Matching Items (9)
Filtering by
- All Subjects: engineering
- All Subjects: Pyrites
Description
A series of pyrite thin films were synthesized using a novel sequential evaporation
technique to study the effects of substrate temperature on deposition rate and micro-structure of
the deposited material. Pyrite was deposited in a monolayer-by-monolayer fashion using
sequential evaporation of Fe under high vacuum, followed by sulfidation at high S pressures
(typically > 1 mTorr to 1 Torr). Thin films were synthesized using two different growth processes; a
one-step process in which a constant growth temperature is maintained throughout growth, and a
three-step process in which an initial low temperature seed layer is deposited, followed by a high
temperature layer, and then finished with a low temperature capping layer. Analysis methods to
analyze the properties of the films included Glancing Angle X-Ray Diffraction (GAXRD),
Rutherford Back-scattering Spectroscopy (RBS), Transmission Electron Microscopy (TEM),
Secondary Ion Mass Spectroscopy (SIMS), 2-point IV measurements, and Hall effect
measurements. Our results show that crystallinity of the pyrite thin film improves and grain size
increases with increasing substrate temperature. The sticking coefficient of Fe was found to
increase with increasing growth temperature, indicating that the Fe incorporation into the growing
film is a thermally activated process.
technique to study the effects of substrate temperature on deposition rate and micro-structure of
the deposited material. Pyrite was deposited in a monolayer-by-monolayer fashion using
sequential evaporation of Fe under high vacuum, followed by sulfidation at high S pressures
(typically > 1 mTorr to 1 Torr). Thin films were synthesized using two different growth processes; a
one-step process in which a constant growth temperature is maintained throughout growth, and a
three-step process in which an initial low temperature seed layer is deposited, followed by a high
temperature layer, and then finished with a low temperature capping layer. Analysis methods to
analyze the properties of the films included Glancing Angle X-Ray Diffraction (GAXRD),
Rutherford Back-scattering Spectroscopy (RBS), Transmission Electron Microscopy (TEM),
Secondary Ion Mass Spectroscopy (SIMS), 2-point IV measurements, and Hall effect
measurements. Our results show that crystallinity of the pyrite thin film improves and grain size
increases with increasing substrate temperature. The sticking coefficient of Fe was found to
increase with increasing growth temperature, indicating that the Fe incorporation into the growing
film is a thermally activated process.
ContributorsWertheim, Alex (Author) / Newman, Nathan (Thesis advisor) / Singh, Rakesh (Committee member) / Bertoni, Mariana (Committee member) / Arizona State University (Publisher)
Created2014
Description
Measurements of the response of superconducting nanowire single photon detector (SNSPD) devices to changes in various forms of input power can be used for characterization of the devices and for probing device-level physics. Two niobium nitride (NbN) superconducting nanowires developed for use as SNSPD devices are embedded as the inductive (L) component in resonant inductor/capacitor (LC) circuits coupled to a microwave transmission line. The capacitors are low loss commercial chip capacitors which limit the internal quality factor of the resonators to approximately $Qi = 170$. The resonator quality factor, approximately $Qr = 23$, is dominated by the coupling to the feedline and limits the detection bandwidth to on the order of 1MHz. In our experiments with this first generation device, we measure the response of the SNSPD devices to changes in thermal and optical power in both the time domain and the frequency domain. Additionally, we explore the non-linear response of the devices to an applied bias current. For these nanowires, we find that the band-gap energy is $\Delta_0 \approx 1.1$meV and that the density of states at the Fermi energy is $N_0 \sim 10^{10}$/eV/$\mu$m$^3$.
