ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Displaying 1 - 10 of 280
Filtering by
Description
The connection between Hollywood costume design and the films of the 007/James Bond franchise, especially in regards to the changing perspective of the “Bond Girl”, is an intricate relationship that has previously been little researched. In the most recent Bond films, in particular, the female characters have become more powerful than the early characters and their roles within the narratives have changed with their characters taking on stronger and more integral roles. This thesis seeks to examine the films of the 007/James Bond franchise and how the rhetoric of the franchise’s costume design affects the representation of femininity and power in regards to the Bond Girls. After an overview of Bond history and costume theory, two films are analyzed as case studies: Dr. No (1962) which marks the beginning of the film franchise and Casino Royale (2006), which marks the more recent turn the films have taken. This thesis examines how the representations of Bond Girls and the use of costume design for their characters have changed over the course of the franchise from the days of Sean Connery to the recent reboot of the franchise with Daniel Craig as 007 James Bond. In addition to an examination of Bond Girl costume design, this thesis considers the role and influence of the costume designers. A designer’s vision of a character is derived from both the writing and the physical features of the actresses before them. Here this thesis considers how the rhetorical choices made by designers have contributed to an understanding of the relationship between femininity and power. Finally it shows how the costumes effect the power of the female characters and how the Bond Girls of today (Casino Royale) compare and/or contrast to Bond Girls of the past (Dr. No). This thesis combines the areas of feminist film theory and costume theory to provide an original rhetorical analysis of the Bond series in relation to costume design and examines the rhetorical statements made by the costume designers in their designs for the characters and how those statements influence the representations of the characters.
ContributorsSeverson, Andrea (Author) / Goggin, Maureen (Thesis advisor) / Ore, Ersula (Committee member) / Lamp, Kathleen (Committee member) / Arizona State University (Publisher)
Created2013
Description
Simultaneously culture heroes and stumbling buffoons, Tricksters bring cultural tools to the people and make the world more habitable. There are common themes in these figures that remain fruitful for the advancement of culture, theory, and critical praxis. This dissertation develops a method for opening a dialogue with Trickster figures. It draws from established literature to present a newly conceived and more flexible Trickster archetype. This archetype is more than a collection of traits; it builds on itself processually to form a method for analysis. The critical Trickster archetype includes the fundamental act of crossing borders; the twin ontologies of ambiguity and liminality; the particular tactics of humor, duplicity, and shape shifting; and the overarching cultural roles of culture hero and stumbling buffoon. Running parallel to each archetypal element, though, are Trickster's overarching critical spirit of Quixotic utopianism and underlying telos of manipulating human relationships. The character 'Q' from Star Trek: The Next Generation is used to demonstrate the critical Trickster archetype. To be more useful for critical cultural studies, Trickster figures must also be connected to their socio-cultural and historical contexts. Thus, this dissertation offers a second set of analytics, a dialogical method that connects Tricksters to the worlds they make more habitable. This dialogical method, developed from the work of M. M. Bakhtin and others, consists of three analytical tools: utterance, intertextuality, and chronotope. Utterance bounds the text for analysis. Intertextuality connects the utterance, the text, to its context. Chronotope suggests particular spatio-temporal relationships that help reveal the cultural significance of a dialogical performance. Performance artists Andre Stitt, Ann Liv Young, and Steven Leyba are used to demonstrate the method of Trickster dialogics. A concluding discussion of Trickster's unique chronotope reveals its contributions to conceptions of utopia and futurity. This dissertation offers theoretical advancements about the significance and tactics of subversive communication practices. It offers a new and unique method for cultural and performative analyses that can be expanded into different kinds of dialogics. Trickster dialogics can also be used generatively to direct and guide the further development of performative praxis.
