In this investigation, copper slag was used as a coarse aggregate in four different mixes of concrete, consisting of 0%, 25%, 50%, and 100% copper slag by volume. Locally available Salt river aggregate was used as a control, and mixes were tested for density, strength, thermal conductivity, specific heat capacity,…
In this investigation, copper slag was used as a coarse aggregate in four different mixes of concrete, consisting of 0%, 25%, 50%, and 100% copper slag by volume. Locally available Salt river aggregate was used as a control, and mixes were tested for density, strength, thermal conductivity, specific heat capacity, and thermal diffusivity. Density was shown to increase with increasing copper slag content, increasing an average of 2298 kg/m^3, 2522 kg/m^3, and 2652 kg/m^3 in the 25%, 50%, and 100% mixes. This represents a 15% increase in density from 0% to 100%. Compressive strength testing indicated that the presence of copper slag in concrete provides no definitive strength benefit over Salt River aggregate. This result was expected, as concrete's strength is primarily derived from the cement matrix and not the aggregate. Thermal conductivity showed a decreasing trend with increasing copper slag content. Th control mix had an average conductivity of 0.660 W/m*K, and the 25%, 50%, and 100% mixes had conductivities of 0.649 W/m*K, 0.647 W/m*K, and 0.519 W/m*K, respectively. This represents 21% drop in thermal conductivity over the control. This result was also expected, as materials formed at higher temperatures, like copper slag, tend to have lower thermal conductivities. Specific heat capacity testing yielded results that were statistically indeterminate, though unlike strength testing this arose from inaccurate assumptions made during testing. This also prevented accurate thermal diffusivity results, as diffusivity is a function of density, thermal conductivity, and specific heat capacity. However, given the trends of the first two parameters, it is plausible to say that diffusivity in copper slag concrete would be lower than that of the control ix. All of these results were plugged into ASU's Pavement Temperature Model to see what effect they had in mitigating the UHI effect.
We describe a secondary analysis of an in vitro experiment that supports the capabilities of a relatively new imaging technique known as functional Magnetic Resonance Electrical Impedance Tomography (fMREIT) to detect conductivity changes in neural tissue caused by activity. Methods: Magnetic Resonance (MR) phase data of active Aplysia ganglia tissue…
We describe a secondary analysis of an in vitro experiment that supports the capabilities of a relatively new imaging technique known as functional Magnetic Resonance Electrical Impedance Tomography (fMREIT) to detect conductivity changes in neural tissue caused by activity. Methods: Magnetic Resonance (MR) phase data of active Aplysia ganglia tissue in artificial seawater (ASW) were collected before and after exposure to an excitotoxin using two different imaging current strengths, and these data were then used to reconstruct conductivity changes throughout the tissue. Results: We found that increases in neural activity led to significant increases in imaged conductivity when using high imaging currents, but these differences in conductivity were not seen in regions that did not contain neural tissue nor in data where there were no differences in neural activity. Conclusion: We conclude that the analysis presented here supports fMREIT as a contrast technique capable of imaging neural activity in live tissue more directly than functional imaging methods such as BOLD fMRI.
Integrating advanced materials with innovative manufacturing techniques has propelled the field of additive manufacturing into new frontiers. This study explores the rapid 3D printing of reduced graphene oxide/polymer composites using Micro-Continuous Liquid Interface Production (μCLIP), a cutting-edge technology known for its speed and precision. A printable ink is formulated with…
Integrating advanced materials with innovative manufacturing techniques has propelled the field of additive manufacturing into new frontiers. This study explores the rapid 3D printing of reduced graphene oxide/polymer composites using Micro-Continuous Liquid Interface Production (μCLIP), a cutting-edge technology known for its speed and precision. A printable ink is formulated with reduced graphene oxide for μCLIP-based 3D printing. The research focuses on optimizing μCLIP parameters to fabricate reduced graphene composites efficiently. The study encompasses material synthesis, ink formulation and explores the resulting material's structural and electrical properties. The marriage of graphene's unique attributes with the rapid prototyping capabilities of μCLIP opens new avenues for scalable and rapid production in applications such as energy storage, sensors, and lightweight structural components. This work contributes to the evolving landscape of advanced materials and additive manufacturing, offering insights into the synthesis, characterization, and potential applications of 3D printed reduced graphene oxide/polymercomposites.