Description
Microwave dielectrics are widely used to make resonators and filters in telecommunication systems. The production of thin films with high dielectric constant and low loss could potentially enable a marked reduction in the size of devices and systems. However, studies of these materials in thin film form are very sparse. In this research, experiments were carried out on practical high-performance dielectrics including ZrTiO4-ZnNb2O6 (ZTZN) and Ba(Co,Zn)1/3Nb2/3O3 (BCZN) with high dielectric constant and low loss tangent. Thin films were deposited by laser ablation on various substrates, with a systematical study of growth conditions like substrate temperature, oxygen pressure and annealing to optimize the film quality, and the compositional, microstructural, optical and electric properties were characterized. The deposited ZTZN films were randomly oriented polycrystalline on Si substrate and textured on MgO substrate with a tetragonal lattice change at elevated temperature. The BCZN films deposited on MgO substrate showed superior film quality relative to that on other substrates, which grow epitaxially with an orientation of (001) // MgO (001) and (100) // MgO (100) when substrate temperature was above 500 oC. In-situ annealing at growth temperature in 200 mTorr oxygen pressure was found to enhance the quality of the films, reducing the peak width of the X-ray Diffraction (XRD) rocking curve to 0.53o and the χmin of channeling Rutherford Backscattering Spectrometry (RBS) to 8.8% when grown at 800oC. Atomic Force Microscopy (AFM) was used to study the topography and found a monotonic decrease in the surface roughness when the growth temperature increased. Optical absorption and transmission measurements were used to determine the energy bandgap and the refractive index respectively. A low-frequency dielectric constant of 34 was measured using a planar interdigital measurement structure. The resistivity of the film is ~3×1010 ohm·cm at room temperature and has an activation energy of thermal activated current of 0.66 eV.
ContributorsLi, You (Author) / Newman, Nathan (Thesis advisor) / Alford, Terry (Committee member) / Singh, Rakesh (Committee member) / Arizona State University (Publisher)
Created2013
Description
In 2022, integrated circuit interconnects will approach 10 nm and the diffusion barrier layers needed to ensure long lasting devices will be at 1 nm. This dimension means the interconnect will be dominated by the interface and it has been shown the interface is currently eroding device performance. The standard interconnect system has three layers - a Copper metal core, a Tantalum Adhesion layer and a Tantalum Nitride Diffusion Barrier Layer. An alternate interconnect schema is a Tantalum Nitride barrier layer and Silver as a metal. The adhesion layer is removed from the system along with changing to an alternate, low resistivity metal. First principles are used to assess the interface of the Silver and Tantalum Nitride. Several stoichiometric 1:1 Tantalum Nitride polymorphs are assessed and it is found that the Fe2P crystal structure is actually the most stable crystal structure which is at odds with the published phase diagram for ambient crystal structure. The surface stability of Fe2P-TaN is assessed and the absorption enthalpy of Silver adatoms is calculated. Finally, the thermodynamic stability of the TaN-Ag interconnect system is assessed.
ContributorsGrumski, Michael (Author) / Adams, James (Thesis advisor) / Krause, Stephen (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2012
Description
Integrated oxide/semiconductor heterostructures have attracted intense interest for device applications which require sharp interfaces and controlled defects. The research of this dissertation has focused on the characterization of perovskite oxide/oxide and oxide/semiconductor heterostructures, and the analysis of interfaces and defect structures, using scanning transmission electrom microscopy (STEM) and related techniques.
The SrTiO3/Si system was initially studied to develop a basic understanding of the integration of perovskite oxides with semiconductors, and successful integration with abrupt interfaces was demonstrated. Defect analysis showed no misfit dislocations but only anti-phase boundaries (APBs) in the SrTiO3 (STO) films. Similar defects were later observed in other perovskite oxide heterostructures.
Ferroelectric BaTiO3 (BTO) thin films deposited directly onto STO substrates, or STO buffer layers with Ge substrates, were grown by molecular beam epitaxy (MBE) in order to control the polarization orientation for field-effect transistors (FETs). STEM imaging and elemental mapping by electron energy-loss spectroscopy (EELS) showed structurally and chemically abrupt interfaces, and the BTO films retained the c-axis-oriented tetragonal structure for both BTO/STO and BTO/STO/Ge heterostructures. The polarization displacement in the BTO films of TiN/BTO/STO heterostructures was investigated. The Ti4+ atomic column displacements and lattice parameters were measured directly using HAADF images. A polarization gradient, which switched from upwards to downwards, was observed in the BTO thin film, and evidence was found for positively-charged oxygen vacancies.
