- Creators: Chen, Tingyong
Description
I studied the properties of novel Co2FeAl0.5Si0.5 (CFAS), ZnGeAs2, and FeS2 (pyrite) thin films for microelectronic applications ranging from spintronic to photovoltaic. CFAS is a half metal with theoretical spin polarization of 100%. I investigated its potential as a spin injector, for spintronic applications, by studying the critical steps involved in the injection of spin polarized electron populations from tunnel junctions containing CFAS electrodes. Epitaxial CFAS thin films with L21 structure and saturation magnetizations of over 1200 emu/cm3 were produced by optimization of the sputtering growth conditions. Point contact Andreev reflection measurements show that the spin polarization at the CFAS electrode surface exceeds 70%. Analyses of the electrical properties of tunnel junctions with a superconducting Pb counter-electrode indicate that transport through native Al oxide barriers is mostly from direct tunneling, while that through the native CFAS oxide barriers is not. ZnGeAs2 is a semiconductor comprised of only inexpensive and earth-abundant elements. The electronic structure and defect properties are similar in many ways to GaAs. Thus, in theory, efficient solar cells could be made with ZnGeAs2 if similar quality material to that of GaAs could be produced. To understand the thermochemistry and determine the rate limiting steps of ZnGeAs2 thin-film synthesis, the (a) thermal decomposition rate and (b) elemental composition and deposition rate of films were measured. It is concluded that the ZnGeAs2 thin film synthesis is a metastable process with an activation energy of 1.08±0.05 eV for the kinetically-limited decomposition rate and an evaporation coefficient of ~10-3. The thermochemical analysis presented here can be used to predict optimal conditions of ZnGeAs2 physical vapor deposition and thermal processing. Pyrite (FeS2) is another semiconductor that has tremendous potential for use in photovoltaic applications if high quality materials could be made. Here, I present the layer-by-layer growth of single-phase pyrite thin-films on heated substrates using sequential evaporation of Fe under high-vacuum followed by sulfidation at S pressures between 1 mTorr and 1 Torr. High-resolution transmission electron microscopy reveals high-quality, defect-free pyrite grains were produces by this method. It is demonstrated that epitaxial pyrite layer was produced on natural pyrite substrates with this method.
ContributorsVahidi, Mahmoud (Author) / Newman, Nathan (Thesis advisor) / Alford, Terry (Committee member) / Singh, Rakesh (Committee member) / Chen, Tingyong (Committee member) / Arizona State University (Publisher)
Created2013
Description
In this dissertation I studied the anomalous Hall effect in MgO/Permalloy/Nonmagnetic Metal(NM) based structure, spin polarized current in YIG/Pt based thin films and the origin of the perpendicular magnetic anisotropy(PMA) in the Ru/Co/Ru based structures.
The anomalous Hall effect is the observation of a nonzero voltage difference across a magnetic material transverse to the current that flows through the material and the external magnetic field. Unlike the ordinary Hall effect which is observed in nonmagnetic metals, the anomalous Hall effect is only observed in magnetic materials and is orders of magnitude larger than the ordinary Hall effect. Unlike quantum anomalous Hall effect which only works in low temperature and extremely large magnetic field, anomalous Hall effect can be measured at room temperature under a relatively small magnetic field. This allows the anomalous Hall effect to have great potential applications in spintronics and be a good characterization tool for ferromagnetic materials especially materials that have perpendicular magnetic anisotropy(PMA).
In my research, it is observed that a polarity change of the Hall resistance in the MgO/Permalloy/NM structure can be obtained when certain nonmagnetic metal is used as the capping layer while no polarity change is observed when some other metal is used as the capping layer. This allows us to tune the polarity of the anomalous Hall effect by changing the thickness of a component of the structure. My conclusion is that an intrinsic mechanism from Berry curvature plays an important role in the sign of anomalous Hall resistivity in the MgO/Py/HM structures. Surface and interfacial scattering also make substantial contribution to the measured Hall resistivity.
Spin polarization(P) is one of the key concepts in spintronics and is defined as the difference in the spin up and spin down electron population near the Fermi level of a conductor. It has great applications in the spintronics field such as the creation of spin transfer torques, magnetic tunnel junction(MTJ), spintronic logic devices.
