Matching Items (94)
Description
This work investigates the impact of wavelength-selective light trapping on photovoltaic efficiency and operating temperature, with a focus on GaAs and Si devices. A nanostructure array is designed to optimize the efficiency of a III-V narrow-band photonic power converter (PPC). Within finite-difference time-domain (FDTD) simulations, a nanotextured GaInP window layer yields a 25× path-length enhancement when integrated with a rear dielectric-metal reflector. Then, nanotexturing of GaInP is experimentally achieved with electron-beam lithography (EBL) and Cl2/Ar plasma etching. Time-resolved photoluminescence (TRPL) measurements show that the GaAs absorber lifetime does not drop due to the nanotexturing process, thus indicating a path to thinner, higher-efficiency PPCs. Next, wavelength-selective light management is examined for enhanced radiative cooling. It is shown that wavelength-selective optimizations of a module’s emissivity can yield 60-65% greater radiative cooling benefits compared to comparative changes across a broader wavelength range. State-of-the-art Si modules that utilize microtextured cover glass are shown to already achieve 99% of the radiative cooling gains that are possible for a photovoltaic device under full sunlight. In contrast, the sub-bandgap reflection (SBR) of Si modules is shown to be far below ideal. The low SBR of modules with textured Si cells (15%-26%) is shown to be the primary reason for their higher operating temperatures than modules with planar GaAs cells (SBR measured at 77%). For textured cells, typical of Si modules, light trapping amplifies parasitic absorption in the encapsulant and the rear mirror, yielding greater heat generation. Optimization of doping and the rear mirror of a Si module could increase the SBR to a maximum of 63%, with further increases available only if parasitic absorption in the encapsulation materials can be reduced. For thin films, increased heat generation may outweigh the photogeneration benefits that are possible with light trapping. These investigations motivate a wavelength-selective application of light trapping: light trapping for near- to above-bandgap photons to increase photogeneration; and out-coupling of light in mid- to far-infrared wavelengths to increase the emission of thermal radiation; but light trapping should ideally be avoided at sub-bandgap energies where there is substantial solar radiation to limit heat generation and material degradation.
ContributorsIrvin, Nicholas P. (Author) / Honsberg, Christiana B. (Thesis advisor) / King, Richard R. (Thesis advisor) / Nemanich, Robert J. (Committee member) / Smith, David J. (Committee member) / Arizona State University (Publisher)
Created2023
Description
The two-dimensional electron gas (2DEG) at SrTiO3-based oxide interfaces has been extensively studied recently for its high carrier density, high electron mobility, superconducting, ferromagnetic, ferrroelectric and magnetoresistance properties, with possible application for all-oxide devices. Understanding the mechanisms behind the 2DEG formation and factors affecting its properties is the primary objective of this dissertation.
Advanced electron microscopy techniques, including aberration-corrected electron microscopy and electron energy-loss spectroscopy (EELS) with energy-loss near-edge structure (ELNES) analysis, were used to characterize the interfaces. Image and spectrum data-processing algorithms, including subpixel atomic position measurement, and novel outlier detection by oversampling, subspace division based EELS background removal and bias-free endmember extraction algorithms for hyperspectral unmixing and mapping were heavily used. Results were compared with density functional theory (DFT) calculations for theoretical explanation.
For the γ-Al2O3/SrTiO3 system, negative-Cs imaging confirmed the formation of crystalline γ-Al2O3. ELNES hyperspectral unmixing combined with DFT calculations revealed that oxygen vacancies, rather than polar discontinuity, were the key to the 2DEG formation. The critical thickness can be explained by shift of the Fermi level due to Ti out diffusion from the substrate to the film.
At the LaTiO3/SrTiO3 interface, aberration-corrected imaging showed crystallinity deterioration in LaTiO3 films a few unit cells away from the interface. ELNES showed that oxygen annealing did not alter the crystallinity but converted Ti3+ near the interface into Ti4+, which explained disappearance of the conductivity.
At the EuO/SrTiO3 interface, both high-resolution imaging and ELNES confirmed EuO formation. ELNES hyperspectral unmixing showed a Ti3+ layer confined to within several unit cells of the interface on the SrTiO3 side, confirming the presence of oxygen vacancies.
