Matching Items (28)
Filtering by
- All Subjects: Materials Science
Description
Advanced composites are being widely used in aerospace applications due to their high stiffness, strength and energy absorption capabilities. However, the assurance of structural reliability is a critical issue because a damage event will compromise the integrity of composite structures and lead to ultimate failure. In this dissertation a novel homogenization based multiscale modeling framework using semi-analytical micromechanics is presented to simulate the response of textile composites. The novelty of this approach lies in the three scale homogenization/localization framework bridging between the constituent (micro), the fiber tow scale (meso), weave scale (macro), and the global response. The multiscale framework, named Multiscale Generalized Method of Cells (MSGMC), continuously bridges between the micro to the global scale as opposed to approaches that are top-down and bottom-up. This framework is fully generalized and capable of modeling several different weave and braids without reformulation. Particular emphasis in this dissertation is placed on modeling the nonlinearity and failure of both polymer matrix and ceramic matrix composites.
ContributorsLiu, Guang (Author) / Chattopadhyay, Aditi (Thesis advisor) / Mignolet, Marc (Committee member) / Jiang, Hanqing (Committee member) / Li, Jian (Committee member) / Rajadas, John (Committee member) / Arizona State University (Publisher)
Created2011
Description
Organic light-emitting diodes (OLEDs) have been successfully implemented in various display applications owing to rapid advancements in material design and device architecture. Their success in the display industry has ignited a rising interest in applying OLEDs for solid-state lighting applications through the development of white OLEDs (WOLEDs). However, to enter the market as a serious competitor, WOLEDs must achieve excellent color quality, high external quantum efficiency (EQE) as well as a long operational lifetime. In this research, novel materials and device architectures were explored to improve the performance of single-stack WOLEDs. A new Pt-based phosphorescent emitter, Pt2O2-p2m, was examined as a single emissive emitter for the development of a stable and efficient single-doped WOLED. A bilayer structure was employed to balance the charges carriers within the emissive layer resulting in low efficiency roll-off at high brightness, realizing a peak EQE of 21.5% and EQEs of 20% at 1000 cd m-2 and 15.3% at 7592 cd m-2. A novel phosphorescent/fluorescent, or hybrid, WOLED device architecture was also proposed. To gather a thorough understanding of blue fluorescent OLEDs prior to its use in a WOLED, a study was conducted to investigate the impact of the material selection on the device performance. The use of an anthracene type host demonstrated an improvement to the operational stability of the blue OLED by reducing the occurrence of degradation events. Additionally, various dopant concentrations and blocking materials revealed vastly different efficiency and lifetime results. Finally, a Pd (II) complex, Pd3O8-Py5, with efficient amber-colored aggregate emission was employed to produce a WOLED. Various host materials were investigated to achieve balanced white emission and the addition of an interlayer composed of a high triplet energy material was used to reduce quenching effects. Through this strategy, a color stable WOLED device with a peak EQE of 45% and an estimated LT95 over 50,000 hours at 1000 cd m-2 was realized. The comprehensive performance of the proposed device architecture competes with WOLED devices that are commercially available and reported within the literature domain, providing a strong foundation to further advance the development of highly efficient and stable single-stack WOLEDs.
