Gallium Nitride (GaN), being a wide-bandgap semiconductor, shows its advantage over the conventional semiconductors like Silicon and Gallium Arsenide for high temperature applications, especially in the temperature range from 300°C to 600°C. Development of stable ohmic contacts to GaN with low contact resistivity has been identified as a prerequisite to the success of GaN high temperature electronics. The focus of this work was primarily derived from the requirement of an appropriate metal contacts to work with GaN-based hybrid solar cell operating at high temperature.
Alloyed Ti/Al/Ni/Au contact and non-alloyed Al/Au contact were developed to form low-resistivity contacts to n-GaN and their stability at high temperature were studied. The alloyed Ti/Al/Ni/Au contact offered a specific contact resistivity (ρc) of 6×10-6 Ω·cm2 at room temperature measured the same as the temperature increased to 400°C. No significant change in ρc was observed after the contacts being subjected to 400°C, 450°C, 500°C, 550°C, and 600°C, respectively, for at least 4 hours in air. Since several device technology prefer non-alloyed contacts Al/Au metal stack was applied to form the contacts to n-type GaN. An initial ρc of 3×10-4 Ω·cm2, measured after deposition, was observed to continuously reduce under thermal stress at 400°C, 450°C, 500°C, 550°C, and 600°C, respectively, finally stabilizing at 5×10-6 Ω·cm2. Both the alloyed and non-alloyed metal contacts showed exceptional capability of stable operation at temperature as high as 600°C in air with low resistivity ~10-6 Ω·cm2, with ρc lowering for the non-alloyed contacts with high temperatures.
The p-GaN contacts showed remarkably superior ohmic behavior at elevated temperatures. Both ρc and sheet resistance (Rsh) of p-GaN decreased by a factor of 10 as the ambient temperature increased from room temperature to 390°C. The annealed Ni/Au contact showed ρc of 2×10-3 Ω·cm2 at room temperature, reduced to 1.6×10-4 Ω·cm2 at 390°C. No degradation was observed after the contacts being subjected to 450°C in air for 48 hours. Indium Tin Oxide (ITO) contacts, which has been widely used as current spreading layer in GaN-base optoelectronic devices, measured an initial ρc [the resistivity of the ITO/p-GaN interface, since the metal/ITO ρc is negligible] of 1×10-2 Ω·cm2 at room temperature. No degradation was observed after the contact being subjected to 450°C in air for 8 hours.
Accelerated life testing (ALT) was performed to further evaluate the contacts stability at high temperatures quantitatively. The ALT results showed that the annealed Ni/Au to p-GaN contacts is more stable in nitrogen ambient, with a lifetime of 2,628 hours at 450°C which is approximately 12 times longer than that at 450°C in air.
Alloyed Ti/Al/Ni/Au contact and non-alloyed Al/Au contact were developed to form low-resistivity contacts to n-GaN and their stability at high temperature were studied. The alloyed Ti/Al/Ni/Au contact offered a specific contact resistivity (ρc) of 6×10-6 Ω·cm2 at room temperature measured the same as the temperature increased to 400°C. No significant change in ρc was observed after the contacts being subjected to 400°C, 450°C, 500°C, 550°C, and 600°C, respectively, for at least 4 hours in air. Since several device technology prefer non-alloyed contacts Al/Au metal stack was applied to form the contacts to n-type GaN. An initial ρc of 3×10-4 Ω·cm2, measured after deposition, was observed to continuously reduce under thermal stress at 400°C, 450°C, 500°C, 550°C, and 600°C, respectively, finally stabilizing at 5×10-6 Ω·cm2. Both the alloyed and non-alloyed metal contacts showed exceptional capability of stable operation at temperature as high as 600°C in air with low resistivity ~10-6 Ω·cm2, with ρc lowering for the non-alloyed contacts with high temperatures.
The p-GaN contacts showed remarkably superior ohmic behavior at elevated temperatures. Both ρc and sheet resistance (Rsh) of p-GaN decreased by a factor of 10 as the ambient temperature increased from room temperature to 390°C. The annealed Ni/Au contact showed ρc of 2×10-3 Ω·cm2 at room temperature, reduced to 1.6×10-4 Ω·cm2 at 390°C. No degradation was observed after the contacts being subjected to 450°C in air for 48 hours. Indium Tin Oxide (ITO) contacts, which has been widely used as current spreading layer in GaN-base optoelectronic devices, measured an initial ρc [the resistivity of the ITO/p-GaN interface, since the metal/ITO ρc is negligible] of 1×10-2 Ω·cm2 at room temperature. No degradation was observed after the contact being subjected to 450°C in air for 8 hours.
