- All Subjects: Materials Science
- Creators: Crozier, Peter
Description
Operando transmission electron microscopy (TEM) is an extension of in-situ TEM in which the performance of the material being observed is measured simultaneously. This is of great value, since structure-performance relationships lie at the heart of materials science. For catalyst materials, like the SiO2-supported Ru nanoparticles studied, the important performance metric, catalyst activity, is measured inside the microscope by determining the gas composition during imaging. This is accomplished by acquisition of electron energy loss spectra (EELS) of the gas in the environmental TEM while catalysis is taking place. In this work, automated methods for rapidly quantifying low-loss and core-loss EELS of gases were developed. A new sample preparation method was also established to increase catalytic conversion inside a differentially-pumped environmental TEM, and the maximum CO conversion observed was about 80%. A system for mixing gases and delivering them to the environmental TEM was designed and built, and a method for locating and imaging nanoparticles in zone axis orientations while minimizing electron dose rate was determined.
After atomic resolution images of Ru nanoparticles observed during CO oxidation were obtained, the shape and surface structures of these particles was investigated. A Wulff model structure for Ru particles was compared to experimental images both by manually rotating the model, and by automatically determining a matching orientation using cross-correlation of shape signatures. From this analysis, it was determined that most Ru particles are close to Wulff-shaped during CO oxidation. While thick oxide layers were not observed to form on Ru during CO oxidation, thin RuO2 layers on the surface of Ru nanoparticles were imaged with atomic resolution for the first time. The activity of these layers is discussed in the context of the literature on the subject, which has thus far been inconclusive. We conclude that disordered oxidized ruthenium, rather than crystalline RuO2 is the most active species.
After atomic resolution images of Ru nanoparticles observed during CO oxidation were obtained, the shape and surface structures of these particles was investigated. A Wulff model structure for Ru particles was compared to experimental images both by manually rotating the model, and by automatically determining a matching orientation using cross-correlation of shape signatures. From this analysis, it was determined that most Ru particles are close to Wulff-shaped during CO oxidation. While thick oxide layers were not observed to form on Ru during CO oxidation, thin RuO2 layers on the surface of Ru nanoparticles were imaged with atomic resolution for the first time. The activity of these layers is discussed in the context of the literature on the subject, which has thus far been inconclusive. We conclude that disordered oxidized ruthenium, rather than crystalline RuO2 is the most active species.
ContributorsMiller, Benjamin (Author) / Crozier, Peter (Thesis advisor) / Liu, Jingyue (Committee member) / McCartney, Martha (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2016
Description
LiNbO3 and ZnO have shown great potential for photochemical surface reactions and specific photocatalytic processes. However, the efficiency of LiNbO3 is limited due to recombination or back reactions and ZnO exhibits a chemical instability in a liquid cell. In this dissertation, both materials were coated with precise thickness of metal oxide layers to passivate the surfaces and to enhance their photocatalytic efficiency. LiNbO3 was coated with plasma enhanced atomic layer deposited (PEALD) ZnO and Al2O3, and molecular beam deposited TiO2 and VO2. On the other hand, PEALD ZnO and single crystal ZnO were passivated with PEALD SiO2 and Al2O3.
Metal oxide/LiNbO3 heterostructures were immersed in aqueous AgNO3 solutions and illuminated with ultraviolet (UV) light to form Ag nanoparticle patterns. Alternatively, Al2O3 and SiO2/ZnO heterostructures were immersed in K3PO4 buffer solutions and studied for photoelectrochemical reactions. A fundamental aspect of the heterostructures is the band alignment and band bending, which was deduced from in situ photoemission measurements.
This research has provided insight to three aspects of the heterostructures. First, the band alignment at the interface of metal oxides/LiNbO3, and Al2O3 or SiO2/ZnO were used to explain the possible charge transfer processes and the direction of carrier flow in the heterostructures. Second, the effect of metal oxide coatings on the LiNbO3 with different internal carrier concentrations was related to the surface photochemical reactions. Third is the surface passivation and degradation mechanism of Al2O3 and SiO2 on ZnO was established. The heterostructures were characterized after stability tests using atomic force microscopy (AFM), scanning electron microscopy (SEM), and cross-section transmission electron microscopy (TEM).
