Ge1-ySny alloys represent a new class of photonic materials for integrated optoelectronics on Si. In this work, the electrical and optical properties of Ge1-ySny alloy films grown on Si, with concentrations in the range 0 ≤ y ≤ 0.04, are studied via a variety of methods. The first microelectronic devices from GeSn films were fabricated using newly developed CMOS-compatible protocols, and the devices were characterized with respect to their electrical properties and optical response. The detectors were found to have a detection range that extends into the near-IR, and the detection edge is found to shift to longer wavelengths with increasing Sn content, mainly due to the compositional dependence of the direct band gap E0. With only 2 % Sn, all of the telecommunication bands are covered by a single detector. Room temperature photoluminescence was observed from GeSn films with Sn content up to 4 %. The peak wavelength of the emission was found to shift to lower energies with increasing Sn content, corresponding to the decrease in the direct band gap E0 of the material. An additional peak in the spectrum was assigned to the indirect band gap. The separation between the direct and indirect peaks was found to decrease with increasing Sn concentration, as expected. Electroluminescence was also observed from Ge/Si and Ge0.98Sn0.02 photodiodes under forward bias, and the luminescence spectra were found to match well with the observed photoluminescence spectra. A theoretical expression was developed for the luminescence due to the direct band gap and fit to the data.
ContributorsMathews, Jay (Author) / Menéndez, Jose (Thesis advisor) / Kouvetakis, John (Thesis advisor) / Drucker, Jeffery (Committee member) / Chizmeshya, Andrew (Committee member) / Ponce, Fernando (Committee member) / Arizona State University (Publisher)
Created2011
Description
Group IV alloy films exhibit the ability to tune both band structure and lattice parameters and have recently attracted attention for their potential applications in Si-photonics and photovoltaics. In this work, several new approaches to produce these alloys directly on Si(100) and Ge(100) wafers are developed. For photovoltaics, use of Ge-buffered Si(100) wafers as a low cost platform for epitaxy of In1-xGaxAs layers was explored. The results indicate that this approach has promise for transitioning from bulk Ge platforms to virtual substrates for a significant cost reduction. The electrical and optical properties of Ge and Ge1-ySny layers produced using several different techniques were explored via fabrication of high performance heterostructure photodiodes. First, a new CVD approach to Ge-like materials was developed in which germanium is alloyed with very small amounts of tin. These alloys exhibited no significant difference in their structural properties or band gap compared to pure Ge, however superior photo response and reduced dark currents were observed from fabricated devices relative to pure Ge on Si reference diodes. Additionally, pure Ge/Si(100) photodiodes were fabricated using layers grown via reactions of Ge4H10 on Si(100) and found to exhibit low dark current densities with high collection efficiencies. Ge1-x-ySixSny materials represent the newest member of group IV alloy family. The ability to decouple the lattice constant and the band gap in this system has led to strong interest both for strain/confinement layers in quantum well structures, and as the possible "missing" 1 eV junction in multijunction photovoltaics. Recent progress in this field has allowed for the first time growth, fabrication and measurement of novel photodiodes based on Ge1-x-ySixSny. This work presents the material, electrical and optical properties of Ge1-x-ySixSny layers and photodiodes grown directly on Ge and Si wafers using two different synthetic approaches. A series of photodiodes containing Sn concentrations from 1-5%, all lattice matched to Ge, was fabricated. The devices exhibited low dark current densities with high collection efficiencies as required for photovoltaics. By measuring the photoresponse, tunable band gaps ranging from 0.85 eV to 1.02 eV were observed.