Heterostructures grown on Ge substrates by atomic layer deposition (ALD) were characterized and compared with MBE-grown samples. A two-step process was needed to overcome interlayer reaction at the beginning of ALD growth. A-site-rich oxide films with thicknesses of at least 2-nm had to be deposited and then crystallized before initiating deposition of the following perovskite oxide layer in order to suppress the formation of amorphous oxide layers on the Ge surface. BTO/STO/Ge, BTO/Ge, SrHfTiO3/Ge and SrZrO3/Ge thin films with excellent crystallinity were grown using this process.
Metal-insulator-metal (MIM) heterostructures were fabricated as ferroelectric capacitors and then electrically stressed to the point of breakdown to correlate structural changes with electrical and physical properties. BaTiO3 on Nb:STO was patterned with different top metal electrodes by focused-ion-beam milling, Au/Ni liftoff, and an isolation-defined approach.
The SrTiO3/Si system was initially studied to develop a basic understanding of the integration of perovskite oxides with semiconductors, and successful integration with abrupt interfaces was demonstrated. Defect analysis showed no misfit dislocations but only anti-phase boundaries (APBs) in the SrTiO3 (STO) films. Similar defects were later observed in other perovskite oxide heterostructures.
Ferroelectric BaTiO3 (BTO) thin films deposited directly onto STO substrates, or STO buffer layers with Ge substrates, were grown by molecular beam epitaxy (MBE) in order to control the polarization orientation for field-effect transistors (FETs). STEM imaging and elemental mapping by electron energy-loss spectroscopy (EELS) showed structurally and chemically abrupt interfaces, and the BTO films retained the c-axis-oriented tetragonal structure for both BTO/STO and BTO/STO/Ge heterostructures. The polarization displacement in the BTO films of TiN/BTO/STO heterostructures was investigated. The Ti4+ atomic column displacements and lattice parameters were measured directly using HAADF images. A polarization gradient, which switched from upwards to downwards, was observed in the BTO thin film, and evidence was found for positively-charged oxygen vacancies.
Heterostructures grown on Ge substrates by atomic layer deposition (ALD) were characterized and compared with MBE-grown samples. A two-step process was needed to overcome interlayer reaction at the beginning of ALD growth. A-site-rich oxide films with thicknesses of at least 2-nm had to be deposited and then crystallized before initiating deposition of the following perovskite oxide layer in order to suppress the formation of amorphous oxide layers on the Ge surface. BTO/STO/Ge, BTO/Ge, SrHfTiO3/Ge and SrZrO3/Ge thin films with excellent crystallinity were grown using this process.
Metal-insulator-metal (MIM) heterostructures were fabricated as ferroelectric capacitors and then electrically stressed to the point of breakdown to correlate structural changes with electrical and physical properties. BaTiO3 on Nb:STO was patterned with different top metal electrodes by focused-ion-beam milling, Au/Ni liftoff, and an isolation-defined approach.
ContributorsWu, Hsinwei (Author) / Smith, David J. (Thesis advisor) / Mccartney, Martha R (Thesis advisor) / Alford, Terry (Committee member) / Bertoni, Mariana (Committee member) / Arizona State University (Publisher)
Created2018
Description
InAs/InAsSb type-II superlattices (T2SLs) can be considered as potential alternatives for conventional HgCdTe photodetectors due to improved uniformity, lower manufacturing costs with larger substrates, and possibly better device performance. This dissertation presents a comprehensive study on the structural, optical and electrical properties of InAs/InAsSb T2SLs grown by Molecular Beam Epitaxy.
The effects of different growth conditions on the structural quality were thoroughly investigated. Lattice-matched condition was successfully achieved and material of exceptional quality was demonstrated.
After growth optimization had been achieved, structural defects could hardly be detected, so different characterization techniques, including etch-pit-density (EPD) measurements, cathodoluminescence (CL) imaging and X-ray topography (XRT), were explored, in attempting to gain better knowledge of the sparsely distributed defects. EPD revealed the distribution of dislocation-associated pits across the wafer. Unfortunately, the lack of contrast in images obtained by CL imaging and XRT indicated their inability to provide any quantitative information about defect density in these InAs/InAsSb T2SLs.
The nBn photodetectors based on mid-wave infrared (MWIR) and long-wave infrared (LWIR) InAs/InAsSb T2SLs were fabricated. The significant difference in Ga composition in the barrier layer coupled with different dark current behavior, suggested the possibility of different types of band alignment between the barrier layers and the absorbers. A positive charge density of 1.8 × 1017/cm3 in the barrier of MWIR nBn photodetector, as determined by electron holography, confirmed the presence of a potential well in its valence band, thus identifying type-II alignment. In contrast, the LWIR nBn photodetector was shown to have type-I alignment because no sign of positive charge was detected in its barrier.
