Matching Items (5)
Filtering by
- All Subjects: Laser
- All Subjects: Molecular beam epitaxy
- Creators: Ning, Cun-Zheng
Description
Nanolasers represents the research frontier in both the areas of photonics and nanotechnology for its interesting properties in low dimension physics, its appealing prospects in integrated photonics, and other on-chip applications. In this thesis, I present my research work on fabrication and characterization of a new type of nanolasers: metallic cavity nanolasers. The last ten years witnessed a dramatic paradigm shift from pure dielectric cavity to metallic cavity in the research of nanolasers. By using low loss metals such as silver, which is highly reflective at near infrared, light can be confined in an ultra small cavity or waveguide with sub-wavelength dimensions, thus enabling sub-wavelength cavity lasers. Based on this idea, I fabricated two different kinds of metallic cavity nanolasers with rectangular and circular geometries with InGaAs as the gain material and silver as the metallic shell. The lasing wavelength is around 1.55 μm, intended for optical communication applications. Continuous wave (CW) lasing at cryogenic temperature under current injection was achieved on devices with a deep sub-wavelength physical cavity volume smaller than 0.2 λ3. Improving device fabrication process is one of the main challenges in the development of metallic cavity nanolasers due to its ultra-small size. With improved fabrication process and device design, CW lasing at room temperature was demonstrated as well on a sub-wavelength rectangular device with a physical cavity volume of 0.67 λ3. Experiments verified that a small circular nanolasers supporting TE¬01 mode can generate an azimuthal polarized laser beam, providing a compact such source under electrical injection. Sources with such polarizations could have many special applications. Study of digital modulation of circular nanolasers showed that laser noise is an important factor that will affect the data rate of the nanolaser when used as the light source in optical interconnects. For future development, improving device fabrication processes is required to improve device performance. In addition, techniques need to be developed to realize nanolaser/Si waveguide integration. In essence, resolving these two critical issues will finally pave the way for these nanolasers to be used in various practical applications.
ContributorsDing, Kang (Author) / Ning, Cun-Zheng (Thesis advisor) / Yu, Hongbin (Committee member) / Palais, Joseph (Committee member) / Zhang, Yong-Hang (Committee member) / Arizona State University (Publisher)
Created2014
Description
Multiple quantum well (MQW) structures have been employed in a variety of solid state devices. The InGaAs/GaAs material system is of special interest for many optoelectronic applications. This study examines epitaxial growth and defect creation in InGaAs/GaAs MQWs at its initial stage. Correlations between physical properties, crystal perfection of epitaxial structures, and growth conditions under which desired properties are achieved appear as highly important for the realization and final performance of semiconductor based devices.
Molecular beam epitaxy was utilized to grow InGaAs/GaAs MQW structures with a variation in deposition temperature Tdep among the samples to change crystalline and physical properties. High resolution x-ray diffraction and transmission electron microscopy were utilized to probe crystal properties, whereas photoluminescence spectroscopy evaluated optical response. An optimal growth temperature Tdep=505°C was found for 20% In composition. The density of 60° primary and secondary dislocation loops increased continuously at lower growth temperatures and reduced crystal perfection, as evaluated by lateral and vertical coherence lengths and diffuse scattering in reciprocal space maps. Likewise, the strength of non-radiative Shockley-Read-Hall recombination increased as deposition temperature was reduced. Elevated deposition temperature led to InGaAs decay in the structures and manifested in different crystalline defects with a rather isotropic distribution and no lateral ordering. High available thermal energy increased atomic surface diffusivity and resulted in growth surface instability against perturbations, manifesting in lateral layer thickness undulations. Carriers in structures grown at elevated temperature experience localization in local energy minima.InGaAs/GaAs MQW structures reveal correlation between their crystal quality and optical properties. It can be suggested that there is an optimal growth temperature range for each In composition with high crystal perfection and best physical response.
Molecular beam epitaxy was utilized to grow InGaAs/GaAs MQW structures with a variation in deposition temperature Tdep among the samples to change crystalline and physical properties. High resolution x-ray diffraction and transmission electron microscopy were utilized to probe crystal properties, whereas photoluminescence spectroscopy evaluated optical response. An optimal growth temperature Tdep=505°C was found for 20% In composition. The density of 60° primary and secondary dislocation loops increased continuously at lower growth temperatures and reduced crystal perfection, as evaluated by lateral and vertical coherence lengths and diffuse scattering in reciprocal space maps. Likewise, the strength of non-radiative Shockley-Read-Hall recombination increased as deposition temperature was reduced. Elevated deposition temperature led to InGaAs decay in the structures and manifested in different crystalline defects with a rather isotropic distribution and no lateral ordering. High available thermal energy increased atomic surface diffusivity and resulted in growth surface instability against perturbations, manifesting in lateral layer thickness undulations. Carriers in structures grown at elevated temperature experience localization in local energy minima.InGaAs/GaAs MQW structures reveal correlation between their crystal quality and optical properties. It can be suggested that there is an optimal growth temperature range for each In composition with high crystal perfection and best physical response.
