The objective of this study centered on two studies including the development of an automated pultrusion system for the manufacturing of TRC composites and ultimately the assessment of composites created with the pultrusion technique and their viability as a relevant structural construction material. Upon planning, fabrication, and continued use of an automated pultrusion system in Arizona State University’s Structures Lab, an initial, comparative study of polypropylene microfiber composites was conducted to assess fiber reinforced concrete composites, manufactured with Filament Winding Technique, and textile reinforced concrete composites, manufactured with Automated Pultrusion Technique, in tensile and flexural mechanical response at similar reinforcement dosages. A secondary study was then conducted to measure the mechanical behavior of carbon, polypropylene, and alkali-resistant glass TRC composites and explore the response of full scale TRC structural shapes, including angle and channel sections. Finally, a study was conducted on the connection type for large scale TRC composite structural sections in tension and compression testing.
Laminated composites are increasingly being used in various industries including <br/>automotive and aerospace. Under a variety of extreme loading conditions such as low and <br/>high-velocity impacts and crash, laminated composites delaminate. To understand how and<br/>when delamination occurs, two types of laboratory tests are conducted - End-notched <br/>Flexure (ENF) test and Double Cantilever Beam (DCB) test. The ENF test is designed to <br/>find the mode II interlaminar fracture toughness, and the DCB test, the mode I interlaminar <br/>fracture toughness. In this thesis, thermopressed Honeywell Spectra Shield® 5231 <br/>composite specimens made of ultra-high molecular weight polyethylene (UHMWPE), <br/>manufactured under two different pressures (3000 psi and 6000 psi), are tested in the <br/>laboratory to find its delamination properties. The test specimen preparation, experimental <br/>procedures, and data reduction to determine the mode I and mode II interlaminar fracture <br/>properties are discussed. The ENF test results show a 15.8% increase in strain energy <br/>release rate for the 6000 psi specimens when compared to the 3000 psi specimens. <br/>Conducting the DCB tests proved to be challenging due to the low compressive strength <br/>of the material and hence required modifications to the test specimens. An estimate of the <br/>mode I interlaminar fracture toughness was found for only two of the 6000 psi specimens.