We present the results of experimentation with a superconducting nanowire that can be operated in two detection modes: i) as a kinetic inductance detector (KID) or ii) as a single photon detector (SPD). When operated as a KID mode in linear mode, the detectors are AC-biased with tones at their resonant frequencies of 45.85 and 91.81MHz. When operated as an SPD in Geiger mode, the resonators are DC biased through cryogenic bias tees and each photon produces a sharp voltage step followed by a ringdown signal at the resonant frequency of the detector. We show that a high AC bias in KID mode is inferior for photon counting experiments compared to operation in a DC-biased SPD mode due to the small fraction of time spent near the critical current with an AC bias. We find a photon count rate of $\Gamma_{KID} = 150~$photons/s/mA in a critically biased KID mode and a photon count rate of $\Gamma_{SPD} = 10^6~$photons/s/mA in SPD mode.
This dissertation additionally presents simulations of a DC-biased, frequency-multiplexed readout of SNSPD devices in Advanced Design System (ADS), LTspice, and Sonnet. A multiplexing factor of 100 is achievable with a total count rate of $>5$MHz. This readout could enable a 10000-pixel array for astronomy or quantum communications. Finally, we present a prototype array design based on lumped element components. An early implementation of the array is presented with 16 pixels in the frequency range of 74.9 to 161MHz. We find good agreement between simulation and experimental data in both the time domain and the frequency domain and present modifications for future versions of the array.
We present the results of experimentation with a superconducting nanowire that can be operated in two detection modes: i) as a kinetic inductance detector (KID) or ii) as a single photon detector (SPD). When operated as a KID mode in linear mode, the detectors are AC-biased with tones at their resonant frequencies of 45.85 and 91.81MHz. When operated as an SPD in Geiger mode, the resonators are DC biased through cryogenic bias tees and each photon produces a sharp voltage step followed by a ringdown signal at the resonant frequency of the detector. We show that a high AC bias in KID mode is inferior for photon counting experiments compared to operation in a DC-biased SPD mode due to the small fraction of time spent near the critical current with an AC bias. We find a photon count rate of $\Gamma_{KID} = 150~$photons/s/mA in a critically biased KID mode and a photon count rate of $\Gamma_{SPD} = 10^6~$photons/s/mA in SPD mode.
This dissertation additionally presents simulations of a DC-biased, frequency-multiplexed readout of SNSPD devices in Advanced Design System (ADS), LTspice, and Sonnet. A multiplexing factor of 100 is achievable with a total count rate of $>5$MHz. This readout could enable a 10000-pixel array for astronomy or quantum communications. Finally, we present a prototype array design based on lumped element components. An early implementation of the array is presented with 16 pixels in the frequency range of 74.9 to 161MHz. We find good agreement between simulation and experimental data in both the time domain and the frequency domain and present modifications for future versions of the array.
ContributorsSchroeder, Edward, Ph.D (Author) / Mauskopf, Philip (Thesis advisor) / Chamberlin, Ralph (Committee member) / Lindsay, Stuart (Committee member) / Newman, Nathan (Committee member) / Easson, Damien (Committee member) / Arizona State University (Publisher)
Created2018
Description
In this project, current-voltage (I-V) and Deep Level Transient Spectroscopy (DLTS) measurements are used to (a) characterize the electrical properties of Nb/p-type Si Schottky barriers, (b) identify the concentration and physical character of the electrically active defects present in the depletion region, and (c) use thermal processing to reduce the concentration or eliminate the defects. Barrier height determinations using temperature-dependent I-V measurements indicate that the barrier height decreases from 0.50 eV to 0.48 eV for anneals above 200 C. The electrically-active defect concentration measured using DLTS (deep level transient spectroscopy) drops markedly after anneals at 250 C.
A significant increase in leakage currents is almost always observed in near-ideal devices upon annealing. In contrast, non-ideal devices dominated by leakage currents annealed at 150 C to 250 C exhibit a significant decrease in such currents.
A significant increase in leakage currents is almost always observed in near-ideal devices upon annealing. In contrast, non-ideal devices dominated by leakage currents annealed at 150 C to 250 C exhibit a significant decrease in such currents.
