Integrated photonics requires high gain optical materials in the telecom wavelength range for optical amplifiers and coherent light sources. Erbium (Er) containing materials are ideal candidates due to the 1.5 μm emission from Er3+ ions. However, the Er density in typical Er-doped materials is less than 1 x 1020 cm-3, thus limiting the maximum optical gain to a few dB/cm, too small to be useful for integrated photonics applications. Er compounds could potentially solve this problem since they contain much higher Er density. So far the existing Er compounds suffer from short lifetime and strong upconversion effects, mainly due to poor quality of crystals produced by various methods of thin film growth and deposition. This dissertation explores a new Er compound: erbium chloride silicate (ECS, Er3(SiO4)2Cl ) in the nanowire form, which facilitates the growth of high quality single crystals. Growth methods for such single crystal ECS nanowires have been established. Various structural and optical characterizations have been carried out. The high crystal quality of ECS material leads to a long lifetime of the first excited state of Er3+ ions up to 1 ms at Er density higher than 1022 cm-3. This Er lifetime-density product was found to be the largest among all Er containing materials. A unique integrating sphere method was developed to measure the absorption cross section of ECS nanowires from 440 to 1580 nm. Pump-probe experiments demonstrated a 644 dB/cm signal enhancement from a single ECS wire. It was estimated that such large signal enhancement can overcome the absorption to result in a net material gain, but not sufficient to compensate waveguide propagation loss. In order to suppress the upconversion process in ECS, Ytterbium (Yb) and Yttrium (Y) ions are introduced as substituent ions of Er in the ECS crystal structure to reduce Er density. While the addition of Yb ions only partially succeeded, erbium yttrium chloride silicate (EYCS) with controllable Er density was synthesized successfully. EYCS with 30 at. % Er was found to be the best. It shows the strongest PL emission at 1.5 μm, and thus can be potentially used as a high gain material.
ContributorsYin, Leijun (Author) / Ning, Cun-Zheng (Thesis advisor) / Chamberlin, Ralph (Committee member) / Yu, Hongbin (Committee member) / Menéndez, Jose (Committee member) / Ponce, Fernando (Committee member) / Arizona State University (Publisher)
Created2013
Description
This thesis summarizes modeling and simulation of plasmonic waveguides and nanolasers. The research includes modeling of dielectric constants of doped semiconductor as a potential plasmonic material, simulation of plasmonic waveguides with different configurations and geometries, simulation and design of plasmonic nanolasers. In the doped semiconductor part, a more accurate model accounting for dielectric constant of doped InAs was proposed. In the model, Interband transitions accounted for by Adachi's model considering Burstein-Moss effect and free electron effect governed by Drude model dominate in different spectral regions. For plasmonic waveguide part, Insulator-Metal-Insulator (IMI) waveguide, silver nanowire waveguide with and without substrate, Metal-Semiconductor-Metal (MSM) waveguide and Metal-Insulator-Semiconductor-Insulator-Metal (MISIM) waveguide were investigated respectively. Modal analysis was given for each part. Lastly, a comparative study of plasmonic and optical modes in an MSM disk cavity was performed by FDTD simulation for room temperature at the telecommunication wavelength. The results show quantitatively that plasmonic modes have advantages over optical modes in the scalability down to small size and the cavity Quantum Electrodynamics(QED) effects due to the possibility of breaking the diffraction limit. Surprisingly for lasing characteristics, though plasmonic modes have large loss as expected, minimal achievable threshold can be attained for whispering gallery plasmonic modes with azimuthal number of 2 by optimizing cavity design at 1.55µm due to interplay of metal loss and radiation loss.
