The two-dimensional electron gas (2DEG) at SrTiO3-based oxide interfaces has been extensively studied recently for its high carrier density, high electron mobility, superconducting, ferromagnetic, ferrroelectric and magnetoresistance properties, with possible application for all-oxide devices. Understanding the mechanisms behind the 2DEG formation and factors affecting its properties is the primary objective of this dissertation.
Advanced electron microscopy techniques, including aberration-corrected electron microscopy and electron energy-loss spectroscopy (EELS) with energy-loss near-edge structure (ELNES) analysis, were used to characterize the interfaces. Image and spectrum data-processing algorithms, including subpixel atomic position measurement, and novel outlier detection by oversampling, subspace division based EELS background removal and bias-free endmember extraction algorithms for hyperspectral unmixing and mapping were heavily used. Results were compared with density functional theory (DFT) calculations for theoretical explanation.
For the γ-Al2O3/SrTiO3 system, negative-Cs imaging confirmed the formation of crystalline γ-Al2O3. ELNES hyperspectral unmixing combined with DFT calculations revealed that oxygen vacancies, rather than polar discontinuity, were the key to the 2DEG formation. The critical thickness can be explained by shift of the Fermi level due to Ti out diffusion from the substrate to the film.
At the LaTiO3/SrTiO3 interface, aberration-corrected imaging showed crystallinity deterioration in LaTiO3 films a few unit cells away from the interface. ELNES showed that oxygen annealing did not alter the crystallinity but converted Ti3+ near the interface into Ti4+, which explained disappearance of the conductivity.
At the EuO/SrTiO3 interface, both high-resolution imaging and ELNES confirmed EuO formation. ELNES hyperspectral unmixing showed a Ti3+ layer confined to within several unit cells of the interface on the SrTiO3 side, confirming the presence of oxygen vacancies.
At the BaTiO3/SrTiO3 interface, spontaneous polarization and local lattice parameters were measured directly in each unit cell column and compared with oxidation state mapping using ELNES with unit-cell resolution. The unusually large polarization near the interface and the polarization gradient were explained by oxygen vacancies and the piezoelectric effect due to epitaxial strain and strain gradient from relaxation.
Advanced electron microscopy techniques, including aberration-corrected electron microscopy and electron energy-loss spectroscopy (EELS) with energy-loss near-edge structure (ELNES) analysis, were used to characterize the interfaces. Image and spectrum data-processing algorithms, including subpixel atomic position measurement, and novel outlier detection by oversampling, subspace division based EELS background removal and bias-free endmember extraction algorithms for hyperspectral unmixing and mapping were heavily used. Results were compared with density functional theory (DFT) calculations for theoretical explanation.
For the γ-Al2O3/SrTiO3 system, negative-Cs imaging confirmed the formation of crystalline γ-Al2O3. ELNES hyperspectral unmixing combined with DFT calculations revealed that oxygen vacancies, rather than polar discontinuity, were the key to the 2DEG formation. The critical thickness can be explained by shift of the Fermi level due to Ti out diffusion from the substrate to the film.
At the LaTiO3/SrTiO3 interface, aberration-corrected imaging showed crystallinity deterioration in LaTiO3 films a few unit cells away from the interface. ELNES showed that oxygen annealing did not alter the crystallinity but converted Ti3+ near the interface into Ti4+, which explained disappearance of the conductivity.
At the EuO/SrTiO3 interface, both high-resolution imaging and ELNES confirmed EuO formation. ELNES hyperspectral unmixing showed a Ti3+ layer confined to within several unit cells of the interface on the SrTiO3 side, confirming the presence of oxygen vacancies.
At the BaTiO3/SrTiO3 interface, spontaneous polarization and local lattice parameters were measured directly in each unit cell column and compared with oxidation state mapping using ELNES with unit-cell resolution. The unusually large polarization near the interface and the polarization gradient were explained by oxygen vacancies and the piezoelectric effect due to epitaxial strain and strain gradient from relaxation.
