Matching Items (22)
Filtering by
- All Subjects: Materials Science
- Creators: Peralta, Pedro
Description
Traditionally nanoporous gold is created by selective dissolution of silver or copper from a binary silver-gold or copper-gold alloy. These alloys serve as prototypical model systems for a phenomenon referred to as stress-corrosion cracking. Stress-corrosion cracking is the brittle failure of a normally ductile material occurring in a corrosive environment under a tensile stress. Silver-gold can experience this type of brittle fracture for a range of compositions. The corrosion process in this alloy results in a bicontinuous nanoscale morphology composed of gold-rich ligaments and voids often referred to as nanoporous gold. Experiments have shown that monolithic nanoporous gold can sustain high speed cracks which can then be injected into parent-phase alloy. This work compares nanoporous gold created from ordered and disordered copper-gold using digital image analysis and electron backscatter diffraction. Nanoporous gold from both disordered copper-gold and silver-gold, and ordered copper-gold show that grain orientation and shape remain largely unchanged by the dealloying process. Comparing the morphology of the nanoporous gold from ordered and disordered copper-gold with digital image analysis, minimal differences are found between the two and it is concluded that they are not statistically significant. This reveals the robust nature of nanoporous gold morphology against small variations in surface diffusion and parent-phase crystal structure.
Then the corrosion penetration down the grain boundary is compared to the depth of crack injections in polycrystal silver-gold. Based on statistical comparison, the crack-injections penetrate into the parent-phase grain boundary beyond the corrosion-induced porosity. To compare crack injections to stress-corrosion cracking, single crystal silver-gold samples are employed. Due to the cleavage-like nature of the fracture surfaces, electron backscatter diffraction is possible and employed to compare the crystallography of stress-corrosion crack surfaces and crack-injection surfaces. From the crystallographic similarities of these fracture surfaces, it is concluded that stress-corrosion can occur via a series of crack-injection events. This relationship between crack injections and stress corrosion cracking is further examined using electrochemical data from polycrystal silver-gold samples during stress-corrosion cracking. The results support the idea that crack injection is a mechanism for stress-corrosion cracking.
Then the corrosion penetration down the grain boundary is compared to the depth of crack injections in polycrystal silver-gold. Based on statistical comparison, the crack-injections penetrate into the parent-phase grain boundary beyond the corrosion-induced porosity. To compare crack injections to stress-corrosion cracking, single crystal silver-gold samples are employed. Due to the cleavage-like nature of the fracture surfaces, electron backscatter diffraction is possible and employed to compare the crystallography of stress-corrosion crack surfaces and crack-injection surfaces. From the crystallographic similarities of these fracture surfaces, it is concluded that stress-corrosion can occur via a series of crack-injection events. This relationship between crack injections and stress corrosion cracking is further examined using electrochemical data from polycrystal silver-gold samples during stress-corrosion cracking. The results support the idea that crack injection is a mechanism for stress-corrosion cracking.
ContributorsKarasz, Erin (Author) / Sieradzki, Karl (Thesis advisor) / Chawla, Nikhilesh (Committee member) / Peralta, Pedro (Committee member) / Rajagopalan, Jagannathan (Committee member) / Arizona State University (Publisher)
Created2020
Description
Nanocrystalline (NC) materials are of great interest to researchers due to their multitude of properties such as exceptional strength and radiation resistance owing to their high fraction of grain boundaries that act as defect sinks for radiation-induced defects, provided they are microstructurally stable. In this dissertation, radiation effects in microstructurally stable bulk NC copper (Cu)- tantalum (Ta) alloys engineered with uniformly dispersed Ta nano-precipitates are systematically probed. Towards this, both ex-situ and in-situ irradiations using heavy (self) ion, helium ion, and concurrent dual ion beams (He+Au) followed by isochronal annealing inside TEM were utilized to understand radiation tolerance and underlying mechanisms of microstructure evolution in stable NC alloys. With systematic self-ion irradiation, the high density of tantalum nanoclusters in Cu-10at.%Ta were observed to act as stable sinks in suppressing radiation hardening, in addition to stabilizing the grain boundaries; while the large incoherent precipitates experienced ballistic mixing and dissolution at high doses. Interestingly, the alloy exhibited a microstructure self-healing mechanism, where with a moderate thermal input, this dissolved tantalum eventually re-precipitated, thus replenishing the sink density. The high stability of these tantalum nanoclusters is attributed to the high positive enthalpy of mixing of tantalum in copper which also acted as a critical driving force against atomic mixing to facilitate re-precipitation of tantalum nanoclusters. Furthermore, these nanoclusters proved to be effective trapping sites for helium, thus sequestering helium into isolated small bubbles and aid in increasing the overall swelling threshold of the alloy. The alloy was then compositionally optimized to reduce the density of large incoherent precipitates without compromising on the grain size and nanocluster density (Cu-3at.%Ta) which resulted in a consistent and more promising response to high dose self-ion irradiation. In-situ helium and dual beam irradiation coupled with isochronal annealing till 723 K, also revealed a comparable microstructural stability and enhanced ability of Cu-3Ta in controlling bubble growth and suppressing swelling compared to Cu-10Ta indicating a promising improvement in radiation tolerance in the optimized composition. Overall, this work helps advancing the current understanding of radiation tolerance in stable nanocrystalline alloys and aid developing design strategies for engineering radiation tolerant materials with stable interfaces.
ContributorsSrinivasan, Soundarya (Author) / Solanki, Kiran (Thesis advisor) / Peralta, Pedro (Committee member) / Alford, Terry (Committee member) / Darling, Kristopher (Committee member) / Arizona State University (Publisher)
Created2021