ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Displaying 1 - 3 of 3
Filtering by
- All Subjects: Shrinkage
- All Subjects: Iron compounds
- Creators: Mobasher, Barzin
Description
Early-age cracks in fresh concrete occur mainly due to high rate of surface evaporation and restraint offered by the contracting solid phase. Available test methods that simulate severe drying conditions, however, were not originally designed to focus on evaporation and transport characteristics of the liquid-gas phases in a hydrating cementitious microstructure. Therefore, these tests lack accurate measurement of the drying rate and data interpretation based on the principles of transport properties is limited. A vacuum-based test method capable of simulating early-age cracks in 2-D cement paste is developed which continuously monitors the weight loss and changes to the surface characteristics. 2-D crack evolution is documented using time-lapse photography. Effects of sample size, w/c ratio, initial curing and fiber content are studied. In the subsequent analysis, the cement paste phase is considered as a porous medium and moisture transport is described based on surface mass transfer and internal moisture transport characteristics. Results indicate that drying occurs in two stages: constant drying rate period (stage I), followed by a falling drying rate period (stage II). Vapor diffusion in stage I and unsaturated flow within porous medium in stage II determine the overall rate of evaporation. The mass loss results are analyzed using diffusion-based models. Results show that moisture diffusivity in stage I is higher than its value in stage II by more than one order of magnitude. The drying model is used in conjunction with a shrinkage model to predict the development of capillary pressures. Similar approach is implemented in drying restrained ring specimens to predict 1-D crack width development. An analytical approach relates diffusion, shrinkage, creep, tensile and fracture properties to interpret the experimental data. Evaporation potential is introduced based on the boundary layer concept, mass transfer, and a driving force consisting of the concentration gradient. Effect of wind velocity is reflected on Reynolds number which affects the boundary layer on sample surface. This parameter along with Schmidt and Sherwood numbers are used for prediction of mass transfer coefficient. Concentration gradient is shown to be a strong function of temperature and relative humidity and used to predict the evaporation potential. Results of modeling efforts are compared with a variety of test results reported in the literature. Diffusivity data and results of 1-D and 2-D image analyses indicate significant effects of fibers on controlling early-age cracks. Presented models are capable of predicting evaporation rates and moisture flow through hydrating cement-based materials during early-age drying and shrinkage conditions.
ContributorsBakhshi, Mehdi (Author) / Mobasher, Barzin (Thesis advisor) / Rajan, Subramaniam D. (Committee member) / Zapata, Claudia E. (Committee member) / Arizona State University (Publisher)
Created2011
Description
Increased priority on the minimization of environmental impacts of conventional construction materials in recent years has motivated increased use of waste materials or bi-products such as fly ash, blast furnace slag with a view to reduce or eliminate the manufacturing/consumption of ordinary portland cement (OPC) which accounts for approximately 5-7% of global carbon dioxide emission. The current study explores, for the first time, the possibility of carbonating waste metallic iron powder to develop carbon-negative sustainable binder systems for concrete. The fundamental premise of this work is that metallic iron will react with aqueous CO2 under controlled conditions to form complex iron carbonates which have binding capabilities. The compressive and flexural strengths of the chosen iron-based binder systems increase with carbonation duration and the specimens carbonated for 4 days exhibit mechanical properties that are comparable to those of companion ordinary portland cement systems. The optimal mixture proportion and carbonation regime for this non-conventional sustainable binder is established based on the study of carbonation efficiency of a series of mixtures using thermogravimetric analysis. The pore- and micro-structural features of this novel binding material are also evaluated. The fracture response of this novel binder is evaluated using strain energy release rate and measurement of fracture process zone using digital image correlation (DIC). The iron-based binder system exhibits significantly higher strain energy release rates when compared to those of the OPC systems in both the unreinforced and glass fiber reinforced states. The iron-based binder also exhibits higher amount of area of fracture process zone due to its ability to undergo inelastic deformation facilitated by unreacted metallic iron particle inclusions in the microstructure that helps crack bridging /deflection. The intrinsic nano-mechanical properties of carbonate reaction product are explored using statistical nanoindentation technique coupled with a stochastic deconvolution algorithm. Effect of exposure to high temperature (up to 800°C) is also studied. Iron-based binder shows significantly higher residual flexural strength after exposure to high temperatures. Results of this comprehensive study establish the viability of this binder type for concrete as an environment-friendly and economical alternative to OPC.
ContributorsDas, Sumanta (Author) / Neithalath, Narayanan (Thesis advisor) / Rajan, S.D. (Committee member) / Mobasher, Barzin (Committee member) / Marzke, Robert (Committee member) / Chawla, Nikhilesh (Committee member) / Stone, David (Committee member) / Arizona State University (Publisher)
Created2015
Description
Concrete develops strength rapidly after mixing and is highly influenced by temperature and curing process. The material characteristics and the rate of property development, along with the exposure conditions influences volume change mechanisms in concrete, and the cracking propensity of the mixtures. Furthermore, the structure geometry (due to restraint as well as the surface area-to-volume ratio) also influences shrinkage and cracking. Thus, goal of this research is to better understand and predict shrinkage cracking in concrete slab systems under different curing conditions. In this research, different concrete mixtures are evaluated on their propensity to shrink based on free shrinkage and restrained shrinkage tests.Furthermore, from the data obtained from restrained ring test, a casted slab is measured for shrinkage. Effects of different orientation of restraints are studied and compared to better understand the shrinking behavior of the concrete mixtures. The results show that the maximum shrinkage is near the edges of the slab and decreases towards the center. Shrinkage near the edges with no restraint is found out to be more than the shrinkage towards the edges with restraining effects.