Accelerated life testing (ALT) was performed to further evaluate the contacts stability at high temperatures quantitatively. The ALT results showed that the annealed Ni/Au to p-GaN contacts is more stable in nitrogen ambient, with a lifetime of 2,628 hours at 450°C which is approximately 12 times longer than that at 450°C in air.
ContributorsZhao, Shirong (Author) / Chowdhury, Srabanti (Thesis advisor) / Goodnick, Stephen (Committee member) / Zhao, Yuji (Committee member) / Nemanich, Robert (Committee member) / Arizona State University (Publisher)
Created2016
Description
In this dissertation, atomic layer processing and surface characterization techniques were used to investigate surface conditions of wide band gap materials, gallium nitride (GaN) and gallium oxide (Ga2O3). These studies largely focused on mitigation and removal of defect formation induced by ions used in conventional plasma-based dry etching techniques. Band bending measured by x-ray photoelectron spectroscopy (XPS) was used to characterize charge compensation at the surface of GaN (0001) and determine densities of charged surface states produced by dry etching. Mitigation and removal of these dry-etch induced defects was investigated by varying inductively coupled plasma (ICP) etching conditions, performing thermal and plasma-based treatments, and development of a novel low-damage, self-limiting atomic layer etching (ALE) process to remove damaged material. Atomic layer deposition (ALD) and ALE techniques were developed for Ga2O3 using trimethylgallium (TMG). Ga2O3 was deposited by ALD on Si using TMG and O2 plasma with a growth rate of 1.0 ± 0.1 Å/cycle. Ga2O3 films were then etched using HF and TMG using a fully thermal ALE process with an etch rate of 0.9 ± Å/cycle. O2 plasma oxidation of GaN for surface conversion to Ga2O3 was investigated as a pathway for ALE of GaN using HF and TMG. This process was characterized using XPS, in situ multi-wavelength ellipsometry, and transmission electron microscopy. This study indicated that the etch rate was lower than anticipated, which was attributed to crystallinity of the converted surface oxide on GaN (0001).
ContributorsHatch, Kevin Andrew (Author) / Nemanich, Robert J (Thesis advisor) / Ponce, Fernando A (Committee member) / Smith, David J (Committee member) / Zhao, Yuji (Committee member) / Arizona State University (Publisher)
Created2021
Description
The availability of bulk gallium nitride (GaN) substrates has generated great interest in the development of vertical GaN-on-GaN power devices. The vertical devices made of GaN have not been able to reach their true potential due to material growth related issues. Power devices typically have patterned p-n, and p-i junctions in lateral, and vertical direction relative to the substrate. Identifying the variations from the intended layer design is crucial for failure analysis of the devices. A most commonly used dopant profiling technique, secondary ion mass spectroscopy (SIMS), does not have the spatial resolution to identify the dopant distribution in patterned devices. The possibility of quantitative dopant profiling at a sub-micron scale for GaN in a scanning electron microscope (SEM) is discussed. The total electron yield in an SEM is shown to be a function of dopant concentration which can potentially be used for quantitative dopant profiling.
Etch-and-regrowth is a commonly employed strategy to generate the desired patterned p-n and p-i junctions. The devices involving etch-and-regrowth have poor performance characteristics like high leakage currents, and lower breakdown voltages. This is due to damage induced by the dry etching process, and the nature of the regrowth interface, which is important to understand in order to address the key issue of leakage currents in etched and regrown devices. Electron holography is used for electrostatic potential profiling across the regrowth interfaces to identify the charges introduced by the etching process. SIMS is used to identify the impurities introduced at the interfaces due to etch-and-regrowth process.
Etch-and-regrowth is a commonly employed strategy to generate the desired patterned p-n and p-i junctions. The devices involving etch-and-regrowth have poor performance characteristics like high leakage currents, and lower breakdown voltages. This is due to damage induced by the dry etching process, and the nature of the regrowth interface, which is important to understand in order to address the key issue of leakage currents in etched and regrown devices. Electron holography is used for electrostatic potential profiling across the regrowth interfaces to identify the charges introduced by the etching process. SIMS is used to identify the impurities introduced at the interfaces due to etch-and-regrowth process.
