Barrett, The Honors College Thesis/Creative Project Collection
Barrett, The Honors College at Arizona State University proudly showcases the work of undergraduate honors students by sharing this collection exclusively with the ASU community.
Barrett accepts high performing, academically engaged undergraduate students and works with them in collaboration with all of the other academic units at Arizona State University. All Barrett students complete a thesis or creative project which is an opportunity to explore an intellectual interest and produce an original piece of scholarly research. The thesis or creative project is supervised and defended in front of a faculty committee. Students are able to engage with professors who are nationally recognized in their fields and committed to working with honors students. Completing a Barrett thesis or creative project is an opportunity for undergraduate honors students to contribute to the ASU academic community in a meaningful way.
Filtering by
- Creators: Chemical Engineering Program
By testing 120-180 µm, 120-350 µm, 250-350 µm, and 430-600 µm dry glass bead ranges, an increase in diameter size is seen to result in both higher shear stress values and an increasing slope of plotted shear stress vs. applied normal stress. From constructed Mohr’s Circles, it is observed that flow function is quite high amongst tested dry materials, all yielding values above 20. A high flow function value (>10) is indicative of a good flow.1 Flow function was observed to increase with increasing diameter size until a slight drop was observed at the 430-600 µm range, possibly due to material quality or being near the size limitation of testing within the FT4, where materials must be less than 1000 µm in diameter.However, no trend could be observed in flowability as diameter size was increased.
Through the use of an antistatic solution, the effect of electrostatic forces generated by colliding particles was tested. No significant effect on the shear stress properties was observed.
Wet material testing occurred with the 120-180 µm glass bead range using a deionized water content of 0%, 1%, 5%, 15%, and 20% by mass. The results of such testing yielded an increase in shear stress values at applied normal stress values as moisture content is increased, as well as a decrease in the resulting flow function parameter. However, this trend changed as 20% moisture content was achieved; the wet material became a consistent paste, and a large drop in shear stress values occurred along with an increase in flowability.
Rotary drums are tools used extensively in various prominent industries for their utility in heating and transporting particulate products. These processes are often inefficient and studies on heat transfer in rotary drums will reduce energy consumption as operating parameters are optimized. Research on this subject has been ongoing at ASU; however, the design of the rotary drum used in these studies is restrictive and experiments using radiation heat transfer have not been possible.<br/><br/>This study focuses on recounting the steps taken to upgrade the rotary drum setup and detailing the recommended procedure for experimental tests using radiant heat transfer upon completed construction of the new setup. To develop an improved rotary drum setup, flaws in the original design were analyzed and resolved. This process resulted in a redesigned drum heating system, an altered thinner drum, and a larger drum box. The recommended procedure for radiant heat transfer tests is focused on determining how particle size, drum fill level, and drum rotation rate impact the radiant heat transfer rate.