ContributorsWang, Haotong (Author) / Ning, Cunzheng (Thesis advisor) / Palais, Joseph (Committee member) / Yu, Hongbin (Committee member) / Arizona State University (Publisher)
Created2014
Description
Nanolasers represents the research frontier in both the areas of photonics and nanotechnology for its interesting properties in low dimension physics, its appealing prospects in integrated photonics, and other on-chip applications. In this thesis, I present my research work on fabrication and characterization of a new type of nanolasers: metallic cavity nanolasers. The last ten years witnessed a dramatic paradigm shift from pure dielectric cavity to metallic cavity in the research of nanolasers. By using low loss metals such as silver, which is highly reflective at near infrared, light can be confined in an ultra small cavity or waveguide with sub-wavelength dimensions, thus enabling sub-wavelength cavity lasers. Based on this idea, I fabricated two different kinds of metallic cavity nanolasers with rectangular and circular geometries with InGaAs as the gain material and silver as the metallic shell. The lasing wavelength is around 1.55 μm, intended for optical communication applications. Continuous wave (CW) lasing at cryogenic temperature under current injection was achieved on devices with a deep sub-wavelength physical cavity volume smaller than 0.2 λ3. Improving device fabrication process is one of the main challenges in the development of metallic cavity nanolasers due to its ultra-small size. With improved fabrication process and device design, CW lasing at room temperature was demonstrated as well on a sub-wavelength rectangular device with a physical cavity volume of 0.67 λ3. Experiments verified that a small circular nanolasers supporting TE¬01 mode can generate an azimuthal polarized laser beam, providing a compact such source under electrical injection. Sources with such polarizations could have many special applications. Study of digital modulation of circular nanolasers showed that laser noise is an important factor that will affect the data rate of the nanolaser when used as the light source in optical interconnects. For future development, improving device fabrication processes is required to improve device performance. In addition, techniques need to be developed to realize nanolaser/Si waveguide integration. In essence, resolving these two critical issues will finally pave the way for these nanolasers to be used in various practical applications.
ContributorsDing, Kang (Author) / Ning, Cun-Zheng (Thesis advisor) / Yu, Hongbin (Committee member) / Palais, Joseph (Committee member) / Zhang, Yong-Hang (Committee member) / Arizona State University (Publisher)
Created2014
Description
In this work, a highly sensitive strain sensing technique is developed to realize in-plane strain mapping for microelectronic packages or emerging flexible or foldable devices, where mechanical or thermal strain is a major concern that could affect the performance of the working devices or even lead to the failure of the devices. Therefore strain sensing techniques to create a contour of the strain distribution is desired.
The developed highly sensitive micro-strain sensing technique differs from the existing strain mapping techniques, such as digital image correlation (DIC)/micro-Moiré techniques, in terms of working mechanism, by filling a technology gap that requires high spatial resolution while simultaneously maintaining a large field-of-view. The strain sensing mechanism relies on the scanning of a tightly focused laser beam onto the grating that is on the sample surface to detect the change in the diffracted beam angle as a result of the strain. Gratings are fabricated on the target substrates to serve as strain sensors, which carries the strain information in the form of variations in the grating period. The geometric structure of the optical system inherently ensures the high sensitivity for the strain sensing, where the nanoscale change of the grating period is amplified by almost six orders into a diffraction peak shift on the order of several hundred micrometers. It significantly amplifies the small signal measurements so that the desired sensitivity and accuracy can be achieved.
The important features, such as strain sensitivity and spatial resolution, for the strain sensing technique are investigated to evaluate the technique. The strain sensitivity has been validated by measurements on homogenous materials with well known reference values of CTE (coefficient of thermal expansion). 10 micro-strain has been successfully resolved from the silicon CTE extraction measurements. Furthermore, the spatial resolution has been studied on predefined grating patterns, which are assembled to mimic the uneven strain distribution across the sample surface. A resolvable feature size of 10 µm has been achieved with an incident laser spot size of 50 µm in diameter.
In addition, the strain sensing technique has been applied to a composite sample made of SU8 and silicon, as well as the microelectronic packages for thermal strain mappings.
The developed highly sensitive micro-strain sensing technique differs from the existing strain mapping techniques, such as digital image correlation (DIC)/micro-Moiré techniques, in terms of working mechanism, by filling a technology gap that requires high spatial resolution while simultaneously maintaining a large field-of-view. The strain sensing mechanism relies on the scanning of a tightly focused laser beam onto the grating that is on the sample surface to detect the change in the diffracted beam angle as a result of the strain. Gratings are fabricated on the target substrates to serve as strain sensors, which carries the strain information in the form of variations in the grating period. The geometric structure of the optical system inherently ensures the high sensitivity for the strain sensing, where the nanoscale change of the grating period is amplified by almost six orders into a diffraction peak shift on the order of several hundred micrometers. It significantly amplifies the small signal measurements so that the desired sensitivity and accuracy can be achieved.
