In this letter, we study the near-field radiative heat transfer between two metamaterial substrates coated with silicon carbide (SiC) thin films. It is known that metamaterials can enhance the near-field heat transfer over ordinary materials due to excitation of magnetic plasmons associated with s polarization, while strong surface phonon polariton exists for SiC. By careful tuning of the optical properties of metamaterial, it is possible to excite electrical and magnetic resonances for the metamaterial and surface phonon polaritons for SiC at different spectral regions, resulting in the enhanced heat transfer. The effect of the SiC film thickness at different vacuum gaps is investigated. Results obtained from this study will be beneficial for application of thin film coatings for energy harvesting.
In this work, a selective solar absorber made of nanostructured titanium gratings deposited on an ultrathin MgF2 spacer and a tungsten ground film is proposed and experimentally demonstrated. Normal absorptance of the fabricated solar absorber is characterized to be higher than 0.9 in the UV, visible and, near infrared (IR) regime, while the mid-IR emittance is around 0.2. The high broadband absorption in the solar spectrum is realized by the excitation of surface plasmon and magnetic polariton resonances, while the low mid-IR emittance is due to the highly reflective nature of the metallic components. Further directional and polarized reflectance measurements show wide-angle and polarization-insensitive high absorption within solar spectrum. Temperature-dependent spectroscopic characterization indicates that the optical properties barely change at elevated temperatures up to 350 °C. The solar-to-heat conversion efficiency with the fabricated metamaterial solar absorber is predicted to be 78% at 100 °C without optical concentration or 80% at 400 °C with 25 suns. The performance could be further improved with better fabrication processes and geometric optimization during metamaterial design. The strong spectral selectivity, favorable diffuse-like behavior, and good thermal stability make the metamaterial selective absorber promising for significantly enhancing solar thermal energy harvesting in various systems at mid to high temperatures.
materials for lithium-based batteries: silicon (Si) and metal lithium (Li). It will focus on
studying the mechanical behaviors of the two materials during charge and discharge and
understanding how these mechanical behaviors may affect their electrochemical
performance.
In the first part, amorphous Si anode will be studied. Despite many existing studies
on silicon (Si) anodes for lithium ion batteries (LIBs), many essential questions still exist
on compound formation, composition, and properties. Here it is shown that some
previously accepted findings do not truthfully reflect the actual lithiation mechanisms in
realistic battery configurations. Furthermore the correlation between structure and
mechanical properties in these materials has not been properly established. Here, a rigorous
and thorough study is performed to comprehensively understand the electrochemical
reaction mechanisms of amorphous-Si (a-Si) in a realistic LIB configuration. In-depth
microstructural characterization was performed and correlations were established between
Li-Si composition, volumetric expansion, and modulus/hardness. It is found that the
lithiation process of a-Si in a real battery setup is a single-phase reaction rather than the
accepted two-phase reaction obtained from in-situ TEM experiments. The findings in this
dissertation establish a reference to quantitatively explain many key metrics for lithiated a
Si as anodes in real LIBs, and can be used to rationally design a-Si based high-performance
LIBs guided by high-fidelity modeling and simulations.
In the second part, Li metal anode will be investigated. Problems related to dendrite
growth on lithium metal anodes such as capacity loss and short circuit present major
barriers to the next-generation high-energy-density batteries. The development of
successful mitigation strategies is impeded by the incomplete understanding of the Li
dendrite growth mechanisms. Here the enabling role of plating residual stress in dendrite
initiation through novel experiments of Li electrodeposition on soft substrates is confirmed,
and the observations is explained with a stress-driven dendrite growth model. Dendrite
growth is mitigated on such soft substrates through surface-wrinkling-induced stress
relaxation in deposited Li film. It is demonstrated that this new dendrite mitigation
mechanism can be utilized synergistically with other existing approaches in the form of
three-dimensional (3D) soft scaffolds for Li plating, which achieves superior coulombic
efficiency over conventional hard copper current collectors under large current density.
The pads were created using varying amounts of LM and matrix materials ranging from copper microspheres to diamond powder mixed into PDMS using a high-speed mixer. The material was then cast into molds and cured to create the pads. Once the pads were created, the difficulty came in quantifying their thermal properties. A stepped bar apparatus (SBA) following ASTM D5470 was created to measure the thermal resistance of the pads but it was determined that thermal conductivity was a more usable metric of the pads’ performance. This meant that the pad’s in-situ thickness was needed during testing, prompting the installation of a linear encoder to measure the thickness. The design and analysis of the necessary modification and proposed future design is further detailed in the following paper.
Insulin-like growth factor 1 (IGF1) is an important biomarker for the management of growth hormone disorders. Recently there has been rising interest in deploying mass spectrometric (MS) methods of detection for measuring IGF1. However, widespread clinical adoption of any MS-based IGF1 assay will require increased throughput and speed to justify the costs of analyses, and robust industrial platforms that are reproducible across laboratories. Presented here is an MS-based quantitative IGF1 assay with performance rating of >1,000 samples/day, and a capability of quantifying IGF1 point mutations and posttranslational modifications. The throughput of the IGF1 mass spectrometric immunoassay (MSIA) benefited from a simplified sample preparation step, IGF1 immunocapture in a tip format, and high-throughput MALDI-TOF MS analysis. The Limit of Detection and Limit of Quantification of the resulting assay were 1.5 μg/L and 5 μg/L, respectively, with intra- and inter-assay precision CVs of less than 10%, and good linearity and recovery characteristics. The IGF1 MSIA was benchmarked against commercially available IGF1 ELISA via Bland-Altman method comparison test, resulting in a slight positive bias of 16%. The IGF1 MSIA was employed in an optimized parallel workflow utilizing two pipetting robots and MALDI-TOF-MS instruments synced into one-hour phases of sample preparation, extraction and MSIA pipette tip elution, MS data collection, and data processing. Using this workflow, high-throughput IGF1 quantification of 1,054 human samples was achieved in approximately 9 hours. This rate of assaying is a significant improvement over existing MS-based IGF1 assays, and is on par with that of the enzyme-based immunoassays. Furthermore, a mutation was detected in ∼1% of the samples (SNP: rs17884626, creating an A→T substitution at position 67 of the IGF1), demonstrating the capability of IGF1 MSIA to detect point mutations and posttranslational modifications.
In vitro rearing is an important and useful tool for honey bee (Apis mellifera L.) studies. However, it often results in intercastes between queens and workers, which are normally are not seen in hive-reared bees, except when larvae older than three days are grafted for queen rearing. Morphological classification (queen versus worker or intercastes) of bees produced by this method can be subjective and generally depends on size differences. Here, we propose an alternative method for caste classification of female honey bees reared in vitro, based on weight at emergence, ovariole number, spermatheca size and size and shape, and features of the head, mandible and basitarsus. Morphological measurements were made with both traditional morphometric and geometric morphometrics techniques. The classifications were performed by principal component analysis, using naturally developed queens and workers as controls. First, the analysis included all the characters. Subsequently, a new analysis was made without the information about ovariole number and spermatheca size. Geometric morphometrics was less dependent on ovariole number and spermatheca information for caste and intercaste identification. This is useful, since acquiring information concerning these reproductive structures requires time-consuming dissection and they are not accessible when abdomens have been removed for molecular assays or in dried specimens. Additionally, geometric morphometrics divided intercastes into more discrete phenotype subsets. We conclude that morphometric geometrics are superior to traditional morphometrics techniques for identification and classification of honey bee castes and intermediates.