ContributorsSalinas, Chema (Author) / de la Garza, Amira (Thesis advisor) / Carlson, Cheree (Committee member) / Olson, Clark (Committee member) / Ellsworth, Angela (Committee member) / Arizona State University (Publisher)
Created2013
Description
This study analyzes syllabi for first-year college composition courses and interview responses to examine how the choices made by instructors affect online course design. Using the Syllabus Assessment Instrument designed by Madson, Melchert and Whipp (2004), this dissertation looks specifically at attendance and participation policies, course behavior policies, contact information, required material choices, course organization decisions and tool decisions to reveal how instructors do or do not accommodate online class pedagogies. This study finds that the choices instructors make in syllabus design provide significant information about the overall online course design itself. Using Selber's multiliteracies as a frame for understanding the choices made by instructors, this study finds that instructors focus primarily on functional literacies in their discourses and in the way they communicate their choices to students. Instructors vary in how they inform students of the mechanics of how to interact with tools, how often to interact with the online course, and how to use the tools within the online course. While these aspects of online courses are important, focusing on these aspects of the online course overshadows alternative perspectives on tool use that could encourage critical reflection by both instructors and students. To help instructors and departments design more effective syllabi and courses, this study raises questions and offers observations about how instructors communicate policies and how they understand these policies and pedagogies in online courses. In providing general guidelines for syllabus design and course design, this study will help writing instructors and composition programs better understand the significance of the choices they make in online course design.
ContributorsPfannenstiel, Amber Nicole (Author) / Goggin, Peter (Thesis advisor) / Daly Goggin, Maureen (Committee member) / Hayes, Elisabeth (Committee member) / Arizona State University (Publisher)
Created2013
Description
The current research examines the influence of disciplines, advisors, committees, language, culture, and previous experiences in students' search and selection of dissertation topics, as well as whether and how students react to those influences during this process. Invention has been an area of research for rhetoricians for centuries, but most modern research focuses exclusively on the pre-writing process in first composition classrooms (Young, 1976). The current research collected survey and interview data from second- and third-year Ph.D. students in natural sciences, social sciences, and humanities at a large research university in the United States. 80 second- and third-year Ph.D. students completed an online survey; 11 students and four of their advisors participated in a semi-structured interview. The results demonstrate that the majority of students spent over three months in the selection of dissertation topics, and the humanities students tended to spend longer time in this process than social sciences or humanities students. Additionally, students have much in common in their perception of the criteria they would use in the selection of dissertation topics, and those criteria are similar to what previous researchers (Isaac, Koenigsknecht, Malaney, & Karras, 1989; Kozma, 1997; Sessions, 1971) have identified. However, when it comes to the actual selection experiences, the interviews show that students do not necessarily apply those criteria rationally. Moreover, disciplines appear to have an overarching effect on students' topic selection. Natural sciences advisors appeared to have more direct involvement in students' topic choice than advisors in social sciences or humanities. The linguistic and cultural backgrounds of the eleven doctoral participants were not found influential in their selection of dissertation topics. Finally, although Ph.D. advisors generally have a good understanding of students' academic progress, their knowledge of the students' personal and professional concerns may differ, and the latter knowledge is crucial in their advising on students' dissertation topic choice. The current study suggests invention in the scholar and researcher level is significantly different from that of first-year composition classrooms. The successful invention of dissertation topics is indispensable of the influence of disciplines, programs as well as the intellectual and practical support students can receive.
ContributorsXia, Jing (Author) / Matsuda, Paul K (Thesis advisor) / James, Mark (Committee member) / Renaud, Claire (Committee member) / Arizona State University (Publisher)
Created2013
Description
After a decade of efforts, accurate and affordable DNA sequencing continues to remain an important goal in current research landscape. This thesis starts with a brief overview of the recent updates in the field of DNA sequencing technologies followed by description of the nanofluidics route to single molecule DNA detection. Chapter 2 presents discusses carbon nanotube(CNT) based nanofluidics. The fabrication and DNA sensing measurements of CNT forest membrane devices are presented. Chapter 3 gives the background for functionalization and recognition aspects of reader molecules. Chapter 4 marks the transition to solid state nanopore nanofluidics. The fabrication of Imidazole functionalized nanopores is discussed. The Single Molecule detection results of DNA from Palladium nanopore devices are presented next. Combining chemical recognition to nanopore technology, it has been possible to prolong the duration of single molecule events from the order of a few micro seconds to upto a few milliseconds. Overall, the work presented in this thesis promises longer single molecule detection time in a nanofludic set up and paves way for novel nanopore- tunnel junction devices that combine recognition chemistry, tunneling device and nanopore approach.
