This dissertation aims to demonstrate a new approach to fabricating solar cells for spectrum-splitting photovoltaic systems with the potential to reduce their cost and complexity of manufacturing, called Monolithically Integrated Laterally Arrayed Multiple Band gap (MILAMB) solar cells. Single crystal semiconductor alloy nanowire (NW) ensembles are grown with the alloy composition and band gap changing continuously across a broad range over the surface of a single substrate in a single, inexpensive growth step by the Dual-Gradient Method. The nanowire ensembles then serve as the absorbing materials in a set of solar cells for spectrum-splitting photovoltaic systems.
Preliminary design and simulation studies based on Anderson's model band line-ups were undertaken for CdPbS and InGaN alloys. Systems of six subcells obtained efficiencies in the 32-38% range for CdPbS and 34-40% for InGaN at 1-240 suns, though both materials systems require significant development before these results could be achieved experimentally. For an experimental demonstration, CdSSe was selected due to its availability. Proof-of-concept CdSSe nanowire ensemble solar cells with two subcells were fabricated simultaneously on one substrate. I-V characterization under 1 sun AM1.5G conditions yielded open-circuit voltages (Voc) up to 307 and 173 mV and short-circuit current densities (Jsc) up to 0.091 and 0.974 mA/cm2 for the CdS- and CdSe-rich cells, respectively. Similar thin film cells were also fabricated for comparison. The nanowire cells showed substantially higher Voc than the film cells, which was attributed to higher material quality in the CdSSe absorber. I-V measurements were also conducted with optical filters to simulate a simple form of spectrum-splitting. The CdS-rich cells showed uniformly higher Voc and fill factor (FF) than the CdSe-rich cells, as expected due to their larger band gaps. This suggested higher power density was produced by the CdS-rich cells on the single-nanowire level, which is the principal benefit of spectrum-splitting. These results constitute a proof-of-concept experimental demonstration of the MILAMB approach to fabricating multiple cells for spectrum-splitting photovoltaics. Future systems based on this approach could help to reduce the cost and complexity of manufacturing spectrum-splitting photovoltaic systems and offer a low cost alternative to multi-junction tandems for achieving high efficiencies.
Preliminary design and simulation studies based on Anderson's model band line-ups were undertaken for CdPbS and InGaN alloys. Systems of six subcells obtained efficiencies in the 32-38% range for CdPbS and 34-40% for InGaN at 1-240 suns, though both materials systems require significant development before these results could be achieved experimentally. For an experimental demonstration, CdSSe was selected due to its availability. Proof-of-concept CdSSe nanowire ensemble solar cells with two subcells were fabricated simultaneously on one substrate. I-V characterization under 1 sun AM1.5G conditions yielded open-circuit voltages (Voc) up to 307 and 173 mV and short-circuit current densities (Jsc) up to 0.091 and 0.974 mA/cm2 for the CdS- and CdSe-rich cells, respectively. Similar thin film cells were also fabricated for comparison. The nanowire cells showed substantially higher Voc than the film cells, which was attributed to higher material quality in the CdSSe absorber. I-V measurements were also conducted with optical filters to simulate a simple form of spectrum-splitting. The CdS-rich cells showed uniformly higher Voc and fill factor (FF) than the CdSe-rich cells, as expected due to their larger band gaps. This suggested higher power density was produced by the CdS-rich cells on the single-nanowire level, which is the principal benefit of spectrum-splitting. These results constitute a proof-of-concept experimental demonstration of the MILAMB approach to fabricating multiple cells for spectrum-splitting photovoltaics. Future systems based on this approach could help to reduce the cost and complexity of manufacturing spectrum-splitting photovoltaic systems and offer a low cost alternative to multi-junction tandems for achieving high efficiencies.