ContributorsBeeler, Richard (Author) / Kouvetakis, John (Thesis advisor) / Menéndez, Jose (Committee member) / Chizmeshya, Andrew (Committee member) / Arizona State University (Publisher)
Created2012
Description
Recently a new materials platform consisting of semiconductors grown on GaSb and InAs substrates with lattice constants close to 6.1 A was proposed by our group for various electronic and optoelectronic applications. This materials platform consists of both II-VI (MgZnCdHg)(SeTe) and III-V (InGaAl)(AsSb) compound semiconductors, which have direct bandgaps spanning the entire energy spectrum from far-IR (~0 eV) up to UV (~3.4 eV). The broad range of bandgaps and material properties make it very attractive for a wide range of applications in optoelectronics, such as solar cells, laser diodes, light emitting diodes, and photodetectors. Moreover, this novel materials system potentially offers unlimited degrees of freedom for integration of electronic and optoelectronic devices onto a single substrate while keeping the best possible materials quality with very low densities of misfit dislocations. This capability is not achievable with any other known lattice-matched semiconductors on any available substrate. In the 6.1-A materials system, the semiconductors ZnTe and GaSb are almost perfectly lattice-matched with a lattice mismatch of only 0.13%. Correspondingly, it is expected that high quality ZnTe/GaSb and GaSb/ZnTe heterostructures can be achieved with very few dislocations generated during growth. To fulfill the task, their MBE growth and material properties are carefully investigated. High quality ZnTe layers grown on various III-V substrates and GaSb grown on ZnTe are successfully achieved using MBE. It is also noticed that ZnTe and GaSb have a type-I band-edge alignment with large band offsets (delta_Ec=0.934 eV, delta_Ev=0.6 eV), which provides strong confinement for both electrons and holes. Furthermore, a large difference in refractive index is found between ZnTe and GaSb (2.7 and 3.9, respectively, at 0.7 eV), leading to excellent optical confinement of the guided optical modes in planar semiconductor lasers or distributed Bragg reflectors (DBR) for vertical-cavity surface-emitting lasers. Therefore, GaSb/ZnTe double-heterostructure and ZnTe/GaSb DBR structure are suitable for use in light emitting devices. In this thesis work, experimental demonstration of these structures with excellent structural and optical properties is reported. During the exploration on the properties of various ZnTe heterostructures, it is found that residual tensile strains exist in the thick ZnTe epilayers when they are grown on GaAs, InP, InAs and GaSb substrates. The presence of tensile strains is due to the difference in thermal expansion coefficients between the epilayers and the substrates. The defect densities in these ZnTe layers become lower as the ZnTe layer thickness increases. Growth of high quality GaSb on ZnTe can be achieved using a temperature ramp during growth. The influence of temperature ramps with different ramping rates in the optical properties of GaSb layer is studied, and the samples grown with a temperature ramp from 360 to 470 C at a rate of 33 C/min show the narrowest bound exciton emission peak with a full width at half maximum of 15 meV. ZnTe/GaSb DBR structures show excellent reflectivity properties in the mid-infrared range. A peak reflectance of 99% with a wide stopband of 480 nm centered at 2.5 um is measured from a ZnTe/GaSb DBR sample of only 7 quarter-wavelength pairs.
ContributorsFan, Jin (Author) / Zhang, Yong-Hang (Thesis advisor) / Smith, David (Committee member) / Yu, Hongbin (Committee member) / Menéndez, Jose (Committee member) / Johnson, Shane (Committee member) / Arizona State University (Publisher)
Created2012
Description
In this dissertation, various characterization techniques have been used to investigate many aspects of the properties of III-nitride materials and devices for optoelectronic applications.
The first part of this work is focused on the evolution of microstructures of BAlN thin films. The films were grown by flow-modulated epitaxy at 1010 oC, with B/(B+Al) gas-flow ratios ranging from 0.06 to 0.18. The boron content obtained from X-ray diffraction (XRD) patterns ranges from x = 0.02 to 0.09, while Rutherford backscattering spectrometry (RBS) measures x = 0.06 to 0.16. Transmission electron microscopy indicates the sole presence of the wurtzite crystal structure in the BAlN films, and a tendency towards twin formation and finer microstructure for B/(B+Al) gas-flow ratios greater than 0.15. The RBS data suggest that the incorporation of B is highly efficient, while the XRD data indicate that the epitaxial growth may be limited by a solubility limit in the crystal phase at about 9%. Electron energy loss spectroscopy has been used to profile spatial variations in the composition of the films. It has also located point defects in the films with nanometer resolution. The defects are identified as B and Al interstitials and N vacancies by comparison of the observed energy thresholds with results of density functional theory calculations.
The second part of this work investigates dislocation clusters observed in thick InxGa1-xN films with 0.07 ≤ x ≤ 0.12. The clusters resemble baskets with a higher indium content at their interior. Threading dislocations at the basket boundaries are of the misfit edge type, and their separation is consistent with misfit strain relaxation due the difference in indium content between the baskets and the surrounding matrix. The base of the baskets exhibits no observable misfit dislocations connected to the threading dislocations, and often no net displacements like those due to stacking faults. It is argued that the origin of these threading dislocation arrays is associated with misfit dislocations at the basal plane that dissociate, forming stacking faults. When the stacking faults form simultaneously satisfying the crystal symmetry, the sum of their translation vectors does add up to zero, consistent with our experimental observations.
