Matching Items (26)
Filtering by

Clear all filters

151523-Thumbnail Image.png
Description
Shock loading is a complex phenomenon that can lead to failure mechanisms such as strain localization, void nucleation and growth, and eventually spall fracture. Studying incipient stages of spall damage is of paramount importance to accurately determine initiation sites in the material microstructure where damage will nucleate and grow and

Shock loading is a complex phenomenon that can lead to failure mechanisms such as strain localization, void nucleation and growth, and eventually spall fracture. Studying incipient stages of spall damage is of paramount importance to accurately determine initiation sites in the material microstructure where damage will nucleate and grow and to formulate continuum models that account for the variability of the damage process due to microstructural heterogeneity. The length scale of damage with respect to that of the surrounding microstructure has proven to be a key aspect in determining sites of failure initiation. Correlations have been found between the damage sites and the surrounding microstructure to determine the preferred sites of spall damage, since it tends to localize at and around the regions of intrinsic defects such as grain boundaries and triple points. However, considerable amount of work still has to be done in this regard to determine the physics driving the damage at these intrinsic weak sites in the microstructure. The main focus of this research work is to understand the physical mechanisms behind the damage localization at these preferred sites. A crystal plasticity constitutive model is implemented with different damage criteria to study the effects of stress concentration and strain localization at the grain boundaries. A cohesive zone modeling technique is used to include the intrinsic strength of the grain boundaries in the simulations. The constitutive model is verified using single elements tests, calibrated using single crystal impact experiments and validated using bicrystal and multicrystal impact experiments. The results indicate that strain localization is the predominant driving force for damage initiation and evolution. The microstructural effects on theses damage sites are studied to attribute the extent of damage to microstructural features such as grain orientation, misorientation, Taylor factor and the grain boundary planes. The finite element simulations show good correlation with the experimental results and can be used as the preliminary step in developing accurate probabilistic models for damage nucleation.
ContributorsKrishnan, Kapil (Author) / Peralta, Pedro (Thesis advisor) / Mignolet, Marc (Committee member) / Sieradzki, Karl (Committee member) / Jiang, Hanqing (Committee member) / Oswald, Jay (Committee member) / Arizona State University (Publisher)
Created2013
151000-Thumbnail Image.png
Description
Gels are three-dimensional polymer networks with entrapped solvent (water etc.). They bear amazing features such as stimuli-responsive (temperature, PH, electric field etc.), high water content and biocompatibility and thus find a lot of applications. To understand the complex physics behind gel's swelling phenomenon, it is important to build up fundamental

Gels are three-dimensional polymer networks with entrapped solvent (water etc.). They bear amazing features such as stimuli-responsive (temperature, PH, electric field etc.), high water content and biocompatibility and thus find a lot of applications. To understand the complex physics behind gel's swelling phenomenon, it is important to build up fundamental mechanical model and extend to complicated cases. In this dissertation, a coupled large deformation and diffusion model regarding gel's swelling behavior is presented. In this model, free-energy of the total gel is constituted by polymer stretching energy and polymer-solvent mixing energy. In-house nonlinear finite element code is implemented with fast computational capability. Complex phenomenon such as buckling and healing of cracked gel by swelling are studied. Due to the wide coverage of polymeric materials and solvents, solvent diffusion in gels not only follows Fickian diffusion law where concentration map is continuous but also follows non-Fickian diffusion law where concentration map shows high gradient. Phenomenological model with viscoelastic polymer constitutive and concentration dependent diffusivity is created. The model well captures this special diffusion phenomenon such as sharp diffusion front and distinctive swollen and unswollen region.
ContributorsZhang, Jiaping (Author) / Jiang, Hanqing (Thesis advisor) / Peralta, Pedro (Committee member) / Dai, Lenore (Committee member) / Rajan, Subramaniam D. (Committee member) / Chawla, Nikhilesh (Committee member) / Arizona State University (Publisher)
Created2012
149487-Thumbnail Image.png
Description
Current trends in the Computer Aided Engineering (CAE) involve the integration of legacy mesh-based finite element software with newer solid-modeling kernels or full CAD systems in order to simplify laborious or highly specialized tasks in engineering analysis. In particular, mesh generation is becoming increasingly automated. In addition, emphasis is increasingly