Capacitance-voltage measurements were performed to investigate the temperature dependence of carrier densities in a metal-oxide-semiconductor (MOS) structure based on MWIR InAs/InAsSb T2SLs, and a nBn structure based on LWIR InAs/InAsSb T2SLs. No carrier freeze-out was observed in either sample, indicating very shallow donor levels. The decrease in carrier density when temperature increased was attributed to the increased density of holes that had been thermally excited from localized states near the oxide/semiconductor interface in the MOS sample. No deep-level traps were revealed in deep-level transient spectroscopy temperature scans.
The effects of different growth conditions on the structural quality were thoroughly investigated. Lattice-matched condition was successfully achieved and material of exceptional quality was demonstrated.
After growth optimization had been achieved, structural defects could hardly be detected, so different characterization techniques, including etch-pit-density (EPD) measurements, cathodoluminescence (CL) imaging and X-ray topography (XRT), were explored, in attempting to gain better knowledge of the sparsely distributed defects. EPD revealed the distribution of dislocation-associated pits across the wafer. Unfortunately, the lack of contrast in images obtained by CL imaging and XRT indicated their inability to provide any quantitative information about defect density in these InAs/InAsSb T2SLs.
The nBn photodetectors based on mid-wave infrared (MWIR) and long-wave infrared (LWIR) InAs/InAsSb T2SLs were fabricated. The significant difference in Ga composition in the barrier layer coupled with different dark current behavior, suggested the possibility of different types of band alignment between the barrier layers and the absorbers. A positive charge density of 1.8 × 1017/cm3 in the barrier of MWIR nBn photodetector, as determined by electron holography, confirmed the presence of a potential well in its valence band, thus identifying type-II alignment. In contrast, the LWIR nBn photodetector was shown to have type-I alignment because no sign of positive charge was detected in its barrier.
Capacitance-voltage measurements were performed to investigate the temperature dependence of carrier densities in a metal-oxide-semiconductor (MOS) structure based on MWIR InAs/InAsSb T2SLs, and a nBn structure based on LWIR InAs/InAsSb T2SLs. No carrier freeze-out was observed in either sample, indicating very shallow donor levels. The decrease in carrier density when temperature increased was attributed to the increased density of holes that had been thermally excited from localized states near the oxide/semiconductor interface in the MOS sample. No deep-level traps were revealed in deep-level transient spectroscopy temperature scans.
ContributorsShen, Xiaomeng (Author) / Zhang, Yong-Hang (Thesis advisor) / Smith, David J. (Thesis advisor) / Alford, Terry (Committee member) / Goryll, Michael (Committee member) / Mccartney, Martha R (Committee member) / Arizona State University (Publisher)
Created2015
Description
In the Rare-earth-Tri-telluride family, (RTe3s) [R=La, Ce, Nd, Sm, Gd, Tb, Dy, Er, Ho, Tm] the emergence of Charge Density Waves, (CDW) has been under investigation for a long time due to broadly tunable properties by either chemical substitution or pressure application. These quasi 2D Layered materials RTe3s undergo Fermi Surface Nesting leading to CDW instability. CDWs are electronic instabilities found in low-dimensional materials with highly anisotropic electronic structures. Since the CDW is predominantly driven by Fermi-surface (FS) nesting, it is especially sensitive to pressure-induced changes in the electronic structure. The FS of RTe3s is a function of p-orbitals of Tellurium atoms, which are arranged in two adjacent planes in the crystal structure. Although the FS and electronic structure possess a nearly four-fold symmetry, RTe3s form an incommensurate CDW.This dissertation is structured as follows: Chapter 1 includes basic ideas of Quantum materials, followed by an introduction to CDW and RTe3s. In Chapter 2, there are fundamentals of crystal growth by Chemical Vapor Transport, including various precursors, transport agent, temperature gradient, and rate of the reaction. After the growth, the crystals were confirmed for lattice vibrations by Raman, for composition by Energy Dispersive Spectroscopy; crystal structure and orientation were confirmed by X-ray Diffraction; magnetic ordering was established by Vibrating sample measurement. Detailed CDW study was done on various RTe3s by Raman spectroscopy. The basic mechanism and instrumentations used in these characterizations are explained in Chapter 3. Chapter 4 includes experimental data for crystal growth and results of these characterizations for Parent RTe3s. Chapter 5 includes fundamental insights on Cationic alloying of RTe3s, along with one alloy system’s crystal growth and characterization. This work tries to explain the behavior of CDW by a Temperature-dependent Raman study of RTe3s established the CDW transition temperature accompanied by Phonon softening; Angle-resolved Raman data confirming the nearly four-fold symmetry; thickness-dependent Raman spectroscopy resulting in the conclusion that as thickness decreases CDW transition temperature increases. Also, CDW transition is analyzed as a function of alloying.
