Description
Photovoltaic (PV) systems are one of the next generation's renewable energy sources for our world energy demand. PV modules are highly reliable. However, in polluted environments, over time, they will collect grime and dust. There are also limited field data studies about soiling losses on PV modules. The study showed how important it is to investigate the effect of tilt angle on soiling. The study includes two sets of mini-modules. Each set has 9 PV modules tilted at 0, 5, 10, 15, 20, 23, 30, 33 and 40°. The first set called "Cleaned" was cleaned every other day. The second set called "Soiled" was never cleaned after the first day. The short circuit current, a measure of irradiance, and module temperature was monitored and recorded every two minutes over three months (January-March 2011). The data were analyzed to investigate the effect of tilt angle on daily and monthly soiling, and hence transmitted solar insolation and energy production by PV modules. The study shows that during the period of January through March 2011 there was an average loss due to soiling of approximately 2.02% for 0° tilt angle. Modules at tilt anlges 23° and 33° also have some insolation losses but do not come close to the module at 0° tilt angle. Tilt anlge 23° has approximately 1.05% monthly insolation loss, and 33° tilt angle has an insolation loss of approximately 0.96%. The soiling effect is present at any tilt angle, but the magnitude is evident: the flatter the solar module is placed the more energy it will lose.
ContributorsCano Valero, José (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Madakannan, Arunachalanadar (Committee member) / Macia, Narciso (Committee member) / Arizona State University (Publisher)
Created2011
Description
The photovoltaic (PV) modules are primarily characterized for their performance with respect to incident irradiance and operating temperature. This work deals with data collection and automation of data processing for the performance and thermal characterizations of PV modules. This is a two-part thesis: The primary part (part-1) deals with the software automation to generate performance matrix as per IEC 61853-1 standard using MPPT (maximum power point tracking) data at the module or system level; the secondary part (part-2) deals with the software automation to predict temperature of rooftop PV modules using the thermal model coefficients generated in the previous studies of the Photovoltaic Reliability Laboratory (PRL). Part 1: The IEC 61853-1 standard published in January 2011 specifies the generation of a target performance matrix of photovoltaic (PV) modules at various temperatures and irradiance levels. In a conventional method, this target matrix is generated using all the data points of several measured I-V curves and the translation procedures defined in IEC 60891 standard. In the proposed method, the target matrix is generated using only three commonly field measured parameters: Module temperature, Incident irradiance and MPPT (Maximum Peak Power Tracking) value. These parameters are loaded into the programmed Excel file and with a click of a button, IEC 61853-1 specified Pmppt matrix is displayed on the screen in about thirty seconds. Part 2: In a previous study at PRL, an extensive thermal model to predict operating temperature of rooftop PV modules was developed with a large number of empirical monthly coefficients for ambient temperature, irradiance and wind speed. Considering that there is large number of coefficients for each air gap of rooftop modules, it became necessary to automate the entire data processing to predict the temperature of rooftop PV modules at different air gaps. This part of the work was dedicated to automatically predict the temperature of rooftop modules at different air gaps for any month in a year just using only four input parameters: Month, Irradiance, Ambient temperature and Wind speed.
ContributorsKoka, Kartheek (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Rogers, Bradley (Committee member) / Macia, Narciso F. (Committee member) / Arizona State University (Publisher)
Created2011
Description
The object of this study was a 26 year old residential Photovoltaic (PV) monocrystalline silicon (c-Si) power plant, called Solar One, built by developer John F. Long in Phoenix, Arizona (a hot-dry field condition). The task for Arizona State University Photovoltaic Reliability Laboratory (ASU-PRL) graduate students was to evaluate the power plant through visual inspection, electrical performance, and infrared thermography. The purpose of this evaluation was to measure and understand the extent of degradation to the system along with the identification of the failure modes in this hot-dry climatic condition. This 4000 module bipolar system was originally installed with a 200 kW DC output of PV array (17 degree fixed tilt) and an AC output of 175 kVA. The system was shown to degrade approximately at a rate of 2.3% per year with no apparent potential induced degradation (PID) effect. The power plant is made of two arrays, the north array and the south array. Due to a limited time frame to execute this large project, this work was performed by two masters students (Jonathan Belmont and Kolapo Olakonu) and the test results are presented in two masters theses. This thesis presents the results obtained on the north array and the other thesis presents the results obtained on the south array. The resulting study showed that PV module design, array configuration, vandalism, installation methods and Arizona environmental conditions have had an effect on this system's longevity and reliability. Ultimately, encapsulation browning, higher series resistance (potentially due to solder bond fatigue) and non-cell interconnect ribbon breakages outside the modules were determined to be the primary causes for the power loss.
