The following is a report that will evaluate the microstructure of the nickel-based superalloy Hastelloy X and its relationship to mechanical properties in different load conditions. Hastelloy X is of interest to the company AORA because its strength and oxidation resistance at high temperatures is directly applicable to their needs in a hybrid concentrated solar module. The literature review shows that the microstructure will produce different carbides at various temperatures, which can be beneficial to the strength of the alloy. These precipitates are found along the grain boundaries and act as pins that limit dislocation flow, as well as grain boundary sliding, and improve the rupture strength of the material. Over time, harmful precipitates form which counteract the strengthening effect of the carbides and reduce rupture strength, leading to failure. A combination of indentation and microstructure mapping was used in an effort to link local mechanical behavior to microstructure variability. Electron backscatter diffraction (EBSD) and energy dispersive spectroscopy (EDS) were initially used as a means to characterize the microstructure prior to testing. Then, a series of room temperature Vickers hardness tests at 50 and 500 gram-force were used to evaluate the variation in the local response as a function of indentation size. The room temperature study concluded that both the hardness and standard deviation increased at lower loads, which is consistent with the grain size distribution seen in the microstructure scan. The material was then subjected to high temperature spherical indentation. Load-displacement curves were essential in evaluating the decrease in strength of the material with increasing temperature. Through linear regression of the unloading portion of the curve, the plastic deformation was determined and compared at different temperatures as a qualitative method to evaluate local strength.
ContributorsCelaya, Andrew Jose (Author) / Peralta, Pedro (Thesis director) / Solanki, Kiran (Committee member) / Barrett, The Honors College (Contributor) / Mechanical and Aerospace Engineering Program (Contributor)
Created2015-05
Description
In real world applications, materials undergo a simultaneous combination of tension, compression, and torsion as a result of high velocity impact. The split Hopkinson pressure bar (SHPB) is an effective tool for analyzing stress-strain response of materials at high strain rates but currently little can be done to produce a synchronized combination of these varying impacts. This research focuses on fabricating a flange which will be mounted on the incident bar of a SHPB and struck perpendicularly by a pneumatically driven striker thus allowing for torsion without interfering with the simultaneous compression or tension. Analytical calculations are done to determine size specifications of the flange to protect against yielding or failure. Based on these results and other design considerations, the flange and a complementary incident bar are created. Timing can then be established such that the waves impact the specimen at the same time causing simultaneous loading of a specimen. This thesis allows research at Arizona State University to individually incorporate all uniaxial deformation modes (tension, compression, and torsion) at high strain rates as well as combining either of the first two modes with torsion. Introduction of torsion will expand the testing capabilities of the SHPB at ASU and allow for more in depth analysis of the mechanical behavior of materials under impact loading. Combining torsion with tension or compression will promote analysis of a material's adherence to the Von Mises failure criterion. This greater understanding of material behavior can be implemented into models and simulations thereby improving the accuracy with which engineers can design new structures.
ContributorsVotroubek, Edward Daniel (Author) / Solanki, Kiran (Thesis director) / Oswald, Jay (Committee member) / Mechanical and Aerospace Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2016-05
Description
Surface Mechanical Attrition Treatment (SMAT) is a process used to coat metallic alloy surfaces with a nanocrystallized layer via mechanical abrasion. SMAT has garnered a significant amount of interest from the scientific community as a surface treatment technique due to the ability of this fine grain top layer to provide several benefits to its constituent alloy, namely significantly higher hardness, fatigue strength, and most pertinently, greatly improved corrosion resistance. Emerging research suggests that SMAT can also be used to apply powder coatings onto target substrates. A given substrate can be installed in a ball mill, where stainless steel balls coated with pure elemental powder deliver sustained impact onto the substrate, embedding the powders onto its surface. This paper will explore the process of coating aluminum 7075 coating with chromium powder via SMAT, and the effects doing so will have on the corrosion resistance properties of the aluminum 7075. Traditionally, high-strength alloys have been treated with chromium via the process of electroplating, where the alloys are subjected to a hexavalent chromium plating procedure that is known to risk releasing toxic carcinogens into the environment. Coating these alloys with SMAT could minimize such negative externalities, while yielding benefits unique to the SMAT coating process itself. Baseline corrosion testing reveals that the corrosion resistance properties of the aluminum 7075 improved marginally when exposed to SMAT without the addition of any chromium powder. A literature review conducted in this paper of select studies on SMAT coating also demonstrates that material properties intrinsic to aluminum 7075 and pure chromium powder, as well as interaction effects occurring between aluminum and chromium when subjected to mechanical alloying, could enable the SMAT coating of aluminum 7075 with chromium to result in greatly enhanced corrosion resistance properties. While this was not accomplished within the duration of the Honors Project due to logistical difficulties brought forth by the COVID-19 epidemic, the baseline corrosion testing performed, as well as the literature review of studies directly relevant to the matter, should hopefully provide some information of value in any future exploration of the topic.
ContributorsMcManus, Matthew Harada (Co-author, Co-author) / Solanki, Kiran (Thesis director) / Beura, Vikrant (Committee member) / School of Politics and Global Studies (Contributor) / Mechanical and Aerospace Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2020-05