ASU Electronic Theses and Dissertations
This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Filtering by
- All Subjects: Creep
- All Subjects: MAT213
- Creators: Mobasher, Barzin
Double cantilever beam and end notched flexure tests were performed experimentally and through simulations to determine the delamination properties of the material at the interlaminar layers. Experimental results gave the mode I critical energy release rate as having a range of 2.18 – 3.26 psi-in and the mode II critical energy release rate as 10.50 psi-in, both for the pre-cracked condition. Simulations were performed to calibrate other cohesive zone parameters required for modeling.
Samples of tested T800/F3900 coupons were processed and examined with scanning electron microscopy to determine and understand the underlying structure of the material. Tested coupons revealed damage and failure occurring at the micro scale for the composite material.
The Creep Testing Experimental Methodology is divided into three main parts which includes: (1) The Pre-cracking Partial Fracture Test; (2) Creep Test; (3) Post Creep Full Fracture Test. The magnitude of load applied to a specific specimen during creep testing was based on the results of average residual strength (ARS) tests, determined using EN14651. Specimens of the synthetic FRC mixture were creep tested at loads nominally equivalent to 30% and 50% of the FR1 value. The creep tests are usually continued until a steady Time versus CMOD response was obtained for the specimen signifying its presence in the secondary stage of creep. The creep recovery response is generated after unloading the specimen from the creep set up and later a full fracture test is carried out to obtain the complete post creep response of the beam under flexure.
The behavior of the Creep Coefficient versus Time response has been studied using various existing models like the ACI 209-R 92 Model and the CEB-FIP Model. Basic and hybrid rheological viscoelastic models have also been used in order to generate the material behavior response. A study has been developed in order to understand the applicability of various viscoelastic models for obtaining the material response of real materials. An analytical model for predicting the Flexural Behavior of FRC under sustained creep loads is presented at the end. This model helps generate the stress strain and Moment Curvature response of FRC beams when subjected to creep loads post initial cracking