The important features, such as strain sensitivity and spatial resolution, for the strain sensing technique are investigated to evaluate the technique. The strain sensitivity has been validated by measurements on homogenous materials with well known reference values of CTE (coefficient of thermal expansion). 10 micro-strain has been successfully resolved from the silicon CTE extraction measurements. Furthermore, the spatial resolution has been studied on predefined grating patterns, which are assembled to mimic the uneven strain distribution across the sample surface. A resolvable feature size of 10 µm has been achieved with an incident laser spot size of 50 µm in diameter.
In addition, the strain sensing technique has been applied to a composite sample made of SU8 and silicon, as well as the microelectronic packages for thermal strain mappings.
ContributorsLiang, Hanshuang (Author) / Yu, Hongbin (Thesis advisor) / Poon, Poh Chieh Benny (Committee member) / Jiang, Hanqing (Committee member) / Zhang, Yong-Hang (Committee member) / Arizona State University (Publisher)
Created2014
Description
Recently a new materials platform consisting of semiconductors grown on GaSb and InAs substrates with lattice constants close to 6.1 A was proposed by our group for various electronic and optoelectronic applications. This materials platform consists of both II-VI (MgZnCdHg)(SeTe) and III-V (InGaAl)(AsSb) compound semiconductors, which have direct bandgaps spanning the entire energy spectrum from far-IR (~0 eV) up to UV (~3.4 eV). The broad range of bandgaps and material properties make it very attractive for a wide range of applications in optoelectronics, such as solar cells, laser diodes, light emitting diodes, and photodetectors. Moreover, this novel materials system potentially offers unlimited degrees of freedom for integration of electronic and optoelectronic devices onto a single substrate while keeping the best possible materials quality with very low densities of misfit dislocations. This capability is not achievable with any other known lattice-matched semiconductors on any available substrate. In the 6.1-A materials system, the semiconductors ZnTe and GaSb are almost perfectly lattice-matched with a lattice mismatch of only 0.13%. Correspondingly, it is expected that high quality ZnTe/GaSb and GaSb/ZnTe heterostructures can be achieved with very few dislocations generated during growth. To fulfill the task, their MBE growth and material properties are carefully investigated. High quality ZnTe layers grown on various III-V substrates and GaSb grown on ZnTe are successfully achieved using MBE. It is also noticed that ZnTe and GaSb have a type-I band-edge alignment with large band offsets (delta_Ec=0.934 eV, delta_Ev=0.6 eV), which provides strong confinement for both electrons and holes. Furthermore, a large difference in refractive index is found between ZnTe and GaSb (2.7 and 3.9, respectively, at 0.7 eV), leading to excellent optical confinement of the guided optical modes in planar semiconductor lasers or distributed Bragg reflectors (DBR) for vertical-cavity surface-emitting lasers. Therefore, GaSb/ZnTe double-heterostructure and ZnTe/GaSb DBR structure are suitable for use in light emitting devices. In this thesis work, experimental demonstration of these structures with excellent structural and optical properties is reported. During the exploration on the properties of various ZnTe heterostructures, it is found that residual tensile strains exist in the thick ZnTe epilayers when they are grown on GaAs, InP, InAs and GaSb substrates. The presence of tensile strains is due to the difference in thermal expansion coefficients between the epilayers and the substrates. The defect densities in these ZnTe layers become lower as the ZnTe layer thickness increases. Growth of high quality GaSb on ZnTe can be achieved using a temperature ramp during growth. The influence of temperature ramps with different ramping rates in the optical properties of GaSb layer is studied, and the samples grown with a temperature ramp from 360 to 470 C at a rate of 33 C/min show the narrowest bound exciton emission peak with a full width at half maximum of 15 meV. ZnTe/GaSb DBR structures show excellent reflectivity properties in the mid-infrared range. A peak reflectance of 99% with a wide stopband of 480 nm centered at 2.5 um is measured from a ZnTe/GaSb DBR sample of only 7 quarter-wavelength pairs.
