![153758-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-08/153758-Thumbnail%20Image.png?versionId=CyHYUOPyw0LVX15nrOHWUC2DOjYu2FpP&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240617/us-west-2/s3/aws4_request&X-Amz-Date=20240617T204225Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=d85caaa077564b67161bd84a7652cb9288337b0f3bb7104c79df53cf4f65062e&itok=h6z0owaY)
First, the surface electronic state configuration was examined with regards to the polarization bound 1013 charges/cm2 that increases with aluminum content. This large bound charge requires compensation either externally by surface states or internally by the space charge regions as relates to band bending. In this work, band bending was measured after different surface treatments of GaN and AlGaN to determine the effects of specific surface states on the electronic state configuration. Results showed oxygen-terminated N-face GaN, Ga-face GaN, and Ga-face Al0.25Ga0.75N surface were characterized by similar band bending regardless of the polarization bound charge, suggesting a Fermi level pinning state ~0.4-0.8 eV below the conduction band minimum. On oxygen-free Ga-face GaN, Al0.15Ga0.85N, Al0.25Ga0.75N, and Al0.35Ga0.65N, band bending increased slightly with aluminum content and thus did not exhibit the same pinning behavior; however, there was still significant compensating charge on these surfaces (~1013 charges/cm2). This charge is likely related to nitrogen vacancies and/or gallium dangling bonds.
In addition, this wozrk investigated the interface electronic state configuration of dielectric/GaN and AlGaN interfaces with regards to deposition conditions and aluminum content. Specifically, oxygen plasma-enhanced atomic layer deposited (PEALD) was used to deposit SiO2. Growth temperature was shown to influence the film quality, where room temperature deposition produced the highest quality films in terms of electrical breakdown. In addition, the valence band offsets (VBOs) appeared to decrease with the deposition temperature, which likely related to an electric field across the Ga2O3 interfacial layer. VBOs were also determined with respect to aluminum content at the PEALD-SiO2/AlxGa1-xN interface, giving 3.0, 2.9, 2.9, and 2.8 eV for 0%, 15%, 25%, and 35% aluminum content, respectively—with corresponding conduction band offsets of 2.5, 2.2, 1.9, and 1.8 eV. This suggests the largest difference manifests in the conduction band, which is in agreement with the charge neutrality level model.
![155013-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-08/155013-Thumbnail%20Image.png?versionId=pUTn76qwj5uwuJO.rKGKUT7tq0Ovo2Ln&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240615/us-west-2/s3/aws4_request&X-Amz-Date=20240615T025317Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=b05c5c62ce1d655004663b82b5c278b4d2d70f73e920c0faadf69de7b9aa28d9&itok=cxx-WsAP)
damage, immune system activation, impaired protein function, or aberrant DNA methylation. In the case of DNA methylation, I demonstrate that inhibiting DNA methylation dynamics can impair long-term memory formation, while the nurse-to- forager transition is not altered. These experiments could serve as the bases for and reference groups of studies testing the effects of metal or metalloid toxicity on DNA methylation. Each potential mechanism provides an avenue for investigating how neural function is influenced by the physiological status of non-neural organs. And from an ecological perspective, my results highlight the need for environmental policy to consider sublethal effects in determining safe environmental toxin loads for honey bees and other insect pollinators.
![155461-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-09/155461-Thumbnail%20Image.png?versionId=5DvVJFUYy17a6fUfSnb1KXrAmOL00Ns1&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240617/us-west-2/s3/aws4_request&X-Amz-Date=20240617T202630Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=0302c2f49c765a6342ed889c10c3c0d8f6dc556f1c66ab00d3687ed14ca9aafb&itok=xoTSa4M6)
Various deposition methods, both physical and chemical, were used to functionalize the ZnO NWs with metal or alloy nanoparticles (NPs) for catalytic transformations of important molecules which are relevant to energy and environment. Cu and PdZn NPs were epitaxially grown on ZnO NWs to make them resistant to sintering at elevated temperatures and thus improved the stability of such catalytic systems for methanol steam reforming (MSR) to produce hydrogen. A series of Pd/ZnO catalysts with different Pd loadings were synthesized and tested for MSR reaction. The CO selectivity was found to be strongly dependent on the size of the Pd: Both PdZn alloy and single Pd atoms yield low CO selectivity while Pd clusters give the highest CO selectivity.
