Matching Items (3)
Description
Alzheimer's Disease (AD) is the sixth leading cause of death in the United States and the most common form of dementia. Its cause remains unknown, but it is known to involve two hallmark pathologies: Amyloid Beta plaques and neurofibrillary tangles (NFTs). Several proteins have been implicated in the formation of neurofibrillary tangles, including Tau and S100B. S100B is a dimeric protein that is typically found bound to Ca(II) or Zn(II). These experiments relate to the involvement of S100B in Alzheimer's Disease-related processes and the results suggest that future research of S100B is warranted. Zn(II)-S100B was found to increase the rate at which tau assembled into paired helical filaments, as well as affect the rate at which tubulin polymerized into microtubules and the morphology of SH-SY5Y neuroblastoma cells after 72 hours of incubation. Zn(II)-S100B also increased the firing rate of hippocampal neurons after 36 hours of incubation. Together, these results suggest several possibilities: Zn(II)-S100B may be a key part of the formation of paired helical filaments (PHFs) that subsequently form NFTs. Zn(II)-S100B may also be competing with tau to bind tubulin, which could lead to an instability of microtubules and subsequent cell death. This finding aligns with the neurodegeneration that is commonly seen in AD and which could be a result of this microtubule instability. Ultimately, these results suggest that S100B is likely involved in several AD-related processes, and if the goal is to find an efficient and effective therapeutic target for AD, the relationship between S100B, particularly Zn(II)-S100B, and tau needs to be further studied.
ContributorsNaegele, Hayley (Author) / Mcgregor, Wade C (Thesis advisor) / Baluch, Debra (Committee member) / Francisco, Wilson (Committee member) / Arizona State University (Publisher)
Created2013
Description
The work presented in this thesis covers the synthesis and characterization of an ionomer that is applicable to zinc-air batteries. Polysulfone polymer is first chloromethylated and then quaternized to create an ion-conducting polymer. Nuclear magnetic resonance (NMR) spectra indicates that the degree of chloromethylation was 114%. The chemical and physical properties that were investigated include: the ionic conductivity, ion exchange capacity, water retention capacity, diameter and thickness swelling ratios, porosity, glass transition temperature, ionic conductivity enhanced by free salt addition, and the concentration and diffusivity of oxygen within the ionomer. It was found that the fully hydrated hydroxide form of the ionomer had a room temperature ionic conductivity of 39.92mS/cm while the chloride form had a room temperature ionic conductivity of 11.80mS/cm. The ion exchange capacity of the ionomer was found to be 1.022mmol/g. The water retention capacity (WRC) of the hydroxide form was found to be 172.6% while the chloride form had a WRC of 67.9%. The hydroxide form of the ionomer had a diameter swelling ratio of 34% and a thickness swelling ratio of 55%. The chloride form had a diameter swelling ratio of 32% and a thickness swelling ratio of 28%. The largest pore size in the ionomer was found to be 32.6nm in diameter. The glass transition temperature of the ionomer is speculated to be 344°C. A definite measurement could not be made. The room temperature ionic conductivity at 50% relative humidity was improved to 12.90mS/cm with the addition of 80% free salt. The concentration and diffusivity of oxygen in the ionomer was found to be 1.3 ±0.2mMol and (0.49 ±0.15)x10-5 cm2/s respectively. The ionomer synthesized in this research had material properties and performance that is comparable to other ionomers reported in the literature. This is an indication that this ionomer is suitable for further study and integration into a zinc-air battery. This thesis is concluded with suggestions for future research that is focused on improving the performance of the ionomer as well as improving the methodology.
ContributorsPadilla, Manuel (Author) / Friesen, Cody A (Thesis advisor) / Buttry, Daniel (Committee member) / Sieradzki, Karl (Committee member) / Arizona State University (Publisher)
Created2012
Description
The experiment performed used bone samples across three modern skeletal collections. These samples were collected from one’s skeletal ranging from superior to inferior regions of their body. These collected skeletal bones were then chemically cleaned, mechanically ground, and then digested to run in an ICP-MS. The concentrations returned from the instrument were then reduced using known standard concentrations and organized to allow for statistical measurements. Findings for this experiment include the insignificance of metal concentrations between groups of individuals who have had joint replacements and those who have not for Cobalt, Chromium, Titanium, and Iron. Concentrations for Titanium were below the limit of detection, therefore, the measured concentrations were approximated to zero. On the other hand, significant findings from the experiment include that there are high concentrations for, Iron and Zinc in general, among all groups of donors. These high concentrations could be due to the high levels of these metals in food, but the large concentration is concerning. There are also high concentrations for Gadolinium, but this is present in the individuals who have had joint replacements as they were likely given Gadolinium for medical purposes such as an MRI. The results found were determined to be valid considering the calculations were compared with a study of similar methodology, and across the studies, the measurements were of similar magnitudes.
ContributorsSadsad, Janelle (Author) / Gordon, Gwyneth (Thesis director) / McGregor, Sarah (Committee member) / Barrett, The Honors College (Contributor) / School of Molecular Sciences (Contributor) / School of Mathematical and Statistical Sciences (Contributor)
Created2022-05