt binders have shown varying performance regarding susceptibility to moisture damage; some bio-oil modifiers significantly increase asphalt binder's susceptibility to moisture damage. This variability in performance is largely due to the large number of bio-masses available for use as sources of bio-oil, as well as the type of processing procedure followed in converting the bio-mass into a bio-oil for modifying asphalt binder. Therefore, there is a need for a method of properly evaluating the potential impact of a bio-oil modifier for asphalt binder on the overall performance of asphalt pavement, in order to properly distinguish whether a particular bio-oil modifier increases or decreases the moisture susceptibility of asphalt binder. Therefore, the goal of this study is a multi-scale investigation of bio-oils with known chemical compositions to determine if there is a correlation between a fundamental property of a bio-oil and the resulting increase or decrease in moisture susceptibility of a binder when it is modified with the bio-oil. For instance, it was found that polarizability of asphalt constituents can be a promising indicator of moisture susceptibility of bitumen. This study will also evaluate the linkage of the fundamental property to newly developed binder-level test methods. It was found that moisture-induced shear thinning of bitumen containing glass beads can differentiate moisture susceptible bitumen samples. Based on the knowledge determined, alternative methods of reducing the moisture susceptibility of asphalt pavement will also be evaluated. It was shown that accumulation of acidic compounds at the interface of bitumen and aggregate could promote moisture damage. It was further found that detracting acidic compounds from the interface could be done by either of neutralizing active site of stone aggregate to reduce affinity for acids or by arresting acidic compounds using active mineral filler. The study results showed there is a strong relation between composition of bitumen and its susceptibility to moisture. This in turn emphasize the importance of integrating knowledge of surface chemistry and bitumen composition into the pavement design and evaluation.