ContributorsBelmont, Jonathan (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Henderson, Mark (Committee member) / Rogers, Bradley (Committee member) / Arizona State University (Publisher)
Created2013
Description
Potential induced degradation (PID) due to high system voltages is one of the major degradation mechanisms in photovoltaic (PV) modules, adversely affecting their performance due to the combined effects of the following factors: system voltage, superstrate/glass surface conductivity, encapsulant conductivity, silicon nitride anti-reflection coating property and interface property (glass/encapsulant; encapsulant/cell; encapsulant/backsheet). Previous studies carried out at ASU's Photovoltaic Reliability Laboratory (ASU-PRL) showed that only negative voltage bias (positive grounded systems) adversely affects the performance of commonly available crystalline silicon modules. In previous studies, the surface conductivity of the glass surface was obtained using either conductive carbon layer extending from the glass surface to the frame or humidity inside an environmental chamber. This thesis investigates the influence of glass surface conductivity disruption on PV modules. In this study, conductive carbon was applied only on the module's glass surface without extending to the frame and the surface conductivity was disrupted (no carbon layer) at 2cm distance from the periphery of frame inner edges. This study was carried out under dry heat at two different temperatures (60 °C and 85 °C) and three different negative bias voltages (-300V, -400V, and -600V). To replicate closeness to the field conditions, half of the selected modules were pre-stressed under damp heat for 1000 hours (DH 1000) and the remaining half under 200 hours of thermal cycling (TC 200). When the surface continuity was disrupted by maintaining a 2 cm gap from the frame to the edge of the conductive layer, as demonstrated in this study, the degradation was found to be absent or negligibly small even after 35 hours of negative bias at elevated temperatures. This preliminary study appears to indicate that the modules could become immune to PID losses if the continuity of the glass surface conductivity is disrupted at the inside boundary of the frame. The surface conductivity of the glass, due to water layer formation in a humid condition, close to the frame could be disrupted just by applying a water repelling (hydrophobic) but high transmittance surface coating (such as Teflon) or modifying the frame/glass edges with water repellent properties.
ContributorsTatapudi, Sai Ravi Vasista (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Srinivasan, Devarajan (Committee member) / Rogers, Bradley (Committee member) / Arizona State University (Publisher)
Created2012
Description
Power rating photovoltaic modules at six irradiance and four temperature matrix levels of IEC 61853-1 draft standard is one of the most important requirements to accurately predict energy production of photovoltaic modules at different climatic conditions. Two studies were carried out in this investigation: a measurement repeatability study and a translation procedure validation study. The repeatability study was carried out to define a testing methodology that allows generating repeatable power rating results under outdoor conditions. The validation study was carried out to validate the accuracy of the four translation procedures: the first three procedures are from the IEC 60891 standard and the fourth procedure is reported by NREL. These translation procedures are needed to translate the measured data from the actual test conditions to the reporting rating conditions required by the IEC 61853-1 draft standard. All the measurements were carried out outdoors on clear days using a manual, 2-axis tracker, located in Mesa/Tempe, Arizona. Four module technologies were investigated: crystalline silicon, amorphous silicon, cadmium telluride, and copper indium gallium selenide. The modules were cooled and then allowed to naturally warm up to obtain current-voltage data at different temperatures. Several black mesh screens with a wide range of transmittance were used for varying irradiance levels. From the measurements repeatability study, it was determined that: (i) a certain minimum distance (2 inches) should be maintained between module surface and the screen surface; (ii) the reference cell should be kept outside the screen (calibrated screen) as opposed to inside the screen (uncalibrated screen); and (iii) the air mass should not exceed 2.5. From the translation procedure validation study, it was determined that the accuracy of the translation procedure depends on the irradiance and temperature range of translation. The difference between measured and translatet power at maximum power point (Pmax) is determined to be less than 3% for all the technologies, all the irradiance/ temperature ranges investigated and all the procedures except Procedure 2 of IEC 60891 standard. For the Procedure 2, the difference was found to fall between 3% and 17% depending on the irradiance range used for the translation. The difference of 17% is very large and unacceptable. This work recommends reinvestigating the cause for this large difference for Procedure 2. Finally, a complete power rating matrix for each of the four module technologies has been successfully generated as per IEC 61853-1 draft standard.