By dispersing single Pd atoms onto ZnO NWs, Pd1/ZnO single-atom catalysts (SACs) was synthesized and their catalytic performance was evaluated for selected catalytic reactions. The experimental results show that the Pd1/ZnO SAC is active for CO oxidation and MSR but is not desirable other reactions. We further synthesized ZnO NWs supported noble metal (M1/ZnO; M=Rh, Pd, Pt, Ir) SACs and studied their catalytic performances for CO oxidation. The catalytic test data shows that all the fabricated noble metal SACs are active for CO oxidation but their activity are significantly different. Structure-performance relationships were investigated.
![158095-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-09/158095-Thumbnail%20Image.png?versionId=rmhtrQOrnM_qoJSwKf9x3Uilp6RH_42n&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240617/us-west-2/s3/aws4_request&X-Amz-Date=20240617T121509Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=92e90faef7f249b259dc0d7ac9ba85a8539a43cc6a75379e1ffc3102c555fa78&itok=K8vLU57F)
The proposed thermal model is then applied to a novel $\Pi$-gate architecture which has been suggested to reduce hot electron generation in the device, compared to the conventional T-gate. Additionally, small signal ac simulations are performed for the determination of cutoff frequencies using the thermal model as well.
Finally, further extensions of the CMC algorithm used in this work are discussed, including 1) higher-order moments of the phonon BTE, 2) coupling to phonon Monte Carlo simulations, and 3) application to other large-bandgap, and therefore high-power, materials such as diamond.
![161665-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-11/161665-Thumbnail%20Image.png?versionId=GB.InQ9rK2gdLpYxpNs6nikQVMtrjNIk&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240617/us-west-2/s3/aws4_request&X-Amz-Date=20240617T103341Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=8fbd4e867c31c2e5acf52c34c2900766baef57d6a3b9a14e25a6a98d11090d5b&itok=2qJWnRaa)
![129533-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-04/129533-Thumbnail%20Image.png?versionId=TESyxf0GZD3DtFRJ5eZsnoQlfL4MMPiB&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240615/us-west-2/s3/aws4_request&X-Amz-Date=20240615T225942Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=a2dbbe07bed5ca022b71a2c948aab8fa6ce8fcbc72ea633d258cfe305532eb5d&itok=KZCsqAJW)
Novel hydride chemistries are employed to deposit light-emitting Ge1-y Snyalloys with y ≤ 0.1 by Ultra-High Vacuum Chemical Vapor Deposition (UHV-CVD) on Ge-buffered Si wafers. The properties of the resultant materials are systematically compared with similar alloys grown directly on Si wafers. The fundamental difference between the two systems is a fivefold (and higher) decrease in lattice mismatch between film and virtual substrate, allowing direct integration of bulk-like crystals with planar surfaces and relatively low dislocation densities. For y ≤ 0.06, the CVD precursors used were digermane Ge2H6 and deuterated stannane SnD4. For y ≥ 0.06, the Ge precursor was changed to trigermane Ge3H8, whose higher reactivity enabled the fabrication of supersaturated samples with the target film parameters. In all cases, the Ge wafers were produced using tetragermane Ge4H10 as the Ge source. The photoluminescence intensity from Ge1-y Sny /Ge films is expected to increase relative to Ge1-y Sny /Si due to the less defected interface with the virtual substrate. However, while Ge1-y Sny /Si films are largely relaxed, a significant amount of compressive strain may be present in the Ge1-y Sny /Ge case. This compressive strain can reduce the emission intensity by increasing the separation between the direct and indirect edges. In this context, it is shown here that the proposed CVD approach to Ge1-y Sny /Ge makes it possible to approach film thicknesses of about 1 μm, for which the strain is mostly relaxed and the photoluminescence intensity increases by one order of magnitude relative to Ge1-y Sny /Si films. The observed strain relaxation is shown to be consistent with predictions from strain-relaxation models first developed for the Si1-x Gex /Si system. The defect structure and atomic distributions in the films are studied in detail using advanced electron-microscopy techniques, including aberration corrected STEM imaging and EELS mapping of the average diamond–cubic lattice.
Background: Meiotic recombination has traditionally been explained based on the structural requirement to stabilize homologous chromosome pairs to ensure their proper meiotic segregation. Competing hypotheses seek to explain the emerging findings of significant heterogeneity in recombination rates within and between genomes, but intraspecific comparisons of genome-wide recombination patterns are rare. The honey bee (Apis mellifera) exhibits the highest rate of genomic recombination among multicellular animals with about five cross-over events per chromatid.
Results: Here, we present a comparative analysis of recombination rates across eight genetic linkage maps of the honey bee genome to investigate which genomic sequence features are correlated with recombination rate and with its variation across the eight data sets, ranging in average marker spacing ranging from 1 Mbp to 120 kbp. Overall, we found that GC content explained best the variation in local recombination rate along chromosomes at the analyzed 100 kbp scale. In contrast, variation among the different maps was correlated to the abundance of microsatellites and several specific tri- and tetra-nucleotides.