ContributorsAmeri, Lydia (Author) / Li, Jian (Thesis advisor) / Adams, James (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2022
Description
Over the past three decades, significant progress in the development of organic light-emitting diodes (OLEDs) has been achieved, enabling OLEDs to become a main component in state-of-the-art displays and next generation solid-state lighting. As this technology advances, it is highly desirable to further improve the device efficiency and operational stability to drive the success of OLEDs in future display and lighting applications. This dissertation aims at developing novel organic emitting materials covering visible and near-infrared (NIR) emissions for efficient and table OLEDs. Firstly, a series of tetradentate Pd(II) complexes, which have attractive phosphorescent aggregate emission performance especially at high brightness level in device settings, have been developed. The luminescent lifetime of Pd(II) complex aggregates was demonstrated to be shorter than 1 μs with a close-to-unity photoluminescence quantum yield. Moreover, a systematic study regarding structure-property relationship was conducted on four tetradentate Pd(II) complexes, i.e., Pd3O3, Pd3O8-P, Pd3O8-Py2, and Pd3O8-Py5, featuring aggregate emission. As a result, an extremely efficient and stable OLED device utilizing Pd3O8-Py5 was achieved. It demonstrated a peak external quantum efficiency (EQE) of 37.3% with a reduced efficiency roll-off retaining a high EQE of 32.5% at 10000 cd m-2, and an estimated LT95 lifetime (time to 95% of the initial luminance) of 48246 h at 1000 cd m-2. Secondly, there is an increasing demand for NIR OLEDs with emission spectra beyond 900 nm to expand their applications in biometric authentication, night vision display, and telecommunication, etc. A stable and efficient NIR Pt(II) porphyrin complex named PtTPTNP-F8 was developed, and exhibited an electroluminescent spectrum at 920 nm. By carefully choosing the host materials, an PtTPTNP-F8 based NIR OLED achieved a EQE of 1.9%. Furthermore, an PtTPTNP-F8 OLED fabricated in a stable device structure demonstrated extraordinary operational stability with LT99 of >1000 h at 20 mA cm-2. Lastly, a series of imidazole-based blue Pt(II) complexes were developed and studied. Results indicated that structural modification of ligand molecules effectively tuned the emission spectral wavelength and bandwidth. Two blue complexes, i.e., Pt2O2 P2M and Pt2O2-PPy5-M, emitting at 472 and 476 nm respectively, exhibited narrow-band emission spectra with a full width at half maximum of 16 nm.
ContributorsCao, Linyu (Author) / Li, Jian (Thesis advisor) / Adams, James (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2021
Description
Perovskite solar cells are one of the rising stars in the solar cell industry. This thesis explores several approaches to enhance the properties of the perovskite layer and the solar cell devices in which they operate. They include studies of different antisolvent additives during spin coating of triple cation perovskites, the use of surfactants to improve the quality of perovskite film microstructures, the applicability of a new fabrication process, and the value of post-deposition thermal and chemical annealing processes.This thesis experimentally analyzes different antisolvents, viz., ethyl acetate, isopropyl alcohol, toluene, and chlorobenzene. It focuses on the antisolvent-assisted crystallization method to achieve homogenous nucleation of the perovskite film. Of all the antisolvents, ethyl acetate-treated films gave the best-performing device, achieving a power conversion efficiency of 15.5%.
This thesis also analyzes the effects of mixed antisolvents on the qualities of triple-cation perovskites. Different solution concentrations of chlorobenzene in ethyl acetate and isopropyl alcohol in ethyl acetate are optimized for optimal supersaturation to achieve enlarged perovskite grains. Evaluations are discussed in the context of solution polarity and boiling point of the antisolvents, where 25% chlorobenzene in ethyl acetate antisolvent mixture shows the best film properties.
Another study discusses a new fabrication process called electrical field-assisted direct ink deposition for large-scale printing of perovskite solar cells. This process involves the formation of nanodroplets under an electrical field deposited onto ITO/glass substrates. As a result, smooth Poly (3,4-ethylene dioxythiophene) polystyrene sulfonate layers are
ii
produced with an average effective electrical resistivity of 4.15104 0.26 -m compared to that of spin-coated films.
A successive chapter discusses the studies of the electrical field-assisted direct ink deposition of the photoactive CH3NH3PbI2 (MAPbI3) layer. Its focus is on the post-deposition chemical annealing of the MAPbI3 films in methylamine gas, termed as methylamine gas-assisted healing and growth of perovskite films. This treatment improved the smoothness, reduced porosity, increased density, and generated more uniform grain sizes. Moreover, it improved the inter-grain boundary contacts by eliminating secondary, fine-grained boundary structures. Mechanisms behind the initial liquefaction of the MAPbI3 film's subsequent re-solidification are discussed.
