Matching Items (6)
Filtering by
- Genre: Masters Thesis
Description
Gold-silver alloy nanoparticles (NPs) capped with adenosine 5'-triphosphate were synthesized by borohydride reduction of dilute aqueous metal precursors. High-resolution transmission electron microscopy showed the as-synthesized particles to be spherical with average diameters ~4 nm. Optical properties were measured by UV-Visible spectroscopy (UV-Vis), and the formation of alloy NPs was verified across all gold:silver ratios by a linear shift in the plasmon band maxima against alloy composition. The molar absorptivities of the NPs decreased non-linearly with increasing gold content from 2.0 x 108 M-1 cm-1 (fÉmax = 404 nm) for pure silver to 4.1 x 107 M-1 cm-1 (fÉmax = 511 nm) for pure gold. The NPs were immobilized onto transparent indium-tin oxide composite electrodes using layer-by-layer (LbL) deposition with poly(diallyldimethylammonium) acting as a cationic binder. The UV-Vis absorbance of the LbL film was used to calculate the surface coverage of alloy NPs on the electrode. Typical preparations had average NP surface coverages of 2.8 x 10-13 mol NPs/cm2 (~5% of cubic closest packing) with saturated films reaching ~20% of ccp for single-layer preparations (1.0 ~ 10-12 mol NPs/cm2). X-ray photoelectron spectroscopy confirmed the presence of alloy NPs in the LbL film and showed silver enrichment of the NP surfaces by ~9%. Irreversible oxidative dissolution (dealloying) of the less noble silver atoms from the NPs on LbL electrodes was performed by cyclic voltammetry (CV) in sulfuric acid. Alloy NPs with higher gold content required larger overpotentials for silver dealloying. Dealloying of the more-noble gold atoms from the alloy NPs was also achieved by CV in sodium chloride. The silver was oxidized first to cohesive silver chloride, and then gold dealloyed to soluble HAuCl4- at higher potentials. Silver oxidation was inhibited during the first oxidative scan, but subsequent cycles showed typical, reversible silver-to-silver chloride voltammetry. The potentials for both silver oxidation and gold dealloying also shifted to more oxidizing potentials with increasing gold content, and both processes converged for alloy NPs with >60% gold content. Charge-mediated electrochemistry of silver NPs immobilized in LbL films, using Fc(meOH) as the charge carrier, showed that 67% of the NPs were electrochemically inactive.
ContributorsStarr, Christopher A (Author) / Buttry, Daniel A (Thesis advisor) / Petuskey, William (Committee member) / Jones, Anne (Committee member) / Arizona State University (Publisher)
Created2014
Description
Alkali treated aluminosilicate (geopolymer) was functionalized by surfactant to increase the hydrophobicity for making Pickering emulsion for the first part of this work. In the first part of this study, alkali treated metakaolin was functionalized with cetyltrimethylammonium bromide ((C16H33)N(CH3)3Br, CTAB). The electrostatic interaction between this quaternary ammonium and the surface of the aluminosilicate which has negative charge has taken place. The particles then were used to prepare Pickering emulsion. The resulting stable dispersions, obtained very fast at very simple conditions with low ratio of aluminosilicate to liquid phase. In the second part, the interaction between geopolymer and glycerol was studied to see the covalent grafting of the geopolymer for making geopolymer composite. The composite material would be the basis material to be used as support catalyst, thin coating reagent and flame retardant material and so on, Variety of techniques, Thermogravimetric (TGA), Particle-induced X-ray emission (PIXE), FTIR, Solid state NMR, Powder X-ray diffraction (PXRD), BET surface area, Elemental analysis (CHN), TEM, SEM and Optical microscopy were used to characterize the functionalized geopolymer.
ContributorsMesgar, Milad (Author) / Seo, Dong-Kuyn (Thesis advisor) / Petuskey, William (Committee member) / Gould, Ian (Committee member) / Arizona State University (Publisher)
Created2012
Description
Many natural and synthetic quinones have shown biological and pharmacological activity. Some of them have also shown anticancer activity. Ubiquinone (CoQ10) which is a natural quinone, is a component of the electron transport chain and participates in generation of ATP (adenosine triphosphate). Cellular oxidative stress is key feature of many neurodegenerative diseases such as Friedreich's ataxia, Alzheimer's disease and Parkinson's disease. The increased generation of reactive oxygen species damages cell membranes and leads to cell death. Analogues of ubiquinone in the form of pyrimidinols and pyridinols, were effective in protecting Friedreich's ataxia lymphocytes from oxidative stress- induced cell death. There were some structural features which could be identified that should be useful for the design of the analogues for cellular protection against oxidative stress. There are quinones such as doxorubicin, daunomycin and topopyrones which have anticancer activity. Here I evaluated topopyrone analogues which poison both topoisomerases I and II. The topopyrone analogues were lethal to human breast cancer cells, but these analogues were not as potent as camptothecin.
