![151433-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-08/151433-Thumbnail%20Image.png?versionId=yGg.1GR1fX4BrSEWZg3acS0WI0ABEi33&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T124908Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=6aeccfa8ce46f19d107fe551c32b28c2682b933fcfba5f459d01765ede0dc8a4&itok=QPT8YJTp)
Description
Sensitivity is a fundamental challenge for in vivo molecular magnetic resonance imaging (MRI). Here, I improve the sensitivity of metal nanoparticle contrast agents by strategically incorporating pure and doped metal oxides in the nanoparticle core, forming a soluble, monodisperse, contrast agent with adjustable T2 or T1 relaxivity (r2 or r1). I first developed a simplified technique to incorporate iron oxides in apoferritin to form "magnetoferritin" for nM-level detection with T2- and T2* weighting. I then explored whether the crystal could be chemically modified to form a particle with high r1. I first adsorbed Mn2+ ions to metal binding sites in the apoferritin pores. The strategic placement of metal ions near sites of water exchange and within the crystal oxide enhance r1, suggesting a mechanism for increasing relaxivity in porous nanoparticle agents. However, the Mn2+ addition was only possible when the particle was simultaneously filled with an iron oxide, resulting in a particle with a high r1 but also a high r2 and making them undetectable with conventional T1-weighting techniques. To solve this problem and decrease the particle r2 for more sensitive detection, I chemically doped the nanoparticles with tungsten to form a disordered W-Fe oxide composite in the apoferritin core. This configuration formed a particle with a r1 of 4,870mM-1s-1 and r2 of 9,076mM-1s-1. These relaxivities allowed the detection of concentrations ranging from 20nM - 400nM in vivo, both passively injected and targeted to the kidney glomerulus. I further developed an MRI acquisition technique to distinguish particles based on r2/r1, and show that three nanoparticles of similar size can be distinguished in vitro and in vivo with MRI. This work forms the basis for a new, highly flexible inorganic approach to design nanoparticle contrast agents for molecular MRI.
ContributorsClavijo Jordan, Maria Veronica (Author) / Bennett, Kevin M (Thesis advisor) / Kodibagkar, Vikram (Committee member) / Sherry, A Dean (Committee member) / Wang, Xiao (Committee member) / Yarger, Jeffery (Committee member) / Arizona State University (Publisher)
Created2012
![152384-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-09/152384-Thumbnail%20Image.png?versionId=gqYiA8_J6eH88SRaGquo0orn3bnjMnMt&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T172818Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=f8a9b6c12b62df45b41041d901877d85db91b398dc1ad6b8e558771887d227b0&itok=ASvPZULr)
Description
Thiol functionalization is one potentially useful way to tailor physical and chemical properties of graphene oxides (GOs) and reduced graphene oxides (RGOs). Despite the ubiquitous presence of thiol functional groups in diverse chemical systems, efficient thiol functionalization has been challenging for GOs and RGOs, or for carbonaceous materials in general. In this work, thionation of GOs has been achieved in high yield through two new methods that also allow concomitant chemical reduction/thermal reduction of GOs; a solid-gas metathetical reaction method with boron sulfides (BxSy) gases and a solvothermal reaction method employing phosphorus decasulfide (P4S10). The thionation products, called "mercapto reduced graphene oxides (m-RGOs)", were characterized by employing X-ray photoelectron spectroscopy, powder X-ray diffraction, UV-Vis spectroscopy, FT-IR spectroscopy, Raman spectroscopy, electron probe analysis, scanning electron microscopy, (scanning) transmission electron microscopy, nano secondary ion mass spectrometry, Ellman assay and atomic force microscopy. The excellent dispersibility of m-RGOs in various solvents including alcohols has allowed fabrication of thin films of m-RGOs. Deposition of m-RGOs on gold substrates was achieved through solution deposition and the m-RGOs were homogeneously distributed on gold surface shown by atomic force microscopy. Langmuir-Blodgett (LB) films of m-RGOs were obtained by transferring their Langmuir films, formed by simple drop casting of m-RGOs dispersion on water surface, onto various substrates including gold, glass and indium tin oxide. The m-RGO LB films showed low sheet resistances down to about 500 kΩ/sq at 92% optical transparency. The successful results make m-RGOs promising for applications in transparent conductive coatings, biosensing, etc.