ContributorsCaselli, Derek (Author) / Ning, Cun-Zheng (Thesis advisor) / Tao, Meng (Committee member) / Yu, Hongbin (Committee member) / Vasileska, Dragica (Committee member) / Arizona State University (Publisher)
Created2014
Description
In this work, I worked on the synthesis and characterization of nanowires and belts, grown using different materials, in Chemical Vapor Deposition (CVD) system with catalytic growth method. Through this thesis, I utilized the Photoluminescence (PL), Secondary Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS) and X-ray diffraction (XRD) analyses to find out the properties of Erbium Chloride Silicate (ECS) and two segment CdS-CdSe samples. In the first part of my research, growth of very new material, Erbium Chloride Silicate (ECS), in form of core/shell Si/ECS and pure ECS nanowires, was demonstrated. This new material has very fascinating properties for new Si based photonic devices. The Erbium density in those nanowires is which is very high value compared to the other Erbium doped materials. It was shown that the luminescence peaks of ECS nanowires are very sharp and stronger than their counterparts. Furthermore, both PL and XRD peaks get sharper and stronger as growth temperature increases and this shows that crystalline quality of ECS nanowires gets better with higher temperature. In the second part, I did a very detail research for growing two segment axial nanowires or radial belts and report that the structure type mostly depends on the growth temperature. Since our final step is to create white light LEDs using single axial nanowires which have three different regions grown with distinct materials and give red, green and blue colors simultaneously, we worked on growing CdS-CdSe nanowires or belts for the first step of our aim. Those products were successfully grown and they gave two luminescence peaks with maximum 160 nm wavelength separation depending on the growth conditions. It was observed that products become more likely belt once the substrate temperature increases. Also, dominance between VLS and VS is very critical to determine the shape of the products and the substitution of CdS by CdSe is very effective; hence, CdSe growth time should be chosen accordingly. However, it was shown two segmented products can be synthesized by picking the right conditions and with very careful analyses. We also demonstrated that simultaneous two colors lasing from a single segmented belt structures is possible with strong enough-pumping-power.
ContributorsTurkdogan, Sunay (Author) / Ning, Cun-Zheng (Thesis advisor) / Tao, Meng (Committee member) / Yu, Hongbin (Committee member) / Arizona State University (Publisher)
Created2012
Description
Nanowires are 1D rod-like structures which are regarded as the basis for future technologies. III-V nanowires have attracted immense attention because of their stability, crystal quality and wide use. In this work, I focus on the growth and characterization of III-V semiconductor nanowires, in particular GaP, InP and InGaP alloys. These nanowires were grown using a hot wall CVD(Chemical Vapor Deposition) setup and are characterized using SEM (Scanning Electron Microscope), EDX (Energy Dispersive X-ray Spectroscopy) and PL (Photoluminescence) techniques.
In the first chapter, Indium Phosphide nanowires were grown using elemental sources (In and P powders). I consider the various kinds of InP morphologies grown using this method. The effect of source temperature on the stoichiometry and optical properties of nanowires is studied. Lasing behavior has been seen in InP nanostructures, showing superior material quality of InP.
InGaP alloy nanowires were grown using compound and elemental sources. Nanowires grown using compound sources have significant oxide incorporation and showed kinky morphology. Nanowires grown using elemental sources had no oxide and showed better optical quality. Also, these samples showed a tunable alloy composition across the entire substrate covering more than 50% of the InGaP alloy system. Integrated intensity showed that the bandgap of the nanowires changed from indirect to direct bandgap with increasing Indium composition. InGaP alloy nanowires were compared with Gallium Phosphide nanowires in terms of PL emission, using InGaP nanowires it is possible to grow nanowires free of defects and oxygen impurities, which are commonly encountered in GaP nanowires.
In the first chapter, Indium Phosphide nanowires were grown using elemental sources (In and P powders). I consider the various kinds of InP morphologies grown using this method. The effect of source temperature on the stoichiometry and optical properties of nanowires is studied. Lasing behavior has been seen in InP nanostructures, showing superior material quality of InP.
InGaP alloy nanowires were grown using compound and elemental sources. Nanowires grown using compound sources have significant oxide incorporation and showed kinky morphology. Nanowires grown using elemental sources had no oxide and showed better optical quality. Also, these samples showed a tunable alloy composition across the entire substrate covering more than 50% of the InGaP alloy system. Integrated intensity showed that the bandgap of the nanowires changed from indirect to direct bandgap with increasing Indium composition. InGaP alloy nanowires were compared with Gallium Phosphide nanowires in terms of PL emission, using InGaP nanowires it is possible to grow nanowires free of defects and oxygen impurities, which are commonly encountered in GaP nanowires.
ContributorsRanga, Praneeth (Author) / Ning, Cun-Zheng (Thesis advisor) / Palais, Joseph (Committee member) / Tao, Meng (Committee member) / Arizona State University (Publisher)
Created2016