ContributorsGogoi, Banashree (Author) / Alford, Terry (Thesis advisor) / Petuskey, William (Thesis advisor) / Gould, Ian (Committee member) / Li, Jian (Committee member) / Arizona State University (Publisher)
Created2023
Description
Modulated nanostructures are short-range periodic composition fluctuations observed in metals, semiconductors, and ceramic alloys and have an important effect on the mechanical, electrical, and magnetic properties of the materials. Their presence is often attributed to spinodal decomposition. In the past, such modulations have been analyzed using X-ray diffraction, electron diffraction, and diffraction contrast imaging techniques. The investigations gave useful information about the spatial distribution of the modulations but nothing about the composition fluctuation of the modulated structure. In this study, the composition amplitude of the fluctuations was directly measured using STEM Imaging and atomic resolution spectroscopy in small unit cell Au-Pt and Cu-Ti alloys. With the development of field emission sources, aberration correctors, and ADF imaging for STEM microscopes, measuring the amplitude of the modulation directly and examining the diffused interface is possible.Au-Pt alloys, featuring a nearly symmetrical solid-state miscibility gap, and a Cu-Ti alloy with an asymmetrical metastable miscibility gap were chosen for investigation. Three Au-Pt alloys of different compositions were analyzed at a specific temperature for varying aging times. The study successfully employed atomic resolution energy dispersive X-ray spectroscopy (EDS) for Au-Pt alloys and atomic resolution electron energy loss spectroscopy (EELS) for Cu-Ti alloys to measure composition variation and diffused interfaces across modulations.
In Au-Pt alloys, it was shown that the wavelength, as well as the composition amplitude of the modulations, increases as the alloy is aged for a longer time. Non-uniform distribution of wavelength and composition amplitude of modulated structures was observed across the samples. Results shows competitive growth mechanisms occurring in nanostructures with a range of wavelengths/amplitudes. Composition of Au-rich and Pt-rich regions deviates significantly from equilibrium at the selected temperature, more aging is necessary to observe coherency loss. Similarly, in Cu-Ti alloys, variations in wavelengths and composition amplitude of modulations were observed, along with clustering and ordering reactions. Ordering was specifically noted in Ti-rich regions of the alloy aged for an extended period. Diffused interfaces were observed in both alloy systems rather than chemically sharp interfaces, and the contrast in HAADF STEM images in both systems was predominantly influenced by strain effects. Hence utilizing HAADF STEM for composition measurement of modulations is impractical due to the impact of strain on HAADF intensity, specifically due to surface relaxation effects.
ContributorsSawant, Ronit Prasad (Author) / Carpenter, Ray (Thesis advisor) / Treacy, Michael (Committee member) / Crozier, Peter (Committee member) / Liu, Jingyue (Committee member) / Arizona State University (Publisher)
Created2024
Description
Organic electronics have remained a research topic of great interest over the past few decades, with organic light emitting diodes (OLEDs) emerging as a disruptive technology for lighting and display applications. While OLED performance has improved significantly over the past decade, key issues remain unsolved such as the development of stable and efficient blue devices. In order to further the development of OLEDs and increase their commercial potential, innovative device architectures, novel emissive materials and high-energy hosts are designed and reported.
OLEDs employing step-wide graded-doped emissive layers were designed to improve charge balance and center the exciton formation zone leading to improved device performance. A red OLED with a peak efficiency of 16.9% and an estimated LT97 over 2,000 hours at 1,000 cd/m2 was achieved. Employing a similar structure, a sky-blue OLED was demonstrated with a peak efficiency of 17.4% and estimated LT70 over 1,300 hours at 1,000 cd/m2. Furthermore, the sky-blue OLEDs color was improved to CIE coordinates of (0.15, 0.25) while maintaining an efficiency of 16.9% and estimated LT70 over 600 hours by incorporating a fluorescent sensitizer. These devices represent literature records at the time of publication for efficient and stable platinum phosphorescent OLEDs.