ContributorsKrishna Murthy, Madhu (Author) / Newman, Nathan (Thesis advisor) / Goryll, Michael (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2018
Description
Lithium metal is a promising anode for the next generation lithium batteries owing to its high capacity (3860 mAh g-1) and the lowest negative reduction potential (-3.04 V). Commercial produced lithium anodes have a native rough surface which deteriorates the cycling performance of the battery. Here, an attempt has been made to deposit lithium on copper from an electrolytic cell consisting of simple electrolyte of pyridine and lithium chloride at room temperature. Water is known to react aggressively with the lithium metal, however in the electrochemical plating process, it has a significant beneficial effect in catalyzing the electrochemical reactions. The effect of trace amounts of water was investigated in air as well as in controlled atmosphere of argon, nitrogen, breathing grade dry air and ultra-zero dry air. The electrochemical products examined by Fourier transform infrared spectroscopy revealed the deposition might require the reduction of pyridine to facilitate the reduction of the lithium salt. Purity of the lithium film was determined by inductively coupled plasma mass spectrometry.
ContributorsPode, Gayatri (Author) / Newman, Nathan (Thesis advisor) / Marshall, Daniel (Committee member) / Tao, Meng (Committee member) / Arizona State University (Publisher)
Created2019
Description
Pyrite is a 0.95 eV bandgap semiconductor which is purported to have great potential in widespread, low–cost photovoltaic cells. A thorough material selection process was used in the design of a pyrite sequential vapor deposition chamber aimed at reducing and possibly eliminating contamination during thin film growth. The design process focused on identifying materials that do not produce volatile components when exposed to high temperatures and high sulfur pressures. Once the materials were identified and design was completed, the ultra–high vacuum growth system was constructed and tested.
Pyrite thin films were deposited using the upgraded sequential vapor deposition chamber by varying the substrate temperature from 250°C to 420°C during deposition, keeping sulfur pressure constant at 1 Torr. Secondary Ion Mass Spectrometry (SIMS) results showed that all contaminants in the films were reduced in concentration by orders of magnitude from those grown with the previous system. Characterization techniques of Rutherford Back–scattering Spectrometry (RBS), X–Ray Diffraction (XRD), Raman Spectroscopy, Optical Profilometry and UV/Vis/Near–IR Spectroscopy were performed on the deposited thin films. The results indicate that stoichiometric ratio of S:Fe, structural–quality (epitaxy), optical roughness and percentage of pyrite in the deposited thin films improve with increase in deposition temperature. A Tauc plot of the optical measurements indicates that the pyrite thin films have a bandgap of 0.94 eV.
Pyrite thin films were deposited using the upgraded sequential vapor deposition chamber by varying the substrate temperature from 250°C to 420°C during deposition, keeping sulfur pressure constant at 1 Torr. Secondary Ion Mass Spectrometry (SIMS) results showed that all contaminants in the films were reduced in concentration by orders of magnitude from those grown with the previous system. Characterization techniques of Rutherford Back–scattering Spectrometry (RBS), X–Ray Diffraction (XRD), Raman Spectroscopy, Optical Profilometry and UV/Vis/Near–IR Spectroscopy were performed on the deposited thin films. The results indicate that stoichiometric ratio of S:Fe, structural–quality (epitaxy), optical roughness and percentage of pyrite in the deposited thin films improve with increase in deposition temperature. A Tauc plot of the optical measurements indicates that the pyrite thin films have a bandgap of 0.94 eV.
ContributorsWalimbe, Aditya (Author) / Newman, Nathan (Thesis advisor) / Alford, Terry (Committee member) / Singh, Rakesh (Committee member) / Arizona State University (Publisher)
Created2016
Description
Measurements of the geometrical magnetoresistance of a conventional semiconductor, gallium arsenide (GaAs), and a more recently developed semiconductor, iron pyrite (FeS2) were measured in the Corbino disc geometry as a function of magnetic field to determine the carrier mobility (μm). These results were compared with measurements of the Hall mobility (μH) made in the Van der Pauw configuration. The scattering coefficient (ξ), defined as the ratio between magnetoresistance and Hall mobility (μm/μH), was determined experimentally for GaAs and natural pyrite from 300 K to 4.2 K. The effect of contact resistance and heating on the measurement accuracy is discussed.
