This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.
In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.
Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.
Filtering by
- All Subjects: Diatoms
- Creators: Alford, Terry
The closely-packed monolayer formation of diatom valves on silicon substrates was accomplished using their hydrodynamic properties and the surface tension of water. Valves dispersed on a hydrophobic surface were able to float-up with a preferential orientation (convex side facing the water surface) when water was added. The floating diatom monolayer was subsequently transferred to a silicon substrate. A closely-packed diatom monolayer on the silicon substrate was obtained after the water evaporated at room temperature.
The diatom monolayer was then directly bonded onto the substrate via a sintering process at high temperature in air. The percentage of bonded valves increased as the temperature increased. The valves started to sinter into the substrate at 1100°C. The sintering process caused shrinkage of the nanopores at temperatures above 1100°C. The more delicate structure was more sensitive to the elevated temperature. The cribellum, the most intricate nanostructure of the diatom (~50 nm), disappeared at 1125°C. The cribrum, consisting of approximated 100-300 nm diameter pores, disappeared at 1150°C. The areola, the micro-chamber-liked structure, can survive up to 1150°C. At 1200°C, the complete nanostructure was destroyed. In addition, cross-section images revealed that the valves fused into the thermally-grown oxide layer that was generated on the substrate at high temperatures.
The silica-sintered diatom close-packed monolayer, processed at 1125°C, was magnesiothermically converted into porous silicon using magnesium silicide. X-ray diffraction, infrared absorption, energy dispersive X-say spectra and secondary electron images confirmed the formation of a Si layer with preserved diatom nano-microstructure. The conversion process and subsequent application of a PEDOT:PSS coating both decreased the light reflection from the sample. The photocurrent and reflectance spectra revealed that the Si-diatom dominantly enhanced light absorption between 414 to 586 nm and 730 to 800 nm. Though some of the structural features disappeared during the sintering process, the diatom is still able to improve light absorption. Therefore, the sintering process can be used for diatom direct bonding in light harvesting applications.