The results indicate that limited thicknesses of ZnO or TiO2 on polarity patterned LiNbO3 (PPLN) enhances the Ag+ photoinduced reduction process. ZnO seems more efficient than TiO2 possibly due to a higher carrier mobility. However, an increase of the ZnO thickness (≥ 4 nm) reduced the effect of the PPLN substrate on the Ag nanoparticle pattern. For the case of Al2O3 and SiO2/ZnO heterostructures, SiO2 remains intact through 1 h stability tests. Unlike SiO2, Al2O3 shows surface degradation after a short stability test of a few minutes. Thus, SiO2 provides improved passivation over Al2O3. A detailed microscopy analysis indicates the underneath ZnO photocorrodes in the SiO2/ZnO samples, which is possibly due to transport of ions through the SiO2 protective layer.
Metal oxide/LiNbO3 heterostructures were immersed in aqueous AgNO3 solutions and illuminated with ultraviolet (UV) light to form Ag nanoparticle patterns. Alternatively, Al2O3 and SiO2/ZnO heterostructures were immersed in K3PO4 buffer solutions and studied for photoelectrochemical reactions. A fundamental aspect of the heterostructures is the band alignment and band bending, which was deduced from in situ photoemission measurements.
This research has provided insight to three aspects of the heterostructures. First, the band alignment at the interface of metal oxides/LiNbO3, and Al2O3 or SiO2/ZnO were used to explain the possible charge transfer processes and the direction of carrier flow in the heterostructures. Second, the effect of metal oxide coatings on the LiNbO3 with different internal carrier concentrations was related to the surface photochemical reactions. Third is the surface passivation and degradation mechanism of Al2O3 and SiO2 on ZnO was established. The heterostructures were characterized after stability tests using atomic force microscopy (AFM), scanning electron microscopy (SEM), and cross-section transmission electron microscopy (TEM).
The results indicate that limited thicknesses of ZnO or TiO2 on polarity patterned LiNbO3 (PPLN) enhances the Ag+ photoinduced reduction process. ZnO seems more efficient than TiO2 possibly due to a higher carrier mobility. However, an increase of the ZnO thickness (≥ 4 nm) reduced the effect of the PPLN substrate on the Ag nanoparticle pattern. For the case of Al2O3 and SiO2/ZnO heterostructures, SiO2 remains intact through 1 h stability tests. Unlike SiO2, Al2O3 shows surface degradation after a short stability test of a few minutes. Thus, SiO2 provides improved passivation over Al2O3. A detailed microscopy analysis indicates the underneath ZnO photocorrodes in the SiO2/ZnO samples, which is possibly due to transport of ions through the SiO2 protective layer.
ContributorsKaur, Manpuneet (Author) / Nemanich, Robert (Thesis advisor) / Dey, Sandwip (Committee member) / Crozier, Peter (Committee member) / Chan, Candace (Committee member) / Arizona State University (Publisher)
Created2016
Description
There is a fundamental attractiveness about harnessing renewable energy in an age when sustainability is an ethical norm. Lithium ion batteries and hydrogen fuels are considered the most promising energy source instead of fossil fuels. This work describes the investigation of new cathode materials and devices architectures for lithium ion batteries, and photocatalysts for their usage in water splitting and waste water treatment.
LiCoO2 and LiNi1/3Mn1/3Co1/3O2 were exfoliated into nanosheets using electrochemical oxidation followed by intercalation of tetraethylammonium cations. The nanosheets were purified using dialysis and electrophoresis. The nanosheets were successfully restacked into functional cathode materials with microwave hydrothermal assistance, indicating that new cathodes can be obtained by reassembling nanosheets. This method can pave the way for the synthesis of materials with novel structures and electrochemical properties, as well as facilitate the fabrication of hybrid and composite structures from different nanosheets as building blocks.
Paper folding techniques are used in order to compact a Li-ion battery and increase its energy per footprint area. Full cells were prepared using Li4Ti5O12 and LiCoO2 powders deposited onto current collectors consisting of paper coated with carbon nanotubes. Folded cells showed higher areal capacities compared to the planar versions. Origami lithium-ion battery made in this method that can be deformed at an unprecedented high level, including folding, bending and twisting.
Spray pyrolysis was used to prepare films of AgInS2 with and without Sn as an extrinsic dopant. The photoelectrochemical performance of these films was evaluated after annealing under a N2 or S atmosphere with different amounts of the Sn dopant. Density Function Theory (DFT) was used to calculate the band structure of AgInS2 and understand the role of Sn doping in the observed properties.
