In this study, two novel sorbents (zeolite 4A and sodium polyacrylate) are tested to investigate if utilizing ultrasonic acoustic energy could decrease the amount of time and overall energy required to regenerate these materials for use in cooling applications. To do this, an experiment was designed employing a cartridge heater and a piezoelectric element to be simultaneously providing heat and acoustic power to a custom designed desorption bed while measuring the bed mass and sorbent temperature at various locations. The results prove to be promising showing that early in the desorption process ultrasound may expedite the desorption process in zeolite by as much as five times and in sodium polyacrylate as much as three times in comparison to providing heat alone. The results also show that in zeolite desorption utilizing ultrasound may be particularly beneficial to initiate desorption whereas in sodium polyacrylate ultrasound appears most promising in the after a temperature threshold is met. These are exciting results and may prove to be significant in the future as more novel heat-based cooling cycles are developed.
ContributorsBertrand, Weston Kyle (Author) / Phelan, Patrick (Thesis advisor) / Bocanegra, Luis (Committee member) / Wang, Liping (Committee member) / Devasenathipathy, Shankar (Committee member) / Arizona State University (Publisher)
Created2018
Description
Thermodynamic development and balance of plant study is completed for a 30 MW solar thermochemical water splitting process that generates hydrogen gas and electric power. The generalized thermodynamic model includes 23 components and 45 states. Quasi-steady state simulations are completed for design point system sizing, annual performance analysis and sensitivity analysis. Detailed consideration is given to water splitting reaction kinetics with governing equations generalized for use with any redox-active metal oxide material. Specific results for Ceria illustrate particle reduction in two solar receivers for target oxygen partial pressure of 10 Pa and particle temperature of 1773 K at a design point DNI of 900 W/m2. Sizes of the recuperator, steam generator and hydrogen separator are calculated at the design point DNI to achieve 100,000 kg of hydrogen production per day from the plant. The total system efficiency of 39.52% is comprised of 50.7% hydrogen fraction and 19.62% electrical fraction. Total plant capital costs and operating costs are estimated to equate a hydrogen production cost of $4.40 per kg for a 25-year plant life. Sensitivity analysis explores the effect of environmental parameters and design parameters on system performance and cost. Improving recuperator effectiveness from 0.7 to 0.8 is a high-value design modification resulting in a 12.1% decrease in hydrogen cost for a modest 2.0% increase in plant $2.85M. At the same time, system efficiency is relatively inelastic to recuperator effectiveness because 81% of excess heat is recovered from the system for electricity production 39 MWh/day and revenue is $0.04 per kWh. Increasing water inlet pressure up to 20 bar reduces the size and cost of super heaters but further pressure rises increasing pump at a rate that outweighs super heater cost savings.
ContributorsBudama, Vishnu Kumar (Author) / Johnson, Nathan (Thesis advisor) / Stechel, Ellen (Committee member) / Rykaczewski, Konrad (Committee member) / Phelan, Patrick (Committee member) / Wang, Robert (Committee member) / Arizona State University (Publisher)
Created2018
Description
Reactive inkjet printing (RIJP) is a direct-write deposition technique that synthesizes and patterns functional materials simultaneously. It is a route to cheap fabrication of highly conductive features on a versatile range of substrates. Silver reactive inks have become a staple of conductive inkjet printing for application in printed and flexible electronics, photovoltaic metallization, and more. However, the high cost of silver makes these less effective for disposable and low-cost applications.
This work aimed to develop a particle-free formulation for a nickel reactive ink capable of metallizing highly pure nickel at temperatures under 100 °C to facilitate printing on substrates like paper or plastic. Nickel offers a significantly cheaper alternative to silver at slightly reduced bulk conductivity.
To meet these aims, three archetypes of inks were formulated. First were a set of glycerol-based inks temperature ink containing nickel acetate, hydrazine, and ammonia in a mixture of water and glycerol. This ink reduced between 115 – 200 °C to produce slightly oxidized deposits of nickel with carbon content around 10 wt %.
The high temperature was addressed in a second series, which replaced glycerol with lower boiling glycols and added sodium hydroxide as a strong base to enhance thermodynamics and kinetics of reduction. These inks reduced between 60 and 100 °C but sodium salts contaminated the final deposits.
In a third set of inks, sodium hydroxide was replaced with tetramethylammonium hydroxide (TMAH), a strong organic base, to address contamination. These inks also reduced between 60 and 100 °C. Pipetting or printing onto gold coated substrates produce metallic flakes coated in a clear, thick residue. EDS measured carbon and oxygen content up to 70 wt % of deposits. The residue was hypothesized to be a non-volatile byproduct of TMAH and acetate.
Recommendations are provided to address the residue. Ultimately the formulated reactive inks did not meet design targets. However, this thesis sets the framework to design an optimal nickel reactive ink in future work.