At the BaTiO3/SrTiO3 interface, spontaneous polarization and local lattice parameters were measured directly in each unit cell column and compared with oxidation state mapping using ELNES with unit-cell resolution. The unusually large polarization near the interface and the polarization gradient were explained by oxygen vacancies and the piezoelectric effect due to epitaxial strain and strain gradient from relaxation.
Advanced electron microscopy techniques, including aberration-corrected electron microscopy and electron energy-loss spectroscopy (EELS) with energy-loss near-edge structure (ELNES) analysis, were used to characterize the interfaces. Image and spectrum data-processing algorithms, including subpixel atomic position measurement, and novel outlier detection by oversampling, subspace division based EELS background removal and bias-free endmember extraction algorithms for hyperspectral unmixing and mapping were heavily used. Results were compared with density functional theory (DFT) calculations for theoretical explanation.
For the γ-Al2O3/SrTiO3 system, negative-Cs imaging confirmed the formation of crystalline γ-Al2O3. ELNES hyperspectral unmixing combined with DFT calculations revealed that oxygen vacancies, rather than polar discontinuity, were the key to the 2DEG formation. The critical thickness can be explained by shift of the Fermi level due to Ti out diffusion from the substrate to the film.
At the LaTiO3/SrTiO3 interface, aberration-corrected imaging showed crystallinity deterioration in LaTiO3 films a few unit cells away from the interface. ELNES showed that oxygen annealing did not alter the crystallinity but converted Ti3+ near the interface into Ti4+, which explained disappearance of the conductivity.
At the EuO/SrTiO3 interface, both high-resolution imaging and ELNES confirmed EuO formation. ELNES hyperspectral unmixing showed a Ti3+ layer confined to within several unit cells of the interface on the SrTiO3 side, confirming the presence of oxygen vacancies.
At the BaTiO3/SrTiO3 interface, spontaneous polarization and local lattice parameters were measured directly in each unit cell column and compared with oxidation state mapping using ELNES with unit-cell resolution. The unusually large polarization near the interface and the polarization gradient were explained by oxygen vacancies and the piezoelectric effect due to epitaxial strain and strain gradient from relaxation.
ContributorsLu, Sirong (Author) / Smith, David J. (Thesis advisor) / McCartney, Martha R. (Thesis advisor) / Chizmeshya, Andrew (Committee member) / Crozier, Peter A. (Committee member) / Arizona State University (Publisher)
Created2018
Description
Compound semiconductors tend to be more ionic if the cations and anions are further apart in atomic columns, such as II-VI compared to III-V compounds, due in part to the greater electronegativity difference between group-II and group-VI atoms. As the electronegativity between the atoms increases, the materials tend to have more insulator-like properties, including higher energy band gaps and lower indices of refraction. This enables significant differences in the optical and electronic properties between III-V, II-VI, and IV-VI semiconductors. Many of these binary compounds have similar lattice constants and therefore can be grown epitaxially on top of each other to create monolithic heterovalent and heterocrystalline heterostructures with optical and electronic properties unachievable in conventional isovalent heterostructures.
Due to the difference in vapor pressures and ideal growth temperatures between the different materials, precise growth methods are required to optimize the structural and optical properties of the heterovalent heterostructures. The high growth temperatures of the III-V materials can damage the II-VI barrier layers, and therefore a compromise must be found for the growth of high-quality III-V and II-VI layers in the same heterostructure. In addition, precise control of the interface termination has been shown to play a significant role in the crystal quality of the different layers in the structure. For non-polar orientations, elemental fluxes of group-II and group-V atoms consistently help to lower the stacking fault and dislocation density in the II-VI/III-V heterovalent heterostructures.
This dissertation examines the epitaxial growth of heterovalent and heterocrystalline heterostructures lattice-matched to GaAs, GaSb, and InSb substrates in a single-chamber growth system. The optimal growth conditions to achieve alternating layers of III-V, II-VI, and IV-VI semiconductors have been investigated using temperature ramps, migration-enhanced epitaxy, and elemental fluxes at the interface. GaSb/ZnTe distributed Bragg reflectors grown in this study significantly outperform similar isovalent GaSb-based reflectors and show great promise for mid-infrared applications. Also, carrier confinement in GaAs/ZnSe quantum wells was achieved with a low-temperature growth technique for GaAs on ZnSe. Additionally, nearly lattice-matched heterocrystalline PbTe/CdTe/InSb heterostructures with strong infrared photoluminescence were demonstrated, along with virtual (211) CdZnTe/InSb substrates with extremely low defect densities for long-wavelength optoelectronic applications.