ContributorsLu, Sirong (Author) / Smith, David J. (Thesis advisor) / McCartney, Martha R. (Thesis advisor) / Chizmeshya, Andrew (Committee member) / Crozier, Peter A. (Committee member) / Arizona State University (Publisher)
Created2018
Description
Don't Hold Your Breath is an evening-length performance created and performed by Sarah "Saza" Kent and EPIK Dance Company that consisted of street and concert dance combined with hip hop theatre, spoken text and live singing. What began as a one-woman show about the choreographer's life, turned in to an ensemble piece that included the stories of many people, including ten community members who were interviewed on their views of life and death after being affected by a diagnosis. The show follows Kat, a young woman tiptoeing the line between her party girl past and the thought of finally growing up and settling down. Typically confident and self-assured, she is now grappling with the idea of life and death. Kat finds herself in an MRI machine that could ultimately determine her fate. As the machine examines her body, she begins to examine her life, causing her to confront some of life's most existential questions. Has she spent her time wisely? Would she do anything differently if given a second chance? When it comes down to it, and all distractions are stripped away, what is truly important? Her thoughts take her to memories of her past and visions for her future as she faces the reality that life is finite and tomorrow is not promised. This document is an account of the show's process and serves as a place of explanation, analysis, and reflection, while also questioning its significance on a personal level all the way to its place in the field.
ContributorsKent, Sarah Kay (Author) / Fitzgerald, Mary (Thesis advisor) / Hinds, Rickerby (Committee member) / Britt, Melissa (Committee member) / Arizona State University (Publisher)
Created2018
Description
Personal histories are deeply rooted into my way of existence, far before my brain became ready to challenge such notions. While Americans have been witnesses to the splintering effects of colonialism and patriarchy on socialization, I ask two questions: (1) Where to stand within a society that promotes the marginalization of both women and brown bodies? And (2) how to combat these harsh realities and protect those most affected?
Being both Black and woman, I decided to embark upon a quest of self-actualization in this document. “Ain’t She Sweet: A Critical Choreographic Study of Identity & Intersectionality,” tracks the creative process and concept design behind my applied project for the Master of Fine Arts in Dance. Developed in extensive rehearsals, community engagement, journaling processes, and lived experiences, the physical product, “Ain’t She Sweet,” explored concepts such as identity, socialization, oppression, decolonization, sexuality, and civil rights. The chapters within this document illustrate the depth of the research conducted to form the evening-length production and an analysis of the completed work.
Being both Black and woman, I decided to embark upon a quest of self-actualization in this document. “Ain’t She Sweet: A Critical Choreographic Study of Identity & Intersectionality,” tracks the creative process and concept design behind my applied project for the Master of Fine Arts in Dance. Developed in extensive rehearsals, community engagement, journaling processes, and lived experiences, the physical product, “Ain’t She Sweet,” explored concepts such as identity, socialization, oppression, decolonization, sexuality, and civil rights. The chapters within this document illustrate the depth of the research conducted to form the evening-length production and an analysis of the completed work.
ContributorsCarney, Laina Reese (Author) / Schupp, Karen (Thesis advisor) / Weitz, Rose (Committee member) / White, Marcus (Committee member) / Fitzgerald, Mary (Committee member) / Arizona State University (Publisher)
Created2019
Description
Places That Shape You documents the development and experience of composing and presenting Places That Shape You, an evening-length dance performance examining the relationship between culture and urban spaces, inspired by the physical parameters that cities provide for our lives. In the performance, a blend of postmodern contemporary movement vocabulary, text, projection, a mattress, 12 phonebooks and an overhead projector were used to a tell a story through the contrast of objects both obsolete and current. Musical collaborator, Austen Mack, created an original score that worked in partnership with the movement, advancing the unfolding of concepts about public and private spaces, community, memory, expectation and abstraction. In collaboration with six dancers, the choreographer conducted movement and archival research investigating personal stories, urban theory, somatic experience, place-making, and memories left in the spaces people inhabit, culminating in an evening length performance.