A newly developed class of emitters, metal-assisted delayed-fluorescence (MADF), are demonstrated to achieve higher-energy emission from a relatively low triplet energy. A green MADF device reaches a peak efficiency of 22% with an estimated LT95 over 350 hours at 1,000 cd/m2. Additionally, a blue charge confined OLED of PtON1a-tBu demonstrated a peak efficiency above 20%, CIE coordinated of (0.16, 0.27), and emission onset at 425 nm.
High triplet energy hosts are required for the realization of stable and efficient deep blue emission. A rigid “M”-type carbazole/fluorene hybrid called mDCzPF and a carbazole/9-silafluorene hybrid called mDCzPSiF are demonstrated to have high triplet energies ET=2.88 eV and 3.03 eV respectively. Both hosts are demonstrated to have reasonable stability and can serve as a template for future material design. The techniques presented here demonstrate alternative approaches for improving the performance of OLED devices and help to bring this technology closer to widespread commercialization.
OLEDs employing step-wide graded-doped emissive layers were designed to improve charge balance and center the exciton formation zone leading to improved device performance. A red OLED with a peak efficiency of 16.9% and an estimated LT97 over 2,000 hours at 1,000 cd/m2 was achieved. Employing a similar structure, a sky-blue OLED was demonstrated with a peak efficiency of 17.4% and estimated LT70 over 1,300 hours at 1,000 cd/m2. Furthermore, the sky-blue OLEDs color was improved to CIE coordinates of (0.15, 0.25) while maintaining an efficiency of 16.9% and estimated LT70 over 600 hours by incorporating a fluorescent sensitizer. These devices represent literature records at the time of publication for efficient and stable platinum phosphorescent OLEDs.
A newly developed class of emitters, metal-assisted delayed-fluorescence (MADF), are demonstrated to achieve higher-energy emission from a relatively low triplet energy. A green MADF device reaches a peak efficiency of 22% with an estimated LT95 over 350 hours at 1,000 cd/m2. Additionally, a blue charge confined OLED of PtON1a-tBu demonstrated a peak efficiency above 20%, CIE coordinated of (0.16, 0.27), and emission onset at 425 nm.
High triplet energy hosts are required for the realization of stable and efficient deep blue emission. A rigid “M”-type carbazole/fluorene hybrid called mDCzPF and a carbazole/9-silafluorene hybrid called mDCzPSiF are demonstrated to have high triplet energies ET=2.88 eV and 3.03 eV respectively. Both hosts are demonstrated to have reasonable stability and can serve as a template for future material design. The techniques presented here demonstrate alternative approaches for improving the performance of OLED devices and help to bring this technology closer to widespread commercialization.
ContributorsKlimes, Kody George (Author) / Li, Jian (Thesis advisor) / Adams, James (Committee member) / Wang, Liping (Committee member) / Arizona State University (Publisher)
Created2019
Description
The fuel cell is a promising device that converts the chemical energy directly into the electrical energy without combustion process. However, the slow reaction rate of the oxygen reduction reaction (ORR) necessitates the development of cathode catalysts for low-temperature fuel cells. After a thorough literature review in Chapter 1, the thesis is divided into three parts as given below in Chapters 2-4.
Chapter 2 describes the study on the Pt and Pt-Me (Me: Co, Ni) alloy nanoparticles supported on the pyrolyzed zeolitic imidazolate framework (ZIF) towards ORR. The Co-ZIF and NiCo-ZIF were synthesized by the solvothermal method and then mixed with Pt precursor. After pyrolysis and acid leaching, the PtCo/NC and PtNiCo/NC were evaluated in proton exchange membrane fuel cells (PEMFC). The peak power density exhibited > 10% and 15% for PtCo/NC and PtNiCo/NC, respectively, compared to that with commercial Pt/C catalyst under identical test conditions.