Due to the difference in vapor pressures and ideal growth temperatures between the different materials, precise growth methods are required to optimize the structural and optical properties of the heterovalent heterostructures. The high growth temperatures of the III-V materials can damage the II-VI barrier layers, and therefore a compromise must be found for the growth of high-quality III-V and II-VI layers in the same heterostructure. In addition, precise control of the interface termination has been shown to play a significant role in the crystal quality of the different layers in the structure. For non-polar orientations, elemental fluxes of group-II and group-V atoms consistently help to lower the stacking fault and dislocation density in the II-VI/III-V heterovalent heterostructures.
This dissertation examines the epitaxial growth of heterovalent and heterocrystalline heterostructures lattice-matched to GaAs, GaSb, and InSb substrates in a single-chamber growth system. The optimal growth conditions to achieve alternating layers of III-V, II-VI, and IV-VI semiconductors have been investigated using temperature ramps, migration-enhanced epitaxy, and elemental fluxes at the interface. GaSb/ZnTe distributed Bragg reflectors grown in this study significantly outperform similar isovalent GaSb-based reflectors and show great promise for mid-infrared applications. Also, carrier confinement in GaAs/ZnSe quantum wells was achieved with a low-temperature growth technique for GaAs on ZnSe. Additionally, nearly lattice-matched heterocrystalline PbTe/CdTe/InSb heterostructures with strong infrared photoluminescence were demonstrated, along with virtual (211) CdZnTe/InSb substrates with extremely low defect densities for long-wavelength optoelectronic applications.
ContributorsLassise, Maxwell Brock (Author) / Zhang, Yong-Hang (Thesis advisor) / Smith, David J. (Committee member) / Johnson, Shane R (Committee member) / Mccartney, Martha R (Committee member) / Arizona State University (Publisher)
Created2019
Description
A highly uniform and repeatable method for synthesizing the single-layer transition metal dichalcogenides (TMDs) molybdenum disulfide, MoS2, and tungsten disulfide, WS2, was developed. This method employed chemical vapor deposition (CVD) of precursors in a custom built cold-wall reaction chamber designed to allow independent control over the growth parameters. Iterations of this reaction chamber were employed to overcome limitations to the growth method. First, molybdenum trioxide, MoO3, and S were co-evaporated from alumina coated W baskets to grow MoS2 on SiO2/Si substrates. Using this method, films were found to have repeatable coverage, but unrepeatable morphology. Second, the reaction chamber was modified to include a pair of custom bubbler delivery systems to transport diethyl sulfide (DES) and molybdenum hexacarbonyl (MHC) to the substrate as a S and Mo precursors. Third, tungsten hexacarbonyl (WHC) replaced MHC as a transition metal precursor for the synthesis of WS2 on Al2O3, substrates. This method proved repeatable in both coverage and morphology allowing the investigation of the effect of varying the flow of Ar, varying the substrate temperature and varying the flux of DES to the sample. Increasing each of these parameters was found to decrease the nucleation density on the sample and, with the exception of the Ar flow, induce multi-layer feature growth. This combination of precursors was also used to investigate the reported improvement in feature morphology when NaCl is placed upstream of the substrate. This was found to have no effect on experiments in the configurations used. A final effort was made to adequately increase the feature size by switching from DES to hydrogen sulfide, H2S, as a source of S. Using H2S and WHC to grow WS2 films on Al2O3, it was found that increasing the substrate temperature and increasing the H2S flow both decrease nucleation density. Increasing the H2S flow induced bi-layer growth. Ripening of synthesized WS2 crystals was demonstrated to occur when the sample was annealed, post-growth, in an Ar, H2, and H2S flow. Finally, it was verified that the final H2S and WHC growth method yielded repeatability and uniformity matching, or improving upon, the other methods and precursors investigated.
ContributorsLunceford, Chad (Author) / Drucker, Jeff (Thesis advisor) / Menéndez, Jose (Committee member) / Smith, David J. (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2019
Description
Semiconductor nanostructures are promising building blocks for light management in thin silicon solar cells and silicon-based tandems due their tunable optical properties. The present dissertation is organized along three main research areas: (1) characterization and modeling of III-V nanowires as active elements of solar cell tandems, (2) modeling of silicon nanopillars for reduced optical losses in ultra-thin silicon solar cells, and (3) characterization and modeling of nanoparticle-based optical coatings for light management.