ContributorsKrishnakumar, Padmini (Author) / Lindsay, Stuart (Thesis advisor) / He, Jin (Committee member) / Vaiana, Sara (Committee member) / Schmidt, Kevin (Committee member) / Arizona State University (Publisher)
Created2013
Description
The thesis studies new methods to fabricate optoelectronic Ge1-ySny/Si(100) alloys and investigate their photoluminescence (PL) properties for possible applications in Si-based photonics including IR lasers. The work initially investigated the origin of the difference between the PL spectrum of bulk Ge, dominated by indirect gap emission, and the PL spectrum of Ge-on-Si films, dominated by direct gap emission. It was found that the difference is due to the supression of self-absorption effects in Ge films, combined with a deviation from quasi-equilibrium conditions in the conduction band of undoped films. The latter is confirmed by a model suggesting that the deviation is caused by the shorter recombination lifetime in the films relative to bulk Ge. The knowledge acquired from this work was then utilized to study the PL properties of n-type Ge1-ySny/Si (y=0.004-0.04) samples grown via chemical vapor deposition of Ge2H6/SnD4/P(GeH3)3. It was found that the emission intensity (I) of these samples is at least 10x stronger than observed in un-doped counterparts and that the Idir/Iind ratio of direct over indirect gap emission increases for high-Sn contents due to the reduced gamma-L valley separation, as expected. Next the PL investigation was expanded to samples with y=0.05-0.09 grown via a new method using the more reactive Ge3H8 in place of Ge2H6. Optical quality, 1-um thick Ge1-ySny/Si(100) layers were produced using Ge3H10/SnD4 and found to exhibit strong, tunable PL near the threshold of the direct-indirect bandgap crossover. A byproduct of this study was the development of an enhanced process to produce Ge3H8, Ge4H10, and Ge5H12 analogs for application in ultra-low temperature deposition of Group-IV semiconductors. The thesis also studies synthesis routes of an entirely new class of semiconductor compounds and alloys described by Si5-2y(III-V)y (III=Al, V= As, P) comprising of specifically designed diamond-like structures based on a Si parent lattice incorporating isolated III-V units. The common theme of the two thesis topics is the development of new mono-crystalline materials on ubiquitous silicon platforms with the objective of enhancing the optoelectronic performance of Si and Ge semiconductors, potentially leading to the design of next generation optical devices including lasers, detectors and solar cells.
ContributorsGrzybowski, Gordon (Author) / Kouvetakis, John (Thesis advisor) / Chizmeshya, Andrew (Committee member) / Menéndez, Jose (Committee member) / Arizona State University (Publisher)
Created2013
Description
The work contained in this dissertation is focused on the optical properties of direct band gap semiconductors which crystallize in a wurtzite structure: more specifically, the III-nitrides and ZnO. By using cathodoluminescence spectroscopy, many of their properties have been investigated, including band gaps, defect energy levels, carrier lifetimes, strain states, exciton binding energies, and effects of electron irradiation on luminescence. Part of this work is focused on p-type Mg-doped GaN and InGaN. These materials are extremely important for the fabrication of visible light emitting diodes and diode lasers and their complex nature is currently not entirely understood. The luminescence of Mg-doped GaN films has been correlated with electrical and structural measurements in order to understand the behavior of hydrogen in the material. Deeply-bound excitons emitting near 3.37 and 3.42 eV are observed in films with a significant hydrogen concentration during cathodoluminescence at liquid helium temperatures. These radiative transitions are unstable during electron irradiation. Our observations suggest a hydrogen-related nature, as opposed to a previous assignment of stacking fault luminescence. The intensity of the 3.37 eV transition