ContributorsAlugubelli, Shanthan Reddy (Author) / Ponce, Fernando A. (Thesis advisor) / McCartney, Martha (Committee member) / Newman, Nathan (Committee member) / Zhao, Yuji (Committee member) / Arizona State University (Publisher)
Created2019
Description
This dissertation covers my doctoral research on the cathodoluminescence (CL) study of the optical properties of III-niride semiconductors.
The first part of this thesis focuses on the optical properties of Mg-doped gallium nitride (GaN:Mg) epitaxial films. GaN is an emerging material for power electronics, especially for high power and high frequency applications. Compared to traditional Si-based devices, GaN-based devices offer superior breakdown properties, faster switching speed, and reduced system size. Some of the current device designs involve lateral p-n junctions which require selective-area doping. Dopant distribution in the selectively-doped regions is a critical issue that can impact the device performance. While most studies on Mg doping in GaN have been reported for epitaxial grown on flat c-plane substrates, questions arise regarding the Mg doping efficiency and uniformity in selectively-doped regions, where growth on surfaces etched away from the exact c-plane orientation is involved. Characterization of doping concentration distribution in lateral structures using secondary ion mass spectroscopy lacks the required spatial resolution. In this work, visualization of acceptor distribution in GaN:Mg epilayers grown by metalorganic chemical vapor deposition (MOCVD) was achieved at sub-micron scale using CL imaging. This was enabled by establishing a correlation among the luminescence characteristics, acceptor concentration, and electrical conductivity of GaN:Mg epilayers. Non-uniformity in acceptor distribution has been observed in epilayers grown on mesa structures and on miscut substrates. It is shown that non-basal-plane surfaces, such as mesa sidewalls and surface step clusters, promotes lateral growth along the GaN basal planes with a reduced Mg doping efficiency. The influence of surface morphology on the Mg doping efficiency in GaN has been studied.
The second part of this thesis focuses on the optical properties of InGaN for photovoltaic applications. The effects of thermal annealing and low energy electron beam irradiation (LEEBI) on the optical properties of MOCVD-grown In0.14Ga0.86N films were studied. A multi-fold increase in luminescence intensity was observed after 800 °C thermal annealing or LEEBI treatment. The mechanism leading to the luminescence intensity increase has been discussed. This study shows procedures that significantly improve the luminescence efficiency of InGaN, which is important for InGaN-based optoelectronic devices.
The first part of this thesis focuses on the optical properties of Mg-doped gallium nitride (GaN:Mg) epitaxial films. GaN is an emerging material for power electronics, especially for high power and high frequency applications. Compared to traditional Si-based devices, GaN-based devices offer superior breakdown properties, faster switching speed, and reduced system size. Some of the current device designs involve lateral p-n junctions which require selective-area doping. Dopant distribution in the selectively-doped regions is a critical issue that can impact the device performance. While most studies on Mg doping in GaN have been reported for epitaxial grown on flat c-plane substrates, questions arise regarding the Mg doping efficiency and uniformity in selectively-doped regions, where growth on surfaces etched away from the exact c-plane orientation is involved. Characterization of doping concentration distribution in lateral structures using secondary ion mass spectroscopy lacks the required spatial resolution. In this work, visualization of acceptor distribution in GaN:Mg epilayers grown by metalorganic chemical vapor deposition (MOCVD) was achieved at sub-micron scale using CL imaging. This was enabled by establishing a correlation among the luminescence characteristics, acceptor concentration, and electrical conductivity of GaN:Mg epilayers. Non-uniformity in acceptor distribution has been observed in epilayers grown on mesa structures and on miscut substrates. It is shown that non-basal-plane surfaces, such as mesa sidewalls and surface step clusters, promotes lateral growth along the GaN basal planes with a reduced Mg doping efficiency. The influence of surface morphology on the Mg doping efficiency in GaN has been studied.
The second part of this thesis focuses on the optical properties of InGaN for photovoltaic applications. The effects of thermal annealing and low energy electron beam irradiation (LEEBI) on the optical properties of MOCVD-grown In0.14Ga0.86N films were studied. A multi-fold increase in luminescence intensity was observed after 800 °C thermal annealing or LEEBI treatment. The mechanism leading to the luminescence intensity increase has been discussed. This study shows procedures that significantly improve the luminescence efficiency of InGaN, which is important for InGaN-based optoelectronic devices.