Cr(VI) removal was investigated using multiple oxide photocatalyst and additives. The efficiency for Cr(VI) removal using these photocatalysts was investigated in synthetic neutral and alkaline water, as well as in cooling tower blowdown water. While sulfite alone can chemically reduce Cr(VI), sulfite in combination with a photocatalyst resulted in faster and complete removal of Cr(VI) in 10 min using a SO32−/Cr(VI) ratio >35 in pH ∼ 8 solutions.
LiCoO2 and LiNi1/3Mn1/3Co1/3O2 were exfoliated into nanosheets using electrochemical oxidation followed by intercalation of tetraethylammonium cations. The nanosheets were purified using dialysis and electrophoresis. The nanosheets were successfully restacked into functional cathode materials with microwave hydrothermal assistance, indicating that new cathodes can be obtained by reassembling nanosheets. This method can pave the way for the synthesis of materials with novel structures and electrochemical properties, as well as facilitate the fabrication of hybrid and composite structures from different nanosheets as building blocks.
Paper folding techniques are used in order to compact a Li-ion battery and increase its energy per footprint area. Full cells were prepared using Li4Ti5O12 and LiCoO2 powders deposited onto current collectors consisting of paper coated with carbon nanotubes. Folded cells showed higher areal capacities compared to the planar versions. Origami lithium-ion battery made in this method that can be deformed at an unprecedented high level, including folding, bending and twisting.
Spray pyrolysis was used to prepare films of AgInS2 with and without Sn as an extrinsic dopant. The photoelectrochemical performance of these films was evaluated after annealing under a N2 or S atmosphere with different amounts of the Sn dopant. Density Function Theory (DFT) was used to calculate the band structure of AgInS2 and understand the role of Sn doping in the observed properties.
Cr(VI) removal was investigated using multiple oxide photocatalyst and additives. The efficiency for Cr(VI) removal using these photocatalysts was investigated in synthetic neutral and alkaline water, as well as in cooling tower blowdown water. While sulfite alone can chemically reduce Cr(VI), sulfite in combination with a photocatalyst resulted in faster and complete removal of Cr(VI) in 10 min using a SO32−/Cr(VI) ratio >35 in pH ∼ 8 solutions.
ContributorsCheng, Qian (Author) / Chan, Candace Kay (Thesis advisor) / Sieradzki, Karl (Committee member) / Crozier, Peter (Committee member) / He, Ximin (Committee member) / Arizona State University (Publisher)
Created2016
Description
Solid electrolytes have great potential to address the safety issues of Li-ion batteries, but better synthesis methods are still required for ceramics electrolytes such as lithium lanthanum titanate (LLTO) and lithium lanthanum zirconate (LLZO). Pellets made from ceramic nanopowders using conventional sintering can be porous due to the agglomeration of nanoparticles (NPs). Electrospinning is a simple and versatile technique for preparing oxide ceramic nanowires (NWs) and was used to prepare electrospun LLTO and LLZO NWs. Pellets prepared from the electrospun LLTO NWs had higher density, less void space, and higher Li+ conductivity compared to those comprised of LLTO prepared with conventional sol-gel methods, which demonstrated the potential that electrospinning can provide towards improving the properties of sol-gel derived ceramics. Cubic phase LLZO was stabilized at room temperature in the form of electrospun NWs without extrinsic dopants. Bulk LLZO with tetragonal structure was transformed to the cubic phase using particle size reduction via ball milling. Heating conditions that promoted particle coalescence and grain growth induced a transformation from the cubic to tetragonal phase in both types of nanostructured LLZO. Composite polymer solid electrolyte was fabricated using LLZO NWs as the filler and showed an improved ionic conductivity at room temperature. Nuclear magnetic resonance studies show that LLZO NWs partially modify the polymer matrix and create preferential pathways for Li+ conduction through the modified polymer regions. Doping did not have significant effect on improving the overall conductivity as the interfaces played a predominant role. By comparing fillers with different morphologies and intrinsic conductivities, it was found that both NW morphology and high intrinsic conductivity are desired.