The first part of this work is focused on the evolution of microstructures of BAlN thin films. The films were grown by flow-modulated epitaxy at 1010 oC, with B/(B+Al) gas-flow ratios ranging from 0.06 to 0.18. The boron content obtained from X-ray diffraction (XRD) patterns ranges from x = 0.02 to 0.09, while Rutherford backscattering spectrometry (RBS) measures x = 0.06 to 0.16. Transmission electron microscopy indicates the sole presence of the wurtzite crystal structure in the BAlN films, and a tendency towards twin formation and finer microstructure for B/(B+Al) gas-flow ratios greater than 0.15. The RBS data suggest that the incorporation of B is highly efficient, while the XRD data indicate that the epitaxial growth may be limited by a solubility limit in the crystal phase at about 9%. Electron energy loss spectroscopy has been used to profile spatial variations in the composition of the films. It has also located point defects in the films with nanometer resolution. The defects are identified as B and Al interstitials and N vacancies by comparison of the observed energy thresholds with results of density functional theory calculations.
The second part of this work investigates dislocation clusters observed in thick InxGa1-xN films with 0.07 ≤ x ≤ 0.12. The clusters resemble baskets with a higher indium content at their interior. Threading dislocations at the basket boundaries are of the misfit edge type, and their separation is consistent with misfit strain relaxation due the difference in indium content between the baskets and the surrounding matrix. The base of the baskets exhibits no observable misfit dislocations connected to the threading dislocations, and often no net displacements like those due to stacking faults. It is argued that the origin of these threading dislocation arrays is associated with misfit dislocations at the basal plane that dissociate, forming stacking faults. When the stacking faults form simultaneously satisfying the crystal symmetry, the sum of their translation vectors does add up to zero, consistent with our experimental observations.
ContributorsWang, Shuo, Ph.D (Author) / Ponce, Fernando A. (Thesis advisor) / Menéndez, Jose (Committee member) / Rez, Peter (Committee member) / McCartney, Martha (Committee member) / Arizona State University (Publisher)
Created2018
Description
Group-IV semiconductor alloys are of interest for Si-integrated optoelectronic applications due to the band gap tunability and enhanced optical capabilities that can be achieved through compositional tuning. This work advances the field by presenting a systematic study of the optical and electronic properties of Ge1-ySny and analogous Ge1-x-ySixSny alloys.
The fundamental direct and indirect band gaps of Ge1-ySny materials are measured by room temperature photoluminescence in samples containing 0 ≤ y ≤ 0.11 and a transition to direct gap materials is found to occur at yc = 0.087. This result is enabled by the development of sample growth and processing protocols that produce high-quality materials epitaxially on Ge-buffered Si(100) substrates. Strategies to optimize the optical performance are explored by varying the film thickness, thermal and surface treatments, and n-type doping. The electrical and optical properties of diodes based on these materials are characterized by current-voltage, optical responsivity, and electroluminescence measurements. These show improved optical performance near yc with tunable emission out to 2500 nm. Measuring the carrier lifetimes in devices with strain relaxed and fully strained interfaces show significantly longer lifetimes in the fully strained case.
The direct and indirect band gaps of Sn-rich (y > x) Ge1-x-ySixSny materials are measured by room temperature photoluminescence on optimized samples. These data confirm a transition to direct gap materials occurs for the ternary alloy as well. Devices based on compositions 0.02 ≤ x ≤ 0.10 and 0.03 ≤ y ≤ 0.11 are characterized by current-voltage, optical responsivity, and electroluminescence measurements and show competitive performance with analogous devices based on Ge1-ySny materials. A detailed study of the direct gap in Ge1-xSix alloys gives parameters crucial en route to a global description of the Ge1-x-ySixSny fundamental band gaps.
Archetypal laser device designs on Si are explored by fabricating degenerate pn junction diodes and highly doped waveguide devices based on high-quality Ge1-ySny materials. The diodes showed tunnel-like current-voltage characteristics and tailored electroluminescence based on the doping profile. The waveguides demonstrate emission under optical stimulation.
The fundamental direct and indirect band gaps of Ge1-ySny materials are measured by room temperature photoluminescence in samples containing 0 ≤ y ≤ 0.11 and a transition to direct gap materials is found to occur at yc = 0.087. This result is enabled by the development of sample growth and processing protocols that produce high-quality materials epitaxially on Ge-buffered Si(100) substrates. Strategies to optimize the optical performance are explored by varying the film thickness, thermal and surface treatments, and n-type doping. The electrical and optical properties of diodes based on these materials are characterized by current-voltage, optical responsivity, and electroluminescence measurements. These show improved optical performance near yc with tunable emission out to 2500 nm. Measuring the carrier lifetimes in devices with strain relaxed and fully strained interfaces show significantly longer lifetimes in the fully strained case.