In my research, spin polarization is measured on platinum layers grown on a YIG layer. Platinum is a nonmagnetic metal with strong spin orbit coupling which intrinsically has zero spin polarization. Nontrivial spin polarization measured by ARS is observed in the Pt layer when it is grown on YIG ferromagnetic insulator. This result is contrary to the zero spin polarization in the Pt layer when it is grown directly on SiO2 substrate. Magnetic proximity effect and spin current pumping from YIG into Pt is proposed as the reason of the nontrivial spin polarization induced in Pt. An even higher spin polarization in the Pt layer is observed when an ultrathin NiO layer or Cu layer is inserted between Pt and YIG which blocks the proximity effect. The spin polarization in the NiO inserted sample shows temperature dependence. This demonstrates that the spin current transmission is further enhanced in ultrathin NiO layers through magnon and spin fluctuations.
Perpendicular Magnetic Anisotropy(PMA) has important applications in spintronics and magnetic storage. In the last chapter, I study the origin of PMA in one of the structures that shows PMA: Ru/Co/Ru. By measuring the ARS curve while changing the magnetic field orientation, the origin of the PMA in this structure is determined to be the strain induced by lattice mismatch.
The anomalous Hall effect is the observation of a nonzero voltage difference across a magnetic material transverse to the current that flows through the material and the external magnetic field. Unlike the ordinary Hall effect which is observed in nonmagnetic metals, the anomalous Hall effect is only observed in magnetic materials and is orders of magnitude larger than the ordinary Hall effect. Unlike quantum anomalous Hall effect which only works in low temperature and extremely large magnetic field, anomalous Hall effect can be measured at room temperature under a relatively small magnetic field. This allows the anomalous Hall effect to have great potential applications in spintronics and be a good characterization tool for ferromagnetic materials especially materials that have perpendicular magnetic anisotropy(PMA).
In my research, it is observed that a polarity change of the Hall resistance in the MgO/Permalloy/NM structure can be obtained when certain nonmagnetic metal is used as the capping layer while no polarity change is observed when some other metal is used as the capping layer. This allows us to tune the polarity of the anomalous Hall effect by changing the thickness of a component of the structure. My conclusion is that an intrinsic mechanism from Berry curvature plays an important role in the sign of anomalous Hall resistivity in the MgO/Py/HM structures. Surface and interfacial scattering also make substantial contribution to the measured Hall resistivity.
Spin polarization(P) is one of the key concepts in spintronics and is defined as the difference in the spin up and spin down electron population near the Fermi level of a conductor. It has great applications in the spintronics field such as the creation of spin transfer torques, magnetic tunnel junction(MTJ), spintronic logic devices.
In my research, spin polarization is measured on platinum layers grown on a YIG layer. Platinum is a nonmagnetic metal with strong spin orbit coupling which intrinsically has zero spin polarization. Nontrivial spin polarization measured by ARS is observed in the Pt layer when it is grown on YIG ferromagnetic insulator. This result is contrary to the zero spin polarization in the Pt layer when it is grown directly on SiO2 substrate. Magnetic proximity effect and spin current pumping from YIG into Pt is proposed as the reason of the nontrivial spin polarization induced in Pt. An even higher spin polarization in the Pt layer is observed when an ultrathin NiO layer or Cu layer is inserted between Pt and YIG which blocks the proximity effect. The spin polarization in the NiO inserted sample shows temperature dependence. This demonstrates that the spin current transmission is further enhanced in ultrathin NiO layers through magnon and spin fluctuations.
Perpendicular Magnetic Anisotropy(PMA) has important applications in spintronics and magnetic storage. In the last chapter, I study the origin of PMA in one of the structures that shows PMA: Ru/Co/Ru. By measuring the ARS curve while changing the magnetic field orientation, the origin of the PMA in this structure is determined to be the strain induced by lattice mismatch.