ContributorsJeon, Kiwan (Author) / Seo, Dong-Kyun (Thesis advisor) / Jones, Anne K (Committee member) / Yarger, Jeffery (Committee member) / Arizona State University (Publisher)
Created2013
![153946-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-08/153946-Thumbnail%20Image.png?versionId=DQviCq93o2o2JwFGa331li4QpMm0yQ1.&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T133704Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=75a3b549dc4ac98435a67974a2f52a0a70c229ce89b516939afa7f9bcd0caad9&itok=8uLgdeqz)
Description
Glycosaminoglycans (GAGs) are a class of complex biomolecules comprised of linear, sulfated polysaccharides whose presence on cell surfaces and in the extracellular matrix involve them in many physiological phenomena as well as in interactions with pathogenic microbes. Decorin binding protein A (DBPA), a Borrelia surface lipoprotein involved in the infectivity of Lyme disease, is responsible for binding GAGs found on decorin, a small proteoglycan present in the extracellular matrix. Different DBPA strains have notable sequence heterogeneity that results in varying levels of GAG-binding affinity. In this dissertation, the structures and GAG-binding mechanisms for three strains of DBPA (B31 and N40 DBPAs from B. burgdorferi and PBr DBPA from B. garinii) are studied to determine why each strain has a different affinity for GAGs. These three strains have similar topologies consisting of five α-helices held together by a hydrophobic core as well as two long flexible segments: a linker between helices one and two and a C-terminal tail. This structural arrangement facilitates the formation of a basic pocket below the flexible linker which is the primary GAG-binding epitope. However, this GAG-binding site can be occluded by the flexible linker, which makes the linker a negative regulator of GAG-binding. ITC and NMR titrations provide KD values that show PBr DBPA binds GAGs with higher affinity than B31 and N40 DBPAs, while N40 binds with the lowest affinity of the three. Work in this thesis demonstrates that much of the discrepancies seen in GAG affinities of the three DBPAs can be explained by the amino acid composition and conformation of the linker. Mutagenesis studies show that B31 DBPA overcomes the pocket obstruction with the BXBB motif in its linker while PBr DBPA has a retracted linker that exposes the basic pocket as well as a secondary GAG-binding site. N40 DBPA, however, does not have any evolutionary modifications to its structure to enhance GAG binding which explains its lower affinity for GAGs. GMSA and ELISA assays, along with NMR PRE experiments, confirm that structural changes in the linker do affect GAG-binding and, as a result, the linker is responsible for regulating GAG affinity.
ContributorsMorgan, Ashli M (Author) / Wang, Xu (Thesis advisor) / Allen, James (Committee member) / Yarger, Jeffery (Committee member) / Arizona State University (Publisher)
Created2015
![137040-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-05/137040-Thumbnail%20Image.png?versionId=iSpIo5MeKYgBKZDcriTlu9gCdiL2EYCQ&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T173931Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=c1a71af0058fdc8a57c7bc7d4e9ffd595a6bb2200c2e9c9786e1034891678d88&itok=U2PgSsb6)
Description
Amino acid analysis (AAA) of egg white lysozyme and bovine Achilles tendon collagen was performed using 1H solution-state nuclear magnetic resonance (NMR) spectroscopy. The proteins were hydrolyzed in 6M HCL with and without 0.02% phenol at 110\u00B0C for 24, 48, and 72 hours. For both proteins, 18 of 20 amino acids were characterized including hydroxyproline and hydroxylysine in collagen, using 1-dimensional (1D) and 2-dimensional (2D) NMR spectroscopy experiments. Errors ranging from <1% to 8% were seen in treatments with and without phenol. Both proteins could be correctly identified within their own species using the online database search AACompIdent. The proposed approach is a simple analytical technique that does not require the use of column separation or amino acid derivatization prior to compositional analysis.