ContributorsAttarde, Yashika (Author) / Tongay, Sefaattin (Thesis advisor) / Botana, Antia (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2021
Description
Diamond transistors are promising as high-power and high-frequency devices having higher efficiencies than conventional transistors. Diamond possesses superior electronic properties, such as a high bandgap (5.47 eV), high breakdown voltage (>10 MV cm−1 ), high electron and hole mobilities [4500 and 3800 cm2 V−1 · s−1, respectively], high electron and hole saturation velocities (1.5 × 107 and 1.05 × 107 cm s−1, respectively), and high thermal conductivity [22 W cm−1 · K−1], compared to conventional semiconductors. Reportedly, the diamond field-effect transistors (FETs) have shown transition frequencies (fT) of 45 and 70 GHz, maximum oscillation frequency (fmax) of 120 GHz, and radiofrequency (RF) power densities of 2.1 and 3.8 W mm−1 at 1 GHz. A two-dimensional-hole-gas (2DHG) surface channel forms on H-diamond by transfer doping from adsorbates/dielectrics in contact with H-diamond surface. However, prior studies indicate that charge transfer at the dielectric/ H-diamond interface could result in relatively low mobility attributed to interface scattering from the transferred negative charge to acceptor region. H-terminated diamond exhibits a negative electron affinity (NEA) of -1.1 to -1.3 eV, which is crucial to enable charge transfer doping. To overcome these limitations modulation doping, that is, selective doping, that leads to spatial separation of the MoO3 acceptor layer from the hole channel on H-diamond has been proposed. Molybdenum oxide (MoO3) was used as dielectric as it has electron affinity of 5.9eV and could align its conduction band minimum (CBM) below the valence band maximum (VBM) of H-terminated diamond. The band alignment provides the driving potential for charge transfer. Hafnium oxide (HfO2) was used as interfacial layer since it is a high-k oxide insulator (∼25), having large Eg (5.6 eV), high critical breakdown field, and high thermal stability. This study presents photoemission measurements of the electronic band alignments of the MoO3/HfO2/H-diamond layer structure to gain insight into the driving potential for the negative charge transfer and the location of the negative charges near the interface, in the HfO2 layer or in the MoO3 layer. The diamond hole concentration, mobility, and sheet resistance were characterized for MoO3/HfO2/H-Diamond with HfO2 layers of 0, 2 and 4 nm thickness.
ContributorsDeshmukh, Aditya Vilasrao (Author) / Nemanich, Robert J. (Thesis advisor) / Alford, Terry (Committee member) / Yang, Sui (Committee member) / Arizona State University (Publisher)
Created2024
Description
Two dimensional (2D) Janus Transition Metal Dichalcogenides (TMDs) are a new class of atomically thin polar materials. In these materials, the top and the bottom atomic layer are made of different chalcogen atoms. To date, several theoretical studies have shown that a broken mirror symmetry induces a colossal electrical field in these materials, which leads to unusual quantum properties. Despite these new properties, the current knowledge in their synthesis is limited only through two independent studies; both works rely on high-temperature processing techniques and are specific to only one type of 2D Janus material - MoSSe. Therefore, there is an urgent need for the development of a new synthesis method to (1) Extend the library of Janus class materials. (2) Improve the quality of 2D crystals. (3) Enable the synthesis of Janus heterostructures. The central hypothesis in this work is that the processing temperature of 2D Janus synthesis can be significantly lowered down to room temperatures by using reactive hydrogen and sulfur radicals while stripping off selenium atoms from the 2D surface. To test this hypothesis, a series of controlled growth studies were performed, and several complementary characterization techniques were used to establish a process–structure-property relationship. The results show that the newly proposed approach, namely Selective Epitaxy and Atomic Replacement (SEAR), is effective in reducing the growth temperature down to ambient conditions. The proposed technique benefits in achieving highly crystalline 2D Janus layers with an excellent optical response. Further studies herein show that this technique can form highly sophisticated lateral and vertical heterostructures of 2D Janus layers. Overall results establish an entirely new growth technique for 2D Janus.layers, which pave ways for the realization of exciting quantum effects in these materials such as Fulde–Ferrell–Larkin–Ovchinnikov (FFLO) state, Majorana fermions, and topological p-wave superconductors.
ContributorsSayyad, Mohammed Yasir (Author) / Tongay, Sefaattin (Thesis advisor) / Crozier, Peter (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2020