ContributorsRavi, Aditya (Author) / Newman, Nathan (Thesis advisor) / Singh, Rakesh (Committee member) / Ferry, David K. (Committee member) / Arizona State University (Publisher)
Created2016
Description
The coexistence of superconductivity and ferromagnetic orders has been the subject of study for many years. It well known that these materials possess two competing order parameters; however the two order parameters can coexist under special circumstances inducing interesting physical phenomena. In recent years the demand of ultra-low-power, high density cryogenic memories has brought considerable interest to integrate superconducting and magnetic thin films in one structure to produce novel memory elements. The operation of the device depends on the unusual electronic properties associated with the Superconductor (S) /Ferromagnetic (F) proximity effect.
Niobium (Nb) based Josephson junction devices were fabricated with barriers containing two ferromagnetic layers separated by a normal metal space layer. In device operation, electrons in the superconductor are injected into the ferromagnets, causing the superconductor wavefunction to shift its phase and decay in amplitude. Such devices have two different states that depend on the relative magnetization of their ferromagnetic barrier layers, parallel or antiparallel. In these different states, the junctions have different phase shifts and critical currents. Superconducting circuits containing these devices can be designed to operate as memory cells using either one of these outputs.
To quantify the shift in phase and amplitude decay of the wavefunction through a common ferromagnet, permalloy, a series of Nb/permalloy/Nb Josephson junctions with varying ferromagnetic layer thicknesses were fabricated. Data have shown that the optimal thickness of a fixed layer composed of permalloy is 2.4 nm, as it shifts the wavefunction phase to π/2, its “pivot point.” If set to precisely this value, the free layer in SFNF'S junctions will switch the junction into either the 0 or π state depending on its magnetic orientation. To minimize the free-layer switching energy dilute Cu-permalloy alloy [Cu0.7(Ni80Fe20)0.3] with a low magnetic saturation (Ms of ~80 emu/cm3) was used as the free layer. These devices exhibit switching energies at small magnetic fields, demonstrating their potential use for low power non-volatile memory for superconductor circuits.
Lastly, to study the proximity effect using other potentially-useful ferromagnetic layers, measurements were performed on Nb/F bilayers and Nb/F/AlOx/Al tunnel junctions with ferromagnets Ni8Fe19, Ni65Fe15Co20, and Pd1-xNix. The dependence of the critical temperature of the bilayers and density of states that propagated through the ferromagnetic layer were studied as a function of thickness. From this study, crucial magnetic and electrical parameters like magnetic coherence lengths (ξF), exchange energy (Eex), and the rate of shift in the wavefunction’s phase and amplitude as a function of thickness were determined.
Niobium (Nb) based Josephson junction devices were fabricated with barriers containing two ferromagnetic layers separated by a normal metal space layer. In device operation, electrons in the superconductor are injected into the ferromagnets, causing the superconductor wavefunction to shift its phase and decay in amplitude. Such devices have two different states that depend on the relative magnetization of their ferromagnetic barrier layers, parallel or antiparallel. In these different states, the junctions have different phase shifts and critical currents. Superconducting circuits containing these devices can be designed to operate as memory cells using either one of these outputs.
To quantify the shift in phase and amplitude decay of the wavefunction through a common ferromagnet, permalloy, a series of Nb/permalloy/Nb Josephson junctions with varying ferromagnetic layer thicknesses were fabricated. Data have shown that the optimal thickness of a fixed layer composed of permalloy is 2.4 nm, as it shifts the wavefunction phase to π/2, its “pivot point.” If set to precisely this value, the free layer in SFNF'S junctions will switch the junction into either the 0 or π state depending on its magnetic orientation. To minimize the free-layer switching energy dilute Cu-permalloy alloy [Cu0.7(Ni80Fe20)0.3] with a low magnetic saturation (Ms of ~80 emu/cm3) was used as the free layer. These devices exhibit switching energies at small magnetic fields, demonstrating their potential use for low power non-volatile memory for superconductor circuits.
