ure of merit (zT) due to quantum connement eects. Improving the eciency of
thermoelectric devices allows for the development of better, more economical waste
heat recovery systems. Such systems may be used as bottoming or co-generation
cycles in conjunction with conventional power cycles to recover some of the wasted
heat. Thermal conductivity measurement systems are an important part of the char-
acterization processes of thermoelectric materials. These systems must possess the
capability of accurately measuring the thermal conductivity of both bulk and thin-lm
samples at dierent ambient temperatures.
This paper discusses the construction, validation, and improvement of a thermal
conductivity measurement platform based on the 3-Omega technique. Room temperature
measurements of thermal conductivity done on control samples with known properties
such as undoped bulk silicon (Si), bulk gallium arsenide (GaAs), and silicon dioxide
(SiO2) thin lms yielded 150 W=m􀀀K, 50 W=m􀀀K, and 1:46 W=m􀀀K respectively.
These quantities were all within 8% of literature values. In addition, the thermal
conductivity of bulk SiO2 was measured as a function of temperature in a Helium-
4 cryostat from 75K to 250K. The results showed good agreement with literature
values that all fell within the error range of each measurement. The uncertainty in
the measurements ranged from 19% at 75K to 30% at 250K. Finally, the system
was used to measure the room temperature thermal conductivity of a nanocomposite
composed of cadmium selenide, CdSe, nanocrystals in an indium selenide, In2Se3,
matrix as a function of the concentration of In2Se3. The observed trend was in
qualitative agreement with the expected behavior.
i
Geology and its tangential studies, collectively known and referred to in this thesis as geosciences, have been paramount to the transformation and advancement of society, fundamentally changing the way we view, interact and live with the surrounding natural and built environment. It is important to recognize the value and importance of this interdisciplinary scientific field while reconciling its ties to imperial and colonizing extractive systems which have led to harmful and invasive endeavors. This intersection among geosciences, (environmental) justice studies, and decolonization is intended to promote inclusive pedagogical models through just and equitable methodologies and frameworks as to prevent further injustices and promote recognition and healing of old wounds. By utilizing decolonial frameworks and highlighting the voices of peoples from colonized and exploited landscapes, this annotated syllabus tackles the issues previously described while proposing solutions involving place-based education and the recentering of land within geoscience pedagogical models. (abstract)
The ASU COVID-19 testing lab process was developed to operate as the primary testing site for all ASU staff, students, and specified external individuals. Tests are collected at various collection sites, including a walk-in site at the SDFC and various drive-up sites on campus; analysis is conducted on ASU campus and results are distributed virtually to all patients via the Health Services patient portal. The following is a literature review on past implementations of various process improvement techniques and how they can be applied to the ABCTL testing process to achieve laboratory goals. (abstract)
Next, a fundamental study is presented on the phase stability and solid-liquid transformation of metallic (In, Sn and Bi) colloidal nanocrystals. Although the phase change of nanoparticles has been a long-standing research topic, the melting behavior of colloidal nanocrytstals is largely unexplored. In addition, this study is of practical importance to nanocrystal-based applications that operate at elevated temperatures. Embedding colloidal nanocrystals into thermally-stable polymer matrices allows preserving nanocrystal size throughout melt-freeze cycles, and therefore enabling observation of stable melting features. Size-dependent melting temperature, melting enthalpy and melting entropy have all been measured and discussed.
In the next two chapters, focus has been switched to developing colloidal nanocrystal-based phase change composites for thermal energy storage applications. In Chapter 4, a polymer matrix phase change nanocomposite has been created. In this composite, the melting temperature and energy density could be independently controlled by tuning nanocrystal diameter and volume fractions. In Chapter 5, a solution-phase synthesis on metal matrix-metal nanocrytal composite is presented. This approach enables excellent morphological control over nanocrystals and demonstrated a phase change composite with a thermal conductivity 2 - 3 orders of magnitude greater than typical phase change materials, such as organics and molten salts.