Current trends in the Computer Aided Engineering (CAE) involve the integration of legacy mesh-based finite element software with newer solid-modeling kernels or full CAD systems in order to simplify laborious or highly specialized tasks in engineering analysis. In particular, mesh generation is becoming increasingly automated. In addition, emphasis is increasingly placed on full assembly (multi-part) models, which in turn necessitates an automated approach to contact analysis. This task is challenging due to increases in algebraic system size, as well as increases in the number of distorted elements - both of which necessitate manual intervention to maintain accuracy and conserve computer resources. In this investigation, it is demonstrated that the use of a mesh-free B-Spline finite element basis for structural contact problems results in significantly smaller algebraic systems than mesh-based approaches for similar grid spacings. The relative error in calculated contact pressure is evaluated for simple two dimensional smooth domains at discrete points within the contact zone and compared to the analytical Hertz solution, as well as traditional mesh-based finite element solutions for similar grid spacings. For smooth curved domains, the relative error in contact pressure is shown to be less than for bi-quadratic Serendipity elements. The finite element formulation draws on some recent innovations, in which the domain to be analyzed is integrated with the use of transformed Gauss points within the domain, and boundary conditions are applied via distance functions (R-functions). However, the basis is stabilized through a novel selective normalization procedure. In addition, a novel contact algorithm is presented in which the B-Spline support grid is re-used for contact detection. The algorithm is demonstrated for two simple 2-dimensional assemblies. Finally, a modified Penalty Method is demonstrated for connecting elements with incompatible bases.
ContributorsGrishin, Alexander (Author) / Shah, Jami J. (Thesis advisor) / Davidson, Joe (Committee member) / Hjelmstad, Keith (Committee member) / Huebner, Ken (Committee member) / Farin, Gerald (Committee member) / Peralta, Pedro (Committee member) / Arizona State University (Publisher)
Created2010
171947-Thumbnail Image.png
Description
Aromatic polymers, with benzene-like rings in their main chains, include materials such as polyurea, an amorphous elastomer capable of dissipating large amounts of energy under dynamic loading, which makes it a promising coating for defensive systems. Although computational research exists that investigates the atomic-level response of polyurea and other amorphous

Aromatic polymers, with benzene-like rings in their main chains, include materials such as polyurea, an amorphous elastomer capable of dissipating large amounts of energy under dynamic loading, which makes it a promising coating for defensive systems. Although computational research exists that investigates the atomic-level response of polyurea and other amorphous aromatic polymers to extreme conditions, there is little experimental work to validate these models 1) at the atomic-scale and 2) under high pressures characteristic of extreme dynamic loading. Understanding structure-property relationships at the atomic-level is important for polymers, considering many of them undergo pressure and temperature-induced structural transformations, which must be understood to formulate accurate predictive models. This work aims to gain a deeper understanding of the high-pressure structural response of aromatic polymers at the atomic-level, with emphasis into the mechanisms associated with high-pressure transformations. Hence, atomic-level structural data at high pressures was obtained in situ via multiangle energy dispersive X-ray diffraction (EDXD) experiments at the Advanced Photon Source (APS) for polyurea and another amorphous aromatic polymer, polysulfone, chosen as a reference due to its relatively simple structure. Pressures up to 6 GPa were applied using a Paris Edinburgh (PE) hydraulic press at room temperature. Select polyurea samples were also heated to 277 °C at 6 GPa. The resulting structure factors and pair distribution functions, along with molecular dynamics simulations of polyurea provided by collaborators, suggest that the structures of both polymers are stable up to 6 GPa, aside from reductions in free-volume between polymer backbones. As higher pressures (≲ 32 GPa) were applied using diamond anvils in combination with the PE press, indications of structural transformations were observed in both polymers that appear similar in nature to the sp2-sp3 hybridization in compressed carbon. The transformation occurs gradually up to at least ~ 26 GPa in PSF, while it does not progress past ~ 15 GPa in polyurea. The changes are largely reversible, especially in polysulfone, consistent with pressure-driven, reversible graphite-diamond transformations in the absence of applied temperature. These results constitute some of the first in situ observations of the mechanisms that drive pressure-induced structural transformations in aromatic polymers.
ContributorsEastmond, Tyler (Author) / Peralta, Pedro (Thesis advisor) / Hoover, Christian (Committee member) / Hrubiak, Rostislav (Committee member) / Mignolet, Marc (Committee member) / Oswald, Jay (Committee member) / Arizona State University (Publisher)
Created2022
168428-Thumbnail Image.png
Description
Over the past few decades there has been significant interest in the design and construction of hypersonic vehicles. Such vehicles exhibit strongly coupled aerodynamics, acoustics, heat transfer, and structural deformations, which can take significant computational efforts to simulate using standard finite element and computational fluid dynamics techniques. This situation has

