Solar energy is leading in renewable energy sources and the aspects surrounding the efforts to harvest light are gaining importance. One such aspect is increasing the light absorption, where heliotropism comes into play. Heliotropism, the ability to track the sun across the sky, can be integrated with solar cells for more efficient photon collection and other optoelectronic systems. Inspired by plants, which optimize incident sunlight in nature, several researchers have made artificial heliotropic and phototropic systems. This project aims to design, synthesize and characterize a material system and evaluate its application in a phototropic system. A gold nanoparticle (Au NP) incorporated poly(N-isopropylacrylamide) (PNIPAAm) hydrogel was synthesized as a photo-thermo-responsive material in our phototropic system. The Au NPs generate heat from the incident via plasmonic resonance to induce a volume phase change of the thermo-responsive hydrogel PNIPAAm. PNIPAAm shrinks or swells at temperature above or below 32°C. Upon irradiation, the Au NP-PNIPAAm micropillar actuates, specifically bending toward the incident light and precisely following the varying incident angle.
Swelling ratio tests, bending angle tests with a static incident light and bending tests with varying angles were carried out on hydrogel samples with varying Au NP concentrations. Swelling ratios ranging from 1.45 to 2.9 were recorded for pure hydrogel samples and samples with very low Au NP concentrations. Swelling ratios of 2.41 and 3.37 were calculated for samples with low and high concentrations of Au NPs, respectively. A bending of up to 88° was observed in Au NP-hydrogel pillars with a low Au NP concentration with a 90° incident angle. The light tracking performance was assessed by the slope of the pillar Bending angle (response angle) vs. Incident light angle plot. A slope of 1 indicates ideal tracking with top of the pillar being normal to the incident light, maximizing the photon absorption. Slopes of 0.82 and 0.56 were observed for the low and high Au NP concentration samples. The rapid and precise incident light tracking of our system has shown the promise in phototropic applications.
Swelling ratio tests, bending angle tests with a static incident light and bending tests with varying angles were carried out on hydrogel samples with varying Au NP concentrations. Swelling ratios ranging from 1.45 to 2.9 were recorded for pure hydrogel samples and samples with very low Au NP concentrations. Swelling ratios of 2.41 and 3.37 were calculated for samples with low and high concentrations of Au NPs, respectively. A bending of up to 88° was observed in Au NP-hydrogel pillars with a low Au NP concentration with a 90° incident angle. The light tracking performance was assessed by the slope of the pillar Bending angle (response angle) vs. Incident light angle plot. A slope of 1 indicates ideal tracking with top of the pillar being normal to the incident light, maximizing the photon absorption. Slopes of 0.82 and 0.56 were observed for the low and high Au NP concentration samples. The rapid and precise incident light tracking of our system has shown the promise in phototropic applications.
ContributorsGopalakrishna, Hamsini (Author) / He, Ximin (Thesis advisor) / Holman, Zachary C (Committee member) / Wang, Liping (Committee member) / Arizona State University (Publisher)
Created2016
Description
Nanomaterials exhibit unique properties that are substantially different from their bulk counterparts. These unique properties have gained recognition and application for various fields and products including sensors, displays, photovoltaics, and energy storage devices. Aerosol Deposition (AD) is a relatively new method for depositing nanomaterials. AD utilizes a nozzle to accelerate the nanomaterial into a deposition chamber under near-vacuum conditions towards a substrate with which the nanomaterial collides and adheres. Traditional methods for designing nozzles at atmospheric conditions are not well suited for nozzle design for AD methods.
Computational Fluid Dynamics (CFD) software, ANSYS Fluent, is utilized to simulate two-phase flows consisting of a carrier gas (Helium) and silicon nanoparticles. The Cunningham Correction Factor is used to account for non-continuous effects at the relatively low pressures utilized in AD.
The nozzle, referred to herein as a boundary layer compensation (BLC) nozzle, comprises an area-ratio which is larger than traditionally designed nozzles to compensate for the thick boundary layer which forms within the viscosity-affected carrier gas flow. As a result, nanoparticles impact the substrate at velocities up to 300 times faster than the baseline nozzle.