ContributorsFan, Jin (Author) / Zhang, Yong-Hang (Thesis advisor) / Smith, David (Committee member) / Yu, Hongbin (Committee member) / Menéndez, Jose (Committee member) / Johnson, Shane (Committee member) / Arizona State University (Publisher)
Created2012
Towards high-efficiency thin-film solar cells: from theoretical analysis to experimental exploration
Description
GaAs single-junction solar cells have been studied extensively in recent years, and have reached over 28 % efficiency. Further improvement requires an optically thick but physically thin absorber to provide both large short-circuit current and high open-circuit voltage. By detailed simulation, it is concluded that ultra-thin GaAs cells with hundreds of nanometers thickness and reflective back scattering can potentially offer efficiencies greater than 30 %. The 300 nm GaAs solar cell with AlInP/Au reflective back scattering is carefully designed and demonstrates an efficiency of 19.1 %. The device performance is analyzed using the semi-analytical model with Phong distribution implemented to account for non-Lambertian scattering. A Phong exponent m of ~12, a non-radiative lifetime of 130 ns, and a specific series resistivity of 1.2 Ω·cm2 are determined.
Thin-film CdTe solar cells have also attracted lots of attention due to the continuous improvements in their device performance. To address the issue of the lower efficiency record compared to detailed-balance limit, the single-crystalline Cd(Zn)Te/MgCdTe double heterostructures (DH) grown on InSb (100) substrates by molecular beam epitaxy (MBE) are carefully studied. The Cd0.9946Zn0.0054Te alloy lattice-matched to InSb has been demonstrated with a carrier lifetime of 0.34 µs observed in a 3 µm thick Cd0.9946Zn0.0054Te/MgCdTe DH sample. The substantial improvement of lifetime is due to the reduction in misfit dislocation density. The recombination lifetime and interface recombination velocity (IRV) of CdTe/MgxCd1-xTe DHs are investigated. The IRV is found to be dependent on both the MgCdTe barrier height and width due to the thermionic emission and tunneling processes. A record-long carrier lifetime of 2.7 µs and a record-low IRV of close to zero have been confirmed experimentally.
The MgCdTe/Si tandem solar cell is proposed to address the issue of high manufacturing costs and poor performance of thin-film solar cells. The MBE grown MgxCd1-xTe/MgyCd1-yTe DHs have demonstrated the required bandgap energy of 1.7 eV, a carrier lifetime of 11 ns, and an effective IRV of (1.869 ± 0.007) × 103 cm/s. The large IRV is attributed to thermionic-emission induced interface recombination. These understandings can be applied to fabricating the high-efficiency low-cost MgCdTe/Si tandem solar cell.
Thin-film CdTe solar cells have also attracted lots of attention due to the continuous improvements in their device performance. To address the issue of the lower efficiency record compared to detailed-balance limit, the single-crystalline Cd(Zn)Te/MgCdTe double heterostructures (DH) grown on InSb (100) substrates by molecular beam epitaxy (MBE) are carefully studied. The Cd0.9946Zn0.0054Te alloy lattice-matched to InSb has been demonstrated with a carrier lifetime of 0.34 µs observed in a 3 µm thick Cd0.9946Zn0.0054Te/MgCdTe DH sample. The substantial improvement of lifetime is due to the reduction in misfit dislocation density. The recombination lifetime and interface recombination velocity (IRV) of CdTe/MgxCd1-xTe DHs are investigated. The IRV is found to be dependent on both the MgCdTe barrier height and width due to the thermionic emission and tunneling processes. A record-long carrier lifetime of 2.7 µs and a record-low IRV of close to zero have been confirmed experimentally.
The MgCdTe/Si tandem solar cell is proposed to address the issue of high manufacturing costs and poor performance of thin-film solar cells. The MBE grown MgxCd1-xTe/MgyCd1-yTe DHs have demonstrated the required bandgap energy of 1.7 eV, a carrier lifetime of 11 ns, and an effective IRV of (1.869 ± 0.007) × 103 cm/s. The large IRV is attributed to thermionic-emission induced interface recombination. These understandings can be applied to fabricating the high-efficiency low-cost MgCdTe/Si tandem solar cell.