Over the past few decades there has been significant interest in the design and construction of hypersonic vehicles. Such vehicles exhibit strongly coupled aerodynamics, acoustics, heat transfer, and structural deformations, which can take significant computational efforts to simulate using standard finite element and computational fluid dynamics techniques. This situation has lead to development of various reduced order modelling (ROM) methods which reduce the parameter space of these simulations so they can be run more quickly. The planned hypersonic vehicles will be constructed by assembling a series of sub-structures, such as panels and stiffeners, that will be welded together creating built-up structures.In this light, the focus of the present investigation is on the formulation and validation of nonlinear reduced order models (NLROMs) of built-up structures that include nonlinear geometric effects induced by the large loads/large response. Moreover, it is recognized that gaps between sub-structures could result from the these intense loadings can thus the inclusion of the nonlinearity introduced by contact separation will also be addressed. These efforts, application to built-up structures and inclusion of contact nonlinearity, represent novel developments of existing NLROM strategies. A hat stiffened panel is selected as a representative example of built-up structure and a compact NRLOM is successfully constructed for this structure which exhibited a potential internal resonance. For the investigation of contact nonlinearity, two structural models were used: a cantilevered beam which can contact several stops and an overlapping plate model which can exhibit the opening/closing of a gap. Successful NLROMs were constructed for these structures with the basis for the plate model determined as a two-step process, i.e., considering the plate without gap first and then enriching the corresponding basis to account for opening of the gap. Adaptions were then successfully made to a Newton-Raphson solver to properly account for contact and the associated forces in static predictions by NLROMs.
ContributorsWainwright, Bret Aaron (Author) / Mignolet, Marc P (Thesis advisor) / Oswald, Jay (Committee member) / Peralta, Pedro (Committee member) / Spottswood, Stephen (Committee member) / Rajan, Subramaniam (Committee member) / Arizona State University (Publisher)
Created2021
168311-Thumbnail Image.png
Description
The increasing demand for structural materials with superior mechanical properties has provided a strong impetus to the discovery of novel materials, and innovations in processing techniques to improve the properties of existing materials. Methods like severe plastic deformation (SPD) and surface mechanical attrition treatment (SMAT) have led to significant enhancement

The increasing demand for structural materials with superior mechanical properties has provided a strong impetus to the discovery of novel materials, and innovations in processing techniques to improve the properties of existing materials. Methods like severe plastic deformation (SPD) and surface mechanical attrition treatment (SMAT) have led to significant enhancement in the strength of traditional structural materials like Al and Fe based alloys via microstructural refinement. However, the nanocrystalline materials produced using these techniques exhibit poor ductility due to the lack of effective strain hardening mechanisms, and as a result the well-known strength-ductility trade-off persists. To overcome this trade-off, researchers have proposed the concept of heterostructured materials, which are composed of domains ranging in size from a few nanometers to several micrometers. Over the last two decades, there has been intense research on the development of new methods to synthesize heterostructured materials. However, none of these methods is capable of providing precise control over key microstructural parameters such as average grain size, grain morphology, and volume fraction and connectivity of coarse and fine grains. Due to the lack of microstructural control, the relationship between these parameters and the deformation behavior of heterostructured materials cannot be investigated systematically, and hence designing heterostructured materials with optimized properties is currently infeasible. This work aims to address this scientific and technological challenge and is composed of two distinct but interrelated parts. The first part concerns the development of a broadly applicable synthesis method to produce heterostructured metallic films with precisely defined architectures. This method exploits two forms of film growth (epitaxial and Volmer-Weber) to generate heterostructured metallic films. The second part investigates the effect of different microstructural parameters on the deformation behavior of heterostructured metallic films with the aim of elucidating their structure-property relationships. Towards this end, freestanding heterostructured Fe films with different architectures were fabricated and uniaxially deformed using MEMS stages. The results from these experiments are presented and their implications for the mechanical properties of heterostructured materials is discussed.
ContributorsBerlia, Rohit (Author) / Rajagopalan, Jagannathan (Thesis advisor) / Sieradzki, Karl (Committee member) / Peralta, Pedro (Committee member) / Crozier, Peter (Committee member) / Solanki, Kiran (Committee member) / Arizona State University (Publisher)
Created2021
189221-Thumbnail Image.png
Description
The relationships between the properties of materials and their microstructures have been a central topic in materials science. The microstructure-property mapping and numerical failure prediction are critical for integrated computational material engineering (ICME). However, the bottleneck of ICME is the lack of a clear understanding of the failure mechanism as