can be correlated with the electrical activation of the Mg acceptors. Next, the acceptor energy level of Mg in InGaN is shown to decrease significantly with an increase in the indium composition. This also corresponds to a decrease in the resistivity of these films. In addition, the hole concentration in multiple quantum well light emitting diode structures is much more uniform in the active region when Mg-doped InGaN (instead of Mg-doped GaN) is used. These results will help improve the efficiency of light emitting diodes, especially in the green/yellow color range. Also, the improved hole transport may prove to be important for the development of photovoltaic devices. Cathodoluminescence studies have also been performed on nanoindented ZnO crystals. Bulk, single crystal ZnO was indented using a sub-micron spherical diamond tip on various surface orientations. The resistance to deformation (the "hardness") of each surface orientation was measured, with the c-plane being the most resistive. This is due to the orientation of the easy glide planes, the c-planes, being positioned perpendicularly to the applied load. The a-plane oriented crystal is the least resistive to deformation. Cathodoluminescence imaging allows for the correlation of the luminescence with the regions located near the indentation. Sub-nanometer shifts in the band edge emission have been assigned to residual strain the crystals. The a- and m-plane oriented crystals show two-fold symmetry with regions of compressive and tensile strain located parallel and perpendicular to the ±c-directions, respectively. The c-plane oriented crystal shows six-fold symmetry with regions of tensile strain extending along the six equivalent a-directions.
ContributorsJuday, Reid (Author) / Ponce, Fernando A. (Thesis advisor) / Drucker, Jeff (Committee member) / Mccartney, Martha R (Committee member) / Menéndez, Jose (Committee member) / Shumway, John (Committee member) / Arizona State University (Publisher)
Created2013
Description
Microwave dielectrics are widely used to make resonators and filters in telecommunication systems. The production of thin films with high dielectric constant and low loss could potentially enable a marked reduction in the size of devices and systems. However, studies of these materials in thin film form are very sparse. In this research, experiments were carried out on practical high-performance dielectrics including ZrTiO4-ZnNb2O6 (ZTZN) and Ba(Co,Zn)1/3Nb2/3O3 (BCZN) with high dielectric constant and low loss tangent. Thin films were deposited by laser ablation on various substrates, with a systematical study of growth conditions like substrate temperature, oxygen pressure and annealing to optimize the film quality, and the compositional, microstructural, optical and electric properties were characterized. The deposited ZTZN films were randomly oriented polycrystalline on Si substrate and textured on MgO substrate with a tetragonal lattice change at elevated temperature. The BCZN films deposited on MgO substrate showed superior film quality relative to that on other substrates, which grow epitaxially with an orientation of (001) // MgO (001) and (100) // MgO (100) when substrate temperature was above 500 oC. In-situ annealing at growth temperature in 200 mTorr oxygen pressure was found to enhance the quality of the films, reducing the peak width of the X-ray Diffraction (XRD) rocking curve to 0.53o and the χmin of channeling Rutherford Backscattering Spectrometry (RBS) to 8.8% when grown at 800oC. Atomic Force Microscopy (AFM) was used to study the topography and found a monotonic decrease in the surface roughness when the growth temperature increased. Optical absorption and transmission measurements were used to determine the energy bandgap and the refractive index respectively. A low-frequency dielectric constant of 34 was measured using a planar interdigital measurement structure. The resistivity of the film is ~3×1010 ohm·cm at room temperature and has an activation energy of thermal activated current of 0.66 eV.