First, the recombination mechanisms in polytype GaAs nanowires are studied through photoluminescence measurements coupled with rate equation analysis. When photons are absorbed in polytype nanowires, electrons and holes quickly thermalize to the band-edges of the zinc-blende and wurtzite phases, recombining indirectly in space across the type-II offset. Using a rate equation model, different configurations of polytype defects along the nanowire are investigated, which compare well with experiment considering spatially indirect recombination between different polytypes, and defect-related recombination due to twin planes and other defects. The presented analysis is a path towards predicting the performance of nanowire-based solar cells.
Following this topic, the optical mechanisms in silicon nanopillar arrays are investigated using full-wave optical simulations in comparison to measured reflectance data. The simulated electric field energy density profiles are used to elucidate the mechanisms contributing to the reduced front surface reflectance. Strong forward scattering and resonant absorption are observed for shorter- and longer- aspect ratio nanopillars, respectively, with the sub-wavelength periodicity causing additional diffraction. Their potential for light-trapping is investigated using full-wave optical simulation of an ultra-thin nanostructured substrate, where the conventional light-trapping limit is exceeded for near-bandgap wavelengths.
Finally, the correlation between the optical properties of silicon nanoparticle layers to their respective pore size distributions is investigated using optical and structural characterization coupled with full-wave optical simulation. The presence of
scattering is experimentally correlated to wider pore size distributions obtained from nitrogen adsorption measurements. The correlation is validated with optical simulation of random and clustered structures, with the latter approximating experimental. Reduced structural inhomogeneity in low-refractive-index nanoparticle inter-layers at the metal/semiconductor interface improves their performance as back reflectors, while reducing parasitic absorption in the metal.
First, the recombination mechanisms in polytype GaAs nanowires are studied through photoluminescence measurements coupled with rate equation analysis. When photons are absorbed in polytype nanowires, electrons and holes quickly thermalize to the band-edges of the zinc-blende and wurtzite phases, recombining indirectly in space across the type-II offset. Using a rate equation model, different configurations of polytype defects along the nanowire are investigated, which compare well with experiment considering spatially indirect recombination between different polytypes, and defect-related recombination due to twin planes and other defects. The presented analysis is a path towards predicting the performance of nanowire-based solar cells.
Following this topic, the optical mechanisms in silicon nanopillar arrays are investigated using full-wave optical simulations in comparison to measured reflectance data. The simulated electric field energy density profiles are used to elucidate the mechanisms contributing to the reduced front surface reflectance. Strong forward scattering and resonant absorption are observed for shorter- and longer- aspect ratio nanopillars, respectively, with the sub-wavelength periodicity causing additional diffraction. Their potential for light-trapping is investigated using full-wave optical simulation of an ultra-thin nanostructured substrate, where the conventional light-trapping limit is exceeded for near-bandgap wavelengths.
Finally, the correlation between the optical properties of silicon nanoparticle layers to their respective pore size distributions is investigated using optical and structural characterization coupled with full-wave optical simulation. The presence of
scattering is experimentally correlated to wider pore size distributions obtained from nitrogen adsorption measurements. The correlation is validated with optical simulation of random and clustered structures, with the latter approximating experimental. Reduced structural inhomogeneity in low-refractive-index nanoparticle inter-layers at the metal/semiconductor interface improves their performance as back reflectors, while reducing parasitic absorption in the metal.
ContributorsVulic, Natasa (Author) / Goodnick, Stephen M (Thesis advisor) / Honsberg, C. (Christiana B.) (Committee member) / Holman, Zachary C (Committee member) / Smith, David J. (Committee member) / Arizona State University (Publisher)
Created2019
Description
InAs/InAsSb type-II superlattices (T2SLs) can be considered as potential alternatives for conventional HgCdTe photodetectors due to improved uniformity, lower manufacturing costs with larger substrates, and possibly better device performance. This dissertation presents a comprehensive study on the structural, optical and electrical properties of InAs/InAsSb T2SLs grown by Molecular Beam Epitaxy.