Chapter 3 is the investigation of the oxygen vacancy (OV) effect in a-MnO2 as a cathode catalyst for alkaline membrane fuel cells (AMFC). The a-MnO2 nanorods were synthesized by hydrothermal method and heated at 300, 400 and 500 ℃ in the air to introduce the OV. The 400 ℃ treated material showed the best ORR performance among all other samples due to more OV in pure a-MnO2 phase. The optimized AMFC electrode showed ~ 45 mW.cm-2, which was slightly lower than that with commercial Pt/C (~60 mW.cm-2).
Chapter 4 is the density functional theory (DFT) study of the protonation effect and active sites towards ORR on a-MnO2 (211) plane. The theoretically optimized oxygen adsorption and hydroxyl ion desorption energies were ~ 1.55-1.95 eV and ~ 0.98-1.45 eV, respectively, by Nørskov et al.’s calculations. All the configurations showed oxygen adsorption and hydroxyl ion desorption energies were ranging from 0.27 to 1.76 eV and 1.59 to 15.0 eV, respectively. The site which was close to two Mn ions showed the best oxygen adsorption and hydroxyl ion desorption energies improvement with the surface protonation.
Based on the results given in Chapters 1-4, the major findings are summarized in Chapter 5.
Chapter 2 describes the study on the Pt and Pt-Me (Me: Co, Ni) alloy nanoparticles supported on the pyrolyzed zeolitic imidazolate framework (ZIF) towards ORR. The Co-ZIF and NiCo-ZIF were synthesized by the solvothermal method and then mixed with Pt precursor. After pyrolysis and acid leaching, the PtCo/NC and PtNiCo/NC were evaluated in proton exchange membrane fuel cells (PEMFC). The peak power density exhibited > 10% and 15% for PtCo/NC and PtNiCo/NC, respectively, compared to that with commercial Pt/C catalyst under identical test conditions.
Chapter 3 is the investigation of the oxygen vacancy (OV) effect in a-MnO2 as a cathode catalyst for alkaline membrane fuel cells (AMFC). The a-MnO2 nanorods were synthesized by hydrothermal method and heated at 300, 400 and 500 ℃ in the air to introduce the OV. The 400 ℃ treated material showed the best ORR performance among all other samples due to more OV in pure a-MnO2 phase. The optimized AMFC electrode showed ~ 45 mW.cm-2, which was slightly lower than that with commercial Pt/C (~60 mW.cm-2).
Chapter 4 is the density functional theory (DFT) study of the protonation effect and active sites towards ORR on a-MnO2 (211) plane. The theoretically optimized oxygen adsorption and hydroxyl ion desorption energies were ~ 1.55-1.95 eV and ~ 0.98-1.45 eV, respectively, by Nørskov et al.’s calculations. All the configurations showed oxygen adsorption and hydroxyl ion desorption energies were ranging from 0.27 to 1.76 eV and 1.59 to 15.0 eV, respectively. The site which was close to two Mn ions showed the best oxygen adsorption and hydroxyl ion desorption energies improvement with the surface protonation.
Based on the results given in Chapters 1-4, the major findings are summarized in Chapter 5.