ContributorsWillcox, Halley (Author) / Fitzgerald, Mary (Thesis advisor) / Lerman, Liz (Committee member) / Rajko, Jessica (Committee member) / Arizona State University (Publisher)
Created2019
Description
Compound semiconductors tend to be more ionic if the cations and anions are further apart in atomic columns, such as II-VI compared to III-V compounds, due in part to the greater electronegativity difference between group-II and group-VI atoms. As the electronegativity between the atoms increases, the materials tend to have more insulator-like properties, including higher energy band gaps and lower indices of refraction. This enables significant differences in the optical and electronic properties between III-V, II-VI, and IV-VI semiconductors. Many of these binary compounds have similar lattice constants and therefore can be grown epitaxially on top of each other to create monolithic heterovalent and heterocrystalline heterostructures with optical and electronic properties unachievable in conventional isovalent heterostructures.
Due to the difference in vapor pressures and ideal growth temperatures between the different materials, precise growth methods are required to optimize the structural and optical properties of the heterovalent heterostructures. The high growth temperatures of the III-V materials can damage the II-VI barrier layers, and therefore a compromise must be found for the growth of high-quality III-V and II-VI layers in the same heterostructure. In addition, precise control of the interface termination has been shown to play a significant role in the crystal quality of the different layers in the structure. For non-polar orientations, elemental fluxes of group-II and group-V atoms consistently help to lower the stacking fault and dislocation density in the II-VI/III-V heterovalent heterostructures.
This dissertation examines the epitaxial growth of heterovalent and heterocrystalline heterostructures lattice-matched to GaAs, GaSb, and InSb substrates in a single-chamber growth system. The optimal growth conditions to achieve alternating layers of III-V, II-VI, and IV-VI semiconductors have been investigated using temperature ramps, migration-enhanced epitaxy, and elemental fluxes at the interface. GaSb/ZnTe distributed Bragg reflectors grown in this study significantly outperform similar isovalent GaSb-based reflectors and show great promise for mid-infrared applications. Also, carrier confinement in GaAs/ZnSe quantum wells was achieved with a low-temperature growth technique for GaAs on ZnSe. Additionally, nearly lattice-matched heterocrystalline PbTe/CdTe/InSb heterostructures with strong infrared photoluminescence were demonstrated, along with virtual (211) CdZnTe/InSb substrates with extremely low defect densities for long-wavelength optoelectronic applications.
Due to the difference in vapor pressures and ideal growth temperatures between the different materials, precise growth methods are required to optimize the structural and optical properties of the heterovalent heterostructures. The high growth temperatures of the III-V materials can damage the II-VI barrier layers, and therefore a compromise must be found for the growth of high-quality III-V and II-VI layers in the same heterostructure. In addition, precise control of the interface termination has been shown to play a significant role in the crystal quality of the different layers in the structure. For non-polar orientations, elemental fluxes of group-II and group-V atoms consistently help to lower the stacking fault and dislocation density in the II-VI/III-V heterovalent heterostructures.
This dissertation examines the epitaxial growth of heterovalent and heterocrystalline heterostructures lattice-matched to GaAs, GaSb, and InSb substrates in a single-chamber growth system. The optimal growth conditions to achieve alternating layers of III-V, II-VI, and IV-VI semiconductors have been investigated using temperature ramps, migration-enhanced epitaxy, and elemental fluxes at the interface. GaSb/ZnTe distributed Bragg reflectors grown in this study significantly outperform similar isovalent GaSb-based reflectors and show great promise for mid-infrared applications. Also, carrier confinement in GaAs/ZnSe quantum wells was achieved with a low-temperature growth technique for GaAs on ZnSe. Additionally, nearly lattice-matched heterocrystalline PbTe/CdTe/InSb heterostructures with strong infrared photoluminescence were demonstrated, along with virtual (211) CdZnTe/InSb substrates with extremely low defect densities for long-wavelength optoelectronic applications.
