The objective of the experimentation was to explore the effect of crosslinker chain length on the morphology of nanofiber mats. Specifically, poly(vinyl alcohol (PVA) was electrospun into nanofiber mats and poly(ethylene) glycol bis(carboxylic acid) (PEG diacid) was used as the crosslinking agent. As-spun fibers had average fiber diameter of 70 ± 30 nm with an average pore size of 0.10 ± 0.16 μm^2. The fiber diameter for the mats crosslinked with the shorter PEG diacid (Mn = 250) increased to 110 ± 40 nm with an average pore size of 0.11 ± 0.04 μm^2. The mats crosslinked with the longer PEG diacid (Mn = 600) had fiber diameters of 180 ± 10 nm with an average pore size 0.01 ± 0.02 μm^2.
The goal of this research project is to create a Mathcad template file capable of statistically modelling the effects of mean and standard deviation on a microparticle batch characterized by the log normal distribution model. Such a file can be applied during manufacturing to explore tolerances and increase cost and time effectiveness. Theoretical data for the time to 60% drug release and the slope and intercept of the log-log plot were collected and subjected to statistical analysis in JMP. Since the scope of this project focuses on microparticle surface degradation drug release with no drug diffusion, the characteristic variables relating to the slope (n = diffusional release exponent) and the intercept (k = kinetic constant) do not directly apply to the distribution model within the scope of the research. However, these variables are useful for analysis when the Mathcad template is applied to other types of drug release models.