Filtering by
- Creators: Liu, Yongming
- Creators: Rajagopalan, Jagannathan
A unique geometry is presented that creates biaxial stresses and strains when subjected to uniaxial loading in order to facilitate further multiaxial fatigue research by reducing the need for the use of specialized multiaxial loading equipment. Cyclic plasticity is a critical process in fatigue and the geometry was successfully designed and fabricated to allow for the continuous monitoring of cyclic plastic strains of magnitude 10^(-4) mm/mm during cyclic loading. Simulation results show that plasticity occurs in a region central to the test specimen while also being subjected to biaxial stresses and strains characterized by average principal direction ratios of 1.18 and 1.39 respectively. Simulation shows fatigue life of the specimen to be 79 thousand cycles, which allows for a reasonable evolution of cyclic plasticity before reaching failure. Issues with the instrumentation process hindered experimental validation of the simulation results.
(i) Comprehensive investigation of micro- and macroscale crack growth behavior in aerospace grade Al 7075 T651 alloy under complex biaxial fatigue loading conditions. The effects of variable amplitude biaxial loading on crack growth characteristics such as crack acceleration and retardation were studied in detail by exclusively analyzing the influence of individual mode-I, mixed-mode and mode-II overload and underload fatigue cycles in an otherwise constant amplitude mode-I baseline load spectrum. The micromechanisms governing crack growth behavior under the complex biaxial loading conditions were identified and correlated with the crack growth behavior and fracture surface morphology through quantitative fractography.
(ii) Development of novel multifunctional nanocomposite materials with improved fatigue resistance and in-situ fatigue damage detection and quantification capabilities. A state-of-the-art processing method was developed for producing sizable carbon nanotube (CNT) membranes for multifunctional composites. The CNT membranes were embedded in glass fiber laminates and in-situ strain sensing and damage quantification was achieved by exploiting the piezoresistive property of the CNT membrane. In addition, improved resistance to fatigue crack growth was observed due to the embedded CNT membrane.
Current practice in fatigue life prediction is based on either physics based modeling or data-driven methods, and is limited to predicting RUL for simple geometries under uniaxial loading conditions. In this research, crack initiation and propagation behavior under uniaxial and complex biaxial fatigue loading is addressed. The crack propagation behavior is studied by performing extensive material characterization and fatigue testing under in-plane biaxial loading, both in-phase and out-of-phase, with different biaxiality ratios. A hybrid prognosis model, which combines machine learning with physics based modeling, is developed to account for the uncertainties in crack propagation and fatigue life prediction due to variabilities in material microstructural characteristics, crack localization information and environmental changes. The methodology iteratively combines localization information with hybrid prognosis models using sequential Bayesian techniques. The results show significant improvements in the localization and prediction accuracy under varying temperature.
For civil infrastructure, especially bridges, pier scour is a major failure mechanism. Currently available techniques are developed from a design perspective and provide highly conservative scour estimates. In this research, a fully probabilistic scour prediction methodology is developed using machine learning to accurately predict scour in real-time under varying flow conditions.