Lastly, to study the proximity effect using other potentially-useful ferromagnetic layers, measurements were performed on Nb/F bilayers and Nb/F/AlOx/Al tunnel junctions with ferromagnets Ni8Fe19, Ni65Fe15Co20, and Pd1-xNix. The dependence of the critical temperature of the bilayers and density of states that propagated through the ferromagnetic layer were studied as a function of thickness. From this study, crucial magnetic and electrical parameters like magnetic coherence lengths (ξF), exchange energy (Eex), and the rate of shift in the wavefunction’s phase and amplitude as a function of thickness were determined.
ContributorsAbd El Qader, Makram (Author) / Newman, Nathan (Thesis advisor) / Rowell, John (Committee member) / Rizzo, Nick (Committee member) / Yu, Hongbin (Committee member) / Arizona State University (Publisher)
Created2016
Description
Electron Paramagnetic Resonance (EPR) has facilitated great scientific advancements in many fields, like material science, engineering, medicine, biology, and health. EPR provided the ability to investigate samples on molecular level to detect chemical composition and identify harmful substances like free radicals. This thesis aims to explore current health and diagnostics EPR research and investigate the free radical content in related paramagnetic centers. Examining paramagnetic diagnostic markers of Cancer, Sicklecell disease, oxidative stress, and food oxidation. After exploring current literature on EPR, an experiment is designed and conducted to test seven different coffee samples (Turkish coffee, Espresso Coffee, European Coffee, Ground Arabic Coffee, American Coffee, Roasted Arabic Coffee, and Green Arabic Coffee), using Bruker ELEXSYS E580 spectrometer at x-band and under both room temperature (298 K) and low temperature (106 -113 K). Several microwave powers (1, mW, 0.25 mW, 0.16 mW, 0.06 mW, 0.04 mW) and different modulation frequency (10 G, 5 G, 3 G) are used. The results revealed average g-value was 2.009, highest linewidth was 16.312. Espresso coffee had the highest concentration of radicals, and green Arabic coffee beans had the lowest. Obtained spectra showed signals of Reactive Oxygen Species (ROS) radicals; believed to be result of natural oxidation process, as well as trace amounts of Fe3+ and other transition metals impurities, likely to be naturally found in coffee or resulting from the process of coffee production.
ContributorsMaki, Husain (Author) / Newman, Nathan (Thesis advisor) / Alford, Terry (Committee member) / Chamberlin, Ralph (Committee member) / Arizona State University (Publisher)
Created2022
Description
Color perception has been widely studied and well modeled with respect to combining visible electromagnetic frequencies, yet new technology provides the means to better explore and test novel temporal frequency characteristics of color perception. Experiment 1 tests how reliably participants categorize static spectral rainbow colors, which can be a useful tool for efficiently identifying those with functional dichromacy, trichromacy, and tetrachromacy. The findings confirm that all individuals discern the four principal opponent process colors, red, yellow, green, and blue, with normal and potential tetrachromats seeing more distinct colors than color blind individuals. Experiment 2 tests the moving flicker fusion rate of the central electromagnetic frequencies within each color category found in Experiment 1 as a test of the Where system. It then compares this to the maximum temporal processing rate for discriminating direction of hue change with colors displayed serially as a test of the What system. The findings confirm respective processing thresholds of about 20 Hz for Where and 2-7 Hz for What processing systems. Experiment 3 tests conditions that optimize false colors based on the spinning Benham’s Top illusion. Findings indicate the same four principal colors emerge as in Experiment 1, but at low saturation levels for trichromats that diminish further for dichromats. Taken together, the three experiments provide an overview of the common categorical boundaries and temporal processing limits of human color vision.
ContributorsKrynen, Richard Chandler (Author) / Mcbeath, Michael K (Thesis advisor) / Homa, Donald (Committee member) / Newman, Nathan (Committee member) / Stone, Greg (Committee member) / Arizona State University (Publisher)
Created2021