Barrett accepts high performing, academically engaged undergraduate students and works with them in collaboration with all of the other academic units at Arizona State University. All Barrett students complete a thesis or creative project which is an opportunity to explore an intellectual interest and produce an original piece of scholarly research. The thesis or creative project is supervised and defended in front of a faculty committee. Students are able to engage with professors who are nationally recognized in their fields and committed to working with honors students. Completing a Barrett thesis or creative project is an opportunity for undergraduate honors students to contribute to the ASU academic community in a meaningful way.
Displaying 1 - 2 of 2
Filtering by
- Creators: Chemical Engineering Program
Description
This thesis investigates an interpenetrating network of polyacrylamide and poly acrylic acid for use in a dynamic tactile display, which presents traditionally two-dimensional electronic screens as three-dimensional topographical models that can be experienced through touch. This kind of display would allow for greater access to traditionally visual information for the visually impaired. This hydrogel demonstrates Upper Critical Solution Temperature (UCST) near room temperature which facilitates a swelling transition, characterized by a sharp increase in swelling as this temperature is surpassed. Through the utilization of light responsive additives, light can trigger this shift, as the additives harness visible light, convert it into heat to raise the gel’s temperature, and increase the volume of the gel. Light-responsive additives explored include chlorophyllin, gold nanoparticles, and carbon black. Each of these additives required unique synthesis planning and strategies in order to optimize the performance of the gels. Synthesized gels were characterized using thermal swelling tests, light response tests and compression tests to determine the material strength. The best performing additive was chlorophyllin and allowed for a 20.8%±4.5% percent weight increase upon exposure to light for 10 minutes. In addition to investigating light-responsive additives, modifications were pursued to alter the overall UCST behavior, such as the addition of sodium chloride. By adding sodium chloride into the hydrogel, the gel was found to have a wider transition. Overall, light-responsive behavior was developed, and further work can be done in improving the response time and degree of swelling in order to make this material more viable for use in a dynamic tactile display.
ContributorsSitterle, Philip Kerry (Author) / Dai, Lenore (Thesis director) / Xu, Yifei (Committee member) / School of Music (Contributor) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2018-12
Description
The purpose of this project is to investigate the swelling ratio exhibited due to photothermal effects of double network polyacrylamide poly(acrylic acid) hydrogels synthesized with carbon black as a light-sensitive chromophore. Optimal carbon black dispersion was achieved in solutions through sonication, using V9A32 carbon black, where dynamic light scattering recorded particle diameters in the range of 195.0-375.8 nanometers for water/carbon black mixtures, 242.4-262.6 nanometers for monomer/carbon black mixtures without initiator, and 1109.3-1783.9 nanometers for monomer/carbon black mixtures including initiator. The double network polyacrylamide poly(acrylic acid) hydrogels with carbon black yielded weight increases of 0.126% and 6.043%, respectively, after 2 minutes and 10 minutes of being exposed to a light stimulus; compared to previous work which showed a double network polyacrylamide poly(acrylic acid) hydrogel with chlorophyllin yielded weight increases of 18.3% and 20.8%, respectively, after 2 minutes and 10 minutes of being exposed to a light stimulus, the carbon black resulted in a less robust response. Future work for application of the light-responsive hydrogels includes the development of a screen covering that will be made of the hydrogels. This covering is intended for use on LED screen displays, where a light change will result in a protrusion from the screen. The purpose behind this application is that technology users who are visually impaired can still determine what their LED device is trying to communicate with them.