The effects of different growth conditions on the structural quality were thoroughly investigated. Lattice-matched condition was successfully achieved and material of exceptional quality was demonstrated.
After growth optimization had been achieved, structural defects could hardly be detected, so different characterization techniques, including etch-pit-density (EPD) measurements, cathodoluminescence (CL) imaging and X-ray topography (XRT), were explored, in attempting to gain better knowledge of the sparsely distributed defects. EPD revealed the distribution of dislocation-associated pits across the wafer. Unfortunately, the lack of contrast in images obtained by CL imaging and XRT indicated their inability to provide any quantitative information about defect density in these InAs/InAsSb T2SLs.
The nBn photodetectors based on mid-wave infrared (MWIR) and long-wave infrared (LWIR) InAs/InAsSb T2SLs were fabricated. The significant difference in Ga composition in the barrier layer coupled with different dark current behavior, suggested the possibility of different types of band alignment between the barrier layers and the absorbers. A positive charge density of 1.8 × 1017/cm3 in the barrier of MWIR nBn photodetector, as determined by electron holography, confirmed the presence of a potential well in its valence band, thus identifying type-II alignment. In contrast, the LWIR nBn photodetector was shown to have type-I alignment because no sign of positive charge was detected in its barrier.
Capacitance-voltage measurements were performed to investigate the temperature dependence of carrier densities in a metal-oxide-semiconductor (MOS) structure based on MWIR InAs/InAsSb T2SLs, and a nBn structure based on LWIR InAs/InAsSb T2SLs. No carrier freeze-out was observed in either sample, indicating very shallow donor levels. The decrease in carrier density when temperature increased was attributed to the increased density of holes that had been thermally excited from localized states near the oxide/semiconductor interface in the MOS sample. No deep-level traps were revealed in deep-level transient spectroscopy temperature scans.
The effects of different growth conditions on the structural quality were thoroughly investigated. Lattice-matched condition was successfully achieved and material of exceptional quality was demonstrated.
After growth optimization had been achieved, structural defects could hardly be detected, so different characterization techniques, including etch-pit-density (EPD) measurements, cathodoluminescence (CL) imaging and X-ray topography (XRT), were explored, in attempting to gain better knowledge of the sparsely distributed defects. EPD revealed the distribution of dislocation-associated pits across the wafer. Unfortunately, the lack of contrast in images obtained by CL imaging and XRT indicated their inability to provide any quantitative information about defect density in these InAs/InAsSb T2SLs.
The nBn photodetectors based on mid-wave infrared (MWIR) and long-wave infrared (LWIR) InAs/InAsSb T2SLs were fabricated. The significant difference in Ga composition in the barrier layer coupled with different dark current behavior, suggested the possibility of different types of band alignment between the barrier layers and the absorbers. A positive charge density of 1.8 × 1017/cm3 in the barrier of MWIR nBn photodetector, as determined by electron holography, confirmed the presence of a potential well in its valence band, thus identifying type-II alignment. In contrast, the LWIR nBn photodetector was shown to have type-I alignment because no sign of positive charge was detected in its barrier.
Capacitance-voltage measurements were performed to investigate the temperature dependence of carrier densities in a metal-oxide-semiconductor (MOS) structure based on MWIR InAs/InAsSb T2SLs, and a nBn structure based on LWIR InAs/InAsSb T2SLs. No carrier freeze-out was observed in either sample, indicating very shallow donor levels. The decrease in carrier density when temperature increased was attributed to the increased density of holes that had been thermally excited from localized states near the oxide/semiconductor interface in the MOS sample. No deep-level traps were revealed in deep-level transient spectroscopy temperature scans.
ContributorsShen, Xiaomeng (Author) / Zhang, Yong-Hang (Thesis advisor) / Smith, David J. (Thesis advisor) / Alford, Terry (Committee member) / Goryll, Michael (Committee member) / Mccartney, Martha R (Committee member) / Arizona State University (Publisher)
Created2015
Description
Fluctuation Electron Microscopy (FEM) has become an effective materials' structure characterization technique, capable of probing medium-range order (MRO) that may be present in amorphous materials. Although its sensitivity to MRO has been exercised in numerous studies, FEM is not yet a quantitative technique. The holdup has been the discrepancy between the computed kinematical variance and the experimental variance, which previously was attributed to source incoherence. Although high-brightness, high coherence, electron guns are now routinely available in modern electron microscopes, they have not eliminated this discrepancy between theory and experiment. The main objective of this thesis was to explore, and to reveal, the reasons behind this conundrum.