Computational Fluid Dynamics (CFD) software, ANSYS Fluent, is utilized to simulate two-phase flows consisting of a carrier gas (Helium) and silicon nanoparticles. The Cunningham Correction Factor is used to account for non-continuous effects at the relatively low pressures utilized in AD.
The nozzle, referred to herein as a boundary layer compensation (BLC) nozzle, comprises an area-ratio which is larger than traditionally designed nozzles to compensate for the thick boundary layer which forms within the viscosity-affected carrier gas flow. As a result, nanoparticles impact the substrate at velocities up to 300 times faster than the baseline nozzle.
ContributorsHoffman, Trent (Author) / Holman, Zachary C (Thesis advisor) / Herrmann, Marcus (Committee member) / Kozicki, Michael (Committee member) / Arizona State University (Publisher)
Created2017
Description
Stress-related failure such as cracking are an important photovoltaic (PV) reliability issue since it accounts for a high percentage of power losses in the midlife-failure and wear-out failure regimes. Cell cracking can only be correlated with module degradation when cracks are of detectable size and detrimental to the performance. Several techniques have been explored to access the deflection and stress status on solar cell, but they have disadvantages such as high surface sensitivity.
This dissertation presents a new and non-destructive method for mapping the deflection on encapsulated solar cells using X-ray topography (XRT). This method is based on Bragg diffraction imaging, where only the areas that meet diffraction conditions will present contrast. By taking XRT images of the solar cell at various sample positions and applying an in-house developed algorithm framework, the cell‘s deflection map is obtained. Error analysis has demonstrated that the errors from the experiment and the data processing are below 4.4 and 3.3%.
Von Karman plate theory has been applied to access the stress state of the solar cells. Under the assumptions that the samples experience pure bending and plain stress conditions, the principal stresses are obtained from the cell deflection data. Results from a statistical analysis using a Weibull distribution suggest that 0.1% of the data points can contribute to critical failure. Both the soldering and lamination processes put large amounts of stress on solar cells. Even though glass/glass packaging symmetry is preferred over glass/backsheet, the solar cells inside the glass/glass packaging experience significantly more stress. Through a series of in-situ four-point bending test, the assumptions behind Von Karman theory are validated for cases where the neutral plane is displaced by the tensile and compressive stresses.
The deflection and stress mapping method is applied to two next generation PV concepts named Flex-circuit and PVMirror. The Flex-circuit module concept replaces traditional metal ribbons with Al foils for electrical contact and PVMirror concept utilizes a curved PV module design with a dichroic film for thermal storage and electrical output. The XRT framework proposed in this dissertation successfully characterized the impact of various novel interconnection and packaging solutions.
This dissertation presents a new and non-destructive method for mapping the deflection on encapsulated solar cells using X-ray topography (XRT). This method is based on Bragg diffraction imaging, where only the areas that meet diffraction conditions will present contrast. By taking XRT images of the solar cell at various sample positions and applying an in-house developed algorithm framework, the cell‘s deflection map is obtained. Error analysis has demonstrated that the errors from the experiment and the data processing are below 4.4 and 3.3%.
Von Karman plate theory has been applied to access the stress state of the solar cells. Under the assumptions that the samples experience pure bending and plain stress conditions, the principal stresses are obtained from the cell deflection data. Results from a statistical analysis using a Weibull distribution suggest that 0.1% of the data points can contribute to critical failure. Both the soldering and lamination processes put large amounts of stress on solar cells. Even though glass/glass packaging symmetry is preferred over glass/backsheet, the solar cells inside the glass/glass packaging experience significantly more stress. Through a series of in-situ four-point bending test, the assumptions behind Von Karman theory are validated for cases where the neutral plane is displaced by the tensile and compressive stresses.
The deflection and stress mapping method is applied to two next generation PV concepts named Flex-circuit and PVMirror. The Flex-circuit module concept replaces traditional metal ribbons with Al foils for electrical contact and PVMirror concept utilizes a curved PV module design with a dichroic film for thermal storage and electrical output. The XRT framework proposed in this dissertation successfully characterized the impact of various novel interconnection and packaging solutions.