ContributorsLiu, Shi (Author) / Zhang, Yong-Hang (Thesis advisor) / Johnson, Shane R (Committee member) / Vasileska, Dragica (Committee member) / Yu, Hongbin (Committee member) / Arizona State University (Publisher)
Created2015
Description
Nanowires are one-dimensional (1D) structures with diameter on the nanometer scales with a high length-to-diameter aspect ratio. Nanowires of various materials including semiconductors, dielectrics and metals have been intensively researched in the past two decades for applications to electrical and optical devices. Typically, nanowires are synthesized using the vapor-liquid-solid (VLS) approach, which allows defect-free 1D growth despite the lattice mismatch between nanowires and substrates. Lattice mismatch issue is a serious problem in high-quality thin film growth of many semiconductors and non-semiconductors. Therefore, nanowires provide promising platforms for the applications requiring high crystal quality materials.
With the 1D geometry, nanowires are natural optical waveguides for light guiding and propagation. By introducing feedback mechanisms to nanowire waveguides, such as the cleaved end facets, the nanowires can work as ultra-small size lasers. Since the first demonstration of the room-temperature ultraviolet nanowire lasers in 2001, the nanowire lasers covering from ultraviolet to mid infrared wavelength ranges have been intensively studied. This dissertation focuses on the optical characterization and laser fabrication of two nanowire materials: erbium chloride silicate nanowires and composition-graded CdSSe semiconductor alloy nanowires.
Chapter 1 – 5 of this dissertation presents a comprehensive characterization of a newly developed erbium compound material, erbium chloride silicate (ECS) in a nanowire form. Extensive experiments demonstrated the high crystal quality and excellent optical properties of ECS nanowires. Optical gain higher than 30 dB/cm at 1.53 μm wavelength is demonstrated on single ECS nanowires, which is higher than the gain of any reported erbium materials. An ultra-high Q photonic crystal micro-cavity is designed on a single ECS nanowire towards the ultra-compact lasers at communication wavelengths. Such ECS nanowire lasers show the potential applications of on-chip photonics integration.
Chapter 6 – 7 presents the design and demonstration of dynamical color-controllable lasers on a single CdSSe alloy nanowire. Through the defect-free VLS growth, engineering of the alloy composition in a single nanowire is achieved. The alloy composition of CdSxSe1-x uniformly varies along the nanowire axis from x=1 to x=0, giving the opportunity of multi-color lasing in a monolithic structure. By looping the wide-bandgap end of the alloy nanowire through nanoscale manipulation, the simultaneous two-color lasing at green and red colors are demonstrated. The 107 nm wavelength separation of the two lasing colors is much larger than the gain bandwidth of typical semiconductors. Since the two-color lasing shares the output port, the color of the total lasing output can be controlled dynamically between the two fundamental colors by changing the relative output power of two lasing colors. Such multi-color lasing and continuous color tuning in a wide spectral range would eventually enable color-by-design lasers to be used for lighting, display and many other applications.
With the 1D geometry, nanowires are natural optical waveguides for light guiding and propagation. By introducing feedback mechanisms to nanowire waveguides, such as the cleaved end facets, the nanowires can work as ultra-small size lasers. Since the first demonstration of the room-temperature ultraviolet nanowire lasers in 2001, the nanowire lasers covering from ultraviolet to mid infrared wavelength ranges have been intensively studied. This dissertation focuses on the optical characterization and laser fabrication of two nanowire materials: erbium chloride silicate nanowires and composition-graded CdSSe semiconductor alloy nanowires.
Chapter 1 – 5 of this dissertation presents a comprehensive characterization of a newly developed erbium compound material, erbium chloride silicate (ECS) in a nanowire form. Extensive experiments demonstrated the high crystal quality and excellent optical properties of ECS nanowires. Optical gain higher than 30 dB/cm at 1.53 μm wavelength is demonstrated on single ECS nanowires, which is higher than the gain of any reported erbium materials. An ultra-high Q photonic crystal micro-cavity is designed on a single ECS nanowire towards the ultra-compact lasers at communication wavelengths. Such ECS nanowire lasers show the potential applications of on-chip photonics integration.