This work aimed to develop a particle-free formulation for a nickel reactive ink capable of metallizing highly pure nickel at temperatures under 100 °C to facilitate printing on substrates like paper or plastic. Nickel offers a significantly cheaper alternative to silver at slightly reduced bulk conductivity.
To meet these aims, three archetypes of inks were formulated. First were a set of glycerol-based inks temperature ink containing nickel acetate, hydrazine, and ammonia in a mixture of water and glycerol. This ink reduced between 115 – 200 °C to produce slightly oxidized deposits of nickel with carbon content around 10 wt %.
The high temperature was addressed in a second series, which replaced glycerol with lower boiling glycols and added sodium hydroxide as a strong base to enhance thermodynamics and kinetics of reduction. These inks reduced between 60 and 100 °C but sodium salts contaminated the final deposits.
In a third set of inks, sodium hydroxide was replaced with tetramethylammonium hydroxide (TMAH), a strong organic base, to address contamination. These inks also reduced between 60 and 100 °C. Pipetting or printing onto gold coated substrates produce metallic flakes coated in a clear, thick residue. EDS measured carbon and oxygen content up to 70 wt % of deposits. The residue was hypothesized to be a non-volatile byproduct of TMAH and acetate.
Recommendations are provided to address the residue. Ultimately the formulated reactive inks did not meet design targets. However, this thesis sets the framework to design an optimal nickel reactive ink in future work.
ContributorsDebruin, Dylan Jerome (Author) / Torres, Cesar (Thesis advisor) / Rykaczewski, Konrad (Thesis advisor) / Hildreth, Owen (Committee member) / Arizona State University (Publisher)
Created2019
Description
As experiencing hot months and thermal stresses is becoming more common, chemically protective fabrics must adapt and provide protections while reducing the heat stress to the body. These concerns affect first responders, warfighters, and workers regularly surrounded by hazardous chemical agents. While adapting traditional garments with cooling devices provides one route to mitigate this issue, these cooling methods add bulk, are time limited, and may not be applicable in locations without logistical support. Here I take inspiration from nature to guide the development of smart fabrics that have high breathability, but self-seal on exposure to target chemical(s), providing a better balance between cooling and protection.
Natural barrier materials were explored as a guide, focusing specifically on prickly pear cacti. These cacti have a natural waxy barrier that provides protection from dehydration and physically changes shape to modify surface wettability and water vapor transport. The results of this study provided a basis for a shape changing polymer to be used to respond directly to hazardous chemicals, swelling to contain the agent.
To create a stimuli responsive material, a novel superabsorbent polymer was synthesized, based on acrylamide chemistry. The polymer was tested for swelling properties in a wide range of organic liquids and found to highly swell in moderately polar organic liquids. To help predict swelling in untested liquids, the swelling of multiple test liquids were compared with their thermodynamic properties to observe trends. As the smart fabric needs to remain breathable to allow evaporative cooling, while retaining functionality when soaked with sweat, absorption of water, as well as that of an absorbing liquid in the presence of water were tested.
Micron sized particles of the developed polymer were deposited on a plastic mesh with pore size and open area similar to common clothing fabric to establish the proof of concept of using a breathable barrier to provide chemical protection. The polymer coated mesh showed minimal additional resistance to water vapor transport, relative to the mesh alone, but blocked more than 99% of a xylene aerosol from penetrating the barrier.
Natural barrier materials were explored as a guide, focusing specifically on prickly pear cacti. These cacti have a natural waxy barrier that provides protection from dehydration and physically changes shape to modify surface wettability and water vapor transport. The results of this study provided a basis for a shape changing polymer to be used to respond directly to hazardous chemicals, swelling to contain the agent.
To create a stimuli responsive material, a novel superabsorbent polymer was synthesized, based on acrylamide chemistry. The polymer was tested for swelling properties in a wide range of organic liquids and found to highly swell in moderately polar organic liquids. To help predict swelling in untested liquids, the swelling of multiple test liquids were compared with their thermodynamic properties to observe trends. As the smart fabric needs to remain breathable to allow evaporative cooling, while retaining functionality when soaked with sweat, absorption of water, as well as that of an absorbing liquid in the presence of water were tested.
Micron sized particles of the developed polymer were deposited on a plastic mesh with pore size and open area similar to common clothing fabric to establish the proof of concept of using a breathable barrier to provide chemical protection. The polymer coated mesh showed minimal additional resistance to water vapor transport, relative to the mesh alone, but blocked more than 99% of a xylene aerosol from penetrating the barrier.
ContributorsManning, Kenneth (Author) / Rykaczewski, Konrad (Thesis advisor) / Burgin, Timothy (Committee member) / Emady, Heather (Committee member) / Green, Matthew (Committee member) / Thomas, Marylaura (Committee member) / Arizona State University (Publisher)
Created2020