ContributorsLassise, Maxwell Brock (Author) / Zhang, Yong-Hang (Thesis advisor) / Smith, David J. (Committee member) / Johnson, Shane R (Committee member) / Mccartney, Martha R (Committee member) / Arizona State University (Publisher)
Created2019
Description
A highly uniform and repeatable method for synthesizing the single-layer transition metal dichalcogenides (TMDs) molybdenum disulfide, MoS2, and tungsten disulfide, WS2, was developed. This method employed chemical vapor deposition (CVD) of precursors in a custom built cold-wall reaction chamber designed to allow independent control over the growth parameters. Iterations of this reaction chamber were employed to overcome limitations to the growth method. First, molybdenum trioxide, MoO3, and S were co-evaporated from alumina coated W baskets to grow MoS2 on SiO2/Si substrates. Using this method, films were found to have repeatable coverage, but unrepeatable morphology. Second, the reaction chamber was modified to include a pair of custom bubbler delivery systems to transport diethyl sulfide (DES) and molybdenum hexacarbonyl (MHC) to the substrate as a S and Mo precursors. Third, tungsten hexacarbonyl (WHC) replaced MHC as a transition metal precursor for the synthesis of WS2 on Al2O3, substrates. This method proved repeatable in both coverage and morphology allowing the investigation of the effect of varying the flow of Ar, varying the substrate temperature and varying the flux of DES to the sample. Increasing each of these parameters was found to decrease the nucleation density on the sample and, with the exception of the Ar flow, induce multi-layer feature growth. This combination of precursors was also used to investigate the reported improvement in feature morphology when NaCl is placed upstream of the substrate. This was found to have no effect on experiments in the configurations used. A final effort was made to adequately increase the feature size by switching from DES to hydrogen sulfide, H2S, as a source of S. Using H2S and WHC to grow WS2 films on Al2O3, it was found that increasing the substrate temperature and increasing the H2S flow both decrease nucleation density. Increasing the H2S flow induced bi-layer growth. Ripening of synthesized WS2 crystals was demonstrated to occur when the sample was annealed, post-growth, in an Ar, H2, and H2S flow. Finally, it was verified that the final H2S and WHC growth method yielded repeatability and uniformity matching, or improving upon, the other methods and precursors investigated.
ContributorsLunceford, Chad (Author) / Drucker, Jeff (Thesis advisor) / Menéndez, Jose (Committee member) / Smith, David J. (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2019
Description
Semiconductor nanostructures are promising building blocks for light management in thin silicon solar cells and silicon-based tandems due their tunable optical properties. The present dissertation is organized along three main research areas: (1) characterization and modeling of III-V nanowires as active elements of solar cell tandems, (2) modeling of silicon nanopillars for reduced optical losses in ultra-thin silicon solar cells, and (3) characterization and modeling of nanoparticle-based optical coatings for light management.
First, the recombination mechanisms in polytype GaAs nanowires are studied through photoluminescence measurements coupled with rate equation analysis. When photons are absorbed in polytype nanowires, electrons and holes quickly thermalize to the band-edges of the zinc-blende and wurtzite phases, recombining indirectly in space across the type-II offset. Using a rate equation model, different configurations of polytype defects along the nanowire are investigated, which compare well with experiment considering spatially indirect recombination between different polytypes, and defect-related recombination due to twin planes and other defects. The presented analysis is a path towards predicting the performance of nanowire-based solar cells.
Following this topic, the optical mechanisms in silicon nanopillar arrays are investigated using full-wave optical simulations in comparison to measured reflectance data. The simulated electric field energy density profiles are used to elucidate the mechanisms contributing to the reduced front surface reflectance. Strong forward scattering and resonant absorption are observed for shorter- and longer- aspect ratio nanopillars, respectively, with the sub-wavelength periodicity causing additional diffraction. Their potential for light-trapping is investigated using full-wave optical simulation of an ultra-thin nanostructured substrate, where the conventional light-trapping limit is exceeded for near-bandgap wavelengths.
Finally, the correlation between the optical properties of silicon nanoparticle layers to their respective pore size distributions is investigated using optical and structural characterization coupled with full-wave optical simulation. The presence of
scattering is experimentally correlated to wider pore size distributions obtained from nitrogen adsorption measurements. The correlation is validated with optical simulation of random and clustered structures, with the latter approximating experimental. Reduced structural inhomogeneity in low-refractive-index nanoparticle inter-layers at the metal/semiconductor interface improves their performance as back reflectors, while reducing parasitic absorption in the metal.