Chapter 6 – 7 presents the design and demonstration of dynamical color-controllable lasers on a single CdSSe alloy nanowire. Through the defect-free VLS growth, engineering of the alloy composition in a single nanowire is achieved. The alloy composition of CdSxSe1-x uniformly varies along the nanowire axis from x=1 to x=0, giving the opportunity of multi-color lasing in a monolithic structure. By looping the wide-bandgap end of the alloy nanowire through nanoscale manipulation, the simultaneous two-color lasing at green and red colors are demonstrated. The 107 nm wavelength separation of the two lasing colors is much larger than the gain bandwidth of typical semiconductors. Since the two-color lasing shares the output port, the color of the total lasing output can be controlled dynamically between the two fundamental colors by changing the relative output power of two lasing colors. Such multi-color lasing and continuous color tuning in a wide spectral range would eventually enable color-by-design lasers to be used for lighting, display and many other applications.
ContributorsLiu, Zhicheng (Author) / Ning, Cun-Zheng (Thesis advisor) / Palais, Joseph (Committee member) / Yu, Hongbin (Committee member) / Yao, Yu (Committee member) / Arizona State University (Publisher)
Created2015
Description
Energy harvesting from ambient is important to configuring Wireless Sensor Networks (WSN) for environmental data collecting. In this work, highly flexible thermoelectric generators (TEGs) have been studied and fabricated to supply power to the wireless sensor notes used for data collecting in hot spring environment. The fabricated flexible TEGs can be easily deployed on the uneven surface of heated rocks at the rim of hot springs. By employing the temperature gradient between the hot rock surface and the air, these TEGs can generate power to extend the battery lifetime of the sensor notes and therefore reduce multiple batteries changes where the environment is usually harsh in hot springs. Also, they show great promise for self-powered wireless sensor notes. Traditional thermoelectric material bismuth telluride (Bi2Te3) and advanced MEMS (Microelectromechanical systems) thin film techniques were used for the fabrication. Test results show that when a flexible TEG array with an area of 3.4cm2 was placed on the hot plate surface of 80°C in the air under room temperature, it had an open circuit voltage output of 17.6mV and a short circuit current output of 0.53mA. The generated power was approximately 7mW/m2.
On the other hand, high pressure, temperatures that can reach boiling, and the pH of different hot springs ranging from <2 to >9 make hot spring ecosystem a unique environment that is difficult to study. WSN allows many scientific studies in harsh environments that are not feasible with traditional instrumentation. However, wireless pH sensing for long time in situ data collection is still challenging for two reasons. First, the existing commercial-off-the-shelf pH meters are frequent calibration dependent; second, biofouling causes significant measurement error and drift. In this work, 2-dimentional graphene pH sensors were studied and calibration free graphene pH sensor prototypes were fabricated. Test result shows the resistance of the fabricated device changes linearly with the pH values (in the range of 3-11) in the surrounding liquid environment. Field tests show graphene layer greatly prevented the microbial fouling. Therefore, graphene pH sensors are promising candidates that can be effectively used for wireless pH sensing in exploration of hot spring ecosystems.
On the other hand, high pressure, temperatures that can reach boiling, and the pH of different hot springs ranging from <2 to >9 make hot spring ecosystem a unique environment that is difficult to study. WSN allows many scientific studies in harsh environments that are not feasible with traditional instrumentation. However, wireless pH sensing for long time in situ data collection is still challenging for two reasons. First, the existing commercial-off-the-shelf pH meters are frequent calibration dependent; second, biofouling causes significant measurement error and drift. In this work, 2-dimentional graphene pH sensors were studied and calibration free graphene pH sensor prototypes were fabricated. Test result shows the resistance of the fabricated device changes linearly with the pH values (in the range of 3-11) in the surrounding liquid environment. Field tests show graphene layer greatly prevented the microbial fouling. Therefore, graphene pH sensors are promising candidates that can be effectively used for wireless pH sensing in exploration of hot spring ecosystems.
ContributorsHan, Ruirui (Author) / Yu, Hongyu (Thesis advisor) / Jiang, Hanqing (Committee member) / Yu, Hongbin (Committee member) / Garnero, Edward (Committee member) / Li, Mingming (Committee member) / Arizona State University (Publisher)
Created2018
Description
Zinc telluride (ZnTe) is an attractive II-VI compound semiconductor with a direct
bandgap of 2.26 eV that is used in many applications in optoelectronic devices. Compared
to the two dimensional (2D) thin-film semiconductors, one-dimensional (1D)
nanowires can have different electronic properties for potential novel applications.
