- Creators: Holman, Zachary
Description
Silicon solar cells with heterojunction carrier collectors based on a-Si/c-Si heterojunction (SHJ) have a potential to overcome the limitations of the conventional diffused junction solar cells and become the next industry standard manufacturing technology of solar cells. A brand feature of SHJ technology is ultrapassivated surfaces with already demonstrated 750 mV open circuit voltages (Voc) and 24.7% efficiency on large area solar cell. Despite very good results achieved in research and development, large volume manufacturing of high efficiency SHJ cells remains a fundamental challenge. The main objectives of this work were to develop a SHJ solar cell fabrication flow using industry compatible tools and processes in a pilot production environment, study the interactions between the used fabrication steps, identify the minimum set of optimization parameters and characterization techniques needed to achieve 20% baseline efficiency, and analyze the losses of power in fabricated SHJ cells by numerical and analytical modeling. This manuscript presents a detailed description of a SHJ solar cell fabrication flow developed at ASU Solar Power Laboratory (SPL) which allows large area solar cells with >750 mV Voc. SHJ cells on 135 um thick 153 cm2 area wafers with 19.5% efficiency were fabricated. Passivation quality of (i)a-Si:H film, bulk conductivity of doped a-Si films, bulk conductivity of ITO, transmission of ITO and the thickness of all films were identified as the minimum set of optimization parameters necessary to set up a baseline high efficiency SHJ fabrication flow. The preparation of randomly textured wafers to minimize the concentration of surface impurities and to avoid epitaxial growth of a-Si films was found to be a key challenge in achieving a repeatable and uniform passivation. This work resolved this issue by using a multi-step cleaning process based on sequential oxidation in nitric/acetic acids, Piranha and RCA-b solutions. The developed process allowed state of the art surface passivation with perfect repeatability and negligible reflectance losses. Two additional studies demonstrated 750 mV local Voc on 50 micron thick SHJ solar cell and < 1 cm/s effective surface recombination velocity on n-type wafers passivated by a-Si/SiO2/SiNx stack.
ContributorsHerasimenka, Stanislau Yur'yevich (Author) / Honsberg, C. (Christiana B.) (Thesis advisor) / Bowden, Stuart G (Thesis advisor) / Tracy, Clarence (Committee member) / Vasileska, Dragica (Committee member) / Holman, Zachary (Committee member) / Sinton, Ron (Committee member) / Arizona State University (Publisher)
Created2013
Description
CdTe/MgCdTe double heterostructures (DHs) integrated with a heavily-doped a-Si:H layer as the hole contact was demonstrated a record open-circuit voltage (VOC) of 1.11 V and an active-area efficiency of 20% in 2016. Despite this significant progress, some of the underlying device physics has not been fully understood. The first part of this dissertation reports a systematic study of the CdTe/MgCdTe DH devices. The CdTe/MgCdTe DHs are grown on InSb(001) substrates. The vertical transport mechanisms across the CdTe and InSb heterovalent interface are investigated with N-CdTe/n-InSb and N-CdTe/p-InSb heterostructures. A transport model including tunneling through CdTe barrier and InSb interband transition is developed to explain the different temperature dependent current-voltage characteristics of these two heterostructures.
Different p-type layers are integrated with the CdTe/MgCdTe DHs to form solar cells with different VOC values and efficiencies. The low VOC of devices with ZnTe:Cu and ZnTe:As hole contacts is attributed to the low built-in voltage and reduced minority carrier lifetime in the CdTe absorber, respectively. The critical requirements for reaching high VOC values are analyzed.
A novel epitaxial lift-off technology for monocrystalline CdTe is developed using a water-soluble and nearly lattice-matched MgTe sacrificial layer grown on InSb substrate. The freestanding CdTe/MgCdTe DH thin films obtained from the lift-off process show improved optical performance due to enhanced light extraction efficiency and photo-recycling effect. This technology enables the possible development of monocrystalline CdTe thin-film solar cells and 1.7/1.1-eV MgCdTe/Si or MgCdTe/Cu(InGa)Se2 tandem solar cells. The monocrystalline CdTe thin-film solar cells and 1.7-eV MgCdTe DH solar cells have been demonstrated with a power conversion efficiency of 9.8% and an active-area efficiency as high as 15.2%, respectively. Additionally, a study of the radiation effects on CdTe DHs under 68-MeV proton irradiation is performed and showed their superior radiation tolerance. All these findings indicate that the monocrystalline CdTe thin-film solar cells are reasonably expected to have low weight, high-efficiency and high power density, ideal for space applications.
ContributorsDing, Jia (Author) / Zhang, Yong-Hang (Thesis advisor) / Vasileska, Dragica (Committee member) / Johnson, Shane (Committee member) / Holman, Zachary (Committee member) / Arizona State University (Publisher)
Created2021