ContributorsYang, Ting (Author) / Chan, Candace K. (Thesis advisor) / Crozier, Peter (Committee member) / Lin, Jerry Ys (Committee member) / Arizona State University (Publisher)
Created2017
Description
Dealloying, the selective electrochemical dissolution of an active component from an alloy, often results in nanoscale bi-continuous solid/void morphologies. These structures are attracting attention for a wide range of applications including catalysis, sensing and actuation. The evolution of these nanoporous structures has been widely studied for the case at low homologous temperature, TH, such as in Ag-Au, Cu-Au, Cu-Pt, etc. Since at low TH the solid-state mobility of the components is of order 10-30 cm2s-1 or less, percolation dissolution is the only mechanism available to support dealloying over technologically relevant time scales. Without the necessity of solid-state mass transport, percolation dissolution involves sharp transitions based on two key features, the parting limit and critical potential.
Dealloying under conditions of high TH, (or high intrinsic diffusivity of the more electrochemically reactive component) is considerably more complicated than at low TH. Since solid-state mass transport is available to support this process, a rich set of morphologies, including negative or void dendrites, Kirkendall voids and bi-continuous porous structures, can evolve. In order to study dealloying at high TH we have examined the behavior of Li-Sn and Li-Pb alloys. The intrinsic diffusivities of Li were measured in these alloys using electrochemical titration and time of flight measurements. Morphology evolution was studied with varying alloy composition, host dimension and imposed electrochemical conditions. Owing to diffusive transport, there is no parting limit for dealloying, however, there is a compositional threshold (pPD) as well as a critical potential for the operation of percolation dissolution and the formation of bi-continuous structures. Negative or void dendrite morphologies evolve at compositions below pPD and at large values of the applied electrochemical potential when the rate of dealloying is limited by solid-state mass transport. This process is isomorphic to dendrite formation in electrodeposition. Kirkendall voiding morphologies evolve below the critical potential over the entire range of alloy compositions.
We summarize our results by introducing dealloying morphology diagrams that we use to graphically illustrate the electrochemical conditions resulting in various morphologies that can form under conditions of low and high TH.
Dealloying under conditions of high TH, (or high intrinsic diffusivity of the more electrochemically reactive component) is considerably more complicated than at low TH. Since solid-state mass transport is available to support this process, a rich set of morphologies, including negative or void dendrites, Kirkendall voids and bi-continuous porous structures, can evolve. In order to study dealloying at high TH we have examined the behavior of Li-Sn and Li-Pb alloys. The intrinsic diffusivities of Li were measured in these alloys using electrochemical titration and time of flight measurements. Morphology evolution was studied with varying alloy composition, host dimension and imposed electrochemical conditions. Owing to diffusive transport, there is no parting limit for dealloying, however, there is a compositional threshold (pPD) as well as a critical potential for the operation of percolation dissolution and the formation of bi-continuous structures. Negative or void dendrite morphologies evolve at compositions below pPD and at large values of the applied electrochemical potential when the rate of dealloying is limited by solid-state mass transport. This process is isomorphic to dendrite formation in electrodeposition. Kirkendall voiding morphologies evolve below the critical potential over the entire range of alloy compositions.
We summarize our results by introducing dealloying morphology diagrams that we use to graphically illustrate the electrochemical conditions resulting in various morphologies that can form under conditions of low and high TH.
ContributorsGeng, Ke (Author) / Sieradzki, Karl (Thesis advisor) / Crozier, Peter (Committee member) / Chan, Candace (Committee member) / Jiao, Yang (Committee member) / Arizona State University (Publisher)
Created2017
Description
Owing to their special characteristics, group III-Nitride semiconductors have attracted special attention for their application in a wide range of optoelectronic devices. Of particular interest are their direct and wide band gaps that span from ultraviolet to the infrared wavelengths. In addition, their stronger bonds relative to the other compound semiconductors makes them thermally more stable, which provides devices with longer life time. However, the lattice mismatch between these semiconductors and their substrates cause the as-grown films to have high dislocation densities, reducing the life time of devices that contain these materials. One possible solution for this problem is to substitute single crystal semiconductor nanowires for epitaxial films. Due to their dimensionality, semiconductor nanowires typically have stress-free surfaces and better physical properties. In order to employ semiconductor nanowires as building blocks for nanoscale devices, a precise control of the nanowires' crystallinity, morphology, and chemistry is necessary. This control can be achieved by first developing a deeper understanding of the processes involved in the synthesis of nanowires, and then by determining the effects of temperature and pressure on their growth. This dissertation focuses on understanding of the growth processes involved in the formation of GaN nanowires. Nucleation and growth events were observed in situ and controlled in real-time using an environmental transmission electron microscope. These observations provide a satisfactory elucidation of the underlying growth mechanism during the formation of GaN nanowires. Nucleation of these nanowires appears to follow the vapor-liquid-solid mechanism. However, nanowire growth is found to follow both the vapor-liquid-solid and vapor-solid-solid mechanisms. Direct evidence of the effects of III/V ratio on nanowire growth is also reported, which provides important information for tailoring the synthesis of GaN nanowires. These findings suggest in situ electron microscopy is a powerful tool to understand the growth of GaN nanowires and also that these experimental approach can be extended to study other binary semiconductor compound such as GaP, GaAs, and InP, or even ternary compounds such as InGaN. However, further experimental work is required to fully elucidate the kinetic effects on the growth process. A better control of the growth parameters is also recommended.