ContributorsLi, Bochao (Author) / Chen, Tingyong (Committee member) / Bennett, Peter (Committee member) / Nemanich, Robert (Committee member) / Qing, Quan (Committee member) / Arizona State University (Publisher)
Created2018
Description
Chemical Vapor Deposition (CVD) is the most widely used method to grow large-scale single layer graphene. However, a systematic experimental study of the relationship between growth parameters and graphene film morphology, especially in the industrially preferred cold wall CVD, has not been undertaken previously. This research endeavored to address this and provide comprehensive insight into the growth physics of graphene on supported solid and liquid Cu films using cold wall CVD.
A multi-chamber UHV system was customized and transformed into a cold wall CVD system to perform experiments. The versatile growth process was completely custom-automated by controlling the process parameters with LabVIEW. Graphene growth was explored on solid electrodeposited, recrystallized and thin sputter deposited Cu films as well as on liquid Cu supported on W/Mo refractory substrates under ambient pressure using Ar, H₂ and CH₄ mixtures.
The results indicate that graphene grown on Cu films using cold wall CVD follows a classical two-dimensional nucleation and growth mechanism. The nucleation density decreases and average size of graphene crystallites increases with increasing dilution of the CH₄/H₂ mixture by Ar, decrease in total flow rate and decrease in CH₄:H₂ ratio at a fixed substrate temperature and chamber pressure. Thus, the resulting morphological changes correspond with those that would be expected if the precursor deposition rate was varied at a fixed substrate temperature for physical deposition using thermal evaporation. The evolution of graphene crystallite boundary morphology with decreasing effective C deposition rate indicates the effect of edge diffusion of C atoms along the crystallite boundaries, in addition to H₂ etching, on graphene crystallite shape.
The roles of temperature gradient, chamber pressure and rapid thermal heating in C precursor-rich environment on graphene growth morphology on thin sputtered Cu films were explained. The growth mechanisms of graphene on substrates annealed under reducing and non-reducing environment were explained from the scaling functions of graphene island size distribution in the pre-coalescence regime. It is anticipated that applying the pre-coalescence size distribution method presented in this work to other 2D material systems may be useful for elucidating atomistic mechanisms of film growth that are otherwise difficult to obtain.
A multi-chamber UHV system was customized and transformed into a cold wall CVD system to perform experiments. The versatile growth process was completely custom-automated by controlling the process parameters with LabVIEW. Graphene growth was explored on solid electrodeposited, recrystallized and thin sputter deposited Cu films as well as on liquid Cu supported on W/Mo refractory substrates under ambient pressure using Ar, H₂ and CH₄ mixtures.
The results indicate that graphene grown on Cu films using cold wall CVD follows a classical two-dimensional nucleation and growth mechanism. The nucleation density decreases and average size of graphene crystallites increases with increasing dilution of the CH₄/H₂ mixture by Ar, decrease in total flow rate and decrease in CH₄:H₂ ratio at a fixed substrate temperature and chamber pressure. Thus, the resulting morphological changes correspond with those that would be expected if the precursor deposition rate was varied at a fixed substrate temperature for physical deposition using thermal evaporation. The evolution of graphene crystallite boundary morphology with decreasing effective C deposition rate indicates the effect of edge diffusion of C atoms along the crystallite boundaries, in addition to H₂ etching, on graphene crystallite shape.
The roles of temperature gradient, chamber pressure and rapid thermal heating in C precursor-rich environment on graphene growth morphology on thin sputtered Cu films were explained. The growth mechanisms of graphene on substrates annealed under reducing and non-reducing environment were explained from the scaling functions of graphene island size distribution in the pre-coalescence regime. It is anticipated that applying the pre-coalescence size distribution method presented in this work to other 2D material systems may be useful for elucidating atomistic mechanisms of film growth that are otherwise difficult to obtain.
ContributorsDas, Shantanu, Ph.D (Author) / Drucker, Jeff (Thesis advisor) / Alford, Terry (Committee member) / Chen, Tingyong (Committee member) / Arizona State University (Publisher)
Created2018
Description
A theoretical study of a three-dimensional (3D) N/S interface with arbitrary spin
polarization and interface geometry is presented. The 3D model gives the same intrinsic
spin polarization and superconducting gap dependence as the 1D model. This
demonstrates that the 1D model can be use to t 3D data.