ContributorsRaghav, Nidhi (Author) / Hecht, Sidney M. (Thesis advisor) / Gould, Ian R (Committee member) / Williams, Peter (Committee member) / Arizona State University (Publisher)
Created2011
Description
For cold chain tracking systems, precision and versatility across varying time intervals and temperature ranges remain integral to effective application in clinical, commercial, and academic settings. Therefore, while electronic and chemistry/physics based cold chain tracking mechanisms currently exist, both have limitations that affect their application across various biospecimens and commercial products, providing the initiative to develop a time temperature visual indicator system that resolves challenges with current cold chain tracking approaches. As a result, a permanganate/oxalic acid time temperature visual indicator system for cold chain tracking has been proposed. At thawing temperatures, the designed permanganate/oxalic acid reaction system undergoes a pink to colorless transition as permanganate, Mn(VII), is reduced to auto-catalytic Mn(II), while oxalate is oxidized to CO2. Therefore, when properly stored and vitrified or frozen, the proposed visual indicator remains pink, whereas exposure to thawing conditions will result in an eventual, time temperature dependent, designed color transition that characterizes compromised biospecimen integrity. To design visual indicator systems for targeted times at specific temperatures, absorbance spectroscopy was utilized to monitor permanganate kinetic curves by absorbance at 525 nm. As a result, throughout the outlined research, the following aims were demonstrated: (i) Design and functionality of 1x (0.5 mM KMnO4) visual indicator systems across various time intervals at temperatures ranging from 25°C to -20°C, (ii) Design and functionality of high concentration, 5x, visual indicator systems across varying targeted time intervals at temperatures ranging from 25°C to 0°C, (iii) Pre-activation stability and long-term stability of the proposed visual indicator systems.
ContributorsLjungberg, Emil (Author) / Borges, Chad (Thesis advisor) / Levitus, Marcia (Committee member) / Williams, Peter (Committee member) / Arizona State University (Publisher)
Created2024
Description
Oxygen fugacity (ƒO2) is a thermodynamic variable used to represent the redox state of a material or a system. It is equivalent to the partial pressure of oxygen in a particular environment corrected for the non-ideal behavior of the gas. ƒO2 is often used to indicate the potential for iron to occur in a more oxidized or reduced state at a particular temperature and pressure in a natural system. Secondary ion mass spectrometry (SIMS) is a powerful analytical instrument that can be used to analyze elemental and isotopic compositional information about microscopic features within solid materials. SIMS analyses of the secondary ion energy distribution of semi-pure metals demonstrate that the energy spectrum of individual mass lines can provide information about alterations in its surface environment.
The application of high-resolution (see Appendix C) energy spectrum calibrations to natural ilmenite led to the investigation of zirconium (90Zr+) and niobium (93Nb+) as potential indicators of sample ƒO2. Energy spectrum measurements were performed on an array of ilmenite crystals from the earth’s upper mantle retrieved from kimberlites and from a reduced meteorite. In all studied materials, variability in the peak shape and width of the energy spectra has been correlated with inferred sample ƒO2. The best descriptor of this relationship is the full-width at half-maximum (FWHM; see Appendix C) of the energy spectra for each sample. It has been estimated that a 1eV change in the FWHM of 93Nb+ energy spectra is roughly equivalent to 1 log unit ƒO2. Simple estimates of precision suggest the FWHM values can be trusted to 1eV and sample ƒO2 can be predicted to ±1 log unit, assuming the temperature of formation is known.
The work of this thesis also explores the applicability of this technique beyond analysis of semi-pure metals and ilmenite crystals from kimberlites. This technique was applied to titanium oxides experimentally formed at known ƒO2 as well as an ilmenite crystal that showed compositional variations across the grain (i.e., core to rim chemical variations). Analyses of titanium oxides formed at known ƒO2 agree with the estimation that 1 eV change in the FWHM of 93Nb+ is equivalent to ~1 log unit ƒO2 (in all cases but one); this is also true for analyses of a natural ilmenite crystal with compositional variations across the grain.
The application of high-resolution (see Appendix C) energy spectrum calibrations to natural ilmenite led to the investigation of zirconium (90Zr+) and niobium (93Nb+) as potential indicators of sample ƒO2. Energy spectrum measurements were performed on an array of ilmenite crystals from the earth’s upper mantle retrieved from kimberlites and from a reduced meteorite. In all studied materials, variability in the peak shape and width of the energy spectra has been correlated with inferred sample ƒO2. The best descriptor of this relationship is the full-width at half-maximum (FWHM; see Appendix C) of the energy spectra for each sample. It has been estimated that a 1eV change in the FWHM of 93Nb+ energy spectra is roughly equivalent to 1 log unit ƒO2. Simple estimates of precision suggest the FWHM values can be trusted to 1eV and sample ƒO2 can be predicted to ±1 log unit, assuming the temperature of formation is known.