ContributorsBaranowski, Michael Edward (Author) / Yarger, Jeffery (Thesis director) / Holland, Gregory (Committee member) / Barrett, The Honors College (Contributor) / Department of Chemistry and Biochemistry (Contributor) / Herberger Institute for Design and the Arts (Contributor)
Created2014-05
![137123-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-05/137123-Thumbnail%20Image.png?versionId=pW9zrDJpm_sEQ.djvp3nZYW1G6x_q0IU&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T163302Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=fe3f36ecf999469677c69144549488c9e9023647bba8dcce9b307e2d19dd6573&itok=R7KAe_uS)
Characterization of a Lipid Coating on the Surface of Silk Produced by the Embiid Antipaluria urichi
Description
Insects of the order Embiidina spin sheets of very thin silk fibers from their forelimbs to build silken shelters on bark and in leaf litter in tropical climates. Their shelters are very stiff and hydrophobic to keep out predators and rain. In this study, the existence of an outer lipid coating on silk produced by the embiid Antipaluria urichi is shown using scanning and transmission electron microscopy, FT-IR, and water drop contact angle analysis. Subsequently, the composition of the lipid layer is then characterized by 1H NMR and GC-MS.
ContributorsOsborn Popp, Thomas Michael (Author) / Yarger, Jeffery (Thesis director) / Holland, Gregory (Committee member) / Barrett, The Honors College (Contributor) / Department of Chemistry and Biochemistry (Contributor)
Created2014-05
![134567-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-05/134567-Thumbnail%20Image.png?versionId=95yeYV7Apd2juPaD_UYYyg3qhUP8ucz4&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T133704Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=6a3d63af4364c20090f529bfc36b60140ccd3a052df083580bc466a80b9c5767&itok=EzoRRWZO)
Description
The parameters of microwave-assisted acid hydrolysis (MAAH) and 1H NMR highly affect the quantitative analysis of protein hydrolysates. Microwave-induction source, NMR spectral resolution, and data analysis are key parameters in the nuclear magnetic resonance – amino acid analysis (NMR-AAA) workflow where errors accrue due to lack of an optimized protocol. Hen egg white lysozyme was hydrolyzed using an 800W domestic microwave oven for varying time points between 10-25 minutes, showing minimal protein hydrolysis after extended time periods. Studies on paramagnetic doping with varying amounts of gadolinium chloride for increased NMR resolution resulted in little T1 reduction in a majority of amino acids and resulted in significant line broadening in concentrations above 1µM. The use of the BAYESIL analysis tool with HOD suppressed 1H-NMR spectra resulted in misplaced template peaks and errors greater than 1% for 10 of 13 profiled amino acids with the highest error being 7.6% (Thr). Comparatively, Chenomx NMR Suite (v7.1) analysis resulted in errors of less than 1% for 9 of 13 profiled amino acids with a highest error value of 3.6% (Lys). Using the optimized protocol, hen egg white lysozyme C was identified at rank 1 with a score of 64 in a Gallus gallus species wide AACompIdent search. This technique reduces error associated with sample handling relative to previously used amino acid analysis (AAA) protocols and requires no derivatization or additional processing of the sample prior to analysis.
ContributorsJordan, Jacob Smith (Author) / Yarger, Jeffery (Thesis director) / Van Horn, Wade (Committee member) / School of Molecular Sciences (Contributor) / Barrett, The Honors College (Contributor)
Created2017-05
![155560-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-09/155560-Thumbnail%20Image.png?versionId=GVT88pKETlWdY6vDnRN64h.rRPc96hHD&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T170631Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=f01a9544fc26ab2effaa0fa2e72ec60cd3f106a4e09c4b7749ee1ccc99d4cfbb&itok=YeXlECCP)
Description
This work describes the investigation of novel cathode and anode materials. Specifically, several mixed polyanion compounds were evaluated as cathodes for Li and Na-ion batteries. Clathrate compounds composed of silicon or germanium arranged in cage-like structures were studied as anodes for Li-ion batteries.
Nanostructured Cu4(OH)6SO4 (brochantite) platelets were synthesized using polymer-assisted titration and microwave-assisted hydrothermal methods. These nanostructures exhibited a capacity of 474 mAh/g corresponding to the full utilization of the copper redox in an conversion reaction. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) studies were preformed to understand the mechanism and structural changes.