ContributorsLiu, Hanxiao (Author) / Ponce, Fernando A. (Thesis advisor) / Zhao, Yuji (Committee member) / Newman, Nathan (Committee member) / Fischer, Alec M (Committee member) / Arizona State University (Publisher)
Created2020
Description
Photonic integrated circuit (PIC) in the visible spectrum opens up new opportunities for frequency metrology, neurophotonics, and quantum technologies. Group III nitride (III-N) compound semiconductor is a new emerging material platform for PIC in visible spectrum. The ultra-wide bandgap of aluminum nitride (AlN) allows broadband transparency. The high quantum efficiency of indium gallium nitride (InGaN) quantum well is the major enabler for solid-state lighting and provides the opportunities for active photonic integration. Additionally, the two-dimensional electron gas induced by spontaneous and polarization charges within III-N materials exhibit large electron mobility, which is promising for the development of high frequency transistors. Moreover, the noncentrosymmetric crystalline structure gives nonzero second order susceptibility, beneficial for the application of second harmonic generation and entangled photon generation in nonlinear and quantum optical technologies. Despite the promising features of III-N materials, the investigations on the III-N based PICs are still primitive, mainly due to the difficulties in material growth and the lack of knowledge on fundamental material parameters. In this work, firstly, the fundamental nonlinear optical properties of III-N materials will be characterized. Then, the fabrication process flow of III-N materials will be established. Thirdly, the waveguide performance will be theoretically and experimentally evaluated. At last, the supercontinuum generation from visible to infrared will be demonstrated by utilizing soliton dynamics in high order guided modes. The outcome from this work paves the way towards fully integrated optical comb in UV and visible spectrum.
ContributorsChen, Hong (Author) / Zhao, Yuji (Thesis advisor) / Yao, Yu (Committee member) / Wang, Liping (Committee member) / Ning, Cun-Zheng (Committee member) / Arizona State University (Publisher)
Created2020
Description
Wide bandgap semiconductors are of much current interest due to their superior electrical properties. This dissertation describes electron microscopy characterization of GaN-on-GaN structures for high-power vertical device applications. Unintentionally-doped (UID) GaN layers grown homoepitaxially via metal-organic chemical vapor deposition on freestanding GaN substrates, were subjected to dry etching, and layers of UID-GaN/p-GaN were over-grown. The as-grown and regrown heterostructures were examined in cross-section using transmission electron microscopy (TEM). Two different etching treatments, fast-etch-only and multiple etches with decreasing power, were employed. The fast-etch-only devices showed GaN-on-GaN interface at etched location, and low device breakdown voltages were measured (~ 45-95V). In comparison, no interfaces were visible after multiple etching steps, and the corresponding breakdown voltages were much higher (~1200-1270V). These results emphasized importance of optimizing surface etching techniques for avoiding degraded device performance.
The morphology of GaN-on-GaN devices after reverse-bias electrical stressing to breakdown was investigated. All failed devices had irreversible structural damage, showing large surface craters (~15-35 microns deep) with lengthy surface cracks. Cross-sectional TEM of failed devices showed high densities of threading dislocations (TDs) around the cracks and near crater surfaces. Progressive ion-milling across damaged devices revealed high densities of TDs and the presence of voids beneath cracks: these features were not observed in unstressed devices. The morphology of GaN substrates grown by hydride vapor-phase epitaxy (HVPE) and by ammonothermal methods were correlated with reverse-bias results. HVPE substrates showed arrays of surface features when observed by X-ray topography (XRT). All fabricated devices that overlapped with these features had typical reverse-bias voltages less than 100V at a leakage current limit of 10-6 A. In contrast, devices not overlapping with such features reached voltages greater than 300V. After etching, HVPE substrate surfaces showed defect clusters and macro-pits, whereas XRT images of ammonothermal substrate revealed no visible features. However, some devices fabricated on ammonothermal substrate failed at low voltages. Devices on HVPE and ammonothermal substrates with low breakdown voltages showed crater-like surface damage and revealed TDs (~25µm deep) and voids; such features were not observed in devices reaching higher voltages. These results should assist in developing protocols to fabricate reliable high-voltage devices.
ContributorsPeri, Prudhvi Ram (Author) / Smith, David J. (Thesis advisor) / Alford, Terry (Committee member) / Mccartney, Martha R (Committee member) / Nemanich, Robert (Committee member) / Zhao, Yuji (Committee member) / Arizona State University (Publisher)
Created2021