ContributorsShi, Xuan, Ph.D (Author) / Kannan, Arunachalanadar Mada (Thesis advisor) / Liu, Jingyue (Committee member) / Nam, Changho (Committee member) / Peng, Xihong (Committee member) / Arizona State University (Publisher)
Created2019
Description
Among the alternative processes for the traditional distillation, adsorption and membrane separations are the two most promising candidates and metal-organic frameworks (MOFs) are the new material candidate as adsorbent or membrane due to their high surface area, various pore sizes, and highly tunable framework functionality. This dissertation presents an investigation of the formation process of MOF membrane, framework defects, and two-dimensional (2D) MOFs, aiming to explore the answers for three critical questions: (1) how to obtain a continuous MOF membrane, (2) how defects form in MOF framework, and (3) how to obtain isolated 2D MOFs. To solve the first problem, the accumulated protons in the MOF synthesis solution is proposed to be the key factor preventing the continuous growth among Universitetet I Oslo-(UiO)-66 crystals. The hypothesis is verified by the growth reactivation under the addition of deprotonating agent. As long as the protons were sufficiently coordinated by the deprotonating agent, the continuous growth of UiO-66 is guaranteed. Moreover, the modulation effect can impact the coordination equilibrium so that an oriented growth of UiO-66 film was achieved in membrane structures. To find the answer for the second problem, the defect formation mechanism in UiO-66 was investigated and the formation of missing-cluster (MC) defects is attributed to the partially-deprotonated ligands. Experimental results show the number of MC defects is sensitive to the addition of deprotonating agent, synthesis temperature, and reactant concentration. Pore size distribution allows an accurate and convenient characterization of the defects. Results show that these defects can cause significant deviations of its pore size distribution from the perfect crystal. The study of the third questions is based on the established bi-phase synthesis method, a facile synthesis method is adopted for the production of high quality 2D MOFs in large scale. Here, pyridine is used as capping reagent to prevent the interplanar hydrogen bond formation. Meanwhile, formic acid and triethylamine as modulator and deprotonating agent to balance the anisotropic growth, crystallinity, and yield in the 2D MOF synthesis. As a result, high quality 2D zinc-terephthalic acid (ZnBDC) and copper-terephthalic acid (CuBDC) with extraordinary aspect ratio samples were successfully synthesized.
ContributorsShan, Bohan (Author) / Mu, Bin (Thesis advisor) / Forzani, Erica (Committee member) / Dai, Lenore (Committee member) / Lin, Jerry (Committee member) / Liu, Jingyue (Committee member) / Arizona State University (Publisher)
Created2019
Description
Non-stoichiometric oxides play a critical role in many catalytic, energy, and sensing technologies, providing the ability to reversibly exchange oxygen with the ambient environment through the creation and annihilation of surface oxygen vacancies. Oxygen exchange at the surfaces of these materials is strongly influenced by atomic structure, which varies significantly across nanoparticle surfaces. The studies presented herein elucidate the relationship between surface structure behaviors and oxygen exchange reactions on ceria (CeO2) catalyst materials. In situ aberration-corrected transmission electron microscopy (AC-TEM) techniques were developed and employed to correlate dynamic atomic-level structural heterogeneities to local oxygen vacancy activity.
A model Ni/CeO2 catalyst was used to probe the role of a ceria support during hydrocarbon reforming reactions, and it was revealed that carbon formation was inhibited on Ni metal nanoparticles due to the removal of lattice oxygen from the ceria support and subsequent oxidation of adsorbed decomposed hydrocarbon products. Atomic resolution observations of surface oxygen vacancy creation and annihilation were performed on CeO2 nanoparticle surfaces using a novel time-resolved in situ AC-TEM approach. Cation displacements were found to be related to oxygen vacancy creation and annihilation, and the most reactive surface oxygen sites were identified by monitoring the frequency of cation displacements. In addition, the dynamic evolution of CeO2 surface structures was characterized with high temporal resolution AC-TEM imaging, which resulted in atomic column positions and occupancies to be determined with a combination of spatial precision and temporal resolution that had not previously been achieved. As a result, local lattice expansions and contractions were observed on ceria surfaces, which were likely related to cyclic oxygen vacancy activity. Finally, local strain fields on CeO2 surfaces were quantified, and it was determined that local strain enhanced the ability of a surface site to create oxygen vacancies. Through the characterization of dynamic surface structures with advanced AC-TEM techniques, an improvement in the fundamental understanding of how ceria surfaces influence and control oxygen exchange reactions was obtained.