Conclusions: The combined evidence from eight medium-scale recombination maps of the honey bee genome suggests that recombination rate variation in this highly recombining genome might be due to the DNA configuration instead of distinct sequence motifs. However, more fine-scale analyses are needed. The empirical basis of eight differing genetic maps allowed for robust conclusions about the correlates of the local recombination rates and enabled the study of the relation between DNA features and variability in local recombination rates, which is particularly relevant in the honey bee genome with its exceptionally high recombination rate.
![129253-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-04/129253-Thumbnail%20Image.png?versionId=zzfY3UcXgXim_mhVNBayjejsgp72DoLr&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240617/us-west-2/s3/aws4_request&X-Amz-Date=20240617T120649Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=9ec79e57dcc4771f71dff8d62bd5cab569f18bb75b47687b5ca58cdc3a1e3b40&itok=_u2-crcn)
In this paper, we report on the highly conductive layer formed at the crystalline γ-alumina/SrTiO3 interface, which is attributed to oxygen vacancies. We describe the structure of thin γ-alumina layers deposited by molecular beam epitaxy on SrTiO3 (001) at growth temperatures in the range of 400–800 °C, as determined by reflection-high-energy electron diffraction, x-ray diffraction, and high-resolution electron microscopy. In situ x-ray photoelectron spectroscopy was used to confirm the presence of the oxygen-deficient layer. Electrical characterization indicates sheet carrier densities of ∼1013 cm−2 at room temperature for the sample deposited at 700 °C, with a maximum electron Hall mobility of 3100 cm2V-1s-1 at 3.2 K and room temperature mobility of 22 cm2V-1s-1. Annealing in oxygen is found to reduce the carrier density and turn a conductive sample into an insulator.
![129317-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-04/129317-Thumbnail%20Image.png?versionId=3nGXYAbkRrUAwaQnE_GxHHGCwkcuGU1L&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240615/us-west-2/s3/aws4_request&X-Amz-Date=20240615T030154Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=3136efb4ca864f53b4e0418cf8a237327e49fd4c8ca5c1c63cf3cca3edc3ace4&itok=tv0sV7Sk)
The development of non-volatile logic through direct coupling of spontaneous ferroelectric polarization with semiconductor charge carriers is nontrivial, with many issues, including epitaxial ferroelectric growth, demonstration of ferroelectric switching and measurable semiconductor modulation. Here we report a true ferroelectric field effect—carrier density modulation in an underlying Ge(001) substrate by switching of the ferroelectric polarization in epitaxial c-axis-oriented BaTiO3 grown by molecular beam epitaxy. Using the density functional theory, we demonstrate that switching of BaTiO3 polarization results in a large electric potential change in Ge. Aberration-corrected electron microscopy confirms BaTiO3 tetragonality and the absence of any low-permittivity interlayer at the interface with Ge. The non-volatile, switchable nature of the single-domain out-of-plane ferroelectric polarization of BaTiO3 is confirmed using piezoelectric force microscopy. The effect of the polarization switching on the conductivity of the underlying Ge is measured using microwave impedance microscopy, clearly demonstrating a ferroelectric field effect.
![129431-Thumbnail Image.png](https://d1rbsgppyrdqq4.cloudfront.net/s3fs-public/styles/width_400/public/2021-04/129431-Thumbnail%20Image.png?versionId=ymrA4hMz7S9.8CSJ99mWwI4vXEQ0Dgp4&X-Amz-Content-Sha256=UNSIGNED-PAYLOAD&X-Amz-Algorithm=AWS4-HMAC-SHA256&X-Amz-Credential=AKIASBVQ3ZQ42ZLA5CUJ/20240617/us-west-2/s3/aws4_request&X-Amz-Date=20240617T204225Z&X-Amz-SignedHeaders=host&X-Amz-Expires=120&X-Amz-Signature=847bd26549f9e44d61fa366ef63e009aa53812fea850e829759a5e6510ede235&itok=zMpOzg7K)
We report a study of the magnetic domain structure of nanocrystalline thin films of nickel-zinc ferrite. The ferrite films were synthesized using aqueous spin-spray coating at low temperature (∼90 °C) and showed high complex permeability in the GHz range. Electron microscopy and microanalysis revealed that the films consisted of columnar grains with uniform chemical composition. Off-axis electron holography combined with magnetic force microscopy indicated a multi-grain domain structure with in-plane magnetization. The correlation between the magnetic domain morphology and crystal structure is briefly discussed.