ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Filtering by
- All Subjects: Materials Science
The crack tip, which presents a preferential trap site for hydrogen segregation, was examined using atomistic methods and the continuum based Rice-Thompson criterion as sufficient concentration of hydrogen can alter the crack tip deformation mechanism. Results suggest that there is a plausible co-existence of the adsorption induced dislocation emission and hydrogen enhanced decohesion mechanisms. In the case of GB-hydrogen interaction, we observed that the segregation of hydrogen along the interface leads to a reduction in cohesive strength resulting in intergranular failure. A methodology was further developed to quantify the role of the GB structure on this behavior.
GBs play a fundamental role in determining the strengthening mechanisms acting as an impediment to the dislocation motion; however, the presence of an unsurmountable barrier for a dislocation can generate slip localization that could further lead to intergranular crack initiation. It was found that the presence of hydrogen increases the strain energy stored within the GB which could lead to a transition in failure mode. Finally, in the case of body centered cubic metals, understanding the complex screw dislocation motion is critical to the development of an accurate continuum description of the plastic behavior. Further, the presence of hydrogen has been shown to drastically alter the plastic deformation, but the precise role of hydrogen is still unclear. Thus, the role of hydrogen on the dislocation mobility was examined using density functional theory and atomistic simulations. Overall, this dissertation provides a novel atomic-scale understanding of the HE mechanism and development of multiscale tools for future endeavors.
Bicrystal samples were shock loaded using flyer-plates via light gas gun and direct laser ablation. Stress, pulse duration, and crystal orientation along the shock direction were varied for a fixed boundary misorientation to determine thresholds for void nucleation and coalescence as functions of these parameters. Pressures for gas gun experiments ranged from 2 to 5 GPa, while pressures for laser ablation experiments varied from 17 to 25 GPa. Samples were soft recovered to perform damage characterization using electron backscattering diffraction (EBSD) and Scanning Electron Microscopy (SEM). Results showed a 14% difference in the thresholds for void nucleation and coalescence between samples with different orientations along the shock direction, which were affected by pulse duration and stress level. Fractography on boundaries with strong damage localization showed many small voids, indicating they experience rapid nucleation, causing early coalescence. Composition analysis was also performed to determine the effect of impurities on damage evolution. Results showed that higher levels of impurities led to more damage. ABAQUS/Explicit models were developed to simulate flyer-plate impact and void growth with the same crystal orientations and experimental conditions. Results are able to match the damage seen in each grain of the target experimentally. The Taylor Factor mismatch at the boundary can also be observed in the model with the higher Taylor Factor grain exhibiting more damage.