A microwave hydrothermal synthesis was developed to prepare a series compounds based on jarosite, AM3(SO4)2(OH)6 (A = K, Na; M = Fe, V). Both the morphology and electrochemical properties showed a compositional dependence. At potentials >1.5 V vs. Li/Li+, an insertion-type reaction was observed in Na,Fe-jarosite but not in K,Fe-jarosite. Reversible insertion-type reactions were observed in both vanadium jarosites between 1 – 4 V with capacities around 40 - 60 mAh/g. Below 1 V vs. Li/Li+, all four jarosite compounds underwent conversion reactions with capacities ~500 mAh/g for the Fe-jarosites.
The electrochemical properties of hydrogen titanium phosphate sulfate, H0.4Ti2(PO4)2.4(SO4)0.6 (HTPS), a new mixed polyanion material with NASICON structure was reported. A capacity of 148 mAh/g corresponding to2 Li+ insertion per formula unit was observed. XRD and XPS were used to characterize the HTPS before and after cycling and to identify the lithium sites. Evaluation of the HTPS in Na-ion cell was also performed, and a discharge capacity of 93 mAh/g was observed.
A systematic investigation of the role of the processing steps, such as ball-milling and acid/base etching, on the electrochemical properties of a silicon clathrate compound with nominal composition of Ba8Al16Si30 was performed. According to the transmission electron microscope (TEM), XPS, and electrochemical analysis, very few Li atoms can be electrochemically inserted, but the introduction of disorder through ball-milling resulted in higher capacity, while the oxidation layer made by the acid/base treatment prevented the reation. The electrochemical property of germanium clathrate was also investigated, unlike the silicon clathrate, the germanium one underwent a conversion reaction.
Nanostructured Cu4(OH)6SO4 (brochantite) platelets were synthesized using polymer-assisted titration and microwave-assisted hydrothermal methods. These nanostructures exhibited a capacity of 474 mAh/g corresponding to the full utilization of the copper redox in an conversion reaction. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) studies were preformed to understand the mechanism and structural changes.
A microwave hydrothermal synthesis was developed to prepare a series compounds based on jarosite, AM3(SO4)2(OH)6 (A = K, Na; M = Fe, V). Both the morphology and electrochemical properties showed a compositional dependence. At potentials >1.5 V vs. Li/Li+, an insertion-type reaction was observed in Na,Fe-jarosite but not in K,Fe-jarosite. Reversible insertion-type reactions were observed in both vanadium jarosites between 1 – 4 V with capacities around 40 - 60 mAh/g. Below 1 V vs. Li/Li+, all four jarosite compounds underwent conversion reactions with capacities ~500 mAh/g for the Fe-jarosites.
The electrochemical properties of hydrogen titanium phosphate sulfate, H0.4Ti2(PO4)2.4(SO4)0.6 (HTPS), a new mixed polyanion material with NASICON structure was reported. A capacity of 148 mAh/g corresponding to2 Li+ insertion per formula unit was observed. XRD and XPS were used to characterize the HTPS before and after cycling and to identify the lithium sites. Evaluation of the HTPS in Na-ion cell was also performed, and a discharge capacity of 93 mAh/g was observed.
A systematic investigation of the role of the processing steps, such as ball-milling and acid/base etching, on the electrochemical properties of a silicon clathrate compound with nominal composition of Ba8Al16Si30 was performed. According to the transmission electron microscope (TEM), XPS, and electrochemical analysis, very few Li atoms can be electrochemically inserted, but the introduction of disorder through ball-milling resulted in higher capacity, while the oxidation layer made by the acid/base treatment prevented the reation. The electrochemical property of germanium clathrate was also investigated, unlike the silicon clathrate, the germanium one underwent a conversion reaction.