The relationships between the properties of materials and their microstructures have been a central topic in materials science. The microstructure-property mapping and numerical failure prediction are critical for integrated computational material engineering (ICME). However, the bottleneck of ICME is the lack of a clear understanding of the failure mechanism as well as an efficient computational framework. To resolve these issues, research is performed on developing novel physics-based and data-driven numerical methods to reveal the failure mechanism of materials in microstructure-sensitive applications. First, to explore the damage mechanism of microstructure-sensitive materials in general loading cases, a nonlocal lattice particle model (LPM) is adopted because of its intrinsic ability to handle the discontinuity. However, the original form of LPM is unsuitable for simulating nonlinear behavior involving tensor calculation. Therefore, a damage-augmented LPM (DLPM) is proposed by introducing the concept of interchangeability and bond/particle-based damage criteria. The proposed DLPM successfully handles the damage accumulation behavior in general material systems under static and fatigue loading cases. Then, the study is focused on developing an efficient physics-based data-driven computational framework. A data-driven model is proposed to improve the efficiency of a finite element analysis neural network (FEA-Net). The proposed model, i.e., MFEA-Net, aims to learn a more powerful smoother in a multigrid context. The learned smoothers have good generalization properties, and the resulted MFEA-Net has linear computational complexity. The framework has been applied to efficiently predict the thermal and elastic behavior of composites with various microstructural fields. Finally, the fatigue behavior of additively manufactured (AM) Ti64 alloy is analyzed both experimentally and numerically. The fatigue experiments show the fatigue life is related with the contour process parameters, which can result in different pore defects, surface roughness, and grain structures. The fractography and grain structures are closely observed using scanning electron microscope. The sample geometry and defect/crack morphology are characterized through micro computed tomography (CT). After processing the pixel-level CT data, the fatigue crack initiation and growth behavior are numerically simulated using MFEA-Net and DLPM. The experiments and simulation results provided valuable insights in fatigue mechanism of AM Ti64 alloy.
ContributorsMeng, Changyu (Author) / Liu, Yongming (Thesis advisor) / Hoover, Christian (Committee member) / Li, Lin (Committee member) / Peralta, Pedro (Committee member) / Wang, Liping (Committee member) / Arizona State University (Publisher)
Created2023
187523-Thumbnail Image.png
Description
The design of energy absorbing structures is driven by application specific requirements like the amount of energy to be absorbed, maximum transmitted stress that is permissible, stroke length, and available enclosing space. Cellular structures like foams are commonly leveraged in nature for energy absorption and have also found use in

The design of energy absorbing structures is driven by application specific requirements like the amount of energy to be absorbed, maximum transmitted stress that is permissible, stroke length, and available enclosing space. Cellular structures like foams are commonly leveraged in nature for energy absorption and have also found use in engineering applications. With the possibility of manufacturing complex cellular shapes using additive manufacturing technologies, there is an opportunity to explore new topologies that improve energy absorption performance. This thesis aims to systematically understand the relationships between four key elements: (i) unit cell topology, (ii) material composition, (iii) relative density, and (iv) fields; and energy absorption behavior, and then leverage this understanding to develop, implement and validate a methodology to design the ideal cellular structure energy absorber. After a review of the literature in the domain of additively manufactured cellular materials for energy absorption, results from quasi-static compression of six cellular structures (hexagonal honeycomb, auxetic and Voronoi lattice, and diamond, Gyroid, and Schwarz-P) manufactured out of AlSi10Mg and Nylon-12. These cellular structures were compared to each other in the context of four design-relevant metrics to understand the influence of cell design on the deformation and failure behavior. Three new and revised metrics for energy absorption were proposed to enable more meaningful comparisons and subsequent design selection. Triply Periodic Minimal Surface (TPMS) structures were found to have the most promising overall performance and formed the basis for the numerical investigation of the effect of fields on the energy absorption performance of TPMS structures. A continuum shell-based methodology was developed to analyze the large deformation behavior of field-driven variable thickness TPMS structures and validated against experimental data. A range of analytical and stochastic fields were then evaluated that modified the TPMS structure, some of which were found to be effective in enhancing energy absorption behavior in the structures while retaining the same relative density. Combining findings from studies on the role of cell geometry, composition, relative density, and fields, this thesis concludes with the development of a design framework that can enable the formulation of cellular material energy absorbers with idealized behavior.
ContributorsShinde, Mandar (Author) / Bhate, Dhruv (Thesis advisor) / Peralta, Pedro (Committee member) / Liu, Yongming (Committee member) / Jiao, Yang (Committee member) / Kwon, Beomjin (Committee member) / Arizona State University (Publisher)
Created2023
193453-Thumbnail Image.png
Description
Energetic materials with granular microstructures find wide applications in military and civilian sectors. A comprehensive understanding of their shock response is crucial for the development of safer explosives and predictive models. Initiation of the explosive reaction, a critical safety concern, is believed to be triggered by the formation of hotspots,