Here, this research extends that exploratory work in an effort to determine if hfg of aqueous nanofluids can be manipulated, i.e., increased or decreased, by the addition of graphite or silver nanoparticles. Our results to date indicate that hfg can be substantially impacted, by up to ± 30% depending on the type of nanoparticle. Moreover, this dissertation reports further experiments with changing surface area based on volume fraction (0.005% to 2%) and various nanoparticle sizes to investigate the mechanisms for hfg modification in aqueous graphite and silver nanofluids. This research also investigates thermophysical properties, i.e., density and surface tension in aqueous nanofluids to support the experimental results of hfg based on the Clausius - Clapeyron equation. This theoretical investigation agrees well with the experimental results. Furthermore, this research investigates the hfg change of aqueous nanofluids with nanoscale studies in terms of melting of silver nanoparticles and hydrophobic interactions of graphite nanofluid. As a result, the entropy change due to those mechanisms could be a main cause of the changes of hfg in silver and graphite nanofluids.
Finally, applying the latent heat results of graphite and silver nanofluids to an actual solar thermal system to identify enhanced performance with a Rankine cycle is suggested to show that the tunable latent heat of vaporization in nanofluilds could be beneficial for real-world solar thermal applications with improved efficiency.
materials for lithium-based batteries: silicon (Si) and metal lithium (Li). It will focus on
studying the mechanical behaviors of the two materials during charge and discharge and
understanding how these mechanical behaviors may affect their electrochemical
performance.
In the first part, amorphous Si anode will be studied. Despite many existing studies
on silicon (Si) anodes for lithium ion batteries (LIBs), many essential questions still exist
on compound formation, composition, and properties. Here it is shown that some
previously accepted findings do not truthfully reflect the actual lithiation mechanisms in
realistic battery configurations. Furthermore the correlation between structure and
mechanical properties in these materials has not been properly established. Here, a rigorous
and thorough study is performed to comprehensively understand the electrochemical
reaction mechanisms of amorphous-Si (a-Si) in a realistic LIB configuration. In-depth
microstructural characterization was performed and correlations were established between
Li-Si composition, volumetric expansion, and modulus/hardness. It is found that the
lithiation process of a-Si in a real battery setup is a single-phase reaction rather than the
accepted two-phase reaction obtained from in-situ TEM experiments. The findings in this
dissertation establish a reference to quantitatively explain many key metrics for lithiated a
Si as anodes in real LIBs, and can be used to rationally design a-Si based high-performance
LIBs guided by high-fidelity modeling and simulations.
In the second part, Li metal anode will be investigated. Problems related to dendrite
growth on lithium metal anodes such as capacity loss and short circuit present major
barriers to the next-generation high-energy-density batteries. The development of
successful mitigation strategies is impeded by the incomplete understanding of the Li
dendrite growth mechanisms. Here the enabling role of plating residual stress in dendrite
initiation through novel experiments of Li electrodeposition on soft substrates is confirmed,
and the observations is explained with a stress-driven dendrite growth model. Dendrite
growth is mitigated on such soft substrates through surface-wrinkling-induced stress
relaxation in deposited Li film. It is demonstrated that this new dendrite mitigation
mechanism can be utilized synergistically with other existing approaches in the form of
three-dimensional (3D) soft scaffolds for Li plating, which achieves superior coulombic
efficiency over conventional hard copper current collectors under large current density.
anohole based metamaterials which are known of the capability of large area fabrication were intensively studied. Most of the studies are only based on the electrical responses of the metamaterials; however, magnetic response, is usually neglected since magnetic material does not exist naturally within the visible or infrared range. For the past few years, artificial magnetic response from nanostructure based metamaterials has been proposed. This reveals the possibility of exciting resonance modes based on magnetic responses in nanowire
anohole metamaterials which can potentially provide additional enhancement on radiative transport. On the other hand, beyond classical far-field radiative heat transfer, near-field radiation which is known of exceeding the Planck’s blackbody limit has also become a hot topic in the field.
This PhD dissertation aims to obtain a deep fundamental understanding of nanowire
anohole based metamaterials in both far-field and near-field in terms of both electrical and magnetic responses. The underlying mechanisms that can be excited by nanowire
anohole metamaterials such as electrical surface plasmon polariton, magnetic hyperbolic mode, magnetic polariton, etc., will be theoretically studied in both far-field and near-field. Furthermore, other than conventional effective medium theory which only considers the electrical response of metamaterials, the artificial magnetic response of metamaterials will also be studied through parameter retrieval of far-field optical and radiative properties for studying near-field radiative transport. Moreover, a custom-made AFM tip based metrology will be employed to experimentally study near-field radiative transfer between a plate and a sphere separated by nanometer vacuum gaps in vacuum. This transformative research will break new ground in nanoscale radiative heat transfer for various applications in energy systems, thermal management, and thermal imaging and sensing.