In this work, we present the study of ZnTe nanowires (NWs) that are synthesized
through a simple vapor-liquid-solid (VLS) method. By controlling the presence or
the absence of Au catalysts and controlling the growth parameters such as growth
temperature, various growth morphologies of ZnTe, such as thin films and nanowires
can be obtained. The characterization of the ZnTe nanostructures and films was
performed using scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy
(EDX), high- resolution transmission electron microscope (HRTEM), X-ray
diffraction (XRD), photoluminescence (PL), Raman spectroscopy and light scattering
measurement. After confirming the crystal purity of ZnTe, two-terminal diodes and
three-terminal transistors were fabricated with both nanowire and planar nano-sheet
configurations, in order to correlate the nanostructure geometry to device performance
including field effect mobility, Schottky barrier characteristics, and turn-on
characteristics. Additionally, optoelectronic properties such as photoconductive gain
and responsivity were compared against morphology. Finally, ZnTe was explored in
conjunction with ZnO in order to form type-II band alignment in a core-shell nanostructure.
Various characterization techniques including scanning electron microscopy,
energy-dispersive X-ray spectroscopy , x-ray diffraction, Raman spectroscopy, UV-vis
reflectance spectra and photoluminescence were used to investigate the modification
of ZnO/ZnTe core/shell structure properties. In PL spectra, the eliminated PL intensity
of ZnO wires is primarily attributed to the efficient charge transfer process
occurring between ZnO and ZnTe, due to the band alignment in the core/shell structure. Moreover, the result of UV-vis reflectance spectra corresponds to the band
gap energy of ZnO and ZnTe, respectively, which confirm that the sample consists of
ZnO/ZnTe core/shell structure of good quality.
bandgap of 2.26 eV that is used in many applications in optoelectronic devices. Compared
to the two dimensional (2D) thin-film semiconductors, one-dimensional (1D)
nanowires can have different electronic properties for potential novel applications.
In this work, we present the study of ZnTe nanowires (NWs) that are synthesized
through a simple vapor-liquid-solid (VLS) method. By controlling the presence or
the absence of Au catalysts and controlling the growth parameters such as growth
temperature, various growth morphologies of ZnTe, such as thin films and nanowires
can be obtained. The characterization of the ZnTe nanostructures and films was
performed using scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy
(EDX), high- resolution transmission electron microscope (HRTEM), X-ray
diffraction (XRD), photoluminescence (PL), Raman spectroscopy and light scattering
measurement. After confirming the crystal purity of ZnTe, two-terminal diodes and
three-terminal transistors were fabricated with both nanowire and planar nano-sheet
configurations, in order to correlate the nanostructure geometry to device performance
including field effect mobility, Schottky barrier characteristics, and turn-on
characteristics. Additionally, optoelectronic properties such as photoconductive gain
and responsivity were compared against morphology. Finally, ZnTe was explored in
conjunction with ZnO in order to form type-II band alignment in a core-shell nanostructure.
Various characterization techniques including scanning electron microscopy,
energy-dispersive X-ray spectroscopy , x-ray diffraction, Raman spectroscopy, UV-vis
reflectance spectra and photoluminescence were used to investigate the modification
of ZnO/ZnTe core/shell structure properties. In PL spectra, the eliminated PL intensity
of ZnO wires is primarily attributed to the efficient charge transfer process
occurring between ZnO and ZnTe, due to the band alignment in the core/shell structure. Moreover, the result of UV-vis reflectance spectra corresponds to the band
gap energy of ZnO and ZnTe, respectively, which confirm that the sample consists of
ZnO/ZnTe core/shell structure of good quality.
ContributorsPeng, Jhih-hong (Author) / Yu, Hongbin (Thesis advisor) / Roedel, Ronald (Committee member) / Goryll, Michael (Committee member) / Zhao, Yuji (Committee member) / Arizona State University (Publisher)
Created2017
Description
The coexistence of superconductivity and ferromagnetic orders has been the subject of study for many years. It well known that these materials possess two competing order parameters; however the two order parameters can coexist under special circumstances inducing interesting physical phenomena. In recent years the demand of ultra-low-power, high density cryogenic memories has brought considerable interest to integrate superconducting and magnetic thin films in one structure to produce novel memory elements. The operation of the device depends on the unusual electronic properties associated with the Superconductor (S) /Ferromagnetic (F) proximity effect.