ContributorsDíaz Rivas, Rosa Estela (Author) / Mahajan, Subhash (Thesis advisor) / Petuskey, William (Committee member) / Crozier, Peter (Committee member) / Arizona State University (Publisher)
Created2010
Description
The increasing demand for structural materials with superior mechanical properties has provided a strong impetus to the discovery of novel materials, and innovations in processing techniques to improve the properties of existing materials. Methods like severe plastic deformation (SPD) and surface mechanical attrition treatment (SMAT) have led to significant enhancement in the strength of traditional structural materials like Al and Fe based alloys via microstructural refinement. However, the nanocrystalline materials produced using these techniques exhibit poor ductility due to the lack of effective strain hardening mechanisms, and as a result the well-known strength-ductility trade-off persists. To overcome this trade-off, researchers have proposed the concept of heterostructured materials, which are composed of domains ranging in size from a few nanometers to several micrometers. Over the last two decades, there has been intense research on the development of new methods to synthesize heterostructured materials. However, none of these methods is capable of providing precise control over key microstructural parameters such as average grain size, grain morphology, and volume fraction and connectivity of coarse and fine grains. Due to the lack of microstructural control, the relationship between these parameters and the deformation behavior of heterostructured materials cannot be investigated systematically, and hence designing heterostructured materials with optimized properties is currently infeasible. This work aims to address this scientific and technological challenge and is composed of two distinct but interrelated parts. The first part concerns the development of a broadly applicable synthesis method to produce heterostructured metallic films with precisely defined architectures. This method exploits two forms of film growth (epitaxial and Volmer-Weber) to generate heterostructured metallic films. The second part investigates the effect of different microstructural parameters on the deformation behavior of heterostructured metallic films with the aim of elucidating their structure-property relationships. Towards this end, freestanding heterostructured Fe films with different architectures were fabricated and uniaxially deformed using MEMS stages. The results from these experiments are presented and their implications for the mechanical properties of heterostructured materials is discussed.
ContributorsBerlia, Rohit (Author) / Rajagopalan, Jagannathan (Thesis advisor) / Sieradzki, Karl (Committee member) / Peralta, Pedro (Committee member) / Crozier, Peter (Committee member) / Solanki, Kiran (Committee member) / Arizona State University (Publisher)
Created2021
Description
Modulated nanostructures are short-range periodic composition fluctuations observed in metals, semiconductors, and ceramic alloys and have an important effect on the mechanical, electrical, and magnetic properties of the materials. Their presence is often attributed to spinodal decomposition. In the past, such modulations have been analyzed using X-ray diffraction, electron diffraction, and diffraction contrast imaging techniques. The investigations gave useful information about the spatial distribution of the modulations but nothing about the composition fluctuation of the modulated structure. In this study, the composition amplitude of the fluctuations was directly measured using STEM Imaging and atomic resolution spectroscopy in small unit cell Au-Pt and Cu-Ti alloys. With the development of field emission sources, aberration correctors, and ADF imaging for STEM microscopes, measuring the amplitude of the modulation directly and examining the diffused interface is possible.Au-Pt alloys, featuring a nearly symmetrical solid-state miscibility gap, and a Cu-Ti alloy with an asymmetrical metastable miscibility gap were chosen for investigation. Three Au-Pt alloys of different compositions were analyzed at a specific temperature for varying aging times. The study successfully employed atomic resolution energy dispersive X-ray spectroscopy (EDS) for Au-Pt alloys and atomic resolution electron energy loss spectroscopy (EELS) for Cu-Ti alloys to measure composition variation and diffused interfaces across modulations.
