Carbon nanomaterials have caught tremendous attention in the last few decades due to their unique physical and chemical properties. Tremendous effort has been made to develop new synthesis techniques for carbon nanomaterials and investigate their properties for different applications. In this work, carbon nanospheres (CNSs), carbon foams (CF), and single-walled carbon nanotubes (SWNTs) were studied for various applications, including water treatment, energy storage, actuators, and sensors.
A facile spray pyrolysis synthesis technique was developed to synthesize individual CNSs with specific surface area (SSA) up to 1106 m2/g. The hollow CNSs showed adsorption of up to 300 mg rhodamine B dye per gram carbon, which is more than 15 times higher than that observed for conventional carbon black. They were also evaluated as adsorbents for removal of arsenate and selenate from water and displayed good binding to both species, outperforming commercial activated carbons for arsenate removal in pH > 8. When evaluated as supercapacitor electrode materials, specific capacitances of up to 112 F/g at a current density of 0.1 A/g were observed. When used as Li-ion battery anode materials, the CNSs achieved a discharge capacity of 270 mAh/g at a current density of 372 mA/g (1C), which is 4-fold higher than that of commercial graphite anode.
Carbon foams were synthesized using direct pyrolysis and had SSA up to 2340 m2/g. When used as supercapacitor electrode materials, a specific capacitance up to 280 F/g was achieved at current density of 0.1 A/g and remained as high as 207 F/g, even at a high current density of 10 A/g.
A printed walking robot was made from common plastic films and coatings of SWNTs. The solid-state thermal bimorph actuators were multifunctional energy transducers powered by heat, light, or electricity. The actuators were also investigated for photo/thermal detection. Electrochemical actuators based on MnO2 were also studied for potential underwater applications.
SWNTs were also used to fabricate printable electrodes for trace Cr(VI) detection, which displayed sensitivity up to 500 nA/ppb for Cr(VI). The limit of detection was shown to be as low as 5 ppb. A flow detection system based on CNT/printed electrodes was also demonstrated.
A facile spray pyrolysis synthesis technique was developed to synthesize individual CNSs with specific surface area (SSA) up to 1106 m2/g. The hollow CNSs showed adsorption of up to 300 mg rhodamine B dye per gram carbon, which is more than 15 times higher than that observed for conventional carbon black. They were also evaluated as adsorbents for removal of arsenate and selenate from water and displayed good binding to both species, outperforming commercial activated carbons for arsenate removal in pH > 8. When evaluated as supercapacitor electrode materials, specific capacitances of up to 112 F/g at a current density of 0.1 A/g were observed. When used as Li-ion battery anode materials, the CNSs achieved a discharge capacity of 270 mAh/g at a current density of 372 mA/g (1C), which is 4-fold higher than that of commercial graphite anode.
Carbon foams were synthesized using direct pyrolysis and had SSA up to 2340 m2/g. When used as supercapacitor electrode materials, a specific capacitance up to 280 F/g was achieved at current density of 0.1 A/g and remained as high as 207 F/g, even at a high current density of 10 A/g.
A printed walking robot was made from common plastic films and coatings of SWNTs. The solid-state thermal bimorph actuators were multifunctional energy transducers powered by heat, light, or electricity. The actuators were also investigated for photo/thermal detection. Electrochemical actuators based on MnO2 were also studied for potential underwater applications.
SWNTs were also used to fabricate printable electrodes for trace Cr(VI) detection, which displayed sensitivity up to 500 nA/ppb for Cr(VI). The limit of detection was shown to be as low as 5 ppb. A flow detection system based on CNT/printed electrodes was also demonstrated.
ContributorsWang, Chengwei, Ph.D (Author) / Chan, Candace K. (Thesis advisor) / Tongay, Sefaattin (Committee member) / Wang, Qing Hua (Committee member) / Seo, Dong (Committee member) / Arizona State University (Publisher)
Created2015
Description
A new nanoparticle deposition technique, Aerosol Impaction-Driven Assembly (AIDA), was extensively characterized for material structures and properties. Aerogel films can be deposited directly onto a substrate with AIDA without the long aging and drying steps in the sol-gel method. Electron microscopy, pore size analysis, thermal conductivity, and optical measurements show the nanoparticle (NP) films to be similar to typical silica aerogel. Haze of nanoparticle films modeled as scattering sites correlates strongly with pore size distribution. Supporting evidence was obtained from particle sizes and aggregates using electron microscopy and small-angle X-ray scattering. NP films showed interlayers of higher porosity and large aggregates formed by tensile film stress.
To better understand film stress and NP adhesion, chemical bonding analyses were performed for samples annealed up to 900 °C. Analysis revealed that about 50% of the NP surfaces are functionalized by hydroxyl (-OH) groups, providing for hydrogen bonding. Ellipsometric porosimetry was used to further understand the mechanical properties by providing a measure of strain upon capillary pressure from filling pores. Upon annealing to 200 °C, the films lost water resulting in closer bonding of NPs and higher Young’s modulus. Upon further annealing up to 900 °C, the films lost hydroxyl bonds while gaining siloxane bonds, reducing Young’s modulus. The application of ellipsometric porosimetry to hydrophilic coatings brings into question the validity of pore size distribution calculations for materials that hold onto water molecules and result in generally smaller calculated pore sizes.
Doped hydrogenated microcrystalline silicon was grown on crystalline silicon NPs, as a test case of an application for NP films to reduce parasitic absorption in silicon heterojunction solar cells. Parasitic absorption of blue light could be reduced because microcrystalline silicon has a mix of direct and indirect bandgap, giving lower blue absorption than amorphous silicon. Using Ultraviolet Raman spectroscopy, the crystallinity of films as thin as 13 nm was determined rapidly (in 1 minute) and non-destructively. A mono-layer of nanocrystals was applied as seeds for p-doped microcrystalline silicon growth and resulted in higher crystallinity films. Applications of the method could be explored for other nanocrystalline materials.
To better understand film stress and NP adhesion, chemical bonding analyses were performed for samples annealed up to 900 °C. Analysis revealed that about 50% of the NP surfaces are functionalized by hydroxyl (-OH) groups, providing for hydrogen bonding. Ellipsometric porosimetry was used to further understand the mechanical properties by providing a measure of strain upon capillary pressure from filling pores. Upon annealing to 200 °C, the films lost water resulting in closer bonding of NPs and higher Young’s modulus. Upon further annealing up to 900 °C, the films lost hydroxyl bonds while gaining siloxane bonds, reducing Young’s modulus. The application of ellipsometric porosimetry to hydrophilic coatings brings into question the validity of pore size distribution calculations for materials that hold onto water molecules and result in generally smaller calculated pore sizes.
Doped hydrogenated microcrystalline silicon was grown on crystalline silicon NPs, as a test case of an application for NP films to reduce parasitic absorption in silicon heterojunction solar cells. Parasitic absorption of blue light could be reduced because microcrystalline silicon has a mix of direct and indirect bandgap, giving lower blue absorption than amorphous silicon. Using Ultraviolet Raman spectroscopy, the crystallinity of films as thin as 13 nm was determined rapidly (in 1 minute) and non-destructively. A mono-layer of nanocrystals was applied as seeds for p-doped microcrystalline silicon growth and resulted in higher crystallinity films. Applications of the method could be explored for other nanocrystalline materials.
ContributorsCarpenter, Joe Victor (Author) / Holman, Zachary C (Thesis advisor) / Bertoni, Mariana I (Committee member) / Chan, Candace K. (Committee member) / Smith, David J. (Committee member) / Arizona State University (Publisher)