ContributorsMeng, Xiaodong (Author) / Bertoni, Marian I (Thesis advisor) / Meier, Rico (Committee member) / Holman, Zachary C (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2019
Description
A new nanoparticle deposition technique, Aerosol Impaction-Driven Assembly (AIDA), was extensively characterized for material structures and properties. Aerogel films can be deposited directly onto a substrate with AIDA without the long aging and drying steps in the sol-gel method. Electron microscopy, pore size analysis, thermal conductivity, and optical measurements show the nanoparticle (NP) films to be similar to typical silica aerogel. Haze of nanoparticle films modeled as scattering sites correlates strongly with pore size distribution. Supporting evidence was obtained from particle sizes and aggregates using electron microscopy and small-angle X-ray scattering. NP films showed interlayers of higher porosity and large aggregates formed by tensile film stress.
To better understand film stress and NP adhesion, chemical bonding analyses were performed for samples annealed up to 900 °C. Analysis revealed that about 50% of the NP surfaces are functionalized by hydroxyl (-OH) groups, providing for hydrogen bonding. Ellipsometric porosimetry was used to further understand the mechanical properties by providing a measure of strain upon capillary pressure from filling pores. Upon annealing to 200 °C, the films lost water resulting in closer bonding of NPs and higher Young’s modulus. Upon further annealing up to 900 °C, the films lost hydroxyl bonds while gaining siloxane bonds, reducing Young’s modulus. The application of ellipsometric porosimetry to hydrophilic coatings brings into question the validity of pore size distribution calculations for materials that hold onto water molecules and result in generally smaller calculated pore sizes.
Doped hydrogenated microcrystalline silicon was grown on crystalline silicon NPs, as a test case of an application for NP films to reduce parasitic absorption in silicon heterojunction solar cells. Parasitic absorption of blue light could be reduced because microcrystalline silicon has a mix of direct and indirect bandgap, giving lower blue absorption than amorphous silicon. Using Ultraviolet Raman spectroscopy, the crystallinity of films as thin as 13 nm was determined rapidly (in 1 minute) and non-destructively. A mono-layer of nanocrystals was applied as seeds for p-doped microcrystalline silicon growth and resulted in higher crystallinity films. Applications of the method could be explored for other nanocrystalline materials.
To better understand film stress and NP adhesion, chemical bonding analyses were performed for samples annealed up to 900 °C. Analysis revealed that about 50% of the NP surfaces are functionalized by hydroxyl (-OH) groups, providing for hydrogen bonding. Ellipsometric porosimetry was used to further understand the mechanical properties by providing a measure of strain upon capillary pressure from filling pores. Upon annealing to 200 °C, the films lost water resulting in closer bonding of NPs and higher Young’s modulus. Upon further annealing up to 900 °C, the films lost hydroxyl bonds while gaining siloxane bonds, reducing Young’s modulus. The application of ellipsometric porosimetry to hydrophilic coatings brings into question the validity of pore size distribution calculations for materials that hold onto water molecules and result in generally smaller calculated pore sizes.
Doped hydrogenated microcrystalline silicon was grown on crystalline silicon NPs, as a test case of an application for NP films to reduce parasitic absorption in silicon heterojunction solar cells. Parasitic absorption of blue light could be reduced because microcrystalline silicon has a mix of direct and indirect bandgap, giving lower blue absorption than amorphous silicon. Using Ultraviolet Raman spectroscopy, the crystallinity of films as thin as 13 nm was determined rapidly (in 1 minute) and non-destructively. A mono-layer of nanocrystals was applied as seeds for p-doped microcrystalline silicon growth and resulted in higher crystallinity films. Applications of the method could be explored for other nanocrystalline materials.
ContributorsCarpenter, Joe Victor (Author) / Holman, Zachary C (Thesis advisor) / Bertoni, Mariana I (Committee member) / Chan, Candace K. (Committee member) / Smith, David J. (Committee member) / Arizona State University (Publisher)
Created2020