The study was started with an analysis of the speckle statistics of tilted dark-field TEM images obtained from an amorphous carbon sample, which confirmed that the structural ordering is sensitively detected by FEM. This analysis also revealed the inconsistency between predictions of the source incoherence model and the experimentally observed variance.
FEM of amorphous carbon, amorphous silicon and ultra nanocrystalline diamond samples was carried out in an attempt to explore the conundrum. Electron probe and sample parameters were varied to observe the scattering intensity variance behavior. Results were compared to models of probe incoherence, diffuse scattering, atom displacement damage, energy loss events and multiple scattering. Models of displacement decoherence matched the experimental results best.
Decoherence was also explored by an interferometric diffraction method using bilayer amorphous samples, and results are consistent with strong displacement decoherence in addition to temporal decoherence arising from the electron source energy spread and energy loss events in thick samples.
It is clear that decoherence plays an important role in the long-standing discrepancy between experimental FEM and its theoretical predictions.
The study was started with an analysis of the speckle statistics of tilted dark-field TEM images obtained from an amorphous carbon sample, which confirmed that the structural ordering is sensitively detected by FEM. This analysis also revealed the inconsistency between predictions of the source incoherence model and the experimentally observed variance.
FEM of amorphous carbon, amorphous silicon and ultra nanocrystalline diamond samples was carried out in an attempt to explore the conundrum. Electron probe and sample parameters were varied to observe the scattering intensity variance behavior. Results were compared to models of probe incoherence, diffuse scattering, atom displacement damage, energy loss events and multiple scattering. Models of displacement decoherence matched the experimental results best.
Decoherence was also explored by an interferometric diffraction method using bilayer amorphous samples, and results are consistent with strong displacement decoherence in addition to temporal decoherence arising from the electron source energy spread and energy loss events in thick samples.
It is clear that decoherence plays an important role in the long-standing discrepancy between experimental FEM and its theoretical predictions.
ContributorsRezikyan, Aram (Author) / Treacy, Michael M.J. (Thesis advisor) / Smith, David J. (Committee member) / McCartney, Martha R. (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2015
Description
Off-axis electron holography (EH) has been used to characterize electrostatic potential, active dopant concentrations and charge distribution in semiconductor nanostructures, including ZnO nanowires (NWs) and thin films, ZnTe thin films, Si NWs with axial p-n junctions, Si-Ge axial heterojunction NWs, and Ge/LixGe core/shell NW.
The mean inner potential (MIP) and inelastic mean free path (IMFP) of ZnO NWs have been measured to be 15.3V±0.2V and 55±3nm, respectively, for 200keV electrons. These values were then used to characterize the thickness of a ZnO nano-sheet and gave consistent values. The MIP and IMFP for ZnTe thin films were measured to be 13.7±0.6V and 46±2nm, respectively, for 200keV electrons. A thin film expected to have a p-n junction was studied, but no signal due to the junction was observed. The importance of dynamical effects was systematically studied using Bloch wave simulations.
The built-in potentials in Si NWs across the doped p-n junction and the Schottky junction due to Au catalyst were measured to be 1.0±0.3V and 0.5±0.3V, respectively. Simulations indicated that the dopant concentrations were ~1019cm-3 for donors and ~1017 cm-3 for acceptors. The effects of positively charged Au catalyst, a possible n+-n--p junction transition region and possible surface charge, were also systematically studied using simulations.
Si-Ge heterojunction NWs were studied. Dopant concentrations were extracted by atom probe tomography. The built-in potential offset was measured to be 0.4±0.2V, with the Ge side lower. Comparisons with simulations indicated that Ga present in the Si region was only partially activated. In situ EH biasing experiments combined with simulations indicated the B dopant in Ge was mostly activated but not the P dopant in Si. I-V characteristic curves were measured and explained using simulations.
The Ge/LixGe core/shell structure was studied during lithiation. The MIP for LixGe decreased with time due to increased Li content. A model was proposed to explain the lower measured Ge potential, and the trapped electron density in Ge core was calculated to be 3×1018 electrons/cm3. The Li amount during lithiation was also calculated using MIP and volume ratio, indicating that it was lower than the fully lithiated phase.