Using this model, a Heusler alloy is investigated. Andreev reflection measurements
show that the spin polarization is 80% in samples sputtered on unheated MgO(100)
substrates and annealed at high temperatures. However, the spin polarization is
considerably smaller in samples deposited on heated substrates.
Ferromagnetic FexSix alloys have been proposed as potential spin injectors into
silicon with a substantial spin polarization. Andreev Reflection Spectroscopy (ARS) is
utilized to determine the spin polarization of both amorphous and crystalline Fe65Si35
alloys. The amorphous phase has a significantly higher spin polarization than that of
the crystalline phase.
In this thesis, (1111) Fe SmO0:82F0:18FeAs and Pb superconductors are used to
measure the spin polarization of a highly spin-polarized material, La0:67Sr0:33MnO3.
Both materials yield the same intrinsic spin polarization, therefore, Fe-superconductors
can be used in ARS. Based on the behavior of the differential conductance for highly
spin polarized LSMO and small polarization of Au, it can be concluded that the Fe-Sc
is not a triplet superconductor.
Zero bias anomaly (ZBA), in point contact Andreev reflection (PCAR), has been
utilized as a characteristic feature to reveal many novel physics. Complexities at a
normal metal/superconducting interface often cause nonessential ZBA-like features,
which may be mistaken as ZBA. In this work, it is shown that an extrinsic ZBA,
which is due to the contact resistance, cannot be suppressed by a highly spin-polarized
current while a nonessential ZBA cannot be affected the contact resistance.
Finally, Cu/Cu multilayer GMR structures were fabricated and the GMR% measured
at 300 K and 4.5 K gave responses of 63% and 115% respectively. Not only
do the GMR structures have a large enhancement of resistance, but by applying an
external magnetic eld it is shown that, unlike most materials, the spin polarization
can be tuned to values of 0.386 to 0.415 from H = 0 kOe to H = 15 kOe.
polarization and interface geometry is presented. The 3D model gives the same intrinsic
spin polarization and superconducting gap dependence as the 1D model. This
demonstrates that the 1D model can be use to t 3D data.
Using this model, a Heusler alloy is investigated. Andreev reflection measurements
show that the spin polarization is 80% in samples sputtered on unheated MgO(100)
substrates and annealed at high temperatures. However, the spin polarization is
considerably smaller in samples deposited on heated substrates.
Ferromagnetic FexSix alloys have been proposed as potential spin injectors into
silicon with a substantial spin polarization. Andreev Reflection Spectroscopy (ARS) is
utilized to determine the spin polarization of both amorphous and crystalline Fe65Si35
alloys. The amorphous phase has a significantly higher spin polarization than that of
the crystalline phase.
In this thesis, (1111) Fe SmO0:82F0:18FeAs and Pb superconductors are used to
measure the spin polarization of a highly spin-polarized material, La0:67Sr0:33MnO3.
Both materials yield the same intrinsic spin polarization, therefore, Fe-superconductors
can be used in ARS. Based on the behavior of the differential conductance for highly
spin polarized LSMO and small polarization of Au, it can be concluded that the Fe-Sc
is not a triplet superconductor.
Zero bias anomaly (ZBA), in point contact Andreev reflection (PCAR), has been
utilized as a characteristic feature to reveal many novel physics. Complexities at a
normal metal/superconducting interface often cause nonessential ZBA-like features,
which may be mistaken as ZBA. In this work, it is shown that an extrinsic ZBA,
which is due to the contact resistance, cannot be suppressed by a highly spin-polarized
current while a nonessential ZBA cannot be affected the contact resistance.
Finally, Cu/Cu multilayer GMR structures were fabricated and the GMR% measured
at 300 K and 4.5 K gave responses of 63% and 115% respectively. Not only
do the GMR structures have a large enhancement of resistance, but by applying an
external magnetic eld it is shown that, unlike most materials, the spin polarization
can be tuned to values of 0.386 to 0.415 from H = 0 kOe to H = 15 kOe.