ContributorsPaghasian, Karen (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Madakannan, Arunachalandar (Committee member) / Macia, Narciso F. (Committee member) / Arizona State University (Publisher)
Created2010
Description
Building applied photovoltaics (BAPV) is a major application sector for photovoltaics (PV). Due to the negative temperature coefficient of power output, the performance of a PV module decreases as the temperature of the module increases. In hot climatic conditions, such as the summer in Arizona, the operating temperature of a BAPV module can reach as high as 90°C. Considering a typical 0.5%/°C power drop for crystalline silicon (c-Si) modules, a performance decrease of approximately 30% would be expected during peak summer temperatures due to the difference between rated temperature (25°C) and operating temperature (~90°C) of the modules. Also, in a worst-case scenario, such as partial shading of the PV cells of air gap-free BAPV modules, some of the components could attain temperatures that would be high enough to compromise the safety and functionality requirements of the module and its components. Based on the temperature and weather data collected over a year in Arizona, a mathematical thermal model has been developed and presented in this paper to predict module temperature for five different air gaps (0", 1", 2", 3", and 4"). For comparison, modules with a thermally-insulated (R30) back were evaluated to determine the worst-case scenario. This thesis also provides key technical details related to the specially-built, simulated rooftop structure; the mounting configuration of the PV modules on the rooftop structure; the LabVIEW program that was developed for data acquisition and the MATLAB program for developing the thermal models. In order to address the safety issue, temperature test results (obtained in accordance with IEC 61730-2 and UL 1703 safety standards) are presented and analyzed for nine different components of a PV module, i.e., the front glass, substrate/backsheet (polymer), PV cell, j-box ambient, j-box surface, positive terminal, backsheet inside j-box, field wiring, and diode. The temperature test results obtained for about 140 crystalline silicon modules from a large number of manufacturers who tested modules between 2006 and 2009 at ASU/TÜV-PTL were analyzed and presented in this paper under three test conditions, i.e., short-circuit, open-circuit, and short-circuit and shaded. Also, the nominal operating cell temperatures (NOCTs) of the BAPV modules and insulated-back PV modules are presented in this paper for use by BAPV module designers and installers.
ContributorsOh, Jaewon (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Rogers, Bradley R (Committee member) / Macia, Narciso F. (Committee member) / Arizona State University (Publisher)
Created2010
Description
Photovoltaic (PV) modules appear to have three classifications of failure: Infant mortality, normal-life failure, and end-of-life failure. Little is known of the end-of-life failures experienced by PV modules due to their inherent longevity. Accelerated Life Testing (ALT) has been at the crux of this lifespan prediction; however, without naturally failing modules an accurate acceleration factor cannot be determined for use in ALT. By observing modules that have been aged in the field, a comparison can be made with modules undergoing accelerated testing. In this study an investigation on about 1900 aged (10-17 years) grid-tied PV modules installed in the desert climatic condition of Arizona was undertaken. The investigation was comprised of a check sheet that documented any visual defects and their severity, infrared (IR) scanning, and current-voltage (I-V) curve measurements. After data was collected on modules, an analysis was performed to classify the failure modes and to determine the annual performance degradation rates.
ContributorsSuleske, Adam Alfred (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Rogers, Bradley (Committee member) / Macia, Narciso (Committee member) / Arizona State University (Publisher)
Created2010
Description
Solar photovoltaic (PV) generation has seen significant growth in 2021, with an increase of around 22% and exceeding 1000 TWh. However, this has also led to reliability and durability issues, particularly potential induced degradation (PID), which can reduce module output by up to 30%. This study uses cell- and module-level analysis to investigate the impact of superstrate, encapsulant, and substrate on PID.The influence of different substrates and encapsulants is studied using one-cell modules, showing that substrates with poor water-blocking properties can worsen PID, and encapsulants with lower volumetric resistance can conduct easily under damp conditions, enabling PID mechanisms (results show maximum degradation of 9%). Applying an anti-soiling coating on the front glass (superstrate) reduces PID by nearly 53%. Typical superstrates have sodium which accelerates the PID process, and therefore, using such coatings can lessen the PID problem.
At the module level, the study examines the influence of weakened interface adhesion strengths in traditional Glass-Backsheet (GB) and emerging Glass-Glass (GG) (primarily bifacial modules) constructions. The findings show nearly 64% more power degradation in GG modules than in GB. Moreover, the current methods for detecting PID use new modules, which can give inaccurate information instead of DH-stressed modules for PID testing, as done in this work.
A comprehensive PID susceptibility analysis for multiple fresh bifacial constructions shows significant degradation from 20 to 50% in various constructions. The presence of glass as the substrate exacerbates the PID problem due to more ionic activity available from the two glass sides. Recovery experiments are also conducted to understand the extent of the PID issue.
Overall, this study identifies, studies, and explains the impact of superstrate, substrate, and encapsulant on the underlying PID mechanisms. Various pre- and post-stress characterization tests, including light and dark current-voltage (I-V) tests, electroluminescence (EL) imaging, infrared (IR) imaging, and UV fluorescence (UVF) imaging, are used to evaluate the findings. This study is significant as it provides insights into the PID issues in solar PV systems, which can help improve their performance and reliability.
