Barrett accepts high performing, academically engaged undergraduate students and works with them in collaboration with all of the other academic units at Arizona State University. All Barrett students complete a thesis or creative project which is an opportunity to explore an intellectual interest and produce an original piece of scholarly research. The thesis or creative project is supervised and defended in front of a faculty committee. Students are able to engage with professors who are nationally recognized in their fields and committed to working with honors students. Completing a Barrett thesis or creative project is an opportunity for undergraduate honors students to contribute to the ASU academic community in a meaningful way.
Filtering by
- All Subjects: Interferometry
- Creators: School of Earth and Space Exploration
Fatigue damage accumulation under multiaxial loading conditions is an important practical problem for which there is a need to collect additional experimental data to calibrate and validate models. In this work, a sample with a special geometry capable of producing biaxial stresses while undergoing uniaxial load was fabricated and tested successfully and used, along with standard dogbone samples, to monitor the evolution of surface roughness development under cyclic loading using optical microscopy. In addition, a Michelson interferometer was successfully designed, built and tested that can be used to monitor surface roughness for lower levels of load than those used in this work. Results of testing and characterization in 2024-T3 samples tested at a maximum stress slightly below their yield strength and load ratio ~ 0.1 indicate that most of the surface roughness development under cyclic loads occurs on the second half of the fatigue, with the bulk of it close to failure. However, samples with load axes perpendicular to the rolling direction showed earlier development of roughness, which correlated with shorter fatigue lives and the expected anisotropy of strength in the material.