First, the recombination mechanisms in polytype GaAs nanowires are studied through photoluminescence measurements coupled with rate equation analysis. When photons are absorbed in polytype nanowires, electrons and holes quickly thermalize to the band-edges of the zinc-blende and wurtzite phases, recombining indirectly in space across the type-II offset. Using a rate equation model, different configurations of polytype defects along the nanowire are investigated, which compare well with experiment considering spatially indirect recombination between different polytypes, and defect-related recombination due to twin planes and other defects. The presented analysis is a path towards predicting the performance of nanowire-based solar cells.
Following this topic, the optical mechanisms in silicon nanopillar arrays are investigated using full-wave optical simulations in comparison to measured reflectance data. The simulated electric field energy density profiles are used to elucidate the mechanisms contributing to the reduced front surface reflectance. Strong forward scattering and resonant absorption are observed for shorter- and longer- aspect ratio nanopillars, respectively, with the sub-wavelength periodicity causing additional diffraction. Their potential for light-trapping is investigated using full-wave optical simulation of an ultra-thin nanostructured substrate, where the conventional light-trapping limit is exceeded for near-bandgap wavelengths.
Finally, the correlation between the optical properties of silicon nanoparticle layers to their respective pore size distributions is investigated using optical and structural characterization coupled with full-wave optical simulation. The presence of
scattering is experimentally correlated to wider pore size distributions obtained from nitrogen adsorption measurements. The correlation is validated with optical simulation of random and clustered structures, with the latter approximating experimental. Reduced structural inhomogeneity in low-refractive-index nanoparticle inter-layers at the metal/semiconductor interface improves their performance as back reflectors, while reducing parasitic absorption in the metal.
ContributorsVulic, Natasa (Author) / Goodnick, Stephen M (Thesis advisor) / Honsberg, C. (Christiana B.) (Committee member) / Holman, Zachary C (Committee member) / Smith, David J. (Committee member) / Arizona State University (Publisher)
Created2019
Description
This document explores a community dance project at an orphanage in Mexico and the investigations following. This project researched how dance can be used to create a transformative and empowering experience for the participant and what discoveries of identity are made through dance. The research took place at an orphanage in Texcoco, Mexico and at Arizona State University. The participants in this research include three dance artists from Arizona State University and 10 ten-year-old children from Mexico. The portion that took place in Mexico was conducted in daily three-hour classes over the span of two weeks. For five months following the two weeks in Mexico, weekly rehearsals were held and a culminating concert was performed on November 20th–22nd of 2015.
ContributorsMay, Emily Ann (Author) / Fitzgerald, Mary (Thesis advisor) / McMahon, Jeff (Committee member) / Rex-Flint, Melissa (Committee member) / Arizona State University (Publisher)
Created2016
Description
Purple World was a choreographic project that investigated improvisational, compositional, design, and technological experiments to research movement possibilities in interdisciplinary and interactive settings. In developing the work, the dancers exchanged different individual perspectives through "movement recall." This movement recall was inspired by the sensations associated with their physical memories from childhood, conditioned movement patterns, and the ways dancers can use their bodies to creatively problem-solve the philosophical questions in their lives. The work united dance, interactive work, structured improvisation, props, and installation. The intersection of discussion with collaborators, creative methods inspired by other artists, and the elements described above provided a structure for the artist to investigate his choreographic artistic identity by cultivating individual movement vocabulary in himself and his dancers.
ContributorsKikuchi, Fumihiro (Author) / Fitzgerald, Mary (Thesis advisor) / Jackson, Naomi (Committee member) / Kim, Marianne (Committee member) / Arizona State University (Publisher)
Created2015
Description
InAs/InAsSb type-II superlattices (T2SLs) can be considered as potential alternatives for conventional HgCdTe photodetectors due to improved uniformity, lower manufacturing costs with larger substrates, and possibly better device performance. This dissertation presents a comprehensive study on the structural, optical and electrical properties of InAs/InAsSb T2SLs grown by Molecular Beam Epitaxy.