Niobium (Nb) based Josephson junction devices were fabricated with barriers containing two ferromagnetic layers separated by a normal metal space layer. In device operation, electrons in the superconductor are injected into the ferromagnets, causing the superconductor wavefunction to shift its phase and decay in amplitude. Such devices have two different states that depend on the relative magnetization of their ferromagnetic barrier layers, parallel or antiparallel. In these different states, the junctions have different phase shifts and critical currents. Superconducting circuits containing these devices can be designed to operate as memory cells using either one of these outputs.
To quantify the shift in phase and amplitude decay of the wavefunction through a common ferromagnet, permalloy, a series of Nb/permalloy/Nb Josephson junctions with varying ferromagnetic layer thicknesses were fabricated. Data have shown that the optimal thickness of a fixed layer composed of permalloy is 2.4 nm, as it shifts the wavefunction phase to π/2, its “pivot point.” If set to precisely this value, the free layer in SFNF'S junctions will switch the junction into either the 0 or π state depending on its magnetic orientation. To minimize the free-layer switching energy dilute Cu-permalloy alloy [Cu0.7(Ni80Fe20)0.3] with a low magnetic saturation (Ms of ~80 emu/cm3) was used as the free layer. These devices exhibit switching energies at small magnetic fields, demonstrating their potential use for low power non-volatile memory for superconductor circuits.
Lastly, to study the proximity effect using other potentially-useful ferromagnetic layers, measurements were performed on Nb/F bilayers and Nb/F/AlOx/Al tunnel junctions with ferromagnets Ni8Fe19, Ni65Fe15Co20, and Pd1-xNix. The dependence of the critical temperature of the bilayers and density of states that propagated through the ferromagnetic layer were studied as a function of thickness. From this study, crucial magnetic and electrical parameters like magnetic coherence lengths (ξF), exchange energy (Eex), and the rate of shift in the wavefunction’s phase and amplitude as a function of thickness were determined.
Niobium (Nb) based Josephson junction devices were fabricated with barriers containing two ferromagnetic layers separated by a normal metal space layer. In device operation, electrons in the superconductor are injected into the ferromagnets, causing the superconductor wavefunction to shift its phase and decay in amplitude. Such devices have two different states that depend on the relative magnetization of their ferromagnetic barrier layers, parallel or antiparallel. In these different states, the junctions have different phase shifts and critical currents. Superconducting circuits containing these devices can be designed to operate as memory cells using either one of these outputs.
To quantify the shift in phase and amplitude decay of the wavefunction through a common ferromagnet, permalloy, a series of Nb/permalloy/Nb Josephson junctions with varying ferromagnetic layer thicknesses were fabricated. Data have shown that the optimal thickness of a fixed layer composed of permalloy is 2.4 nm, as it shifts the wavefunction phase to π/2, its “pivot point.” If set to precisely this value, the free layer in SFNF'S junctions will switch the junction into either the 0 or π state depending on its magnetic orientation. To minimize the free-layer switching energy dilute Cu-permalloy alloy [Cu0.7(Ni80Fe20)0.3] with a low magnetic saturation (Ms of ~80 emu/cm3) was used as the free layer. These devices exhibit switching energies at small magnetic fields, demonstrating their potential use for low power non-volatile memory for superconductor circuits.
Lastly, to study the proximity effect using other potentially-useful ferromagnetic layers, measurements were performed on Nb/F bilayers and Nb/F/AlOx/Al tunnel junctions with ferromagnets Ni8Fe19, Ni65Fe15Co20, and Pd1-xNix. The dependence of the critical temperature of the bilayers and density of states that propagated through the ferromagnetic layer were studied as a function of thickness. From this study, crucial magnetic and electrical parameters like magnetic coherence lengths (ξF), exchange energy (Eex), and the rate of shift in the wavefunction’s phase and amplitude as a function of thickness were determined.
ContributorsAbd El Qader, Makram (Author) / Newman, Nathan (Thesis advisor) / Rowell, John (Committee member) / Rizzo, Nick (Committee member) / Yu, Hongbin (Committee member) / Arizona State University (Publisher)
Created2016