Description
In this project, current-voltage (I-V) and Deep Level Transient Spectroscopy (DLTS) measurements are used to (a) characterize the electrical properties of Nb/p-type Si Schottky barriers, (b) identify the concentration and physical character of the electrically active defects present in the depletion region, and (c) use thermal processing to reduce the concentration or eliminate the defects. Barrier height determinations using temperature-dependent I-V measurements indicate that the barrier height decreases from 0.50 eV to 0.48 eV for anneals above 200 C. The electrically-active defect concentration measured using DLTS (deep level transient spectroscopy) drops markedly after anneals at 250 C.
A significant increase in leakage currents is almost always observed in near-ideal devices upon annealing. In contrast, non-ideal devices dominated by leakage currents annealed at 150 C to 250 C exhibit a significant decrease in such currents.
A significant increase in leakage currents is almost always observed in near-ideal devices upon annealing. In contrast, non-ideal devices dominated by leakage currents annealed at 150 C to 250 C exhibit a significant decrease in such currents.
ContributorsKrishna Murthy, Madhu (Author) / Newman, Nathan (Thesis advisor) / Goryll, Michael (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2018
Description
Global photovoltaic (PV) module installation in 2018 is estimated to exceed 100 GW, and crystalline Si (c-Si) solar cell-based modules have a share more than 90% of the global PV market. To reduce the social cost of PV electricity, further developments in reliability of solar panels are expected. These will lead to realize longer module lifetime and reduced levelized cost of energy. As many as 86 failure modes are observed in PV modules [1] and series resistance increase is one of the major durability issues of all. Series resistance constitutes emitter sheet resistance, metal-semiconductor contact resistance, and resistance across the metal-solder ribbon. Solder bond degradation at the cell interconnect is one of the primary causes for increase in series resistance, which is also considered to be an invisible defect [1]. Combination of intermetallic compounds (IMC) formation during soldering and their growth due to solid state diffusion over its lifetime result in formation of weak interfaces between the solar cell and the interconnect. Thermal cycling under regular operating conditions induce thermo-mechanical fatigue over these weak interfaces resulting in contact reduction or loss. Contact reduction or loss leads to increase in series resistance which further manifests into power and fill factor loss. The degree of intermixing of metallic interfaces and contact loss depends on climatic conditions as temperature and humidity (moisture ingression into the PV module laminate) play a vital role in reaction kinetics of these layers. Modules from Arizona and Florida served as a good sample set to analyze the effects of hot and humid climatic conditions respectively. The results obtained in the current thesis quantifies the thickness of IMC formation from SEM-EDS profiles, where similar modules obtained from different climatic conditions were compared. The results indicate the thickness of the IMC and detachment degree to be growing with age and operating temperatures of the module. This can be seen in CuxSny IMC which is thicker in the case of Arizona module. The results obtained from FL
ii
aged modules also show that humidity accelerates the formation of IMC as they showed thicker AgxSny layer and weak interconnect-contact interfaces as compared to Arizona modules. It is also shown that climatic conditions have different effects on rate at which CuxSny and AgxSny intermetallic compounds are formed.
ii
aged modules also show that humidity accelerates the formation of IMC as they showed thicker AgxSny layer and weak interconnect-contact interfaces as compared to Arizona modules. It is also shown that climatic conditions have different effects on rate at which CuxSny and AgxSny intermetallic compounds are formed.
ContributorsBuddha, Viswa Sai Pavan (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Alford, Terry (Thesis advisor) / Srinivasan, Devarajan (Committee member) / Arizona State University (Publisher)
Created2018
Description
Electron Paramagnetic Resonance (EPR) has facilitated great scientific advancements in many fields, like material science, engineering, medicine, biology, and health. EPR provided the ability to investigate samples on molecular level to detect chemical composition and identify harmful substances like free radicals. This thesis aims to explore current health and diagnostics EPR research and investigate the free radical content in related paramagnetic centers. Examining paramagnetic diagnostic markers of Cancer, Sicklecell disease, oxidative stress, and food oxidation. After exploring current literature on EPR, an experiment is designed and conducted to test seven different coffee samples (Turkish coffee, Espresso Coffee, European Coffee, Ground Arabic Coffee, American Coffee, Roasted Arabic Coffee, and Green Arabic Coffee), using Bruker ELEXSYS E580 spectrometer at x-band and under both room temperature (298 K) and low temperature (106 -113 K). Several microwave powers (1, mW, 0.25 mW, 0.16 mW, 0.06 mW, 0.04 mW) and different modulation frequency (10 G, 5 G, 3 G) are used. The results revealed average g-value was 2.009, highest linewidth was 16.312. Espresso coffee had the highest concentration of radicals, and green Arabic coffee beans had the lowest. Obtained spectra showed signals of Reactive Oxygen Species (ROS) radicals; believed to be result of natural oxidation process, as well as trace amounts of Fe3+ and other transition metals impurities, likely to be naturally found in coffee or resulting from the process of coffee production.
ContributorsMaki, Husain (Author) / Newman, Nathan (Thesis advisor) / Alford, Terry (Committee member) / Chamberlin, Ralph (Committee member) / Arizona State University (Publisher)
Created2022