ContributorsGifford, Jessica Anna (Author) / Chen, Tingyong (Thesis advisor) / Bennett, Peter (Committee member) / Nemanich, Robert (Committee member) / Tsen, Kong-Thon (Committee member) / Arizona State University (Publisher)
Created2015
Description
An electrical current with high spin polarization is desirable for the performance of novel spintronics devices, such as magnetic tunnel junction and giant magnetoresistance devices. The generation of spin polarized current can be from ferromagnetic materials or triplet superconductors.
Anomalous Hall effect (AHE) is an effective way to study the properties of magnetic structures. The scattering of electrons by the magnetic moments affects the change of resistance, which can be used to detect the magnetization. In this dissertation, AHE is used to study the perpendicular magnetic anisotropy (PMA) structures, including Co/Pt and Ta/CoFeB/MgO.
Domain walls exist in all ferromagnetic materials. This dissertation studies the domain wall movement in the Ta/CoFeB/MgO structure. A single domain is observed by measuring the anomalous Hall effect. On the other hand, a zero Hall step is successfully observed in a single layer of magnetic material for the first time, which can be used to fabricate advanced domain wall spintronics devices.
Besides the normal ferromagnetic material, the generation of spin polarized current in superconductor is also important for Spintronics. The electrons in superconductors form Cooper pairs. In this dissertation, Andreev Reflection Spectroscopy (ARS) is used to study the spin configuration in Cooper pairs.
Generally, ferromagnetism and superconductivity can not co-exist. In this dissertation, the Bi/Ni bilayer structure has been studied with ARS, and the measurement results show a triplet superconductivity below 4K. The appearance of superconductivity is believed to be attributed to the Bi-Ni interface, and the triplet Cooper pair makes it a promising candidate in superconducting spintronics.
Besides, a Bi3Ni single crystal is also studied with ARS. The measurements show a singlet superconductivity in this material, which further proves the importance of the Bi/Ni interface to achieve triplet superconductivity.
Finally, ARS is also used to study NbSe2 monolayer, a 2D superconductor. The monolayer is verified by the measurements of critical temperature and critical field, which are different from the values of multilayer or bulk. Andreev reflection results show that NbSe2 monolayer is a singlet superconductor and there is no node exist in the superconducting gap for a in plane magnetic field up to 58 kOe.
Anomalous Hall effect (AHE) is an effective way to study the properties of magnetic structures. The scattering of electrons by the magnetic moments affects the change of resistance, which can be used to detect the magnetization. In this dissertation, AHE is used to study the perpendicular magnetic anisotropy (PMA) structures, including Co/Pt and Ta/CoFeB/MgO.
Domain walls exist in all ferromagnetic materials. This dissertation studies the domain wall movement in the Ta/CoFeB/MgO structure. A single domain is observed by measuring the anomalous Hall effect. On the other hand, a zero Hall step is successfully observed in a single layer of magnetic material for the first time, which can be used to fabricate advanced domain wall spintronics devices.
Besides the normal ferromagnetic material, the generation of spin polarized current in superconductor is also important for Spintronics. The electrons in superconductors form Cooper pairs. In this dissertation, Andreev Reflection Spectroscopy (ARS) is used to study the spin configuration in Cooper pairs.
Generally, ferromagnetism and superconductivity can not co-exist. In this dissertation, the Bi/Ni bilayer structure has been studied with ARS, and the measurement results show a triplet superconductivity below 4K. The appearance of superconductivity is believed to be attributed to the Bi-Ni interface, and the triplet Cooper pair makes it a promising candidate in superconducting spintronics.
Besides, a Bi3Ni single crystal is also studied with ARS. The measurements show a singlet superconductivity in this material, which further proves the importance of the Bi/Ni interface to achieve triplet superconductivity.
Finally, ARS is also used to study NbSe2 monolayer, a 2D superconductor. The monolayer is verified by the measurements of critical temperature and critical field, which are different from the values of multilayer or bulk. Andreev reflection results show that NbSe2 monolayer is a singlet superconductor and there is no node exist in the superconducting gap for a in plane magnetic field up to 58 kOe.
ContributorsZhao, Gejian (Author) / Chen, Tingyong (Thesis advisor) / Bennett, Peter (Committee member) / Nemanich, Robert (Committee member) / Qing, Quan (Committee member) / Arizona State University (Publisher)
Created2018