Filtering by
- All Subjects: Semiconductors
- Creators: Ponce, Fernando A.
- Creators: Department of Finance
Part of this work is focused on InAs quantum dots (QDs) embedded in AlGaAs matrices. This QD system is important for the realization of intermediate-band solar cells, which has three light absorption paths for high efficiency photovoltaics. The suppression of plastic strain relaxation in the QDs shows a significant improvement of the optoelectronic properties. A partial capping followed by a thermal annealing step is used to achieve spool-shaped QDs with a uniform height following the thickness of the capping layer. This step keeps the height of the QDs below a critical value that is required for plastic relaxation. The spool-shaped QDs exhibit two photoluminescence peaks that are attributed to ground and excited state transitions. The luminescence peak width is associated with the QD diameter distribution. An InAs cover layer formed during annealing is found responsible for the loss of the confinement of the excited states in smaller QDs.
The second part of this work is focused on the investigation of the InxGa1-xN thin films having different bandgaps for double-junction solar cells. InxGa1-xN films with x ≤ 0.15 were grown by metal organic chemical vapor deposition. The defects in films with different indium contents have been studied. Their effect on the optical properties of the film have been investigated by cathodoluminescence. InxGa1-xN films with indium contents higher than 20% were grown by molecular beam epitaxy. The strain relaxation in the films has been measured from electron diffraction patterns taken in cross-sectional TEM specimens. Moiré fringes in some of the films reveal interfacial strain relaxation that is explained by a critical thickness model.
Shockley Read Hall recombination plays a dominant role in the thermal droop effect when the current injection is low. Since the blue light emitting diode is based on Gallium Nitride, we need to take into consideration the effect of piezoelectric polarization in the quantum wells. The effects of the piezoelectric fields were studied based on the Gallium Nitride plane orientations. It was found in a Gallium Nitride light emitting diodes simulation study that more the number of quantum wells, lower would be the Radiative recombination rate. The problem of exacerbated spatial separation of electron hole wavefunctions in a thick single quantum well structure lead to the development of a dual well structure where one well assisted the other during high temperature operations. The Electron Blocking Layer was reduced in thickness and was made only 10 nm thick with a 5 nm Gallium Nitride buffer between it and the active region wells. The main reason for reducing the electron blocking layer thickness was to reduce the valance band offset and improve hole transport into the active region. Three different dual well designs were simulated of 3nm, 6nm and 9nm wide wells. The output parameters like the Power Spectral Density, Electron bound density, Light Output Power and Electron-Hole wavefunction overlaps were calculated. It was found that one of the wells acted as an assisting well where it had very little radiative recombination activity in it at room temperature.
As the temperature increased, it was observed that the electrons in the main well started to overflow out of it and into the assisting well where the radiative recombination rate increased significantly. This lead to a boost in Internal Quantum Efficiency.
This paper serves as an analysis of the current operational conditions of a real-world company – referred to as “Company X” – with respect to the IC substrate industry. The cost of substrates, a crucial component in the production of Company X’s product, has recently diverged from Company X’s predictions and is contributing to declining profitability. This analysis aims to discover the underlying cause for price divergence and recommend potential resolutions to improve the forecast of substrate costs and profitability. The paper is organized as follows: Chapter 1 is an introduction to IC substrates and the industry as a whole, Chapter 2 is a breakdown of the specific factors responsible for substrate prices, and Chapter 3 delivers a final recommendation to Company X and concludes the paper.