ContributorsKarow, Matthias (Author) / Honsberg, C. (Christiana B.) (Thesis advisor) / Faleev, Nikolai N (Committee member) / Ning, Cun-Zheng (Committee member) / Arizona State University (Publisher)
Created2014
Description
Dual-wavelength laser sources have various existing and potential applications in wavelength division multiplexing, differential techniques in spectroscopy for chemical sensing, multiple-wavelength interferometry, terahertz-wave generation, microelectromechanical systems, and microfluidic lab-on-chip systems. In the drive for ever smaller and increasingly mobile electronic devices, dual-wavelength coherent light output from a single semiconductor laser diode would enable further advances and deployment of these technologies. The output of conventional laser diodes is however limited to a single wavelength band with a few subsequent lasing modes depending on the device design. This thesis investigates a novel semiconductor laser device design with a single cavity waveguide capable of dual-wavelength laser output with large spectral separation. The novel dual-wavelength semiconductor laser diode uses two shorter- and longer-wavelength active regions that have separate electron and hole quasi-Fermi energy levels and carrier distributions. The shorter-wavelength active region is based on electrical injection as in conventional laser diodes, and the longer-wavelength active region is then pumped optically by the internal optical field of the shorter-wavelength laser mode, resulting in stable dual-wavelength laser emission at two different wavelengths quite far apart. Different designs of the device are studied using a theoretical model developed in this work to describe the internal optical pumping scheme. The carrier transport and separation of the quasi-Fermi distributions are then modeled using a software package that solves Poisson's equation and the continuity equations to simulate semiconductor devices. Three different designs are grown using molecular beam epitaxy, and broad-area-contact laser diodes are processed using conventional methods. The modeling and experimental results of the first generation design indicate that the optical confinement factor of the longer-wavelength active region is a critical element in realizing dual-wavelength laser output. The modeling predicts lower laser thresholds for the second and third generation designs; however, the experimental results of the second and third generation devices confirm challenges related to the epitaxial growth of the structures in eventually demonstrating dual-wavelength laser output.
ContributorsGreen, Benjamin C (Author) / Zhang, Yong-Hang (Thesis advisor) / Ning, Cun-Zheng (Committee member) / Tao, Nongjian (Committee member) / Roedel, Ronald J (Committee member) / Arizona State University (Publisher)
Created2011
Description
This dissertation addresses challenges pertaining to multi-junction (MJ) solar cells from material development to device design and characterization. Firstly, among the various methods to improve the energy conversion efficiency of MJ solar cells using, a novel approach proposed recently is to use II-VI (MgZnCd)(SeTe) and III-V (AlGaIn)(AsSb) semiconductors lattice-matched on GaSb or InAs substrates for current-matched subcells with minimal defect densities. CdSe/CdTe superlattices are proposed as a potential candidate for a subcell in the MJ solar cell designs using this material system, and therefore the material properties of the superlattices are studied. The high structural qualities of the superlattices are obtained from high resolution X-ray diffraction measurements and cross-sectional transmission electron microscopy images. The effective bandgap energies of the superlattices obtained from the photoluminescence (PL) measurements vary with the layer thicknesses, and are smaller than the bandgap energies of either the constituent material. Furthermore, The PL peak position measured at the steady state exhibits a blue shift that increases with the excess carrier concentration. These results confirm a strong type-II band edge alignment between CdSe and CdTe. The valence band offset between unstrained CdSe and CdTe is determined as 0.63 eV±0.06 eV by fitting the measured PL peak positions using the Kronig-Penney model. The blue shift in PL peak position is found to be primarily caused by the band bending effect based on self-consistent solutions of the Schrödinger and Poisson equations. Secondly, the design of the contact grid layout is studied to maximize the power output and energy conversion efficiency for concentrator solar cells. Because the conventional minimum power loss method used for the contact design is not accurate in determining the series resistance loss, a method of using a distributed series resistance model to maximize the power output is proposed for the contact design. It is found that the junction recombination loss in addition to the series resistance loss and shadowing loss can significantly affect the contact layout. The optimal finger spacing and maximum efficiency calculated by the two methods are close, and the differences are dependent on the series resistance and saturation currents of solar cells. Lastly, the accurate measurements of external quantum efficiency (EQE) are important for the design and development of MJ solar cells. However, the electrical and optical couplings between the subcells have caused EQE measurement artifacts. In order to interpret the measurement artifacts, DC and small signal models are built for the bias condition and the scan of chopped monochromatic light in the EQE measurements. Characterization methods are developed for the device parameters used in the models. The EQE measurement artifacts are found to be caused by the shunt and luminescence coupling effects, and can be minimized using proper voltage and light biases. Novel measurement methods using a pulse voltage bias or a pulse light bias are invented to eliminate the EQE measurement artifacts. These measurement methods are nondestructive and easy to implement. The pulse voltage bias or pulse light bias is superimposed on the conventional DC voltage and light biases, in order to control the operating points of the subcells and counterbalance the effects of shunt and luminescence coupling. The methods are demonstrated for the first time to effectively eliminate the measurement artifacts.