ContributorsLi, You (Author) / Newman, Nathan (Thesis advisor) / Alford, Terry (Committee member) / Singh, Rakesh (Committee member) / Arizona State University (Publisher)
Created2013
Description
This dissertation is focused on material property exploration and analysis using computational quantum mechanics methods. Theoretical calculations were performed on the recently discovered hexahydride materials A2SiH6 (A=Rb, K) to calculate the lattice dynamics of the systems in order to check for structural stability, verify the experimental Raman and infrared spectrospcopy results, and obtain the theoretical free energies of formation. The electronic structure of the systems was calculated and the bonding and ionic properties of the systems were analyzed. The novel hexahydrides were compared to the important hydrogen storage material KSiH3. This showed that the hypervalent nature of the SiH62- ions reduced the Si-H bonding strength considerably. These hydrogen rich compounds could have promising energy applications as they link to alternative hydrogen fuel technology. The carbide systems Li-C (A=Li,Ca,Mg) were studied using \emph{ab initio} and evolutionary algorithms at high pressures. At ambient pressure Li2C2 and CaC2 are known to contain C22- dumbbell anions and CaC2 is polymorphic. At elevated pressure both CaC2 and Li2C2 display polymorphism. At ambient pressure the Mg-C system contains several experimentally known phases, however, all known phases are shown to be metastable with respect to the pure elements Mg and C. First principle investigation of the configurational space of these compounds via evolutionary algorithms results in a variety of metastable and unique structures. The binary compounds ZnSb and ZnAs are II-V electron-poor semiconductors with interesting thermoelectric properties. They contain rhomboid rings composed of Zn2Sb2 (Zn2As2) with multi-centered covalent bonds which are in turn covalently bonded to other rings via two-centered, two-electron bonds. Ionicity was explored via Bader charge analysis and it appears that the low ionicity that these materials display is a necessary condition of their multicentered bonding. Both compounds were found to have narrow, indirect band gaps with multi-valley valence and conduction bands; which are important characteristics for high thermopower in thermoelectric materials. Future work is needed to analyze the lattice properties of the II-V CdSb-type systems, especially in order to find the origin of the extremely low thermal conductivity that these systems display.
ContributorsBenson, Daryn Eugene (Author) / Häussermann, Ulrich (Thesis advisor) / Shumway, John (Thesis advisor) / Chamberlin, Ralph (Committee member) / Sankey, Otto (Committee member) / Treacy, Mike (Committee member) / Arizona State University (Publisher)
Created2013
Description
Rhetorical theorist Kenneth Burke has asserted the significance of paying equal, if not more attention to, propagandist rhetoric, arguing that "there are other ways of burning books on the pyre-and the favorite method of the hasty reviewer is to deprive himself and his readers by inattention." Despite Burke's exhortation, attention to white supremacist discourse has been relatively meager. Historians Clive Webb and Charles Eagles have called for further research on white supremacy arguing that attention to white supremacist discourse is important both to fully understand and appreciate pro-civil rights rhetoric in context and to develop a more complex understanding of white supremacist rhetoric. This thesis provides a close examination of the literature and rhetoric of two white supremacist organizations: the Citizens' Council, an organization that sprang up in response to the 1954 landmark decision of Brown v. Board of Education and Stromfront.org, a global online forum community that hosts space for supporters of white supremacy. Memory scholars Barbie Zelizer, John Bodnar, and Stephen Brown note the usability of memory to shape social, political, and cultural aspects of society and the potential implications of such shaping. Drawing from this scholarship, the analysis of these texts focuses specifically on the rhetorical shaping of memory as a vehicle to promote white supremacy. Through an analysis of the Citizens' Council's use of historical events, national figures and cultural stereotypes, Chapter 1 explicates the organization's attempt to form a memorial narrative that worked to promote political goals, create a sense of solidarity through resistance, and indoctrinate the youth in the ideology of white supremacy. Chapter 2 examines the rhetorical use of memory on Stormfront and explains how the website capitalizes upon the wide reaching global impact of World War II to construct a memorial narrative that can be accessed by a global audience of white supremacists. Ultimately, this thesis offers a focused review of the rhetorical signatures of two white supremacist groups with the aim of combating contemporary instantiations of racist discourse.
ContributorsLadenburg, Kenneth (Author) / Ore, Ersula (Thesis advisor) / Miller, Keith (Committee member) / Bebout, Lee (Committee member) / Arizona State University (Publisher)
Created2013