The work of this thesis also explores the applicability of this technique beyond analysis of semi-pure metals and ilmenite crystals from kimberlites. This technique was applied to titanium oxides experimentally formed at known ƒO2 as well as an ilmenite crystal that showed compositional variations across the grain (i.e., core to rim chemical variations). Analyses of titanium oxides formed at known ƒO2 agree with the estimation that 1 eV change in the FWHM of 93Nb+ is equivalent to ~1 log unit ƒO2 (in all cases but one); this is also true for analyses of a natural ilmenite crystal with compositional variations across the grain.
ContributorsDillon, Sarah Marie (Author) / Hervig, Richard L (Thesis advisor) / Shim, Sang-Heon (Committee member) / Williams, Peter (Committee member) / Arizona State University (Publisher)
Created2019
Description
The microstructure development of Inconel alloy 718 (IN718) during conventional processing has been extensively studied and much has been discovered as to the mechanisms behind the exceptional creep resistance that the alloy exhibits. More recently with the development of large scale 3D printing of alloys such as IN718 a new dimension of complexity has emerged in the understanding of alloy microstructure development, hence, potential alloy development opportunity for IN718.
This study is a broad stroke at discovering possible alternate microstructures developing in Direct-Metal-Laser-Sintering (DMLS) processed IN718 compared to those in conventional wrought IN718. The main inspiration for this study came from creep test results from several DMLS IN718 samples at Honeywell that showed a significant
improvement in creep capabilities for DMLS718 compared to cast and wrought IN718 (Honeywell).
From this data the steady-state creep rates were evaluated and fitted to current creep models in order to identify active creep mechanisms in conventional and DMLS IN718 and illuminate the potential factors responsible for the improved creep behavior in DMSL processed IN718.
Because rapid heating and cooling can introduce high internal stress and impact microstructural development, such as gamma double prime formations (Oblak et al.), leading to differences in material behavior, DMLS and conventional IN718 materials are studied using SEM and TEM characterization to investigate sub-micron and/or nano-scale
microstructural differences developed in the DMLS samples as a result of their complex thermal history and internal stress.
The preliminary analysis presented in this body of work is an attempt to better understand the effect of DMLS processing in quest for development of optimization techniques for DMLS as a whole. A historical sketch of nickel alloys and the development of IN718 is given. A literature review detailing the microstructure of IN718 is presented. Creep data analysis and identification of active creep mechanisms are evaluated. High-resolution microstructural characterization of DMLS and wrought IN718 are discussed in detail throughout various chapters of this thesis. Finally, an initial effort in developing a processing model that would allow for parameter optimization is presented.
This study is a broad stroke at discovering possible alternate microstructures developing in Direct-Metal-Laser-Sintering (DMLS) processed IN718 compared to those in conventional wrought IN718. The main inspiration for this study came from creep test results from several DMLS IN718 samples at Honeywell that showed a significant
improvement in creep capabilities for DMLS718 compared to cast and wrought IN718 (Honeywell).
From this data the steady-state creep rates were evaluated and fitted to current creep models in order to identify active creep mechanisms in conventional and DMLS IN718 and illuminate the potential factors responsible for the improved creep behavior in DMSL processed IN718.
Because rapid heating and cooling can introduce high internal stress and impact microstructural development, such as gamma double prime formations (Oblak et al.), leading to differences in material behavior, DMLS and conventional IN718 materials are studied using SEM and TEM characterization to investigate sub-micron and/or nano-scale
microstructural differences developed in the DMLS samples as a result of their complex thermal history and internal stress.
The preliminary analysis presented in this body of work is an attempt to better understand the effect of DMLS processing in quest for development of optimization techniques for DMLS as a whole. A historical sketch of nickel alloys and the development of IN718 is given. A literature review detailing the microstructure of IN718 is presented. Creep data analysis and identification of active creep mechanisms are evaluated. High-resolution microstructural characterization of DMLS and wrought IN718 are discussed in detail throughout various chapters of this thesis. Finally, an initial effort in developing a processing model that would allow for parameter optimization is presented.
ContributorsRogers, Blake Kenton (Author) / Tasooji, Amaneh (Thesis advisor) / Petuskey, William (Committee member) / Rogers, Bradley (Committee member) / Arizona State University (Publisher)
Created2017