since the late 1990s, with the ultimate goal of improving the multi-threat capabilities of
traditional soft-body armor while significantly improving its protective efficiency - the amount
of layers of armor material required to defeat threats. To create a novel, superior materials
system to reinforce Kevlar armor for the Norica Capstone project, this thesis set out to
synthesize, recover, and characterize zinc oxide nanowire colloids.
The materials synthesized were successfully utilized in the wider Capstone effort to
dramatically enhance the protective abilities of Kevlar, while the data obtained on the 14
hydrothermal synthesis attempts and numerous challenges at recovery provided critical
information on the synthesis parameters involved in the reliable, scalable mass production of the
nanomaterial additive. Additionally, recovery was unconventionally facilitated in the absence of
a vacuum filtration apparatus with nanoscale filters by intentionally inducing electrostatic
agglomeration of the nanowires during standard gravity filtration. The subsequent application of
these nanowires constituted a pioneering use in the production of nanowire-reinforced
STF-based Kevlar coatings, and support the future development and, ultimately, the
commercialization of lighter and more-protective soft armor systems.
My thesis, Design of Hierarchically Porous Materials Containing Covalent Organic Frameworks, focuses on testing the validity of incorporating nanoporous organic materials into macroporous scaffolding to improve the functionality of covalent organic frameworks as materials for filtration applications. The macroporous scaffold was based off of a material recently described in literature and the bulk of the experimentation was focused on the effects of the necessary processing for the creation of the macroporous material on the structure of the covalent organic frameworks. The property primarily investigated was the Brunauer-Emmett-Teller surface area, as the applicability of the frameworks is largely determined by their nanoporous surface area.
The recent discoveries of 2D van der Waals (vdW) materials have led to the realization of 2D magnetic crystals. Previously debated and thought impossible, transition metal halides (TMH) have given rise to layer dependent magnetism. Using these TMH as a basis, an alloy composing of Fe1-xNixCl2 (where 0 ≤ x ≤ 1) was grown using chemical vapor transport. The intrigue for this alloy composition stems from the interest in spin canting and magnet moment behavior since NiCl2 has in-plane ferromagnetism whereas FeCl2 has out-of-plane ferromagnetism. While in its infancy, this project lays out a foundation to fully develop and characterize this TMH via cationic alloying. To study the magnetic properties of this alloy system, Vibrating Sample Magnetometry was employed extensively to measure the magnetism as a function of temperature as well as applied magnetic field. Future work with use a combination of X-Ray Diffraction, Raman, Scanning Electron Microscopy, and Energy-Dispersive X-Ray Spectroscopy Mapping to verify homogeneous alloying rather than phase separation. Additionally, ellipsometry will be used with Kramer-Kronig relations to extract the dielectric constant from Fe1-xNixCl2. This work lays the foundation for future, fruitful work to prepare this vdW cationic alloy for eventual device applications.