The direct and indirect band gaps of Sn-rich (y > x) Ge1-x-ySixSny materials are measured by room temperature photoluminescence on optimized samples. These data confirm a transition to direct gap materials occurs for the ternary alloy as well. Devices based on compositions 0.02 ≤ x ≤ 0.10 and 0.03 ≤ y ≤ 0.11 are characterized by current-voltage, optical responsivity, and electroluminescence measurements and show competitive performance with analogous devices based on Ge1-ySny materials. A detailed study of the direct gap in Ge1-xSix alloys gives parameters crucial en route to a global description of the Ge1-x-ySixSny fundamental band gaps.
Archetypal laser device designs on Si are explored by fabricating degenerate pn junction diodes and highly doped waveguide devices based on high-quality Ge1-ySny materials. The diodes showed tunnel-like current-voltage characteristics and tailored electroluminescence based on the doping profile. The waveguides demonstrate emission under optical stimulation.
ContributorsGallagher, James Dennis (Author) / Menéndez, Jose (Thesis advisor) / Kouvetakis, John (Thesis advisor) / Chizmeshya, Andrew (Committee member) / Ponce, Fernando (Committee member) / Arizona State University (Publisher)
Created2015
Description
ABSTRACT This thesis focuses on structural characterizations and optical properties of Si, Ge based semiconductor alloys. Two material systems are characterized: Si-based III-V/IV alloys, which represent a possible pathway to augment the optical performance of elemental silicon as a solar cell absorber layer, and Ge-based Ge1-ySny and Ge1-x-ySixSny systems which are applicable to long wavelength optoelectronics. Electron microscopy is the primary tool used to study structural properties. Electron Energy Loss spectroscopy (EELS), Ellipsometry, Photoluminescence and Raman Spectroscopy are combined to investigate electronic band structures and bonding properties. The experiments are closely coupled with structural and property modeling and theory. A series of III-V-IV alloys have been synthesized by the reaction of M(SiH3)3 (M = P, As) with Al atoms from a Knudsen cell. In the AlPSi3 system, bonding configurations and elemental distributions are characterized by scanning transmission electron microscopy (STEM)/EELS and correlated with bulk optical behavior. The incorporation of N was achieved by addition of N(SiH3)3 into the reaction mixture yielding [Al(As1-xNx)]ySi5-2yalloys. A critical point analysis of spectroscopic ellipsometry data reveals the existence of direct optical transitions at energies as low as 2.5 eV, well below the lowest direct absorption edge of Si at 3.3 eV. The compositional dependence of the lowest direct gap and indirect gap in Ge1-ySny alloys extracted from room temperature photoluminescence indicates a crossover concentration of yc =0.073, much lower than virtual crystal approximation but agrees well with large atomic supercells predictions. A series of Ge-rich Ge1-x-ySixSny samples with a fixed 3-4% Si content and progressively increasing Sn content in the 4-10% range are grown and characterized by electron microscopy and photoluminescence. The ternary represents an attractive alternative to Ge1-ySny for applications in IR optoelectronic technologies.
ContributorsJiang, Liying (Author) / Menéndez, Jose (Thesis advisor) / Kouvetakis, John (Thesis advisor) / Smith, David J. (Committee member) / Chizmeshya, Andrew V.G (Committee member) / Chamberlin, Ralph (Committee member) / Arizona State University (Publisher)
Created2014
Description
The study of subwavelength behavior of light and nanoscale lasing has broad
potential applications in various forms of computation i.e. optical and quantum, as well as
in energy engineering. Although this field has been under active research, there has been
little work done on describing the behaviors of threshold and saturation. Particularly, how
the gain-molecule behavior affects the lasing behavior has yet to be investigated.
In this work, the interaction of surface-plasmon-polaritons (SPPs) and molecules is
observed in lasing. Various phenomenologies are observed related to the appearance of the
threshold and saturation regions. The lasing profile, as a visual delimiter of lasing threshold
and saturation, is introduced and used to study various parametrical dependencies of lasing,
including the number-density of molecules, the molecular thickness and the frequency
detuning between the molecular transition frequency and the SPP resonant frequency. The
molecular population distributions are studied in terminal and dynamical methods and are
found to contain unexpected and theoretically challenging properties. Using an average
dynamical analysis, the simulated spontaneous emission cascade can be clearly seen.