ContributorsMahmood, Farrukh ibne (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Rogers, Bradley (Committee member) / Oh, Jaewon (Committee member) / Rajadas, John (Committee member) / Arizona State University (Publisher)
Created2023
Description
This study introduces a new outdoor accelerated testing method called “Field Accelerated Stress Testing (FAST)” for photovoltaic (PV) modules performed at two
different climatic sites in Arizona (hot-dry) and Florida (hot-humid). FAST is a combined
accelerated test methodology that simultaneously accounts for all the field-specific stresses
and accelerates only key stresses, such as temperature, to forecast the failure modes by 2-
7 times in advance depending on the activation energy of the degradation mechanism (i.e.,
10th year reliability issues can potentially be predicted in the 2nd year itself for an
acceleration factor of 5). In this outdoor combined accelerated stress study, the
temperatures of test modules were increased (by 16-19℃ compared to control modules)
using thermal insulations on the back of the modules. All other conditions (ambient
temperature, humidity, natural sunlight, wind speed, wind direction, and tilt angle) were
left constant for both test modules (with back thermal insulation) and control modules
(without thermal insulation). In this study, a total of sixteen 4-cell modules with two different construction types (glass/glass [GG] and glass/backsheet [GB]) and two different encapsulant types (ethylene
vinyl acetate [EVA] and polyolefin elastomer [POE]), were investigated at both sites with
eight modules at each site (four insulated and four non-insulated modules at each site). All
the modules were extensively characterized before installation in the field and after field
exposure over two years. The methods used for characterizing the devices included I-V
(current-voltage curves), EL (electroluminescence), UVF (ultraviolet fluorescence), and
reflectance. The key findings of this study are: i) the GG modules tend to operate at a higher temperature (1-3℃) than the GB modules at both sites of Arizona and Florida (a lower
lifetime is expected for GG modules compared to GB modules); ii) the GG modules tend
to experience a higher level of encapsulant discoloration and grid finger degradation than
the GB modules at both sites (a higher level of the degradation rate is expected in GG
modules compared to GB modules); and, iii) the EVA-based modules tend to have a higher
level of discoloration and finger degradation compared to the POE-based modules at both
sites.
ContributorsThayumanavan, Rishi Gokul (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Phelan, Patrick (Thesis advisor) / Calhoun, Ronald (Committee member) / Arizona State University (Publisher)
Created2023
Description
Global photovoltaic (PV) module installation in 2018 is estimated to exceed 100 GW, and crystalline Si (c-Si) solar cell-based modules have a share more than 90% of the global PV market. To reduce the social cost of PV electricity, further developments in reliability of solar panels are expected. These will lead to realize longer module lifetime and reduced levelized cost of energy. As many as 86 failure modes are observed in PV modules [1] and series resistance increase is one of the major durability issues of all. Series resistance constitutes emitter sheet resistance, metal-semiconductor contact resistance, and resistance across the metal-solder ribbon. Solder bond degradation at the cell interconnect is one of the primary causes for increase in series resistance, which is also considered to be an invisible defect [1]. Combination of intermetallic compounds (IMC) formation during soldering and their growth due to solid state diffusion over its lifetime result in formation of weak interfaces between the solar cell and the interconnect. Thermal cycling under regular operating conditions induce thermo-mechanical fatigue over these weak interfaces resulting in contact reduction or loss. Contact reduction or loss leads to increase in series resistance which further manifests into power and fill factor loss. The degree of intermixing of metallic interfaces and contact loss depends on climatic conditions as temperature and humidity (moisture ingression into the PV module laminate) play a vital role in reaction kinetics of these layers. Modules from Arizona and Florida served as a good sample set to analyze the effects of hot and humid climatic conditions respectively. The results obtained in the current thesis quantifies the thickness of IMC formation from SEM-EDS profiles, where similar modules obtained from different climatic conditions were compared. The results indicate the thickness of the IMC and detachment degree to be growing with age and operating temperatures of the module. This can be seen in CuxSny IMC which is thicker in the case of Arizona module. The results obtained from FL
ii
aged modules also show that humidity accelerates the formation of IMC as they showed thicker AgxSny layer and weak interconnect-contact interfaces as compared to Arizona modules. It is also shown that climatic conditions have different effects on rate at which CuxSny and AgxSny intermetallic compounds are formed.
ii
aged modules also show that humidity accelerates the formation of IMC as they showed thicker AgxSny layer and weak interconnect-contact interfaces as compared to Arizona modules. It is also shown that climatic conditions have different effects on rate at which CuxSny and AgxSny intermetallic compounds are formed.
ContributorsBuddha, Viswa Sai Pavan (Author) / Tamizhmani, Govindasamy (Thesis advisor) / Alford, Terry (Thesis advisor) / Srinivasan, Devarajan (Committee member) / Arizona State University (Publisher)
Created2018