A model Ni/CeO2 catalyst was used to probe the role of a ceria support during hydrocarbon reforming reactions, and it was revealed that carbon formation was inhibited on Ni metal nanoparticles due to the removal of lattice oxygen from the ceria support and subsequent oxidation of adsorbed decomposed hydrocarbon products. Atomic resolution observations of surface oxygen vacancy creation and annihilation were performed on CeO2 nanoparticle surfaces using a novel time-resolved in situ AC-TEM approach. Cation displacements were found to be related to oxygen vacancy creation and annihilation, and the most reactive surface oxygen sites were identified by monitoring the frequency of cation displacements. In addition, the dynamic evolution of CeO2 surface structures was characterized with high temporal resolution AC-TEM imaging, which resulted in atomic column positions and occupancies to be determined with a combination of spatial precision and temporal resolution that had not previously been achieved. As a result, local lattice expansions and contractions were observed on ceria surfaces, which were likely related to cyclic oxygen vacancy activity. Finally, local strain fields on CeO2 surfaces were quantified, and it was determined that local strain enhanced the ability of a surface site to create oxygen vacancies. Through the characterization of dynamic surface structures with advanced AC-TEM techniques, an improvement in the fundamental understanding of how ceria surfaces influence and control oxygen exchange reactions was obtained.
ContributorsLawrence, Ethan Lee (Author) / Crozier, Peter A. (Thesis advisor) / Lin, Jerry (Committee member) / Liu, Jingyue (Committee member) / Petuskey, William (Committee member) / Arizona State University (Publisher)
Created2019
Description
This dissertation describes fundamental studies of hollow carbon nanostructures, which may be used as electrodes for practical energy storage applications such as batteries or supercapacitors. Electron microscopy is heavily utilized for the nanoscale characterization. To control the morphology of hollow carbon nanostructures, ZnO nanowires serve as sacrificial templates. The first part of this dissertation focuses on the optimization of synthesis parameters and the scale-up production of ZnO nanowires by vapor transport method. Uniform ZnO nanowires with 40 nm width can be produced by using 1100 °C reaction temperature and 20 sccm oxygen flow rate, which are the two most important parameters.
The use of ethanol as carbon source with or without water steam provides uniform carbonaceous deposition on ZnO nanowire templates. The amount of as-deposited carbonaceous material can be controlled by reaction temperature and reaction time. Due to the catalytic property of ZnO surface, the thicknesses of carbonaceous layers are typically in nanometers. Different methods to remove the ZnO templates are explored, of which hydrogen reduction at temperatures higher than 700 °C is most efficient. The ZnO templates can also be removed under ethanol environment, but the temperatures need to be higher than 850 °C for practical use.
Characterizations of hollow carbon nanofibers show that the hollow carbon nanostructures have a high specific surface area (>1100 m2/g) with the presence of mesopores (~3.5 nm). The initial data on energy storage as electrodes of electrochemical double layer capacitors show that high specific capacitance (> 220 F/g) can be obtained, which is related to the high surface area and unique porous hollow structure with a thin wall.
The use of ethanol as carbon source with or without water steam provides uniform carbonaceous deposition on ZnO nanowire templates. The amount of as-deposited carbonaceous material can be controlled by reaction temperature and reaction time. Due to the catalytic property of ZnO surface, the thicknesses of carbonaceous layers are typically in nanometers. Different methods to remove the ZnO templates are explored, of which hydrogen reduction at temperatures higher than 700 °C is most efficient. The ZnO templates can also be removed under ethanol environment, but the temperatures need to be higher than 850 °C for practical use.
Characterizations of hollow carbon nanofibers show that the hollow carbon nanostructures have a high specific surface area (>1100 m2/g) with the presence of mesopores (~3.5 nm). The initial data on energy storage as electrodes of electrochemical double layer capacitors show that high specific capacitance (> 220 F/g) can be obtained, which is related to the high surface area and unique porous hollow structure with a thin wall.
ContributorsSong, Yian (Author) / Liu, Jingyue (Committee member) / Smith, David (Committee member) / McCartney, Martha (Committee member) / Chen, Tingyong (Committee member) / Arizona State University (Publisher)
Created2016