In Au-Pt alloys, it was shown that the wavelength, as well as the composition amplitude of the modulations, increases as the alloy is aged for a longer time. Non-uniform distribution of wavelength and composition amplitude of modulated structures was observed across the samples. Results shows competitive growth mechanisms occurring in nanostructures with a range of wavelengths/amplitudes. Composition of Au-rich and Pt-rich regions deviates significantly from equilibrium at the selected temperature, more aging is necessary to observe coherency loss. Similarly, in Cu-Ti alloys, variations in wavelengths and composition amplitude of modulations were observed, along with clustering and ordering reactions. Ordering was specifically noted in Ti-rich regions of the alloy aged for an extended period. Diffused interfaces were observed in both alloy systems rather than chemically sharp interfaces, and the contrast in HAADF STEM images in both systems was predominantly influenced by strain effects. Hence utilizing HAADF STEM for composition measurement of modulations is impractical due to the impact of strain on HAADF intensity, specifically due to surface relaxation effects.
ContributorsSawant, Ronit Prasad (Author) / Carpenter, Ray (Thesis advisor) / Treacy, Michael (Committee member) / Crozier, Peter (Committee member) / Liu, Jingyue (Committee member) / Arizona State University (Publisher)
Created2024
Description
Photocatalytic water splitting is a promising technique to produce H2 fuels from water using sustainable solar energy. To better design photocatalysts, the understanding of charge transfer at surfaces/interfaces and the corresponding structure change during the reaction is very important. Local structural and chemical information on nanoparticle surfaces or interfaces can be achieved through characterizations on transmission electron microscopy (TEM). Emphasis should be put on materials structure changes during the reactions in their “working conditions”. Environmental TEM with in situ light illumination system allows the photocatalysts to be studied under light irradiation when exposed to H2O vapor. A set of ex situ and in situ TEM characterizations are carried out on typical types of TiO2 based photocatalysts. The observed structure changes during the reaction are correlated with the H2 production rate for structure-property relationships.
A surface disordering was observed in situ when well-defined anatase TiO2 rhombohedral nanoparticles were exposed to 1 Torr H2O vapor and 10suns light inside the environmental TEM. The disordering is believed to be related to high density of hydroxyl groups formed on surface oxygen vacancies during water splitting reactions.
Pt co-catalyst on TiO2 is able to split pure water producing H2 and O2. The H2 production rate drops during the reaction. Particle size growth during reaction was discovered with Z-contrast images. The particle size growth is believed to be a photo-electro-chemical Ostwald ripening.
Characterizations were also carried out on a more complicated photocatalyst system: Ni/NiO core/shell co-catalyst on TiO2. A decrease of the H2 production rate resulting from photo-corrosion was observed. The Ni is believed to be oxidized to Ni2+ by OH• radicals which are intermediate products of H2O oxidation. The mechanism that the OH• radicals leak into the cores through cracks on NiO shells is more supported by experiments.
Overall this research has done a comprehensive ex situ and in situ TEM characterizations following some typical TiO2 based photocatalysts during reactions. This research has shown the technique availability to study photocatalyst inside TEM in photocatalytic conditions. It also demonstrates the importance to follow structure changes of materials during reactions in understanding deactivation mechanisms.
A surface disordering was observed in situ when well-defined anatase TiO2 rhombohedral nanoparticles were exposed to 1 Torr H2O vapor and 10suns light inside the environmental TEM. The disordering is believed to be related to high density of hydroxyl groups formed on surface oxygen vacancies during water splitting reactions.
Pt co-catalyst on TiO2 is able to split pure water producing H2 and O2. The H2 production rate drops during the reaction. Particle size growth during reaction was discovered with Z-contrast images. The particle size growth is believed to be a photo-electro-chemical Ostwald ripening.
Characterizations were also carried out on a more complicated photocatalyst system: Ni/NiO core/shell co-catalyst on TiO2. A decrease of the H2 production rate resulting from photo-corrosion was observed. The Ni is believed to be oxidized to Ni2+ by OH• radicals which are intermediate products of H2O oxidation. The mechanism that the OH• radicals leak into the cores through cracks on NiO shells is more supported by experiments.