The mean inner potential (MIP) and inelastic mean free path (IMFP) of ZnO NWs have been measured to be 15.3V±0.2V and 55±3nm, respectively, for 200keV electrons. These values were then used to characterize the thickness of a ZnO nano-sheet and gave consistent values. The MIP and IMFP for ZnTe thin films were measured to be 13.7±0.6V and 46±2nm, respectively, for 200keV electrons. A thin film expected to have a p-n junction was studied, but no signal due to the junction was observed. The importance of dynamical effects was systematically studied using Bloch wave simulations.
The built-in potentials in Si NWs across the doped p-n junction and the Schottky junction due to Au catalyst were measured to be 1.0±0.3V and 0.5±0.3V, respectively. Simulations indicated that the dopant concentrations were ~1019cm-3 for donors and ~1017 cm-3 for acceptors. The effects of positively charged Au catalyst, a possible n+-n--p junction transition region and possible surface charge, were also systematically studied using simulations.
Si-Ge heterojunction NWs were studied. Dopant concentrations were extracted by atom probe tomography. The built-in potential offset was measured to be 0.4±0.2V, with the Ge side lower. Comparisons with simulations indicated that Ga present in the Si region was only partially activated. In situ EH biasing experiments combined with simulations indicated the B dopant in Ge was mostly activated but not the P dopant in Si. I-V characteristic curves were measured and explained using simulations.
The Ge/LixGe core/shell structure was studied during lithiation. The MIP for LixGe decreased with time due to increased Li content. A model was proposed to explain the lower measured Ge potential, and the trapped electron density in Ge core was calculated to be 3×1018 electrons/cm3. The Li amount during lithiation was also calculated using MIP and volume ratio, indicating that it was lower than the fully lithiated phase.
ContributorsGan, Zhaofeng (Author) / Mccartney, Martha R (Thesis advisor) / Smith, David J. (Thesis advisor) / Drucker, Jeffery (Committee member) / Bennett, Peter A (Committee member) / Arizona State University (Publisher)
Created2015
Description
This dissertation research has involved microscopic characterization of magnetic nanostructures using off-axis electron holography and Lorentz microscopy. The nanostructures investigated have included Co nanoparticles (NPs), Au/Fe/GaAs shell/core nanowires (NWs), carbon spirals with magnetic cores, magnetic nanopillars, Ni-Zn-Co spinel ferrite and CoFe/Pd multilayers. The studies have confirmed the capability of holography to describe the behavior of magnetic structures at the nanoscale.
The phase changes caused by the fringing fields of chains consisting of Co NPs were measured and calculated. The difference between chains with different numbers of Co NPs followed the trend indicated by calculations. Holography studies of Au/Fe/GaAs NWs grown on (110) GaAs substrates with rotationally non-uniform coating confirmed that Fe was present in the shell and that the shell behaved as a bar magnet. No fringing field was observed from NWs with cylindrical coating grown on (111)B GaAs substrates. The most likely explanation is that magnetic fields are confined within the shells and form closed loops. The multiple-magnetic-domain structure of iron carbide cores in carbon spirals was imaged using phase maps of the fringing fields. The strength and range of this fringing field was insufficient for manipulating the carbon spirals with an external applied magnetic field. No magnetism was revealed for CoPd/Fe/CoPd magnetic nanopillars. Degaussing and MFM scans ruled out the possibility that saturated magnetization and sample preparation had degraded the anisotropy, and the magnetism, respectively. The results suggested that these nanopillars were not suitable as candidates for prototypical bit information storage devices.
Observations of Ni-Zn-Co spinel ferrite thin films in plan-view geometry indicated a multigrain magnetic domain structure and the magnetic fields were oriented in-plane only with no preferred magnetization distribution. This domain structure helps explain this ferrite's high permeability at high resonance frequency, which is an unusual character.
Perpendicular magnetic anisotropy (PMA) of CoFe/Pd multilayers was revealed using holography. Detailed microscopic characterization showed structural factors such as layer waviness and interdiffusion that could contribute to degradation of the PMA. However, these factors are overwhelmed by the dominant effect of the CoFe layer thickness, and can be ignored when considering magnetic domain structure.