ContributorsLi, Jingjing (Author) / Zhang, Yong-Hang (Thesis advisor) / Tao, Meng (Committee member) / Schroder, Dieter (Committee member) / Vasileska, Dragica (Committee member) / Arizona State University (Publisher)
Created2012
Description
Nanowires are one-dimensional (1D) structures with diameter on the nanometer scales with a high length-to-diameter aspect ratio. Nanowires of various materials including semiconductors, dielectrics and metals have been intensively researched in the past two decades for applications to electrical and optical devices. Typically, nanowires are synthesized using the vapor-liquid-solid (VLS) approach, which allows defect-free 1D growth despite the lattice mismatch between nanowires and substrates. Lattice mismatch issue is a serious problem in high-quality thin film growth of many semiconductors and non-semiconductors. Therefore, nanowires provide promising platforms for the applications requiring high crystal quality materials.
With the 1D geometry, nanowires are natural optical waveguides for light guiding and propagation. By introducing feedback mechanisms to nanowire waveguides, such as the cleaved end facets, the nanowires can work as ultra-small size lasers. Since the first demonstration of the room-temperature ultraviolet nanowire lasers in 2001, the nanowire lasers covering from ultraviolet to mid infrared wavelength ranges have been intensively studied. This dissertation focuses on the optical characterization and laser fabrication of two nanowire materials: erbium chloride silicate nanowires and composition-graded CdSSe semiconductor alloy nanowires.
Chapter 1 – 5 of this dissertation presents a comprehensive characterization of a newly developed erbium compound material, erbium chloride silicate (ECS) in a nanowire form. Extensive experiments demonstrated the high crystal quality and excellent optical properties of ECS nanowires. Optical gain higher than 30 dB/cm at 1.53 μm wavelength is demonstrated on single ECS nanowires, which is higher than the gain of any reported erbium materials. An ultra-high Q photonic crystal micro-cavity is designed on a single ECS nanowire towards the ultra-compact lasers at communication wavelengths. Such ECS nanowire lasers show the potential applications of on-chip photonics integration.
Chapter 6 – 7 presents the design and demonstration of dynamical color-controllable lasers on a single CdSSe alloy nanowire. Through the defect-free VLS growth, engineering of the alloy composition in a single nanowire is achieved. The alloy composition of CdSxSe1-x uniformly varies along the nanowire axis from x=1 to x=0, giving the opportunity of multi-color lasing in a monolithic structure. By looping the wide-bandgap end of the alloy nanowire through nanoscale manipulation, the simultaneous two-color lasing at green and red colors are demonstrated. The 107 nm wavelength separation of the two lasing colors is much larger than the gain bandwidth of typical semiconductors. Since the two-color lasing shares the output port, the color of the total lasing output can be controlled dynamically between the two fundamental colors by changing the relative output power of two lasing colors. Such multi-color lasing and continuous color tuning in a wide spectral range would eventually enable color-by-design lasers to be used for lighting, display and many other applications.
With the 1D geometry, nanowires are natural optical waveguides for light guiding and propagation. By introducing feedback mechanisms to nanowire waveguides, such as the cleaved end facets, the nanowires can work as ultra-small size lasers. Since the first demonstration of the room-temperature ultraviolet nanowire lasers in 2001, the nanowire lasers covering from ultraviolet to mid infrared wavelength ranges have been intensively studied. This dissertation focuses on the optical characterization and laser fabrication of two nanowire materials: erbium chloride silicate nanowires and composition-graded CdSSe semiconductor alloy nanowires.
Chapter 1 – 5 of this dissertation presents a comprehensive characterization of a newly developed erbium compound material, erbium chloride silicate (ECS) in a nanowire form. Extensive experiments demonstrated the high crystal quality and excellent optical properties of ECS nanowires. Optical gain higher than 30 dB/cm at 1.53 μm wavelength is demonstrated on single ECS nanowires, which is higher than the gain of any reported erbium materials. An ultra-high Q photonic crystal micro-cavity is designed on a single ECS nanowire towards the ultra-compact lasers at communication wavelengths. Such ECS nanowire lasers show the potential applications of on-chip photonics integration.
Chapter 6 – 7 presents the design and demonstration of dynamical color-controllable lasers on a single CdSSe alloy nanowire. Through the defect-free VLS growth, engineering of the alloy composition in a single nanowire is achieved. The alloy composition of CdSxSe1-x uniformly varies along the nanowire axis from x=1 to x=0, giving the opportunity of multi-color lasing in a monolithic structure. By looping the wide-bandgap end of the alloy nanowire through nanoscale manipulation, the simultaneous two-color lasing at green and red colors are demonstrated. The 107 nm wavelength separation of the two lasing colors is much larger than the gain bandwidth of typical semiconductors. Since the two-color lasing shares the output port, the color of the total lasing output can be controlled dynamically between the two fundamental colors by changing the relative output power of two lasing colors. Such multi-color lasing and continuous color tuning in a wide spectral range would eventually enable color-by-design lasers to be used for lighting, display and many other applications.
ContributorsLiu, Zhicheng (Author) / Ning, Cun-Zheng (Thesis advisor) / Palais, Joseph (Committee member) / Yu, Hongbin (Committee member) / Yao, Yu (Committee member) / Arizona State University (Publisher)
Created2015