Finally, theoretical derivations of simple 1D strands of dipoles are presented in both
the exact and mean-field approximation, within the density matrix formalism. Some
preliminary findings are presented, detailing the observed behaviors of some simple
systems.
potential applications in various forms of computation i.e. optical and quantum, as well as
in energy engineering. Although this field has been under active research, there has been
little work done on describing the behaviors of threshold and saturation. Particularly, how
the gain-molecule behavior affects the lasing behavior has yet to be investigated.
In this work, the interaction of surface-plasmon-polaritons (SPPs) and molecules is
observed in lasing. Various phenomenologies are observed related to the appearance of the
threshold and saturation regions. The lasing profile, as a visual delimiter of lasing threshold
and saturation, is introduced and used to study various parametrical dependencies of lasing,
including the number-density of molecules, the molecular thickness and the frequency
detuning between the molecular transition frequency and the SPP resonant frequency. The
molecular population distributions are studied in terminal and dynamical methods and are
found to contain unexpected and theoretically challenging properties. Using an average
dynamical analysis, the simulated spontaneous emission cascade can be clearly seen.
Finally, theoretical derivations of simple 1D strands of dipoles are presented in both
the exact and mean-field approximation, within the density matrix formalism. Some
preliminary findings are presented, detailing the observed behaviors of some simple
systems.
ContributorsBrewer, Andre J (Author) / Sukharev, Maxim (Thesis advisor) / Rivera, Daniel E (Thesis advisor) / Menéndez, Jose (Committee member) / Arizona State University (Publisher)
Created2017
Description
Sn-based group IV materials such as Ge1-xSnx and Ge1-x-ySixSny alloys have great potential for developing Complementary Metal Oxide Semiconductor (CMOS) compatible devices on Si because of their tunable band structure and lattice constants by controlling Si and/or Sn contents. Growth of Ge1-xSnx binaries through Molecular Beam Epitaxy (MBE) started in the early 1980s, producing Ge1-xSnx epilayers with Sn concentrations varying from 0 to 100%. A Chemical Vapor Deposition (CVD) method was developed in the early 2000s for growing Ge1-xSnx alloys of device quality, by utilizing various chemical precursors. This method dominated the growth of Ge1-xSnx alloys rapidly because of the great crystal quality of Ge1-xSnx achieved. As the first practical ternary alloy completely based on group IV elements, Ge1-x-ySixSny decouples bandgap and lattice constant, becoming a prospective CMOS compatible alloy. At the same time, Ge1-x-ySixSny ternary system could serve as a thermally robust alternative to Ge1-ySny binaries given that it becomes a direct semiconductor at a Sn concentration of 6%-10%. Ge1-x-ySixSny growths by CVD is summarized in this thesis. With the Si/Sn ratio kept at ~3.7, the ternary alloy system is lattice matched to Ge, resulting a tunable direct bandgap of 0.8-1.2 eV. With Sn content higher than Si content, the ternary alloy system could have an indirect-to-direct transition, as observed for Ge1-xSnx binaries. This thesis summarizes the development of Ge1-xSnx and Ge1-x-ySixSny alloys through MBE and CVD in recent decades and introduces an innovative direct injection method for synthesizing Ge1-x-ySixSny ternary alloys with Sn contents varying from 5% to 12% and Si contents kept at 1%-2%. Grown directly on Si (100) substrates in a Gas-phase Molecular Epitaxy (GSME) reactor, both intrinsic and n-type doped Ge1-x-ySixSny with P with thicknesses of 250-760 nm have been achieved by deploying gas precursors Ge4H10, Si4H10, SnD4 and P(SiH3)3 at the unprecedented low growth temperatures of 190-220 °C. Compressive strain is reduced and crystallinity of the Ge1-x-ySixSny epilayer is improved after rapid thermal annealing (RTA) treatments. High Resolution X-ray Diffraction (HR-XRD), Rutherford Backscattering Spectrometry (RBS), cross-sectional Transmission Electron Microscope (XTEM) and Atomic Force Microscope (AFM) have been combined to characterize the structural properties of the Ge1-x-ySixSny samples, indicating good crystallinity and flat surfaces.
ContributorsHu, Ding (Author) / Kouvetakis, John (Thesis advisor) / Menéndez, Jose (Committee member) / Trovitch, Ryan (Committee member) / Arizona State University (Publisher)
Created2019