The phase changes caused by the fringing fields of chains consisting of Co NPs were measured and calculated. The difference between chains with different numbers of Co NPs followed the trend indicated by calculations. Holography studies of Au/Fe/GaAs NWs grown on (110) GaAs substrates with rotationally non-uniform coating confirmed that Fe was present in the shell and that the shell behaved as a bar magnet. No fringing field was observed from NWs with cylindrical coating grown on (111)B GaAs substrates. The most likely explanation is that magnetic fields are confined within the shells and form closed loops. The multiple-magnetic-domain structure of iron carbide cores in carbon spirals was imaged using phase maps of the fringing fields. The strength and range of this fringing field was insufficient for manipulating the carbon spirals with an external applied magnetic field. No magnetism was revealed for CoPd/Fe/CoPd magnetic nanopillars. Degaussing and MFM scans ruled out the possibility that saturated magnetization and sample preparation had degraded the anisotropy, and the magnetism, respectively. The results suggested that these nanopillars were not suitable as candidates for prototypical bit information storage devices.
Observations of Ni-Zn-Co spinel ferrite thin films in plan-view geometry indicated a multigrain magnetic domain structure and the magnetic fields were oriented in-plane only with no preferred magnetization distribution. This domain structure helps explain this ferrite's high permeability at high resonance frequency, which is an unusual character.
Perpendicular magnetic anisotropy (PMA) of CoFe/Pd multilayers was revealed using holography. Detailed microscopic characterization showed structural factors such as layer waviness and interdiffusion that could contribute to degradation of the PMA. However, these factors are overwhelmed by the dominant effect of the CoFe layer thickness, and can be ignored when considering magnetic domain structure.
ContributorsZhang, Desai (Author) / Mccartney, Martha R (Thesis advisor) / Smith, David J. (Thesis advisor) / Crozier, Peter A. (Committee member) / Petusky, William T (Committee member) / Chamberlin, Ralph V (Committee member) / Arizona State University (Publisher)
Created2015
Description
The research described in this dissertation involved the use of transmission electron microscopy (TEM) to characterize II-VI and III-V compound semiconductor quantum dots (QDs) and dilute-nitride alloys grown by molecular beam epitaxy (MBE) and intended for photovoltaic applications. The morphology of CdTe QDs prepared by the post-annealing MBE method were characterized by various microscopy techniques including high-resolution transmission electron microscopy (HR-TEM), and high-angle annular-dark-field scanning transmission electron microscopy (HAADF-STEM). Extensive observations revealed that the of QD shapes were not well-defined, and the QD size and spatial distribution were not determined by the amount of CdTe deposition. These results indicated that the formation of II-VI QDs using a post-annealing treatment did not follow the conventional growth mechanism for III-V and IV-IV materials. The structural properties of dilute-nitride GaAsNx films grown using plasma-assisted MBE were characterized by TEM and HAADF-STEM. A significant amount of the nitrogen incorporated into the dilute nitride films was found to be interstitial, and that fluctuations in local nitrogen composition also occurred during growth. Post-growth partial relaxation of strain resulted in the formation of {110}-oriented microcracks in the sample with the largest substitutional nitrogen composition. Single- and multi-layered InAs QDs grown on GaAsSb/GaAs composite substrates were investigated using HR-TEM and HAADF-STEM. Correlation between the structural and optoelectronic properties revealed that the GaAsSb barrier layers had played an important role in tuning the energy-band alignments but without affecting the overall structural morphology. However, according to both XRD measurement and electron microscopy the densities of dislocations increased as the number of QD layers built up. An investigation of near-wetting layer-free InAs QDs incorporated with AlAs/GaAs spacer layers was carried out. The microscopy observations revealed that both embedded and non-embedded near-wetting layer-free InAs QDs did not have well-defined shapes unlike conventional InAs QDs. According to AFM analysis and plan-view TEM characterization, the InAs QDs incorporated with spacer layers had smaller dot density and more symmetrical larger sizes with an apparent bimodal size distribution (two distinct families of large and small dots) in comparison with conventional InAs QDs grown without any spacer layer.
ContributorsTang, Dinghao (Author) / Smith, David J. (Thesis advisor) / Crozier, Peter A. (Committee member) / Liu, Jingyue (Committee member) / Mccartney, Martha R (Committee member) / Arizona State University (Publisher)
Created2014