Energetic materials with granular microstructures find wide applications in military and civilian sectors. A comprehensive understanding of their shock response is crucial for the development of safer explosives and predictive models. Initiation of the explosive reaction, a critical safety concern, is believed to be triggered by the formation of hotspots, i.e., localized high-temperature regions. Although direct observation of hotspots remains elusive, computational simulations offer a window into their behavior. This work investigates effect of porosity on reactivity of hotspots in Pentaerythritol Tetranitrate (PETN) and potential shock surrogate Meso-Erythritol (ME). Building upon findings that link hotspot size and temperature to material heterogeneity, this research integrates experimental characterization of ME and mesoscale simulations of both ME and PETN to quantify how the pore distribution influences hotspots. Results showed that shock impedance of ME is within 10% of PETN up to 1 GPa, highlighting its potential as a shock surrogate for weak shocks. Gas gun tests with ME validated Hugoniot parameters in literature, which were used in a P-α compaction model, validating that mesoscale simulations of shock loaded ME agree with experiments within measured uncertainty. This mesoscale approach was then applied to PETN by using synthetically generated microstructures, which demonstrates that enlarging pore size in PETN results in more individually reactive hotspots and greater variability in thermodynamic states over time than increasing pore count or starting with a lower porosity. A higher pore count produces a more right-skewed temperature distribution, indicating a greater total number of hotspots compared to other conditions. Simulations also show that air in individual pores lowers the peak hotspot temperatures due to work done compressing the air and affects secondary hotspot formation. Hotspots within 0.15 μm can react at temperatures below 800 K, their proximity enabling them to bypass thermal quenching via local heat transfer.
ContributorsWilde, Zakary Robert (Author) / Peralta, Pedro (Thesis advisor) / Arizona State University (Publisher)
Created2024
157170-Thumbnail Image.png
Description
In this research, a new cutting edge wear estimator for micro-endmilling is developed and the reliabillity of the estimator is evaluated. The main concept of this estimator is the minimum chip thickness effect. This estimator predicts the cutting edge radius by detecting the drop in the chip production rate as

In this research, a new cutting edge wear estimator for micro-endmilling is developed and the reliabillity of the estimator is evaluated. The main concept of this estimator is the minimum chip thickness effect. This estimator predicts the cutting edge radius by detecting the drop in the chip production rate as the cutting edge of a micro- endmill slips over the workpiece when the minimum chip thickness becomes larger than the uncut chip thickness, thus transitioning from the shearing to the ploughing dominant regime. The chip production rate is investigated through simulation and experiment. The simulation and the experiment show that the chip production rate decreases when the minimum chip thickness becomes larger than the uncut chip thickness. Also, the reliability of this estimator is evaluated. The probability of correct estimation of the cutting edge radius is more than 80%. This cutting edge wear estimator could be applied to an online tool wear estimation system. Then, a large number of cutting edge wear data could be obtained. From the data, a cutting edge wear model could be developed in terms of the machine control parameters so that the optimum control parameters could be applied to increase the tool life and the machining quality as well by minimizing the cutting edge wear rate.

In addition, in order to find the stable condition of the machining, the stabillity lobe of the system is created by measuring the dynamic parameters. This process is needed prior to the cutting edge wear estimation since the chatter would affect the cutting edge wear and the chip production rate. In this research, a new experimental set-up for measuring the dynamic parameters is developed by using a high speed camera with microscope lens and a loadcell. The loadcell is used to measure the stiffness of the tool-holder assembly of the machine and the high speed camera is used to measure the natural frequency and the damping ratio. From the measured data, a stability lobe is created. Even though this new method needs further research, it could be more cost-effective than the conventional methods in the future.
ContributorsLee, Jue-Hyun (Author) / SODEMANN, ANGELA A (Thesis advisor) / Shuaib, Abdelrahman (Committee member) / Hsu, Keng (Committee member) / Artemiadis, Panagiotis (Committee member) / Liu, Yongming (Committee member) / Arizona State University (Publisher)
Created2019