ContributorsZhao, Ran (Author) / Chan, Candace K. (Thesis advisor) / Buttry, Daniel (Committee member) / Yarger, Jeffery (Committee member) / Arizona State University (Publisher)
Created2017
![168410-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2022-08/168410-Thumbnail%20Image.png?versionId=JhCy_7SXHo84YK.DqK2Q0ezLkz9R..4h&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T173931Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=0f338b66fa2b3983b50dd224efd9f658873e1aa716ec93fe41dcc48555e3d0de&itok=oG5s3vjZ)
Description
Transition metal oxides are used for numerous applications, includingsemiconductors, batteries, solar cells, catalysis, magnetic devices, and are commonly
observed in interstellar media. However, the atomic-scale properties which dictate the
overall bulk material activity is still lacking fundamental details. Most importantly, how
the electron shells of metals and O atoms mix is inherently significant to reactivity. This
thesis compares the binding and excited state properties of highly correlated first-row
transition metal oxides using four separate transition metal systems of Ti, Cr, Fe and Ni.
Laser ablation coupled with femtosecond pump-probe spectroscopy is utilized to resolve
the time-dependent excited state relaxation dynamics of atomically precise neutral
clusters following 400 nm (3.1 eV) photoexcitation. All transition metal oxides form
unique stable stoichiometries with excited state dynamics that evolve due to oxidation,
size, or geometry. Theoretical calculations assist in experimental analysis, showing
correlations between charge transfer characteristics, electron and hole localization, and
magnetic properties to the experimentally determined excited state lifetimes.
This thesis finds that neutral Ti and Cr form stable stoichiometries of MO2 (M =
Ti, Cr) which easily lose up to two O atoms, while neutral Fe and Ni primarily form MO
(M = Fe, Ni) geometries with suboxides also produced. TiO2 clusters possess excited
state lifetimes that increase with additional cluster units to ~600 fs, owing to a larger
delocalization of excited charge carriers with cluster size. CrO2 clusters show a unique
inversed metallic behavior with O content, where the fast (~30 fs) metallic relaxation
component associated with electron scattering increases with higher O content, connected
to the percent of ligand-to-metal charge transfer (LMCT) character and higher density of
states. FeO clusters show a decreased lifetime with size, reaching a plateau of ~150 fs at
the size of (FeO)5 related to the density of states as clusters form 3D geometries. Finally,
neutral (NiO)n clusters all have similar fast lifetimes (~110 fs), with suboxides possessing
unexpected electronic transitions involving s-orbitals, increasing excited state lifetimes
up to 80% and causing long-lived states lasting over 2.5 ps. Similarities are drawn
between each cluster system, providing valuable information about each metal oxide
species and the evolution of excited state dynamics as a result of the occupied d-shell.
The work presented within this thesis will lead to novel materials of increased reactivity
while facilitating a deeper fundamental understanding on the effect of electron
interactions on chemical properties.
ContributorsGarcia, Jacob M. (Author) / Sayres, Scott G (Thesis advisor) / Yarger, Jeffery (Committee member) / Steimle, Timothy (Committee member) / Arizona State University (Publisher)
Created2021
![](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/embryo_11701/Hamburger19550119.pdf.jpg?versionId=pUxuhZhkk8yDWZmuThMp8KwQpUl2hij2&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T153356Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=dfdda4f04845ff20bfcec486435b314b59588e6bd35171b54d2797a92403a132&itok=D9S1DYh6)
ContributorsHamburger, Viktor, 1900-2001 (Creator) / Marine Biological Laboratory (Woods Hole, Mass.) (Publisher) / Arizona Board of Regents (Publisher) / Baltzer, Fritz, 1884- (Contributor)
Created1955-01-19
![](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/embryo_11701/Hamburger19520531.pdf.jpg?versionId=kxhdwWNsAOZ0CKObJGv63FlFA05jcLqC&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240427/us-west-2/s3/aws4_request&X-Amz-Date=20240427T164753Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=cfbc85121cc87b5bd02677f2cbad6a406212b216d8c59c397a70c0a14a322d70&itok=Of6NCR1V)
ContributorsHamburger, Viktor, 1900-2001 (Creator) / Marine Biological Laboratory (Woods Hole, Mass.) (Publisher) / Arizona Board of Regents (Publisher) / Baltzer, Fritz, 1884- (Contributor)
Created1952-05-31