Overall this research has done a comprehensive ex situ and in situ TEM characterizations following some typical TiO2 based photocatalysts during reactions. This research has shown the technique availability to study photocatalyst inside TEM in photocatalytic conditions. It also demonstrates the importance to follow structure changes of materials during reactions in understanding deactivation mechanisms.
ContributorsZhang, Liuxian (Author) / Crozier, Peter (Thesis advisor) / Smith, David (Committee member) / Chan, Candace (Committee member) / Liu, Jingyue (Committee member) / Arizona State University (Publisher)
Created2015
Description
The origins of carrier mobility (μe) were thoroughly investigated in hydrogenated indium oxide (IO:H) and zinc-tin oxide (ZTO) transparent conducting oxide (TCO) thin films. A carrier transport model was developed for IO:H which studied the effects of ionized impurity scattering, polar optical phonon scattering, and grain boundary scattering. Ionized impurity scattering dominated at temperatures below ~240 K. A reduction in scattering charge Z from +2 to +1 as atomic %H increased from ~3 atomic %H to ~5 atomic %H allowed μe to attain >100 cm^2/Vs at ~5 atomic %H.
In highly hydrogenated IO:H, ne significantly decreased as temperature increased from 5 K to 140 K. To probe this unusual behavior, samples were illuminated, then ne, surface work function (WF), and spatially resolved microscopic current mapping were measured and tracked. Large increases in ne and corresponding decreases in WF were observed---these both exhibited slow reversions toward pre-illumination values over 6-12 days. A hydrogen-related defect was proposed as source of the photoexcitation, while a lattice defect diffusion mechanism causes the extended decay. Both arise from an under-coordination of the In.
An enhancement of μe was observed with increasing amorphous fraction in IO:H. An increase in population of corner- and edge-sharing polyhedra consisting of metal cations and oxygen anions is thought to be the origin. This indicates some measure of medium-range order in the amorphous structure, and gives rise to a general principle dictating μe in TCOs---even amorphous TCOs. Testing this principle resulted in observing an enhancement of μe up to 35 cm^2/Vs in amorphous ZTO (a-ZTO), one of the highest reported a-ZTO μe values (at ne > 10^19 cm^-3) to date. These results highlight the role of local distortions and cation coordination in determining the microscopic origins of carrier generation and transport. In addition, the strong likelihood of under-coordination of one cation species leading to high carrier concentrations is proposed. This diverges from the historical indictment of oxygen vacancies controlling carrier population in crystalline oxides, which by definition cannot occur in amorphous systems, and provides a framework to discuss key structural descriptors in these disordered phase materials.
In highly hydrogenated IO:H, ne significantly decreased as temperature increased from 5 K to 140 K. To probe this unusual behavior, samples were illuminated, then ne, surface work function (WF), and spatially resolved microscopic current mapping were measured and tracked. Large increases in ne and corresponding decreases in WF were observed---these both exhibited slow reversions toward pre-illumination values over 6-12 days. A hydrogen-related defect was proposed as source of the photoexcitation, while a lattice defect diffusion mechanism causes the extended decay. Both arise from an under-coordination of the In.
An enhancement of μe was observed with increasing amorphous fraction in IO:H. An increase in population of corner- and edge-sharing polyhedra consisting of metal cations and oxygen anions is thought to be the origin. This indicates some measure of medium-range order in the amorphous structure, and gives rise to a general principle dictating μe in TCOs---even amorphous TCOs. Testing this principle resulted in observing an enhancement of μe up to 35 cm^2/Vs in amorphous ZTO (a-ZTO), one of the highest reported a-ZTO μe values (at ne > 10^19 cm^-3) to date. These results highlight the role of local distortions and cation coordination in determining the microscopic origins of carrier generation and transport. In addition, the strong likelihood of under-coordination of one cation species leading to high carrier concentrations is proposed. This diverges from the historical indictment of oxygen vacancies controlling carrier population in crystalline oxides, which by definition cannot occur in amorphous systems, and provides a framework to discuss key structural descriptors in these disordered phase materials.
ContributorsHusein, Sebastian S.T. (Author) / Bertoni, Mariana I. (Thesis advisor) / Stuckelberger, Michael (Committee member) / Holman, Zachary C. (Committee member) / Crozier, Peter (Committee member) / Arizona State University (Publisher)
Created2020