The effects of different growth conditions on the structural quality were thoroughly investigated. Lattice-matched condition was successfully achieved and material of exceptional quality was demonstrated.
After growth optimization had been achieved, structural defects could hardly be detected, so different characterization techniques, including etch-pit-density (EPD) measurements, cathodoluminescence (CL) imaging and X-ray topography (XRT), were explored, in attempting to gain better knowledge of the sparsely distributed defects. EPD revealed the distribution of dislocation-associated pits across the wafer. Unfortunately, the lack of contrast in images obtained by CL imaging and XRT indicated their inability to provide any quantitative information about defect density in these InAs/InAsSb T2SLs.
The nBn photodetectors based on mid-wave infrared (MWIR) and long-wave infrared (LWIR) InAs/InAsSb T2SLs were fabricated. The significant difference in Ga composition in the barrier layer coupled with different dark current behavior, suggested the possibility of different types of band alignment between the barrier layers and the absorbers. A positive charge density of 1.8 × 1017/cm3 in the barrier of MWIR nBn photodetector, as determined by electron holography, confirmed the presence of a potential well in its valence band, thus identifying type-II alignment. In contrast, the LWIR nBn photodetector was shown to have type-I alignment because no sign of positive charge was detected in its barrier.
Capacitance-voltage measurements were performed to investigate the temperature dependence of carrier densities in a metal-oxide-semiconductor (MOS) structure based on MWIR InAs/InAsSb T2SLs, and a nBn structure based on LWIR InAs/InAsSb T2SLs. No carrier freeze-out was observed in either sample, indicating very shallow donor levels. The decrease in carrier density when temperature increased was attributed to the increased density of holes that had been thermally excited from localized states near the oxide/semiconductor interface in the MOS sample. No deep-level traps were revealed in deep-level transient spectroscopy temperature scans.
The effects of different growth conditions on the structural quality were thoroughly investigated. Lattice-matched condition was successfully achieved and material of exceptional quality was demonstrated.
After growth optimization had been achieved, structural defects could hardly be detected, so different characterization techniques, including etch-pit-density (EPD) measurements, cathodoluminescence (CL) imaging and X-ray topography (XRT), were explored, in attempting to gain better knowledge of the sparsely distributed defects. EPD revealed the distribution of dislocation-associated pits across the wafer. Unfortunately, the lack of contrast in images obtained by CL imaging and XRT indicated their inability to provide any quantitative information about defect density in these InAs/InAsSb T2SLs.
The nBn photodetectors based on mid-wave infrared (MWIR) and long-wave infrared (LWIR) InAs/InAsSb T2SLs were fabricated. The significant difference in Ga composition in the barrier layer coupled with different dark current behavior, suggested the possibility of different types of band alignment between the barrier layers and the absorbers. A positive charge density of 1.8 × 1017/cm3 in the barrier of MWIR nBn photodetector, as determined by electron holography, confirmed the presence of a potential well in its valence band, thus identifying type-II alignment. In contrast, the LWIR nBn photodetector was shown to have type-I alignment because no sign of positive charge was detected in its barrier.
Capacitance-voltage measurements were performed to investigate the temperature dependence of carrier densities in a metal-oxide-semiconductor (MOS) structure based on MWIR InAs/InAsSb T2SLs, and a nBn structure based on LWIR InAs/InAsSb T2SLs. No carrier freeze-out was observed in either sample, indicating very shallow donor levels. The decrease in carrier density when temperature increased was attributed to the increased density of holes that had been thermally excited from localized states near the oxide/semiconductor interface in the MOS sample. No deep-level traps were revealed in deep-level transient spectroscopy temperature scans.
ContributorsShen, Xiaomeng (Author) / Zhang, Yong-Hang (Thesis advisor) / Smith, David J. (Thesis advisor) / Alford, Terry (Committee member) / Goryll, Michael (Committee member) / Mccartney, Martha R (Committee member) / Arizona State University (Publisher)
Created2015