This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Filtering by
- All Subjects: Physics
polarization and interface geometry is presented. The 3D model gives the same intrinsic
spin polarization and superconducting gap dependence as the 1D model. This
demonstrates that the 1D model can be use to t 3D data.
Using this model, a Heusler alloy is investigated. Andreev reflection measurements
show that the spin polarization is 80% in samples sputtered on unheated MgO(100)
substrates and annealed at high temperatures. However, the spin polarization is
considerably smaller in samples deposited on heated substrates.
Ferromagnetic FexSix alloys have been proposed as potential spin injectors into
silicon with a substantial spin polarization. Andreev Reflection Spectroscopy (ARS) is
utilized to determine the spin polarization of both amorphous and crystalline Fe65Si35
alloys. The amorphous phase has a significantly higher spin polarization than that of
the crystalline phase.
In this thesis, (1111) Fe SmO0:82F0:18FeAs and Pb superconductors are used to
measure the spin polarization of a highly spin-polarized material, La0:67Sr0:33MnO3.
Both materials yield the same intrinsic spin polarization, therefore, Fe-superconductors
can be used in ARS. Based on the behavior of the differential conductance for highly
spin polarized LSMO and small polarization of Au, it can be concluded that the Fe-Sc
is not a triplet superconductor.
Zero bias anomaly (ZBA), in point contact Andreev reflection (PCAR), has been
utilized as a characteristic feature to reveal many novel physics. Complexities at a
normal metal/superconducting interface often cause nonessential ZBA-like features,
which may be mistaken as ZBA. In this work, it is shown that an extrinsic ZBA,
which is due to the contact resistance, cannot be suppressed by a highly spin-polarized
current while a nonessential ZBA cannot be affected the contact resistance.
Finally, Cu/Cu multilayer GMR structures were fabricated and the GMR% measured
at 300 K and 4.5 K gave responses of 63% and 115% respectively. Not only
do the GMR structures have a large enhancement of resistance, but by applying an
external magnetic eld it is shown that, unlike most materials, the spin polarization
can be tuned to values of 0.386 to 0.415 from H = 0 kOe to H = 15 kOe.
Anomalous Hall effect (AHE) is an effective way to study the properties of magnetic structures. The scattering of electrons by the magnetic moments affects the change of resistance, which can be used to detect the magnetization. In this dissertation, AHE is used to study the perpendicular magnetic anisotropy (PMA) structures, including Co/Pt and Ta/CoFeB/MgO.
Domain walls exist in all ferromagnetic materials. This dissertation studies the domain wall movement in the Ta/CoFeB/MgO structure. A single domain is observed by measuring the anomalous Hall effect. On the other hand, a zero Hall step is successfully observed in a single layer of magnetic material for the first time, which can be used to fabricate advanced domain wall spintronics devices.
Besides the normal ferromagnetic material, the generation of spin polarized current in superconductor is also important for Spintronics. The electrons in superconductors form Cooper pairs. In this dissertation, Andreev Reflection Spectroscopy (ARS) is used to study the spin configuration in Cooper pairs.
Generally, ferromagnetism and superconductivity can not co-exist. In this dissertation, the Bi/Ni bilayer structure has been studied with ARS, and the measurement results show a triplet superconductivity below 4K. The appearance of superconductivity is believed to be attributed to the Bi-Ni interface, and the triplet Cooper pair makes it a promising candidate in superconducting spintronics.
Besides, a Bi3Ni single crystal is also studied with ARS. The measurements show a singlet superconductivity in this material, which further proves the importance of the Bi/Ni interface to achieve triplet superconductivity.
Finally, ARS is also used to study NbSe2 monolayer, a 2D superconductor. The monolayer is verified by the measurements of critical temperature and critical field, which are different from the values of multilayer or bulk. Andreev reflection results show that NbSe2 monolayer is a singlet superconductor and there is no node exist in the superconducting gap for a in plane magnetic field up to 58 kOe.
Layers of gallium phosphide (GaP) grown on silicon (Si) substrates were characterized by TEM and aberration-corrected scanning transmission electron microscopy (AC-STEM). High defect densities were observed for samples with GaP layer thicknesses 250nm and above. Anti-phase boundaries (APBs) within the GaP layers were observed at interfaces with the Si surfaces which were neither atomically flat nor abrupt, contradicting conventional understanding of APB formation.
Microcrystalline-Si (μc-Si) layers grown on crystalline-Si (c-Si) substrates were investigated. Without nanoparticle seeding, an undesired amorphous-Si (a-Si) layer grew below the μc-Si layer. With seeding, the undesired a-Si layer grew above the μc-Si layer, but μc-Si growth proceeded immediately at the c-Si surface. Ellipsometry measurements of percent crystallinity did not match TEM images, but qualitative agreement was found between TEM results and Ultraviolet Raman spectroscopy.
TEM and Xray spectroscopy were used to study metal-induced crystallization and layer exchange for aluminum/ germanium (Al/Ge). Only two samples definitively exhibited both Ge crystallization and layer exchange, and neither process was complete in either sample. The results were finally considered as inconclusive since no reliable path towards layer exchange and crystallization was established.
Plan-view TEM images of indium arsenide (InAs) quantum dots with gallium arsenide antimonide (GaAsSb) spacer layers revealed the termination of some threading dislocations in a sample with spacer-layer thicknesses of 2nm, while a sample with 15-nm-thick spacer layers showed a dense, cross-hatched pattern. Cross-sectional TEM images of samples with 5-nm and 10-nm spacer-layer thicknesses showed less layer undulation in the latter sample. These observations supported photoluminescence (PL) and Xray diffraction (XRD) results, which indicated that GaAsSb spacer layers with 10-nm thickness yielded the highest quality material for photovoltaic device applications.
a-Si/c-Si samples treated by hydrogen plasma were investigated using high-resolution TEM. No obvious structural differences were observed that would account for the large differences measured in minority carrier lifetimes. This key result suggested that other factors such as point defects, hydrogen content, or interface charge must be affecting the lifetimes.