ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Filtering by
- All Subjects: nanotechnology
- Creators: Smith, David J.
First, the recombination mechanisms in polytype GaAs nanowires are studied through photoluminescence measurements coupled with rate equation analysis. When photons are absorbed in polytype nanowires, electrons and holes quickly thermalize to the band-edges of the zinc-blende and wurtzite phases, recombining indirectly in space across the type-II offset. Using a rate equation model, different configurations of polytype defects along the nanowire are investigated, which compare well with experiment considering spatially indirect recombination between different polytypes, and defect-related recombination due to twin planes and other defects. The presented analysis is a path towards predicting the performance of nanowire-based solar cells.
Following this topic, the optical mechanisms in silicon nanopillar arrays are investigated using full-wave optical simulations in comparison to measured reflectance data. The simulated electric field energy density profiles are used to elucidate the mechanisms contributing to the reduced front surface reflectance. Strong forward scattering and resonant absorption are observed for shorter- and longer- aspect ratio nanopillars, respectively, with the sub-wavelength periodicity causing additional diffraction. Their potential for light-trapping is investigated using full-wave optical simulation of an ultra-thin nanostructured substrate, where the conventional light-trapping limit is exceeded for near-bandgap wavelengths.
Finally, the correlation between the optical properties of silicon nanoparticle layers to their respective pore size distributions is investigated using optical and structural characterization coupled with full-wave optical simulation. The presence of
scattering is experimentally correlated to wider pore size distributions obtained from nitrogen adsorption measurements. The correlation is validated with optical simulation of random and clustered structures, with the latter approximating experimental. Reduced structural inhomogeneity in low-refractive-index nanoparticle inter-layers at the metal/semiconductor interface improves their performance as back reflectors, while reducing parasitic absorption in the metal.
To better understand film stress and NP adhesion, chemical bonding analyses were performed for samples annealed up to 900 °C. Analysis revealed that about 50% of the NP surfaces are functionalized by hydroxyl (-OH) groups, providing for hydrogen bonding. Ellipsometric porosimetry was used to further understand the mechanical properties by providing a measure of strain upon capillary pressure from filling pores. Upon annealing to 200 °C, the films lost water resulting in closer bonding of NPs and higher Young’s modulus. Upon further annealing up to 900 °C, the films lost hydroxyl bonds while gaining siloxane bonds, reducing Young’s modulus. The application of ellipsometric porosimetry to hydrophilic coatings brings into question the validity of pore size distribution calculations for materials that hold onto water molecules and result in generally smaller calculated pore sizes.
Doped hydrogenated microcrystalline silicon was grown on crystalline silicon NPs, as a test case of an application for NP films to reduce parasitic absorption in silicon heterojunction solar cells. Parasitic absorption of blue light could be reduced because microcrystalline silicon has a mix of direct and indirect bandgap, giving lower blue absorption than amorphous silicon. Using Ultraviolet Raman spectroscopy, the crystallinity of films as thin as 13 nm was determined rapidly (in 1 minute) and non-destructively. A mono-layer of nanocrystals was applied as seeds for p-doped microcrystalline silicon growth and resulted in higher crystallinity films. Applications of the method could be explored for other nanocrystalline materials.